CN108707397A - A kind of dust-proof coating on plastic plate - Google Patents
A kind of dust-proof coating on plastic plate Download PDFInfo
- Publication number
- CN108707397A CN108707397A CN201810554988.4A CN201810554988A CN108707397A CN 108707397 A CN108707397 A CN 108707397A CN 201810554988 A CN201810554988 A CN 201810554988A CN 108707397 A CN108707397 A CN 108707397A
- Authority
- CN
- China
- Prior art keywords
- parts
- dust
- plastic plate
- proof coating
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of dust-proof coating on plastic plate, is related to plastic processing production technical field, it is characterised in that：Material including following parts by weight is made, 14-20 parts of resin, 1-4 parts of lithium metasilicate, 1-5 parts of isophorone diamine, 9-13 parts of modified wollastonite powder, 2-5 parts of Isooctyl acrylate monomer, 2-5 parts of aromatic urethane propylene acid esters, 1-4 parts of inositol hexaphosphate, 1-5 parts of lemon juice, 4-8 parts of Coconut Fatty Acid Monoethanolamide, 4-8 parts of polyethylene glycol octyl phenylate, 7-12 parts of anti-aging agent, 9-14 parts of biological agent, 30-35 parts of deionized water.The method of the present invention is reasonable, easy to implement, amount of dust is low in a short time and has heat resistance.
Description
Technical field
The present invention relates to plastic processing production technical fields, and in particular to the dust-proof coating on a kind of plastic plate.
Background technology
Plastics are to pass through high-molecular compound made of addition polymerization or polycondensation polymerized using monomer as raw material
(macromolecules), it is commonly called as plastics (plastics) or resin (resin), can freely change ingredient and body styles,
It is made of the additives such as synthetic resin and filler, plasticizer, stabilizer, lubricant, colorant.
The main component of plastics is resin.This noun of resin is initially the lipid secreted out of by animals and plants and gains the name, such as
Rosin, shellac etc., resin refer to the high-molecular compound not yet mixed with various additives.Resin accounts for about plastics total weight
40%~100%.The basic performance of plastics depends mainly on the person's character of resin, but additive also plays an important role.Some modelings
Material is substantially made of synthetic resin, and additive, such as organic glass, polystyrene are free of or contain less.
Plastics, it is one kind in synthetic resin in fact, and shape is similar with the pine resin in natural resin, by chemical hand
Duan Jinhang is artificial synthesized, and is referred to as plastics.
And the performance of the dust protection of present plastics is all not particularly good, and be frequently necessary to wipe, and dust heap
It is easy to impact to using after product is too many, and cannot have within the time limit of certain short-term in processing of some plastics
More dusts, but such plastics are particularly few.
Invention content
Technical problem to be solved by the present invention lies in overcome existing technological deficiency provide a kind of method rationally, embodiment party
Just, in a short time amount of dust it is low and with heat resistance a kind of plastic plate on dust-proof coating.
