CN106282986A - Heating nickel chromium triangle flat filament - Google Patents
Heating nickel chromium triangle flat filament Download PDFInfo
- Publication number
- CN106282986A CN106282986A CN201610718297.4A CN201610718297A CN106282986A CN 106282986 A CN106282986 A CN 106282986A CN 201610718297 A CN201610718297 A CN 201610718297A CN 106282986 A CN106282986 A CN 106282986A
- Authority
- CN
- China
- Prior art keywords
- weight
- weight portion
- main body
- treatment liquid
- coating treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of heating nickel chromium triangle flat filament, it includes nichrome main body, this nichrome main body is through aluminum coated steel, described aluminum coated steel comprises the steps: 1) 1～2 weight portion hexamethylenamine, 2.4 weight portion ATMPs, 2.5 weight portion hexyldecanol, 0.7 weight portion Trimethyllaurylammonium chloride are put in 40 parts by weight of deionized water successively, stir；2) put into 5.6 weight account polyethylene alcohol, 8.5 parts by weight of acrylic acid second fat, 1.3 weight portion Igepon Ts, 0.7 weight portion hexamethylenetetramine the most successively, continue stirring, to being sufficiently mixed uniformly, prepare coating treatment liquid；3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.Heating nickel chromium triangle flat filament of the present invention, its nichrome body surfaces is covered with protecting film, and performance is good, and surface smoothness is good.
Description
Technical field
The present invention relates to heating nickel chromium triangle flat filament.
Background technology
Existing heating nickel chromium triangle flat filament, the abrasion-resistant of its nichrome main body, antioxidation, corrosion-resistant, antirust, weather-proof
Performance has much room for improvement, and surface smoothness is the most not ideal enough.
Summary of the invention
It is an object of the invention to provide a kind of heating nickel chromium triangle flat filament, its nichrome main body is at overlay film
Reason, nichrome body surfaces is covered with protecting film, has the abrasion-resistant of excellence, antioxidation, corrosion-resistant, antirust, weather resistance, and
Surface smoothness is good.
For achieving the above object, the technical scheme is that a kind of heating nickel chromium triangle flat filament of design, it includes nickel
Evanohm main body, this nichrome main body is through aluminum coated steel, and described aluminum coated steel comprises the steps:
1) by 1～2 weight portion hexamethylenamine, 2.4 weight portion ATMPs, 2.5 weight portion hexyldecanol, 0.7
Weight portion Trimethyllaurylammonium chloride puts in 40 parts by weight of deionized water successively, stirs；
2) put into the most successively 5.6 weight account polyethylene alcohol, 8.5 parts by weight of acrylic acid second fat, 1.3 weight portion Igepon Ts,
0.7 weight portion hexamethylenetetramine, continues stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid；
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Preferably, heating nickel chromium triangle flat filament, it includes nichrome main body, and this nichrome main body is at overlay film
Reason, described aluminum coated steel comprises the steps:
1) by 1 weight portion hexamethylenamine, 2.4 weight portion ATMPs, 2.5 weight portion hexyldecanol, 0.7 weight
Part Trimethyllaurylammonium chloride puts in 40 parts by weight of deionized water successively, stirs；
2) put into the most successively 5.6 weight account polyethylene alcohol, 8.5 parts by weight of acrylic acid second fat, 1.3 weight portion Igepon Ts,
0.7 weight portion hexamethylenetetramine, continues stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid；
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Preferably, heating nickel chromium triangle flat filament, it includes nichrome main body, and this nichrome main body is at overlay film
Reason, described aluminum coated steel comprises the steps:
1) by 2 weight portion hexamethylenamine, 2.4 weight portion ATMPs, 2.5 weight portion hexyldecanol, 0.7 weight
Part Trimethyllaurylammonium chloride puts in 40 parts by weight of deionized water successively, stirs；
2) put into the most successively 5.6 weight account polyethylene alcohol, 8.5 parts by weight of acrylic acid second fat, 1.3 weight portion Igepon Ts,
0.7 weight portion hexamethylenetetramine, continues stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid；
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Preferably, heating nickel chromium triangle flat filament, it includes nichrome main body, and this nichrome main body is at overlay film
Reason, described aluminum coated steel comprises the steps:
1) by 1.2 weight portion hexamethylenamine, 2.4 weight portion ATMPs, 2.5 weight portion hexyldecanol, 0.7 weight
Amount part Trimethyllaurylammonium chloride puts in 40 parts by weight of deionized water successively, stirs；
2) put into the most successively 5.6 weight account polyethylene alcohol, 8.5 parts by weight of acrylic acid second fat, 1.3 weight portion Igepon Ts,
0.7 weight portion hexamethylenetetramine, continues stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid；
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Advantages of the present invention and having the beneficial effects that: a kind of heating nickel chromium triangle flat filament, its nichrome main body are provided
Through aluminum coated steel, nichrome body surfaces is covered with protecting film, have excellence abrasion-resistant, antioxidation, corrosion-resistant, antirust,
Weather resistance, and surface smoothness is good.
