CN106380939A - Movable gas station container - Google Patents
Movable gas station container Download PDFInfo
- Publication number
- CN106380939A CN106380939A CN201610781817.6A CN201610781817A CN106380939A CN 106380939 A CN106380939 A CN 106380939A CN 201610781817 A CN201610781817 A CN 201610781817A CN 106380939 A CN106380939 A CN 106380939A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- weight
- parts
- protective paint
- movable gas
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a movable gas station container. The metal box surface of the container is coated with a protective paint. The protective paint is prepared by the following steps: 1) successively pouring 1-2 parts by weight of iron oxide red, 0.8 part by weight of triethylene tetramine, 1.2 parts by weight of sodium N-oleoyl-N-methyltaurinate, 0.7 part by weight of sodium tripolyphosphate and 9 parts by weight of E-42 epoxy resin into 26 parts by weight of deionized water, and uniformly stirring; and 2) successively pouring 13 parts by weight of an EVA emulsion, 2.2 parts by weight of chlorinated polyethylene, 0.7 part by weight of cetylpyridinium chloride, 0.7 part by weight of disodium hydrogen phosphate and 0.4 part by weight of potassium persulphate, and continuously stirring until the materials are fully and uniformly mixed so as to prepare the protective paint. As the metal box surface of the movable gas station container is coated with the protective paint, long-term use of the movable gas station container can be guaranteed.
Description
Technical field
The present invention relates to a kind of movable gas filling station container.
Background technology
Existing movable gas filling station container, antirust, corrosion-resistant, antioxidation, the weather resistance of its metal cabinet need to be changed
Enter, the life-time service of impact movable gas filling station container.
Content of the invention
It is an object of the invention to provide a kind of movable gas filling station container, its metal cabinet surface-coated has protection
Paint, makes metal cabinet have excellent antirust, corrosion-resistant, antioxidation, weather resistance, thus ensureing movable gas filling station container
Can life-time service.
For achieving the above object, the technical scheme is that a kind of movable gas filling station container of design, including metal
Casing, this metal cabinet surface is covered with protective paint, and described protective paint is made by the steps：
1) by 1～2 weight portion iron oxide red, 0.8 weight portion triethylene tetramine, 1.2 weight portion oleoyl methylamine ethyl sulfonic acid sodium,
0.7 weight portion sodium tripolyphosphate, 9 weight portion E-42 epoxy resin put in 26 parts by weight of deionized water successively, stir；
2) put into successively again 13 parts of EVA emulsions, 2.2 weight portion chlorinated polyethylenees, 0.7 weight portion cetylpyridinium chloride, 0.7
Parts by weight of phosphoric acid disodium hydrogen, 0.4 weight portion potassium peroxydisulfate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Preferably, movable gas filling station container, including metal cabinet, this metal cabinet surface is covered with protective paint, institute
State protective paint to be made by the steps：
1) by 1 weight portion iron oxide red, 0.8 weight portion triethylene tetramine, 1.2 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 0.7
Weight portion sodium tripolyphosphate, 9 weight portion E-42 epoxy resin put in 26 parts by weight of deionized water successively, stir；
2) put into successively again 13 parts of EVA emulsions, 2.2 weight portion chlorinated polyethylenees, 0.7 weight portion cetylpyridinium chloride, 0.7
Parts by weight of phosphoric acid disodium hydrogen, 0.4 weight portion potassium peroxydisulfate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Preferably, movable gas filling station container, including metal cabinet, this metal cabinet surface is covered with protective paint, institute
State protective paint to be made by the steps：
1) by 2 weight portion iron oxide reds, 0.8 weight portion triethylene tetramine, 1.2 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 0.7
Weight portion sodium tripolyphosphate, 9 weight portion E-42 epoxy resin put in 26 parts by weight of deionized water successively, stir；
2) put into successively again 13 parts of EVA emulsions, 2.2 weight portion chlorinated polyethylenees, 0.7 weight portion cetylpyridinium chloride, 0.7
Parts by weight of phosphoric acid disodium hydrogen, 0.4 weight portion potassium peroxydisulfate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Preferably, movable gas filling station container, including metal cabinet, this metal cabinet surface is covered with protective paint, institute
State protective paint to be made by the steps：
1) by 1.2 weight portion iron oxide reds, 0.8 weight portion triethylene tetramine, 1.2 weight portion oleoyl methylamine ethyl sulfonic acid sodium,
0.7 weight portion sodium tripolyphosphate, 9 weight portion E-42 epoxy resin put in 26 parts by weight of deionized water successively, stir；
2) put into successively again 13 parts of EVA emulsions, 2.2 weight portion chlorinated polyethylenees, 0.7 weight portion cetylpyridinium chloride, 0.7
Parts by weight of phosphoric acid disodium hydrogen, 0.4 weight portion potassium peroxydisulfate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Advantages of the present invention and having the beneficial effects that：There is provided a kind of movable gas filling station container, its metal cabinet surface
It is coated with protective paint, makes metal cabinet have excellent antirust, corrosion-resistant, antioxidation, weather resistance, thus ensureing portable adding
Gas station container energy life-time service.
