CN106366858A - Movable shear edge - Google Patents
Movable shear edge Download PDFInfo
- Publication number
- CN106366858A CN106366858A CN201610778237.1A CN201610778237A CN106366858A CN 106366858 A CN106366858 A CN 106366858A CN 201610778237 A CN201610778237 A CN 201610778237A CN 106366858 A CN106366858 A CN 106366858A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- weight portion
- protective paint
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a movable shear edge. The surface of a metal body is coated with protective paint. The protective paint is prepared through the following steps that 1, by weight, 1-2 parts of silicon dioxide, 0.2 part of titanium dioxide, 1.2 parts of alkyl sodium sulfonate, 2.3 parts of hexyldecanol and 8 parts of modified waterborne epoxy resin emulsion are sequentially added into 20 parts of deionized water and stirred to be uniform; 2, by weight, 11 parts of bisphenol A type epoxy resin, 0.6 part of HD1 biuret, 1.3 parts of polyoxyethylene stearate, 0.8 part of N-phenyl-2-naphthylamine and 1.1 parts of benzotriazole are sequentially added and continue to be stirred till sufficient and uniform mixing is achieved, and the protective paint is obtained. According to the movable shear edge, the surface of the metal body is coated with the protective paint, and it is ensured that the movable shear edge can be used for a long time.
Description
Technical field
The present invention relates to a kind of activity cutting edge.
Background technology
Existing activity cutting edge, the heat-resisting, antioxidation of its metal master, antirust, decay resistance have much room for improvement, impact activity
The life-time service of cutting edge.
Content of the invention
It is an object of the invention to provide a kind of activity cutting edge, its metal body surface is coated with protective paint, makes metal master
Body has excellent heat-resisting, antioxidation, antirust, decay resistance, thus Support activity cutting edge energy life-time service.
For achieving the above object, the technical scheme is that a kind of design activity cutting edge, including metal master, this metal
Body surfaces are covered with protective paint, and described protective paint is made by the steps:
1) by 1～2 parts by weight of silica, 0.2 parts by weight of titanium dioxide, 1.2 weight portion sodium alkyl sulfonates, 2.3 weight
Part hexyldecanol, 8 part by weight modified aqueous epoxy resin emulsions put in 20 parts by weight of deionized water successively, stir；
2) 11 parts by weight of bisphenol a type epoxy resin, 0.6 weight portion hdl biuret, 1.3 weight portion Hard Fat are put into again successively
Sour polyoxyethylene ester, 0.8 weight portion n- phenyl-2-naphthylamine, 1.1 weight portion BTAs, continue stirring, equal to being sufficiently mixed
Even, prepared protective paint.
Preferably, movable cutting edge, including metal master, this metal body surface is covered with protective paint, and described protective paint leads to
Cross following steps to prepare:
1) will be own to 1 parts by weight of silica, 0.2 parts by weight of titanium dioxide, 1.2 weight portion sodium alkyl sulfonates, 2.3 weight portions
Base decanol, 8 part by weight modified aqueous epoxy resin emulsions put in 20 parts by weight of deionized water successively, stir；
2) 11 parts by weight of bisphenol a type epoxy resin, 0.6 weight portion hdl biuret, 1.3 weight portion Hard Fat are put into again successively
Sour polyoxyethylene ester, 0.8 weight portion n- phenyl-2-naphthylamine, 1.1 weight portion BTAs, continue stirring, equal to being sufficiently mixed
Even, prepared protective paint.
Preferably, movable cutting edge, including metal master, this metal body surface is covered with protective paint, and described protective paint leads to
Cross following steps to prepare:
1) will be own to 2 parts by weight of silica, 0.2 parts by weight of titanium dioxide, 1.2 weight portion sodium alkyl sulfonates, 2.3 weight portions
Base decanol, 8 part by weight modified aqueous epoxy resin emulsions put in 20 parts by weight of deionized water successively, stir；
2) 11 parts by weight of bisphenol a type epoxy resin, 0.6 weight portion hdl biuret, 1.3 weight portion Hard Fat are put into again successively
Sour polyoxyethylene ester, 0.8 weight portion n- phenyl-2-naphthylamine, 1.1 weight portion BTAs, continue stirring, equal to being sufficiently mixed
Even, prepared protective paint.