The technical problems to be solved by the invention are realized using technical solution below：
A kind of dust-proof coating on plastic plate, it is characterised in that：Material including following parts by weight is made,
14-20 parts of resin, 1-4 parts of lithium metasilicate, 1-5 parts of isophorone diamine, 9-13 parts of modified wollastonite powder, acrylic acid are different
2-5 parts of monooctyl ester, 2-5 parts of aromatic urethane propylene acid esters, 1-4 parts of inositol hexaphosphate, 1-5 parts of lemon juice, coconut oil list second
4-8 parts of alkylolamides, 4-8 parts of polyethylene glycol octyl phenylate, 7-12 parts of anti-aging agent, 9-14 parts of biological agent, 30-35 parts of deionized water；
The resin is E-12 epoxy resin, amino resins, polyamide, vinyl ester resin, bismaleimide
One kind in resin；
The anti-aging agent includes one kind in anti-aging agent RD, antioxidant A, antioxidant D, anti-aging agent CPPD, antioxidant A W；
The preparation method of the modified wollastonite powder is：Wollastonite is ground to and crossed 300-400 mesh sieve, is then added
Methyl tributanoximo silane is stirred 10min at normal temperatures, then heats to 80-85 DEG C of heat preservation grinding 30min, adds water
The solution that solid content reaches 25-35% is made in stirring, and gained mixed liquor is sent into dry in spray dryer, obtained 20-40 purposes
Spheric granules, and dried at 100-110 DEG C；
The weight part ratio of the methyl tributanoximo silane and wollastonite is 1：3.2；
The biological agent includes that the material of following parts by weight is made,
1 part of talcum, 2 parts of fructus amomi, 3 parts of sealwort, 4 parts of curcuma zedoary, 5 parts of Caulis Spatholobi, 6 parts of calamine, 1 part of borneol, 2 parts of tortoiseshell,
3 parts of amber, 4 parts of concha mauritiae, 5 parts of cinnabar, 6 parts of Poria cocos；
Preparation method is：Above-mentioned material is placed in 85-95 DEG C of drying equipment and is tiled, 4-5 hour is then dried,
It is then placed in milling apparatus and is ground into powder；
The preparation method of dust-proof coating on a kind of plastic plate includes：Above-mentioned material is sequentially placed into reaction kettle
In be uniformly mixed, be warming up to 150-200 DEG C, insulated and stirred 3-5h obtains mixture, then cools to 100-150 DEG C, mixing is stirred
It mixes to the formation preferable slurry of mobility.
Beneficial effects of the present invention are：The coating used can apply multilayer, and can mix and make with other japannings, coating etc.
With, thus enhanced convenience, and the wear-resisting, heat-resisting of product, corrosion-resistant performance are all very good, and with good anti-
The performance of water, it will be able to guarantee be not in due to bubble, vapor and occur fold, cracking, fracture the problems such as, and
And bond properties, the wear-resisting property of product are very good, and the biological assistant used can play the role of neutralizing a toxin, in this way
Just human body is not just injured, and contain a large amount of mineral in biological assistant all without toxin when production, use
Matter etc. can increase the hardness and strength of product, increase the service life of product；And contain a large amount of cleaning member in product
Element can improve the smooth degree of plastic product surface and reduce the adsorption rate of dust after the process.Product energy of the present invention
It being enough on a variety of basic materials, coating is with a wide range of features, and few, at low cost, the nontoxic no side reaction of material consumption, processability is good,
Molding is easy.
Specific implementation mode
In order to make the technical means, the creative features, the aims and the efficiencies achieved by the present invention be easy to understand, below into
One step illustrates the present invention.
Embodiment 1
A kind of dust-proof coating on plastic plate, it is characterised in that：Material including following parts by weight is made,
14 parts of resin, 1 part of lithium metasilicate, 1 part of isophorone diamine, 9 parts of modified wollastonite powder, 2 parts of Isooctyl acrylate monomer, virtue
Fragrant 2 parts of adoption urethane propylene acid esters, 1 part of inositol hexaphosphate, 1 part of lemon juice, 4 parts of Coconut Fatty Acid Monoethanolamide, polyethylene glycol
4 parts of octyl phenylate, 7 parts of anti-aging agent, 9 parts of biological agent, 30 parts of deionized water；
The resin is E-12 epoxy resin, amino resins, polyamide, vinyl ester resin, bismaleimide
One kind in resin；
The anti-aging agent includes one kind in anti-aging agent RD, antioxidant A, antioxidant D, anti-aging agent CPPD, antioxidant A W；
The preparation method of the modified wollastonite powder is：Wollastonite is ground to and crossed 300-400 mesh sieve, is then added
Methyl tributanoximo silane is stirred 10min at normal temperatures, then heats to 80-85 DEG C of heat preservation grinding 30min, adds water
The solution that solid content reaches 25-35% is made in stirring, and gained mixed liquor is sent into dry in spray dryer, obtained 20-40 purposes
Spheric granules, and dried at 100-110 DEG C；
The weight part ratio of the methyl tributanoximo silane and wollastonite is 1：3.2；
The biological agent includes that the material of following parts by weight is made,
1 part of talcum, 2 parts of fructus amomi, 3 parts of sealwort, 4 parts of curcuma zedoary, 5 parts of Caulis Spatholobi, 6 parts of calamine, 1 part of borneol, 2 parts of tortoiseshell,
3 parts of amber, 4 parts of concha mauritiae, 5 parts of cinnabar, 6 parts of Poria cocos；
Preparation method is：Above-mentioned material is placed in 85-95 DEG C of drying equipment and is tiled, 4-5 hour is then dried,
It is then placed in milling apparatus and is ground into powder；
The preparation method of dust-proof coating on a kind of plastic plate includes：Above-mentioned material is sequentially placed into reaction kettle
In be uniformly mixed, be warming up to 150-200 DEG C, insulated and stirred 3-5h obtains mixture, then cools to 100-150 DEG C, mixing is stirred
It mixes to the formation preferable slurry of mobility.
