CN106119827A - Steel plate passivator - Google Patents
Steel plate passivator Download PDFInfo
- Publication number
- CN106119827A CN106119827A CN201610749682.5A CN201610749682A CN106119827A CN 106119827 A CN106119827 A CN 106119827A CN 201610749682 A CN201610749682 A CN 201610749682A CN 106119827 A CN106119827 A CN 106119827A
- Authority
- CN
- China
- Prior art keywords
- parts
- passivator
- steel plate
- resistant
- acid esters
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of steel plate passivator, the most composed of the following components: 1~2 part of silicon dioxide, 1.3 parts of dodecyl sodium sulfates, 0.9 part of aluminum silicon powder, 0.7 part of cobalt nitrate, 2.2 parts of carboxymethyl celluloses, 6.5 parts of polyoxyethylene stearic acid esters, 0.7 part of zinc dihydrogen phosphate, 1.8 parts of sodium alkyl benzene sulfonates, 1.5 parts of ammonium titanium fluorides, 43 parts of deionized waters.Steel plate passivator of the present invention, can be used for the Passivation Treatment of metal, forms uniform passivation protection film in metal surface, and protecting film has antirust, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, the weather resistance of excellence, and surface smoothness is good.
Description
Technical field
The present invention relates to steel plate passivator.
Background technology
Existing steel plate passivator, for the Passivation Treatment of metal, at metal surface formation passivation protection film, but protecting film
Antirust, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, weather resistance have much room for improvement, and surface smoothness is the most not ideal enough.
Summary of the invention
It is an object of the invention to provide a kind of steel plate passivator, can be used for the Passivation Treatment of metal, in metal surface shape
Uniformly passivation protection film, protecting film has antirust, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, the weather resistance of excellence, and table
Face fineness is good.
For achieving the above object, the technical scheme is that a kind of steel plate passivator of design, by weight by following
Component forms:
1~2 part of silicon dioxide,
1.3 parts of dodecyl sodium sulfates,
0.9 part of aluminum silicon powder,
0.7 part of cobalt nitrate,
2.2 parts of carboxymethyl celluloses,
6.5 parts of polyoxyethylene stearic acid esters,
0.7 part of zinc dihydrogen phosphate,
1.8 parts of sodium alkyl benzene sulfonates,
1.5 parts of ammonium titanium fluorides,
43 parts of deionized waters.
Preferably, steel plate passivator, the most composed of the following components:
1 part of silicon dioxide,
1.3 parts of dodecyl sodium sulfates,
0.9 part of aluminum silicon powder,
0.7 part of cobalt nitrate,
2.2 parts of carboxymethyl celluloses,
6.5 parts of polyoxyethylene stearic acid esters,
0.7 part of zinc dihydrogen phosphate,
1.8 parts of sodium alkyl benzene sulfonates,
1.5 parts of ammonium titanium fluorides,
43 parts of deionized waters.
Preferably, steel plate passivator, the most composed of the following components:
2 parts of silicon dioxide,
1.3 parts of dodecyl sodium sulfates,
0.9 part of aluminum silicon powder,
0.7 part of cobalt nitrate,
2.2 parts of carboxymethyl celluloses,
6.5 parts of polyoxyethylene stearic acid esters,
0.7 part of zinc dihydrogen phosphate,
1.8 parts of sodium alkyl benzene sulfonates,
1.5 parts of ammonium titanium fluorides,
43 parts of deionized waters.
Preferably, steel plate passivator, the most composed of the following components:
1.2 parts of silicon dioxide,
1.3 parts of dodecyl sodium sulfates,
0.9 part of aluminum silicon powder,
0.7 part of cobalt nitrate,
2.2 parts of carboxymethyl celluloses,
6.5 parts of polyoxyethylene stearic acid esters,
0.7 part of zinc dihydrogen phosphate,
1.8 parts of sodium alkyl benzene sulfonates,
1.5 parts of ammonium titanium fluorides,
43 parts of deionized waters.
Advantages of the present invention and having the beneficial effects that: a kind of steel plate passivator is provided, can be used for the Passivation Treatment of metal,
Metal surface forms uniform passivation protection film, and protecting film has antirust, the abrasion-resistant of excellence, corrosion-resistant, heat-resisting, cold-resistant, resistance to
Wait performance, and surface smoothness is good.