Preferably, movable cutting edge, including metal master, this metal body surface is covered with protective paint, and described protective paint leads to
Cross following steps to prepare:
1) by 1.2 parts by weight of silica, 0.2 parts by weight of titanium dioxide, 1.2 weight portion sodium alkyl sulfonates, 2.3 weight portions
Hexyldecanol, 8 part by weight modified aqueous epoxy resin emulsions put in 20 parts by weight of deionized water successively, stir；
2) 11 parts by weight of bisphenol a type epoxy resin, 0.6 weight portion hdl biuret, 1.3 weight portion Hard Fat are put into again successively
Sour polyoxyethylene ester, 0.8 weight portion n- phenyl-2-naphthylamine, 1.1 weight portion BTAs, continue stirring, equal to being sufficiently mixed
Even, prepared protective paint.
Advantages of the present invention and having the beneficial effects that: provide a kind of activity cutting edge, its metal body surface is coated with protection
Paint, makes metal master have excellent heat-resisting, antioxidation, antirust, decay resistance, thus Support activity cutting edge can make for a long time
With.
The performance of " protective paint " and purposes are determined by its component and proportioning, and the different component meeting in " protective paint "
Influence each other, component and its proportioning can determine the final performance of " protective paint ", such as fruit component and its proportioning be not mutually coordinated, single
The beneficial effect that component is brought, even can be eliminated by other components abatement, when serious, different component is mutually conflicted, and rises
Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " protection
The optimal component of paint " and proportioning so that multiple component combine, mutually coordinated and produce positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Movable cutting edge, including metal master, this metal body surface is covered with protective paint, and described protective paint passes through following walking
Rapid preparation:
1) by 1～2 parts by weight of silica, 0.2 parts by weight of titanium dioxide, 1.2 weight portion sodium alkyl sulfonates, 2.3 weight
Part hexyldecanol, 8 part by weight modified aqueous epoxy resin emulsions put in 20 parts by weight of deionized water successively, stir；
2) 11 parts by weight of bisphenol a type epoxy resin, 0.6 weight portion hdl biuret, 1.3 weight portion Hard Fat are put into again successively
Sour polyoxyethylene ester, 0.8 weight portion n- phenyl-2-naphthylamine, 1.1 weight portion BTAs, continue stirring, equal to being sufficiently mixed
Even, prepared protective paint.
Embodiment 2
Movable cutting edge, including metal master, this metal body surface is covered with protective paint, and described protective paint passes through following walking
Rapid preparation:
1) will be own to 1 parts by weight of silica, 0.2 parts by weight of titanium dioxide, 1.2 weight portion sodium alkyl sulfonates, 2.3 weight portions
Base decanol, 8 part by weight modified aqueous epoxy resin emulsions put in 20 parts by weight of deionized water successively, stir；
2) 11 parts by weight of bisphenol a type epoxy resin, 0.6 weight portion hdl biuret, 1.3 weight portion Hard Fat are put into again successively
Sour polyoxyethylene ester, 0.8 weight portion n- phenyl-2-naphthylamine, 1.1 weight portion BTAs, continue stirring, equal to being sufficiently mixed
Even, prepared protective paint.
Embodiment 3
Movable cutting edge, including metal master, this metal body surface is covered with protective paint, and described protective paint passes through following walking
Rapid preparation:
1) will be own to 2 parts by weight of silica, 0.2 parts by weight of titanium dioxide, 1.2 weight portion sodium alkyl sulfonates, 2.3 weight portions
Base decanol, 8 part by weight modified aqueous epoxy resin emulsions put in 20 parts by weight of deionized water successively, stir；
2) 11 parts by weight of bisphenol a type epoxy resin, 0.6 weight portion hdl biuret, 1.3 weight portion Hard Fat are put into again successively
Sour polyoxyethylene ester, 0.8 weight portion n- phenyl-2-naphthylamine, 1.1 weight portion BTAs, continue stirring, equal to being sufficiently mixed
Even, prepared protective paint.
