CN107629606A - A kind of high resistance chromium nickel electrothermal alloy - Google Patents
A kind of high resistance chromium nickel electrothermal alloy Download PDFInfo
- Publication number
- CN107629606A CN107629606A CN201711102576.9A CN201711102576A CN107629606A CN 107629606 A CN107629606 A CN 107629606A CN 201711102576 A CN201711102576 A CN 201711102576A CN 107629606 A CN107629606 A CN 107629606A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- main body
- treatment liquid
- coating treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high resistance chromium nickel electrothermal alloy, it includes nichrome main body, and the nichrome main body passes through aluminum coated steel, and the aluminum coated steel comprises the following steps:1)1~2 parts by weight fatty alcohol polyoxyethylene ether sulfate, 5.8 parts by weight of lemon acid, 2.6 parts by weight diethylene glycol phenyl ethers, 4.3 parts by weight bipentaerythrites are put into 52 parts by weight of deionized water successively, stirred;2)Put into 1.3 parts by weight ammonium titanium fluorides, 2.4 parts by weight of polypropylene acid sodium, 3.5 parts by weight triethanolamine oleates, 1.7 parts by weight hexamethylenetetramines successively again, continue to stir, to being sufficiently mixed uniformly, coating treatment liquid is made;3)Nichrome main body is inserted in coating treatment liquid and impregnated, is dried after taking-up.High resistance chromium nickel electrothermal alloy of the present invention, its nichrome body surfaces are covered with protecting film, and performance is good, and surface smoothness is good.
Description
Technical field
The present invention relates to a kind of high resistance chromium nickel electrothermal alloy.
Background technology
Existing high resistance chromium nickel electrothermal alloy, it is the abrasion-resistant of its nichrome main body, anti-oxidant, corrosion-resistant, antirust, weather-proof
Performance has much room for improvement, and surface smoothness is also not ideal enough.
The content of the invention
It is an object of the invention to provide a kind of high resistance chromium nickel electrothermal alloy, and its nichrome main body is by overlay film
Reason, nichrome body surfaces are covered with protecting film, have excellent abrasion-resistant, anti-oxidant, corrosion-resistant, antirust, weather resistance, and
Surface smoothness is good.
To achieve the above object, the technical scheme is that designing a kind of high resistance chromium nickel electrothermal alloy, it includes nickel
Evanohm main body, the nichrome main body pass through aluminum coated steel, and the aluminum coated steel comprises the following steps:
1)By 1~2 parts by weight fatty alcohol polyoxyethylene ether sulfate, 5.8 parts by weight of lemon acid, 2.6 parts by weight diethylene glycol benzene
Base ether, 4.3 parts by weight bipentaerythrites are put into 52 parts by weight of deionized water successively, are stirred;
2)Put into 1.3 parts by weight ammonium titanium fluorides, 2.4 parts by weight of polypropylene acid sodium, 3.5 parts by weight triethanolamine oleates successively again
Soap, 1.7 parts by weight hexamethylenetetramines, continue to stir, and to being sufficiently mixed uniformly, coating treatment liquid is made;
3)Nichrome main body is inserted in coating treatment liquid and impregnated, is dried after taking-up.
Preferably, a kind of high resistance chromium nickel electrothermal alloy, it includes nichrome main body, and the nichrome main body is by covering
Film process, the aluminum coated steel comprise the following steps:
1)By 1.2 parts by weight fatty alcohol polyoxyethylene ether sulfates, 5.8 parts by weight of lemon acid, 2.6 parts by weight diethylene glycol phenyl
Ether, 4.3 parts by weight bipentaerythrites are put into 52 parts by weight of deionized water successively, are stirred;
2)Put into 1.3 parts by weight ammonium titanium fluorides, 2.4 parts by weight of polypropylene acid sodium, 3.5 parts by weight triethanolamine oleates successively again
Soap, 1.7 parts by weight hexamethylenetetramines, continue to stir, and to being sufficiently mixed uniformly, coating treatment liquid is made;
3)Nichrome main body is inserted in coating treatment liquid and impregnated, is dried after taking-up.
The advantages of the present invention are:A kind of high resistance chromium nickel electrothermal alloy, its nichrome main body are provided
By aluminum coated steel, nichrome body surfaces are covered with protecting film, have excellent abrasion-resistant, anti-oxidant, corrosion-resistant, antirust,
Weather resistance, and surface smoothness is good.
The performance and purposes of " coating treatment liquid " determined by its component and proportioning, and in " coating treatment liquid " not
It can be influenced each other with component, component and its proportioning can determine the final performance of " coating treatment liquid ", such as fruit component and its proportioning not
It is mutually coordinated, beneficial effect caused by single component, it can be cut down by other components and even eliminate, when serious, different groups
Split-phase mutually contradicts, and does not have whole synthesis effect, produces negative interaction and substandard products.The present invention by a large amount of creative works, repeatedly
Checking, obtains the optimal component and proportioning of " coating treatment liquid " so that multiple components combine, mutually coordinated and produce
Positive comprehensive effect.
