CN106381005A - Dust-proof paint special for iron craft - Google Patents
Dust-proof paint special for iron craft Download PDFInfo
- Publication number
- CN106381005A CN106381005A CN201610725682.1A CN201610725682A CN106381005A CN 106381005 A CN106381005 A CN 106381005A CN 201610725682 A CN201610725682 A CN 201610725682A CN 106381005 A CN106381005 A CN 106381005A
- Authority
- CN
- China
- Prior art keywords
- parts
- dust
- proof paint
- iron
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a dust-proof paint special for iron craft. The dust-proof paint comprises the following components by weight: 50-70 parts of resin, 30-40 parts of a waterborne polyurethane emulsion, 15-19 parts of nano silica, 2-6 parts of magnesium carbonate, 3-7 parts of sodium alginate, 6-8 parts of dimethyldichlorosilane, 12-17 parts of polyterephthalyl alcohol, 5-9 parts of oxalic acid polyester, 3-8 parts of glass fibre reinforced plastic particles, 1-3 parts of an anti-settling agent, 1-5 parts of a dispersant and 19-25 parts of water. The dust-proof paint prepared by the method provided by the invention has the characteristics of few preparation component, simple preparation process, and good dustproof performance. After coating iron crafts with the dust-proof paint prepared by the invention, in flying dust weather or in factories with a lot of dust, the product surfaces cannot be stained with dust. The dust-proof paint has good quality and stable performance, and has no need for manual wiping.
Description
Technical field
The present invention relates to a kind of coating, specifically a kind of iron handicraft Special dustproof coating.
Background technology
Handicraft, the product being processed raw material, semi-finished product by craft or machine, is to one group of value art work
General name, handicraft derive from life, but create higher than life value；It is people's crystallization of wisdom, fully demonstrates
The creativeness of the mankind and artistry, are the priceless treasures of the mankind.
Handicraft is broadly divided into ceramics, resin craft, iron craftworks and plastic crafts etc., wherein iron
Handicraft is to apply more widely one kind, and pottery iron craftworks usual surface before dispatching from the factory all can scribble one one-tenth painting
Material, but these coating existing are easily stained with dust on surface, need not manually periodically be wiped, and also serious have impact on iron
The outward appearance of handicraft.
Content of the invention
For above-mentioned technical problem, the present invention provides a kind of iron handicraft Special dustproof coating, and prepared composition is few, preparation
Process is simple, anti-dust performance is good, and the dirt resistance coatings that the present invention is prepared are coated in iron handicraft afterwards in airborne dust sky
In gas or the big factory of amount of dust, product surface all will not be stained with dust, and quality is good, and stable performance, without manual wipping.
The technical problem to be solved employs the following technical solutions to realize：
A kind of iron handicraft Special dustproof coating, this dirt resistance coatings is grouped into by the group of following weight portion：Resin 50-70
Part, aqueous polyurethane emulsion 30-40 part, nano silicon 15-19 part, magnesium carbonate 2-6 part, sodium alginate 3-7 part, dimethyl
Dichlorosilane 6-8 part, poly- terephthalyl alcohol 12-17 part, ethanedioic acid polyester 5-9 part, glass steel particles 3-8 part, anti-settling agent 1-3
Part, dispersant 1-5 part and water 19-25 part.
A kind of iron handicraft Special dustproof coating, this dirt resistance coatings is grouped into by the group of following optimum weight part：Resin
60 parts, 35 parts of aqueous polyurethane emulsion, 17 parts of nano silicon, 4 parts of magnesium carbonate, 5 parts of sodium alginate, dimethyldichlorosilane
7 parts, 14 parts of poly- terephthalyl alcohol, 7 parts of ethanedioic acid polyester, 5 parts of glass steel particles, 2 parts of anti-settling agent, 3 parts of dispersant and 22 parts of water.
As a preferred technical solution of the present invention, described water type is deionized water.
As a preferred technical solution of the present invention, described resinous type is epoxy resin.
The invention has the beneficial effects as follows：Compared to existing technology, the dirt resistance coatings preparing by the way, are prepared into
Divide few, preparation process is simple, anti-dust performance is good, after the dirt resistance coatings that the present invention is prepared are coated in iron handicraft
In airborne dust weather or the big factory of amount of dust, product surface all will not be stained with dust, and quality is good, and stable performance need not manually be wiped
Wipe.
