CN106280630A - Heating high-resistance electrothermic alloy silk - Google Patents
Heating high-resistance electrothermic alloy silk Download PDFInfo
- Publication number
- CN106280630A CN106280630A CN201610717407.5A CN201610717407A CN106280630A CN 106280630 A CN106280630 A CN 106280630A CN 201610717407 A CN201610717407 A CN 201610717407A CN 106280630 A CN106280630 A CN 106280630A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- weight portion
- main body
- treatment liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of heating high-resistance electrothermic alloy silk, it includes nichrome main body, this nichrome main body is through aluminum coated steel, described aluminum coated steel comprises the steps: 1) 1~2 parts sulfuric acid sodium, 0.7 weight portion bis-imdazoline, 1.9 weight portion γ (methacryloxypropyl) propyl trimethoxy silicanes, 2.2 parts by weight of fatty polyoxyethylenated alcohol carboxylates are put in 40 parts by weight of deionized water successively, stir;2) put into 4.3 parts by weight of propylene glycol phenylates, 5.5 parts by weight of acrylonitrile, 1.6 weight portion SASs, 0.7 weight portion 2 aminoethyl 17 alkenyl imidazoline the most successively, continue stirring, to being sufficiently mixed uniformly, prepare coating treatment liquid;3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.Heating high-resistance electrothermic alloy silk of the present invention, its nichrome body surfaces is covered with protecting film, and performance is good, and surface smoothness is good.
Description
Technical field
The present invention relates to heating high-resistance electrothermic alloy silk.
Background technology
Existing heating high-resistance electrothermic alloy silk, the abrasion-resistant of its nichrome main body, antioxidation, corrosion-resistant,
Antirust, weather resistance has much room for improvement, and surface smoothness is the most not ideal enough.
Summary of the invention
It is an object of the invention to provide a kind of heating high-resistance electrothermic alloy silk, its nichrome main body is passed through
Aluminum coated steel, nichrome body surfaces is covered with protecting film, has the abrasion-resistant of excellence, antioxidation, corrosion-resistant, antirust, weather-proof
Performance, and surface smoothness is good.
For achieving the above object, the technical scheme is that a kind of heating high-resistance electrothermic alloy silk of design,
It includes nichrome main body, and this nichrome main body is through aluminum coated steel, and described aluminum coated steel comprises the steps:
1) by 1~2 parts sulfuric acid sodium, 0.7 weight portion bis-imdazoline, 1.9 weight portion γ-(methacryloxypropyl) third
Base trimethoxy silane, 2.2 parts by weight of fatty polyoxyethylenated alcohol carboxylates put in 40 parts by weight of deionized water successively, stirring
Uniformly;
2) 4.3 parts by weight of propylene glycol phenylates, 5.5 parts by weight of acrylonitrile, the 1.6 secondary alkyl sulfonic acids of weight portion are put into the most successively
Sodium, 0.7 weight portion 2-aminoethyl 17 alkenyl imidazoline, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Preferably, heating high-resistance electrothermic alloy silk, it includes nichrome main body, this nichrome main body warp
Crossing aluminum coated steel, described aluminum coated steel comprises the steps:
1) by 1 parts sulfuric acid sodium, 0.7 weight portion bis-imdazoline, 1.9 weight portion γ-(methacryloxypropyl) propyl group
Trimethoxy silane, 2.2 parts by weight of fatty polyoxyethylenated alcohol carboxylates put in 40 parts by weight of deionized water successively, and stirring is all
Even;
2) 4.3 parts by weight of propylene glycol phenylates, 5.5 parts by weight of acrylonitrile, the 1.6 secondary alkyl sulfonic acids of weight portion are put into the most successively
Sodium, 0.7 weight portion 2-aminoethyl 17 alkenyl imidazoline, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Preferably, heating high-resistance electrothermic alloy silk, it includes nichrome main body, this nichrome main body warp
Crossing aluminum coated steel, described aluminum coated steel comprises the steps:
1) by 2 parts sulfuric acid sodium, 0.7 weight portion bis-imdazoline, 1.9 weight portion γ-(methacryloxypropyl) propyl group
Trimethoxy silane, 2.2 parts by weight of fatty polyoxyethylenated alcohol carboxylates put in 40 parts by weight of deionized water successively, and stirring is all
Even;
2) 4.3 parts by weight of propylene glycol phenylates, 5.5 parts by weight of acrylonitrile, the 1.6 secondary alkyl sulfonic acids of weight portion are put into the most successively