Performance and the purposes of " coating treatment liquid " are determined by its component and proportioning, and in " coating treatment liquid " not
Can influence each other with component, component and proportioning thereof can determine the final performance of " coating treatment liquid ", such as fruit component and proportioning thereof not
Mutually coordinated, that single component is brought beneficial effect, even can be eliminated by other components abatement, the when of serious, and different groups
Split-phase is conflicted mutually, does not has whole synthesis effect, produces negative interaction and substandard products.The present invention is by a large amount of creative works, repeatedly
Checking, obtains optimal component and the proportioning of " coating treatment liquid " so that multiple components combine, mutually coordinated and produce
Forward comprehensive effect.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.Following example are only used for more
Add and clearly demonstrate technical scheme, and can not limit the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Heating nickel chromium triangle flat filament, it includes nichrome main body, and this nichrome main body is through aluminum coated steel, described
Aluminum coated steel comprises the steps:
1) by 1～2 weight portion hexamethylenamine, 2.4 weight portion ATMPs, 2.5 weight portion hexyldecanol, 0.7
Weight portion Trimethyllaurylammonium chloride puts in 40 parts by weight of deionized water successively, stirs；
2) put into the most successively 5.6 weight account polyethylene alcohol, 8.5 parts by weight of acrylic acid second fat, 1.3 weight portion Igepon Ts,
0.7 weight portion hexamethylenetetramine, continues stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid；
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Embodiment 2
Heating nickel chromium triangle flat filament, it includes nichrome main body, and this nichrome main body is through aluminum coated steel, described
Aluminum coated steel comprises the steps:
1) by 1 weight portion hexamethylenamine, 2.4 weight portion ATMPs, 2.5 weight portion hexyldecanol, 0.7 weight
Part Trimethyllaurylammonium chloride puts in 40 parts by weight of deionized water successively, stirs；
2) put into the most successively 5.6 weight account polyethylene alcohol, 8.5 parts by weight of acrylic acid second fat, 1.3 weight portion Igepon Ts,
0.7 weight portion hexamethylenetetramine, continues stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid；
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Embodiment 3
Heating nickel chromium triangle flat filament, it includes nichrome main body, and this nichrome main body is through aluminum coated steel, described
Aluminum coated steel comprises the steps:
1) by 2 weight portion hexamethylenamine, 2.4 weight portion ATMPs, 2.5 weight portion hexyldecanol, 0.7 weight
Part Trimethyllaurylammonium chloride puts in 40 parts by weight of deionized water successively, stirs；
2) put into the most successively 5.6 weight account polyethylene alcohol, 8.5 parts by weight of acrylic acid second fat, 1.3 weight portion Igepon Ts,
0.7 weight portion hexamethylenetetramine, continues stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid；
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Embodiment 4
Heating nickel chromium triangle flat filament, it includes nichrome main body, and this nichrome main body is through aluminum coated steel, described
Aluminum coated steel comprises the steps:
1) by 1.2 weight portion hexamethylenamine, 2.4 weight portion ATMPs, 2.5 weight portion hexyldecanol, 0.7 weight
Amount part Trimethyllaurylammonium chloride puts in 40 parts by weight of deionized water successively, stirs；
2) put into the most successively 5.6 weight account polyethylene alcohol, 8.5 parts by weight of acrylic acid second fat, 1.3 weight portion Igepon Ts,
0.7 weight portion hexamethylenetetramine, continues stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid；
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
In the various embodiments described above, the surface of nichrome main body is covered with protecting film, have excellence abrasion-resistant, antioxidation,
Corrosion-resistant, antirust, weather resistance, and surface smoothness is good.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvements and modifications, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. heating nickel chromium triangle flat filament, it is characterised in that it includes nichrome main body, this nichrome main body is through overlay film
Processing, described aluminum coated steel comprises the steps:
1) by 1～2 weight portion hexamethylenamine, 2.4 weight portion ATMPs, 2.5 weight portion hexyldecanol, 0.7 weight
Part Trimethyllaurylammonium chloride puts in 40 parts by weight of deionized water successively, stirs；
2) 5.6 weight account polyethylene alcohol, 8.5 parts by weight of acrylic acid second fat, 1.3 weight portion Igepon Ts, 0.7 weight are put into the most successively
Amount part hexamethylenetetramine, continues stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid；
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Heating nickel chromium triangle flat filament the most according to claim 1, it is characterised in that it includes nichrome main body, should
Nichrome main body is through aluminum coated steel, and described aluminum coated steel comprises the steps:
1) by 1 weight portion hexamethylenamine, 2.4 weight portion ATMPs, 2.5 weight portion hexyldecanol, 0.7 weight portion chlorine
Change lauryl trimethyl ammonium to put into successively in 40 parts by weight of deionized water, stir；
2) 5.6 weight account polyethylene alcohol, 8.5 parts by weight of acrylic acid second fat, 1.3 weight portion Igepon Ts, 0.7 weight are put into the most successively
Amount part hexamethylenetetramine, continues stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid；
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Heating nickel chromium triangle flat filament the most according to claim 1, it is characterised in that it includes nichrome main body, should
Nichrome main body is through aluminum coated steel, and described aluminum coated steel comprises the steps:
1) by 2 weight portion hexamethylenamine, 2.4 weight portion ATMPs, 2.5 weight portion hexyldecanol, 0.7 weight portion chlorine
Change lauryl trimethyl ammonium to put into successively in 40 parts by weight of deionized water, stir；
2) 5.6 weight account polyethylene alcohol, 8.5 parts by weight of acrylic acid second fat, 1.3 weight portion Igepon Ts, 0.7 weight are put into the most successively
Amount part hexamethylenetetramine, continues stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid；
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.
Heating nickel chromium triangle flat filament the most according to claim 1, it is characterised in that it includes nichrome main body, should
Nichrome main body is through aluminum coated steel, and described aluminum coated steel comprises the steps:
1) by 1.2 weight portion hexamethylenamine, 2.4 weight portion ATMPs, 2.5 weight portion hexyldecanol, 0.7 weight portion
Trimethyllaurylammonium chloride puts in 40 parts by weight of deionized water successively, stirs；
2) 5.6 weight account polyethylene alcohol, 8.5 parts by weight of acrylic acid second fat, 1.3 weight portion Igepon Ts, 0.7 weight are put into the most successively
Amount part hexamethylenetetramine, continues stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid；
3) nichrome main body is inserted in coating treatment liquid and impregnate, take out post-drying.