Specific embodiment
In order that the technological means of present invention realization and creation characteristic are easy to understand, below the present invention is explained further
State.
Embodiment one：
A kind of iron handicraft Special dustproof coating, this dirt resistance coatings is grouped into by the group of following weight portion：50 parts of resin,
30 parts of aqueous polyurethane emulsion, 15 parts of nano silicon, 2 parts of magnesium carbonate, 3 parts of sodium alginate, 6 parts of dimethyldichlorosilane,
12 parts of poly- terephthalyl alcohol, 5 parts of ethanedioic acid polyester, 3 parts of glass steel particles, 1 part of anti-settling agent, 1 part of dispersant and 19 parts of water.
Described water type is deionized water.
Described resinous type is epoxy resin.
Embodiment two：
A kind of iron handicraft Special dustproof coating, this dirt resistance coatings is grouped into by the group of following weight portion：60 parts of resin,
35 parts of aqueous polyurethane emulsion, 17 parts of nano silicon, 4 parts of magnesium carbonate, 5 parts of sodium alginate, 7 parts of dimethyldichlorosilane,
14 parts of poly- terephthalyl alcohol, 7 parts of ethanedioic acid polyester, 5 parts of glass steel particles, 2 parts of anti-settling agent, 3 parts of dispersant and 22 parts of water.
Described water type is deionized water.
Described resinous type is epoxy resin.
Embodiment three：
A kind of iron handicraft Special dustproof coating, this dirt resistance coatings is grouped into by the group of following weight portion：70 parts of resin,
40 parts of aqueous polyurethane emulsion, 19 parts of nano silicon, 6 parts of magnesium carbonate, 7 parts of sodium alginate, 8 parts of dimethyldichlorosilane,
17 parts of poly- terephthalyl alcohol, 9 parts of ethanedioic acid polyester, 8 parts of glass steel particles, 3 parts of anti-settling agent, 5 parts of dispersant and 25 parts of water.
Described water type is deionized water.
Described resinous type is epoxy resin.
By implementing one, implementing two and implementing three dirt resistance coatings that prepare, compared to existing technology in common coating,
The dirt resistance coatings that the present invention is prepared by above-described embodiment, prepared composition is few, preparation process is simple, and anti-dust performance is good, will
The dirt resistance coatings that the present invention prepares produce after being coated in iron handicraft in airborne dust weather or the big factory of amount of dust
Dust all will not be stained with product surface, and quality is good, and stable performance, without manual wipping.
General principle, principal character and the advantages of the present invention of the present invention have been shown and described above.The technology of the industry
The simply present invention it should be appreciated that the present invention is not restricted to the described embodiments, described in above-described embodiment and specification for the personnel
Principle, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, these change and
Improvement both falls within scope of the claimed invention.Claimed scope is by appending claims and its equivalent
Thing defines.
Claims (4)
1. a kind of iron handicraft Special dustproof coating it is characterised in that：This dirt resistance coatings is grouped into by the group of following weight portion：
Resin 50-70 part, aqueous polyurethane emulsion 30-40 part, nano silicon 15-19 part, magnesium carbonate 2-6 part, sodium alginate 3-7
Part, dimethyldichlorosilane 6-8 part, poly- terephthalyl alcohol 12-17 part, ethanedioic acid polyester 5-9 part, glass steel particles 3-8 part, anti-
Heavy agent 1-3 part, dispersant 1-5 part and water 19-25 part.
2. a kind of iron handicraft Special dustproof coating according to claim 1 it is characterised in that：This dirt resistance coatings by with
The group of lower optimum weight part is grouped into：60 parts of resin, 35 parts of aqueous polyurethane emulsion, 17 parts of nano silicon, magnesium carbonate 4
Part, 5 parts of sodium alginate, 7 parts of dimethyldichlorosilane, 14 parts of poly- terephthalyl alcohol, 7 parts of ethanedioic acid polyester, glass steel particles 5
Part, 2 parts of anti-settling agent, 3 parts of dispersant and 22 parts of water.
3. a kind of iron handicraft Special dustproof coating according to claim 1 and 2 it is characterised in that：Described water class
Type is deionized water.
4. a kind of iron handicraft Special dustproof coating according to claim 1 and 2 it is characterised in that：Described resin
Type is epoxy resin.