Sodium, 0.7 weight portion 2-aminoethyl 17 alkenyl imidazoline, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Preferably, heating high-resistance electrothermic alloy silk, it includes nichrome main body, this nichrome main body warp
Crossing aluminum coated steel, described aluminum coated steel comprises the steps:
1) by 1.2 parts sulfuric acid sodium, 0.7 weight portion bis-imdazoline, 1.9 weight portion γ-(methacryloxypropyl) third
Base trimethoxy silane, 2.2 parts by weight of fatty polyoxyethylenated alcohol carboxylates put in 40 parts by weight of deionized water successively, stirring
Uniformly;
2) 4.3 parts by weight of propylene glycol phenylates, 5.5 parts by weight of acrylonitrile, the 1.6 secondary alkyl sulfonic acids of weight portion are put into the most successively
Sodium, 0.7 weight portion 2-aminoethyl 17 alkenyl imidazoline, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Advantages of the present invention and having the beneficial effects that: a kind of heating high-resistance electrothermic alloy silk, its nickel chromium triangle are provided
Alloy bulk is covered with protecting film through aluminum coated steel, nichrome body surfaces, has the abrasion-resistant of excellence, antioxidation, corrosion resistant
Erosion, antirust, weather resistance, and surface smoothness is good.
Performance and the purposes of " coating treatment liquid " are determined by its component and proportioning, and in " coating treatment liquid " not
Can influence each other with component, component and proportioning thereof can determine the final performance of " coating treatment liquid ", such as fruit component and proportioning thereof not
Mutually coordinated, that single component is brought beneficial effect, even can be eliminated by other components abatement, the when of serious, and different groups
Split-phase is conflicted mutually, does not has whole synthesis effect, produces negative interaction and substandard products.The present invention is by a large amount of creative works, repeatedly
Checking, obtains optimal component and the proportioning of " coating treatment liquid " so that multiple components combine, mutually coordinated and produce
Forward comprehensive effect.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.Following example are only used for more
Add and clearly demonstrate technical scheme, and can not limit the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Heating high-resistance electrothermic alloy silk, it includes nichrome main body, and this nichrome main body is through overlay film
Processing, described aluminum coated steel comprises the steps:
1) by 1~2 parts sulfuric acid sodium, 0.7 weight portion bis-imdazoline, 1.9 weight portion γ-(methacryloxypropyl) third
Base trimethoxy silane, 2.2 parts by weight of fatty polyoxyethylenated alcohol carboxylates put in 40 parts by weight of deionized water successively, stirring
Uniformly;
2) 4.3 parts by weight of propylene glycol phenylates, 5.5 parts by weight of acrylonitrile, the 1.6 secondary alkyl sulfonic acids of weight portion are put into the most successively
Sodium, 0.7 weight portion 2-aminoethyl 17 alkenyl imidazoline, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Embodiment 2
Heating high-resistance electrothermic alloy silk, it includes nichrome main body, and this nichrome main body is through overlay film
Processing, described aluminum coated steel comprises the steps:
1) by 1 parts sulfuric acid sodium, 0.7 weight portion bis-imdazoline, 1.9 weight portion γ-(methacryloxypropyl) propyl group
Trimethoxy silane, 2.2 parts by weight of fatty polyoxyethylenated alcohol carboxylates put in 40 parts by weight of deionized water successively, and stirring is all
Even;
2) 4.3 parts by weight of propylene glycol phenylates, 5.5 parts by weight of acrylonitrile, the 1.6 secondary alkyl sulfonic acids of weight portion are put into the most successively
Sodium, 0.7 weight portion 2-aminoethyl 17 alkenyl imidazoline, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Embodiment 3
Heating high-resistance electrothermic alloy silk, it includes nichrome main body, and this nichrome main body is through overlay film
Processing, described aluminum coated steel comprises the steps:
1) by 2 parts sulfuric acid sodium, 0.7 weight portion bis-imdazoline, 1.9 weight portion γ-(methacryloxypropyl) propyl group
Trimethoxy silane, 2.2 parts by weight of fatty polyoxyethylenated alcohol carboxylates put in 40 parts by weight of deionized water successively, and stirring is all
Even;
