CN103194136A - Epoxy self-leveling floor coating and preparation method thereof - Google Patents
Epoxy self-leveling floor coating and preparation method thereof Download PDFInfo
- Publication number
- CN103194136A CN103194136A CN 201310089507 CN201310089507A CN103194136A CN 103194136 A CN103194136 A CN 103194136A CN 201310089507 CN201310089507 CN 201310089507 CN 201310089507 A CN201310089507 A CN 201310089507A CN 103194136 A CN103194136 A CN 103194136A
- Authority
- CN
- China
- Prior art keywords
- component
- epoxy
- percent
- resistance
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of coatings, and particularly relates to an epoxy self-leveling floor coating and a preparation method thereof. The epoxy self-leveling floor coating mainly comprises a component 1 and a component 2, wherein the component 1 comprises the following ingredients by mass percent: 40-45 percent of epoxy resin, 5-15 percent of active diluent, 10-15 percent of pigment, 25-45 percent of packing, 0.5-1 percent of dispersant, 0.5-1 percent of deformer, 0.5-1 percent of flow promoter and 0.2-0.5 percent of anti-sedimentation agent; and the component 2 is a curing agent with equal equivalence to the epoxy resin. The epoxy self-leveling floor coating has good chemical properties of water resistance, oil resistance, acid resistance, alkali resistance and salt fog resistance as well as physical properties of abrasion resistance, punching resistance and washing resistance, is flat, beautiful, easily cleaned and easily repaired and maintained, and can meet all the requirements of modern industrial floor; the coating and the preparation method are coincident with the environmental protection ideas and have no harm on human bodies; and the construction is simple, the curing time does not exceed 24 hours, and the coating and the preparation method thereof have a wide application prospect.
Description
Technical field
The present invention relates to paint field, specifically is a kind of epoxy self-leveling floor coating and preparation method thereof.
Background technology
Modern industry has various requirement to terrace, and as electronics, industrial requirements terraces such as food, medicine do not play ash, and is totally dustless; Mechanical industry requires the anti-strong mechanical shock of terrace, wear-resistant, the roll off that can stand vehicle such as forklift for a long time; Industrial plant such as lathe, instrument, instrument often are subjected to various oils infiltrations, are difficult to thorough removing, require the terrace oil-proofness good; Chemical industry then requires the corrosion of the various chemical mediators of Horizon ability.Shortcomings separately such as terrace protecting materials commonly used such as sand-cement slurry, terrazzo, grouan are difficult to satisfy the requirement of modern industrialization.
Summary of the invention
The invention provides a kind of epoxy self-leveling floor coating that can be widely used in all trades and professions of environmental protection, it mainly is made up of first, component B.Wherein, described first component comprises the following composition that accounts for first component mass percent:
Resins, epoxy 40-45%;
Reactive thinner 5-15%;
Pigment 10-15%;
Filler 25-45%;
Dispersion agent 0.5-1%;
Defoamer 0.5-1%;
Flow agent 0.5-1%;
Anti-settling agent 0.2-0.5%;
Described component B is the solidifying agent with the Resins, epoxy equivalent.
Further improve, the Resins, epoxy in the described first component is SM828; Reactive thinner is 660; Pigment is mineral dye; Filler is one or more in calcium carbonate, talcum powder and the silica powder; Dispersion agent is German BYK 163; Flow agent is BYK 354; Defoamer is BYK A530: anti-settling agent is aerosil.
Further improve, the solidifying agent in the described component B is cashew nut oil modified solidifying agent 3182.
The present invention also provides a kind of preparation method of epoxy self-leveling floor coating: reactive thinner and Resins, epoxy are mixed, add dispersion machine, treat that resin dispersion evenly after, add various auxiliary agents, be uniformly dispersed then, add quantitative pigment and filler, high speed dispersion is even, carry out sand milling through sand mill again, up to fineness≤30 μ m, get final product discharging, make the first component this moment, in the first component, add component B again, leave standstill for some time froth breaking after, can make described epoxy self-leveling floor coating.
Beneficial effect of the present invention is:
1, have excellent water tolerance. physical property such as chemical property such as oil-proofness, acidproof, alkali resistance and salt air corrosion and wear resistance, anti-stampability, abrasion resistance, and smooth, beautiful, do not crack, do not rise ash, easy cleaning, easy-maintaining maintenance, almost can satisfy modern industry to whole needs of terrace.
2, meet environmental protection concept, be a kind of environmental protection coating material, harmless.
3, construction is simple, is no more than 24 hours set time, has broad prospect of application.