Performance and the purposes of " steel plate passivator " are determined by its component and proportioning, and in " steel plate passivator " not
Can influence each other with component, component and proportioning thereof can determine the final performance of " steel plate passivator ", such as fruit component and proportioning thereof not
Mutually coordinated, that single component is brought beneficial effect, even can be eliminated by other components abatement, the when of serious, and different groups
Split-phase is conflicted mutually, does not has whole synthesis effect, produces negative interaction and substandard products.The present invention is by a large amount of creative works, repeatedly
Checking, obtains optimal component and the proportioning of " steel plate passivator " so that multiple components combine, mutually coordinated and produce
Forward comprehensive effect.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.Following example are only used for more
Add and clearly demonstrate technical scheme, and can not limit the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Steel plate passivator, the most composed of the following components:
1~2 part of silicon dioxide,
1.3 parts of dodecyl sodium sulfates,
0.9 part of aluminum silicon powder,
0.7 part of cobalt nitrate,
2.2 parts of carboxymethyl celluloses,
6.5 parts of polyoxyethylene stearic acid esters,
0.7 part of zinc dihydrogen phosphate,
1.8 parts of sodium alkyl benzene sulfonates,
1.5 parts of ammonium titanium fluorides,
43 parts of deionized waters.
Embodiment 2
Steel plate passivator, the most composed of the following components:
1 part of silicon dioxide,
1.3 parts of dodecyl sodium sulfates,
0.9 part of aluminum silicon powder,
0.7 part of cobalt nitrate,
2.2 parts of carboxymethyl celluloses,
6.5 parts of polyoxyethylene stearic acid esters,
0.7 part of zinc dihydrogen phosphate,
1.8 parts of sodium alkyl benzene sulfonates,
1.5 parts of ammonium titanium fluorides,
43 parts of deionized waters.
Embodiment 3
Steel plate passivator, the most composed of the following components:
2 parts of silicon dioxide,
1.3 parts of dodecyl sodium sulfates,
0.9 part of aluminum silicon powder,
0.7 part of cobalt nitrate,
2.2 parts of carboxymethyl celluloses,
6.5 parts of polyoxyethylene stearic acid esters,
0.7 part of zinc dihydrogen phosphate,
1.8 parts of sodium alkyl benzene sulfonates,
1.5 parts of ammonium titanium fluorides,
43 parts of deionized waters.
Embodiment 4
Steel plate passivator, the most composed of the following components:
1.2 parts of silicon dioxide,
1.3 parts of dodecyl sodium sulfates,
0.9 part of aluminum silicon powder,
0.7 part of cobalt nitrate,
2.2 parts of carboxymethyl celluloses,
6.5 parts of polyoxyethylene stearic acid esters,
0.7 part of zinc dihydrogen phosphate,
1.8 parts of sodium alkyl benzene sulfonates,
1.5 parts of ammonium titanium fluorides,
43 parts of deionized waters.
Through the various embodiments described above light plate passivator, can be used for the Passivation Treatment of metal, formed uniformly in metal surface
Passivation protection film, protecting film has antirust, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, the weather resistance of excellence, and surface smoothness
Good.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvements and modifications, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. steel plate passivator, it is characterised in that the most composed of the following components:
1~2 part of silicon dioxide,
1.3 parts of dodecyl sodium sulfates,
0.9 part of aluminum silicon powder,
0.7 part of cobalt nitrate,
2.2 parts of carboxymethyl celluloses,
6.5 parts of polyoxyethylene stearic acid esters,
0.7 part of zinc dihydrogen phosphate,
1.8 parts of sodium alkyl benzene sulfonates,
1.5 parts of ammonium titanium fluorides,
43 parts of deionized waters.
Steel plate passivator the most according to claim 1, it is characterised in that the most composed of the following components:
1 part of silicon dioxide,
1.3 parts of dodecyl sodium sulfates,
0.9 part of aluminum silicon powder,
0.7 part of cobalt nitrate,
2.2 parts of carboxymethyl celluloses,
6.5 parts of polyoxyethylene stearic acid esters,
0.7 part of zinc dihydrogen phosphate,
1.8 parts of sodium alkyl benzene sulfonates,
1.5 parts of ammonium titanium fluorides,
43 parts of deionized waters.
Steel plate passivator the most according to claim 1, it is characterised in that the most composed of the following components:
2 parts of silicon dioxide,
1.3 parts of dodecyl sodium sulfates,
0.9 part of aluminum silicon powder,
0.7 part of cobalt nitrate,
2.2 parts of carboxymethyl celluloses,
6.5 parts of polyoxyethylene stearic acid esters,
0.7 part of zinc dihydrogen phosphate,
1.8 parts of sodium alkyl benzene sulfonates,
1.5 parts of ammonium titanium fluorides,
43 parts of deionized waters.
Steel plate passivator the most according to claim 1, it is characterised in that the most composed of the following components:
1.2 parts of silicon dioxide,
1.3 parts of dodecyl sodium sulfates,
0.9 part of aluminum silicon powder,
0.7 part of cobalt nitrate,
2.2 parts of carboxymethyl celluloses,
6.5 parts of polyoxyethylene stearic acid esters,
0.7 part of zinc dihydrogen phosphate,
1.8 parts of sodium alkyl benzene sulfonates,
1.5 parts of ammonium titanium fluorides,
43 parts of deionized waters.