Embodiment 4
Movable cutting edge, including metal master, this metal body surface is covered with protective paint, and described protective paint passes through following walking
Rapid preparation:
1) by 1.2 parts by weight of silica, 0.2 parts by weight of titanium dioxide, 1.2 weight portion sodium alkyl sulfonates, 2.3 weight portions
Hexyldecanol, 8 part by weight modified aqueous epoxy resin emulsions put in 20 parts by weight of deionized water successively, stir；
2) 11 parts by weight of bisphenol a type epoxy resin, 0.6 weight portion hdl biuret, 1.3 weight portion Hard Fat are put into again successively
Sour polyoxyethylene ester, 0.8 weight portion n- phenyl-2-naphthylamine, 1.1 weight portion BTAs, continue stirring, equal to being sufficiently mixed
Even, prepared protective paint.
The movable cutting edge of the various embodiments described above, its metal body surface is coated with protective paint, so that metal master is had excellent
Heat-resisting, antioxidation, antirust, decay resistance, thus Support activity cutting edge energy life-time service.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. it is characterised in that including metal master, this metal body surface is covered with protective paint to a kind of activity cutting edge, described anti-
Vernix is made by the steps:
1) will be own to 1～2 parts by weight of silica, 0.2 parts by weight of titanium dioxide, 1.2 weight portion sodium alkyl sulfonates, 2.3 weight portions
Base decanol, 8 part by weight modified aqueous epoxy resin emulsions put in 20 parts by weight of deionized water successively, stir；
2) put into successively again 11 parts by weight of bisphenol a type epoxy resin, 0.6 weight portion hdl biuret, 1.3 weight portion stearic acid gather
Oxygen vinyl acetate, 0.8 weight portion n- phenyl-2-naphthylamine, 1.1 weight portion BTAs, continue stirring, uniform to being sufficiently mixed,
Prepared protective paint.
2. it is characterised in that including metal master, this metal body surface covers activity cutting edge according to claim 1
There is protective paint, described protective paint is made by the steps:
1) by 1 parts by weight of silica, 0.2 parts by weight of titanium dioxide, 1.2 weight portion sodium alkyl sulfonates, the 2.3 weight portion hexyl last of the ten Heavenly stems
Alcohol, 8 part by weight modified aqueous epoxy resin emulsions put in 20 parts by weight of deionized water successively, stir；
2) put into successively again 11 parts by weight of bisphenol a type epoxy resin, 0.6 weight portion hdl biuret, 1.3 weight portion stearic acid gather
Oxygen vinyl acetate, 0.8 weight portion n- phenyl-2-naphthylamine, 1.1 weight portion BTAs, continue stirring, uniform to being sufficiently mixed,
Prepared protective paint.
3. it is characterised in that including metal master, this metal body surface covers activity cutting edge according to claim 1
There is protective paint, described protective paint is made by the steps:
1) by 2 parts by weight of silica, 0.2 parts by weight of titanium dioxide, 1.2 weight portion sodium alkyl sulfonates, the 2.3 weight portion hexyl last of the ten Heavenly stems
Alcohol, 8 part by weight modified aqueous epoxy resin emulsions put in 20 parts by weight of deionized water successively, stir；
2) put into successively again 11 parts by weight of bisphenol a type epoxy resin, 0.6 weight portion hdl biuret, 1.3 weight portion stearic acid gather
Oxygen vinyl acetate, 0.8 weight portion n- phenyl-2-naphthylamine, 1.1 weight portion BTAs, continue stirring, uniform to being sufficiently mixed,
Prepared protective paint.
4. it is characterised in that including metal master, this metal body surface covers activity cutting edge according to claim 1
There is protective paint, described protective paint is made by the steps:
1) by 1.2 parts by weight of silica, 0.2 parts by weight of titanium dioxide, 1.2 weight portion sodium alkyl sulfonates, 2.3 weight portion hexyls
Decanol, 8 part by weight modified aqueous epoxy resin emulsions put in 20 parts by weight of deionized water successively, stir；
2) put into successively again 11 parts by weight of bisphenol a type epoxy resin, 0.6 weight portion hdl biuret, 1.3 weight portion stearic acid gather
Oxygen vinyl acetate, 0.8 weight portion n- phenyl-2-naphthylamine, 1.1 weight portion BTAs, continue stirring, uniform to being sufficiently mixed,
Prepared protective paint.