Embodiment 2
A kind of dust-proof coating on plastic plate, it is characterised in that：Material including following parts by weight is made,
20 parts of resin, 4 parts of lithium metasilicate, 5 parts of isophorone diamine, 13 parts of modified wollastonite powder, 5 parts of Isooctyl acrylate monomer,
5 parts of aromatic urethane propylene acid esters, 4 parts of inositol hexaphosphate, 5 parts of lemon juice, 8 parts of Coconut Fatty Acid Monoethanolamide, poly- second two
8 parts of alcohol octyl phenylate, 12 parts of anti-aging agent, 14 parts of biological agent, 35 parts of deionized water；
The resin is E-12 epoxy resin, amino resins, polyamide, vinyl ester resin, bismaleimide
One kind in resin；
The anti-aging agent includes one kind in anti-aging agent RD, antioxidant A, antioxidant D, anti-aging agent CPPD, antioxidant A W；
The preparation method of the modified wollastonite powder is：Wollastonite is ground to and crossed 300-400 mesh sieve, is then added
Methyl tributanoximo silane is stirred 10min at normal temperatures, then heats to 80-85 DEG C of heat preservation grinding 30min, adds water
The solution that solid content reaches 25-35% is made in stirring, and gained mixed liquor is sent into dry in spray dryer, obtained 20-40 purposes
Spheric granules, and dried at 100-110 DEG C；
The weight part ratio of the methyl tributanoximo silane and wollastonite is 1：3.2；
The biological agent includes that the material of following parts by weight is made,
1 part of talcum, 2 parts of fructus amomi, 3 parts of sealwort, 4 parts of curcuma zedoary, 5 parts of Caulis Spatholobi, 6 parts of calamine, 1 part of borneol, 2 parts of tortoiseshell,
3 parts of amber, 4 parts of concha mauritiae, 5 parts of cinnabar, 6 parts of Poria cocos；
Preparation method is：Above-mentioned material is placed in 85-95 DEG C of drying equipment and is tiled, 4-5 hour is then dried,
It is then placed in milling apparatus and is ground into powder；
The preparation method of dust-proof coating on a kind of plastic plate includes：Above-mentioned material is sequentially placed into reaction kettle
In be uniformly mixed, be warming up to 150-200 DEG C, insulated and stirred 3-5h obtains mixture, then cools to 100-150 DEG C, mixing is stirred
It mixes to the formation preferable slurry of mobility.