2) 4.3 parts by weight of propylene glycol phenylates, 5.5 parts by weight of acrylonitrile, the 1.6 secondary alkyl sulfonic acids of weight portion are put into the most successively
Sodium, 0.7 weight portion 2-aminoethyl 17 alkenyl imidazoline, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Embodiment 4
Heating high-resistance electrothermic alloy silk, it includes nichrome main body, and this nichrome main body is through overlay film
Processing, described aluminum coated steel comprises the steps:
1) by 1.2 parts sulfuric acid sodium, 0.7 weight portion bis-imdazoline, 1.9 weight portion γ-(methacryloxypropyl) third
Base trimethoxy silane, 2.2 parts by weight of fatty polyoxyethylenated alcohol carboxylates put in 40 parts by weight of deionized water successively, stirring
Uniformly;
2) 4.3 parts by weight of propylene glycol phenylates, 5.5 parts by weight of acrylonitrile, the 1.6 secondary alkyl sulfonic acids of weight portion are put into the most successively
Sodium, 0.7 weight portion 2-aminoethyl 17 alkenyl imidazoline, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
In the various embodiments described above, the surface of nichrome main body is covered with protecting film, have excellence abrasion-resistant, antioxidation,
Corrosion-resistant, antirust, weather resistance, and surface smoothness is good.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvements and modifications, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. heating high-resistance electrothermic alloy silk, it is characterised in that it includes nichrome main body, this nichrome main body
Through aluminum coated steel, described aluminum coated steel comprises the steps:
1) by 1~2 parts sulfuric acid sodium, 0.7 weight portion bis-imdazoline, 1.9 weight portion γ-(methacryloxypropyl) propyl group three
Methoxy silane, 2.2 parts by weight of fatty polyoxyethylenated alcohol carboxylates put in 40 parts by weight of deionized water successively, and stirring is all
Even;
2) put into the most successively 4.3 parts by weight of propylene glycol phenylates, 5.5 parts by weight of acrylonitrile, 1.6 weight portion SASs, 0.7
Weight portion 2-aminoethyl 17 alkenyl imidazoline, continues stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Heating high-resistance electrothermic alloy silk the most according to claim 1, it is characterised in that it includes nichrome
Main body, this nichrome main body is through aluminum coated steel, and described aluminum coated steel comprises the steps:
1) by 1 parts sulfuric acid sodium, 0.7 weight portion bis-imdazoline, 1.9 weight portion γ-(methacryloxypropyl) propyl group front three
TMOS, 2.2 parts by weight of fatty polyoxyethylenated alcohol carboxylates put in 40 parts by weight of deionized water successively, stir;
2) put into the most successively 4.3 parts by weight of propylene glycol phenylates, 5.5 parts by weight of acrylonitrile, 1.6 weight portion SASs, 0.7
Weight portion 2-aminoethyl 17 alkenyl imidazoline, continues stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Heating high-resistance electrothermic alloy silk the most according to claim 1, it is characterised in that it includes nichrome
Main body, this nichrome main body is through aluminum coated steel, and described aluminum coated steel comprises the steps:
1) by 2 parts sulfuric acid sodium, 0.7 weight portion bis-imdazoline, 1.9 weight portion γ-(methacryloxypropyl) propyl group front three
TMOS, 2.2 parts by weight of fatty polyoxyethylenated alcohol carboxylates put in 40 parts by weight of deionized water successively, stir;
2) put into the most successively 4.3 parts by weight of propylene glycol phenylates, 5.5 parts by weight of acrylonitrile, 1.6 weight portion SASs, 0.7
Weight portion 2-aminoethyl 17 alkenyl imidazoline, continues stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Heating high-resistance electrothermic alloy silk the most according to claim 1, it is characterised in that it includes nichrome
Main body, this nichrome main body is through aluminum coated steel, and described aluminum coated steel comprises the steps:
1) by 1.2 parts sulfuric acid sodium, 0.7 weight portion bis-imdazoline, 1.9 weight portion γ-(methacryloxypropyl) propyl group three
Methoxy silane, 2.2 parts by weight of fatty polyoxyethylenated alcohol carboxylates put in 40 parts by weight of deionized water successively, and stirring is all
Even;
2) put into the most successively 4.3 parts by weight of propylene glycol phenylates, 5.5 parts by weight of acrylonitrile, 1.6 weight portion SASs, 0.7
Weight portion 2-aminoethyl 17 alkenyl imidazoline, continues stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.