Embodiment
Embodiment 1
8.3kg reactive thinner 660 and 2kg Resins, epoxy SM828 are mixed, add 0.2kg BYK 163, after treating that resin dispersion evenly, add 0.2kg BYK 354,0.2kg BYK A530,0.1kg aerosil, be uniformly dispersed then, add 2kg mineral dye and 7kg calcium carbonate, high speed dispersion is even, carry out sand milling through sand mill again, up to fineness≤30 μ m, get final product discharging, make the first component this moment, add the cashew nut oil modified solidifying agent 3182 with Resins, epoxy SM828 equivalent again in the first component, leave standstill for some time froth breaking after, can make described epoxy self-leveling floor coating.
High Solid paint performance test according to embodiment 1 preparation is as follows:
Former lacquer outward appearance: no foreign matter, no lump easily stirs into viscous liquid.
Paint film color and outward appearance: meet the requirement of model aberration, smooth smooth.
Fineness: 10 μ m.
Viscosity, (being coated with-4), s:60-80%.
Time of drying: surface drying≤8h does solid work≤24h.
Hardness (pencil) 〉=3H.
Sticking power :≤1 grade.
Gloss (60 °): 〉=95%.
Shock-resistance: 〉=50cm.
Snappiness≤1 grade.
Acid resistance (immerses 20%H
2SO
472h in the solution): non-foaming, do not come off non-corrosive.
Alkali resistance (immerses 20%H
a72h in the OH solution):, non-foaming, do not come off non-corrosive.
Oil-proofness (immersing 48h in the machine oil): outward appearance does not have considerable change, and is non-foaming, do not come off.
Water tolerance (240h): non-foaming, non-corrosive allows slight look to become and loss of gloss.
Embodiment 2
8kg reactive thinner 660 and 2kg Resins, epoxy SM828 are mixed, add 0.1kg and divide BYK 163, after treating that resin dispersion evenly, add 0.1kg BYK 354,0.1kg BYK A530,0.1kg aerosil, be uniformly dispersed then, add 2kg mineral dye and 7kg calcium carbonate, high speed dispersion is even, carry out sand milling through sand mill again, up to fineness≤30 μ m, get final product discharging, make the first component this moment, add the cashew nut oil modified solidifying agent 3182 with Resins, epoxy SM828 equivalent again in the first component, leave standstill for some time froth breaking after, can make described epoxy self-leveling floor coating.
Embodiment 3
9 kg reactive thinners 660 and 1kg Resins, epoxy SM828 are mixed, add 0.1kg BYK 163, after treating that resin dispersion evenly, add 0.1kg BYK 354,0.1kg BYK A530,0.1kg aerosil, be uniformly dispersed then, add 3kg mineral dye and 6kg silica powder, high speed dispersion is even, carry out sand milling through sand mill again, up to fineness≤30 μ m, get final product discharging, make the first component this moment, add the cashew nut oil modified solidifying agent 3182 with Resins, epoxy SM828 equivalent again in the first component, leave standstill for some time froth breaking after, can make described epoxy self-leveling floor coating.
The concrete application approach of the present invention is a lot, and the above only is preferred implementation of the present invention, should be understood that; for those skilled in the art; under the prerequisite that does not break away from the principle of the invention, can also make some improvement, these improvement also should be considered as protection scope of the present invention.
Claims (4)
1. epoxy self-leveling floor coating, it is characterized in that: be made up of first, component B, wherein, described first component comprises the following composition that accounts for first component mass percent:
Resins, epoxy 40-45%;
Reactive thinner 5-15%;
Pigment 10-15%;
Filler 25-45%;
Dispersion agent 0.5-1%;
Defoamer 0.5-1%;
Flow agent 0.5-1%;
Anti-settling agent 0.2-0.5%;
Described component B is the solidifying agent with the Resins, epoxy equivalent.
2. a kind of epoxy self-leveling floor coating according to claim 1, it is characterized in that: the Resins, epoxy in the described first component is SM828; Reactive thinner is 660; Pigment is mineral dye; Filler is one or more in calcium carbonate, talcum powder and the silica powder; Dispersion agent is German BYK 163; Flow agent is BYK 354; Defoamer is BYK A530: anti-settling agent is aerosil.
3. a kind of epoxy self-leveling floor coating according to claim 1, it is characterized in that: the solidifying agent in the described component B is cashew nut oil modified solidifying agent 3182.
4. one kind prepares the described method of claim 1, it is characterized in that: reactive thinner and Resins, epoxy are mixed, add dispersion machine, after treating that resin dispersion evenly, add various auxiliary agents, be uniformly dispersed then, add pigment and filler, high speed dispersion is even, carries out sand milling through sand mill again, up to fineness≤30 μ m, get final product discharging, make the first component this moment, adds component B again in the first component, after leaving standstill for some time froth breaking, can make described epoxy self-leveling floor coating.