Embodiment 3
A kind of dust-proof coating on plastic plate, it is characterised in that：Material including following parts by weight is made,
16 parts of resin, 2 parts of lithium metasilicate, 3 parts of isophorone diamine, 11 parts of modified wollastonite powder, 4 parts of Isooctyl acrylate monomer,
3 parts of aromatic urethane propylene acid esters, 3 parts of inositol hexaphosphate, 3 parts of lemon juice, 6 parts of Coconut Fatty Acid Monoethanolamide, poly- second two
6 parts of alcohol octyl phenylate, 8 parts of anti-aging agent, 12 parts of biological agent, 34 parts of deionized water；
The resin is E-12 epoxy resin, amino resins, polyamide, vinyl ester resin, bismaleimide
One kind in resin；
The anti-aging agent includes one kind in anti-aging agent RD, antioxidant A, antioxidant D, anti-aging agent CPPD, antioxidant A W；
The preparation method of the modified wollastonite powder is：Wollastonite is ground to and crossed 300-400 mesh sieve, is then added
Methyl tributanoximo silane is stirred 10min at normal temperatures, then heats to 80-85 DEG C of heat preservation grinding 30min, adds water
The solution that solid content reaches 25-35% is made in stirring, and gained mixed liquor is sent into dry in spray dryer, obtained 20-40 purposes
Spheric granules, and dried at 100-110 DEG C；
The weight part ratio of the methyl tributanoximo silane and wollastonite is 1：3.2；
The biological agent includes that the material of following parts by weight is made,
1 part of talcum, 2 parts of fructus amomi, 3 parts of sealwort, 4 parts of curcuma zedoary, 5 parts of Caulis Spatholobi, 6 parts of calamine, 1 part of borneol, 2 parts of tortoiseshell,
3 parts of amber, 4 parts of concha mauritiae, 5 parts of cinnabar, 6 parts of Poria cocos；
Preparation method is：Above-mentioned material is placed in 85-95 DEG C of drying equipment and is tiled, 4-5 hour is then dried,
It is then placed in milling apparatus and is ground into powder；
The preparation method of dust-proof coating on a kind of plastic plate includes：Above-mentioned material is sequentially placed into reaction kettle
In be uniformly mixed, be warming up to 150-200 DEG C, insulated and stirred 3-5h obtains mixture, then cools to 100-150 DEG C, mixing is stirred
It mixes to the formation preferable slurry of mobility.
A kind of coating on plastic plate, it is characterised in that：Material including following parts by weight is made,
16 parts of polyvinyl resin, 3 parts of isophorone diamine, 11 parts of wollastonite in powder, 4 parts of Isooctyl acrylate monomer, fragrant adoption
3 parts of urethane propylene acid esters, 8 parts of antioxidant A, 34 parts of water；
Preparation method：Above-mentioned material is put into reaction kettle, 40-50 points are stirred in 110-120 DEG C of temperature
Clock is then pressed into three-roller, is ground into powder.
By experiment, the performance and effect of 1-3 of the embodiment of the present invention and comparative example, such as following table are measured：
Continuing the cleaning time is counted after using that day to carry out conventional cleaning in finger, and the adhesive rate of product dust is less than 5-
9%.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (2)
1. the dust-proof coating on a kind of plastic plate, it is characterised in that：Material including following parts by weight is made,
14-20 parts of resin, 1-4 parts of lithium metasilicate, 1-5 parts of isophorone diamine, 9-13 parts of modified wollastonite powder, Isooctyl acrylate monomer
2-5 parts, 2-5 parts of aromatic urethane propylene acid esters, 1-4 parts of inositol hexaphosphate, 1-5 parts of lemon juice, coconut oil monoethanol acyl
4-8 parts of amine, 4-8 parts of polyethylene glycol octyl phenylate, 7-12 parts of anti-aging agent, 9-14 parts of biological agent, 30-35 parts of deionized water.
2. the dust-proof coating on a kind of plastic plate according to claim 1, it is characterised in that：A kind of plastic plate
On the preparation method of dust-proof coating include：Above-mentioned material is sequentially placed into reaction kettle and is uniformly mixed, 150-200 is warming up to
DEG C, insulated and stirred 3-5h obtains mixture, then cools to 100-150 DEG C, mixes to form mobility and preferably starch
Body.