Embodiment
With reference to embodiment, the embodiment of the present invention is further described.Following examples are only used for more
Add and clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied is:
Embodiment 1
A kind of high resistance chromium nickel electrothermal alloy, it includes nichrome main body, and the nichrome main body passes through aluminum coated steel, described
Aluminum coated steel comprises the following steps:
1)By 1 parts by weight fatty alcohol polyoxyethylene ether sulfate, 5.8 parts by weight of lemon acid, 2.6 parts by weight diethylene glycol phenyl
Ether, 4.3 parts by weight bipentaerythrites are put into 52 parts by weight of deionized water successively, are stirred;
2)Put into 1.3 parts by weight ammonium titanium fluorides, 2.4 parts by weight of polypropylene acid sodium, 3.5 parts by weight triethanolamine oleates successively again
Soap, 1.7 parts by weight hexamethylenetetramines, continue to stir, and to being sufficiently mixed uniformly, coating treatment liquid is made;
3)Nichrome main body is inserted in coating treatment liquid and impregnated, is dried after taking-up.
Embodiment 2
A kind of high resistance chromium nickel electrothermal alloy, it includes nichrome main body, and the nichrome main body passes through aluminum coated steel, described
Aluminum coated steel comprises the following steps:
1)By 2 parts by weight fatty alcohol polyoxyethylene ether sulfates, 5.8 parts by weight of lemon acid, 2.6 parts by weight diethylene glycol phenyl
Ether, 4.3 parts by weight bipentaerythrites are put into 52 parts by weight of deionized water successively, are stirred;
2)Put into 1.3 parts by weight ammonium titanium fluorides, 2.4 parts by weight of polypropylene acid sodium, 3.5 parts by weight triethanolamine oleates successively again
Soap, 1.7 parts by weight hexamethylenetetramines, continue to stir, and to being sufficiently mixed uniformly, coating treatment liquid is made;
3)Nichrome main body is inserted in coating treatment liquid and impregnated, is dried after taking-up.
Embodiment 3
A kind of high resistance chromium nickel electrothermal alloy, it includes nichrome main body, and the nichrome main body passes through aluminum coated steel, described
Aluminum coated steel comprises the following steps:
1)By 1.2 parts by weight fatty alcohol polyoxyethylene ether sulfates, 5.8 parts by weight of lemon acid, 2.6 parts by weight diethylene glycol phenyl
Ether, 4.3 parts by weight bipentaerythrites are put into 52 parts by weight of deionized water successively, are stirred;
2)Put into 1.3 parts by weight ammonium titanium fluorides, 2.4 parts by weight of polypropylene acid sodium, 3.5 parts by weight triethanolamine oleates successively again
Soap, 1.7 parts by weight hexamethylenetetramines, continue to stir, and to being sufficiently mixed uniformly, coating treatment liquid is made;
3)Nichrome main body is inserted in coating treatment liquid and impregnated, is dried after taking-up.
Surface through nichrome main body in the various embodiments described above is covered with protecting film, have excellent abrasion-resistant, it is anti-oxidant,
Corrosion-resistant, antirust, weather resistance, and surface smoothness is good.
Described above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, some improvements and modifications can also be made, these improvements and modifications
Also it should be regarded as protection scope of the present invention.
Claims (2)
1. a kind of high resistance chromium nickel electrothermal alloy, it is characterised in that it includes nichrome main body, and the nichrome main body is passed through
Aluminum coated steel, the aluminum coated steel comprise the following steps:
1)By 1~2 parts by weight fatty alcohol polyoxyethylene ether sulfate, 5.8 parts by weight of lemon acid, 2.6 parts by weight diethylene glycol benzene
Base ether, 4.3 parts by weight bipentaerythrites are put into 52 parts by weight of deionized water successively, are stirred;
2)Put into 1.3 parts by weight ammonium titanium fluorides, 2.4 parts by weight of polypropylene acid sodium, 3.5 parts by weight triethanolamine oleates successively again
Soap, 1.7 parts by weight hexamethylenetetramines, continue to stir, and to being sufficiently mixed uniformly, coating treatment liquid is made;
3)Nichrome main body is inserted in coating treatment liquid and impregnated, is dried after taking-up.
2. high resistance chromium nickel electrothermal alloy according to claim 1, it is characterised in that it includes nichrome main body, should
Nichrome main body passes through aluminum coated steel, and the aluminum coated steel comprises the following steps:
1)By 1.2 parts by weight fatty alcohol polyoxyethylene ether sulfates, 5.8 parts by weight of lemon acid, 2.6 parts by weight diethylene glycol phenyl
Ether, 4.3 parts by weight bipentaerythrites are put into 52 parts by weight of deionized water successively, are stirred;
2)Put into 1.3 parts by weight ammonium titanium fluorides, 2.4 parts by weight of polypropylene acid sodium, 3.5 parts by weight triethanolamine oleates successively again
Soap, 1.7 parts by weight hexamethylenetetramines, continue to stir, and to being sufficiently mixed uniformly, coating treatment liquid is made;
3)Nichrome main body is inserted in coating treatment liquid and impregnated, is dried after taking-up.