The performance of " protective paint " and purposes are determined by its component and proportioning, and the different component meeting in " protective paint "
Influence each other, component and its proportioning can determine the final performance of " protective paint ", such as fruit component and its proportioning be not mutually coordinated, single
The beneficial effect that component is brought, even can be eliminated by other components abatement, when serious, different component is mutually conflicted, and rises
Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " protection
The optimal component of paint " and proportioning so that multiple component combine, mutually coordinated and produce positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is：
Embodiment 1
Movable gas filling station container, including metal cabinet, this metal cabinet surface is covered with protective paint, described protective paint
It is made by the steps：
1) by 1～2 weight portion iron oxide red, 0.8 weight portion triethylene tetramine, 1.2 weight portion oleoyl methylamine ethyl sulfonic acid sodium,
0.7 weight portion sodium tripolyphosphate, 9 weight portion E-42 epoxy resin put in 26 parts by weight of deionized water successively, stir；
2) put into successively again 13 parts of EVA emulsions, 2.2 weight portion chlorinated polyethylenees, 0.7 weight portion cetylpyridinium chloride, 0.7
Parts by weight of phosphoric acid disodium hydrogen, 0.4 weight portion potassium peroxydisulfate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Embodiment 2
Movable gas filling station container, including metal cabinet, this metal cabinet surface is covered with protective paint, described protective paint
It is made by the steps：
1) by 1 weight portion iron oxide red, 0.8 weight portion triethylene tetramine, 1.2 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 0.7
Weight portion sodium tripolyphosphate, 9 weight portion E-42 epoxy resin put in 26 parts by weight of deionized water successively, stir；
2) put into successively again 13 parts of EVA emulsions, 2.2 weight portion chlorinated polyethylenees, 0.7 weight portion cetylpyridinium chloride, 0.7
Parts by weight of phosphoric acid disodium hydrogen, 0.4 weight portion potassium peroxydisulfate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Embodiment 3
Movable gas filling station container, including metal cabinet, this metal cabinet surface is covered with protective paint, described protective paint
It is made by the steps：
1) by 2 weight portion iron oxide reds, 0.8 weight portion triethylene tetramine, 1.2 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 0.7
Weight portion sodium tripolyphosphate, 9 weight portion E-42 epoxy resin put in 26 parts by weight of deionized water successively, stir；
2) put into successively again 13 parts of EVA emulsions, 2.2 weight portion chlorinated polyethylenees, 0.7 weight portion cetylpyridinium chloride, 0.7
Parts by weight of phosphoric acid disodium hydrogen, 0.4 weight portion potassium peroxydisulfate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Embodiment 4
Movable gas filling station container, including metal cabinet, this metal cabinet surface is covered with protective paint, described protective paint
It is made by the steps：
1) by 1.2 weight portion iron oxide reds, 0.8 weight portion triethylene tetramine, 1.2 weight portion oleoyl methylamine ethyl sulfonic acid sodium,
0.7 weight portion sodium tripolyphosphate, 9 weight portion E-42 epoxy resin put in 26 parts by weight of deionized water successively, stir；
2) put into successively again 13 parts of EVA emulsions, 2.2 weight portion chlorinated polyethylenees, 0.7 weight portion cetylpyridinium chloride, 0.7
Parts by weight of phosphoric acid disodium hydrogen, 0.4 weight portion potassium peroxydisulfate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
The movable gas filling station container of the various embodiments described above, its metal cabinet surface-coated has protective paint, makes metal box
Body has excellent antirust, corrosion-resistant, antioxidation, weather resistance, thus ensureing movable gas filling station container energy life-time service.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. a kind of movable gas filling station container is it is characterised in that include metal cabinet, this metal cabinet surface is covered with protection
Paint, described protective paint is made by the steps：
1) by 1～2 weight portion iron oxide red, 0.8 weight portion triethylene tetramine, 1.2 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 0.7
Weight portion sodium tripolyphosphate, 9 weight portion E-42 epoxy resin put in 26 parts by weight of deionized water successively, stir；
2) 13 parts of EVA emulsions, 2.2 weight portion chlorinated polyethylenees, 0.7 weight portion cetylpyridinium chloride, 0.7 weight are put into again successively
Part disodium hydrogen phosphate, 0.4 weight portion potassium peroxydisulfate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
2. movable gas filling station container according to claim 1 is it is characterised in that include metal cabinet, this metal box
Body surface face is covered with protective paint, and described protective paint is made by the steps：
1) by 1 weight portion iron oxide red, 0.8 weight portion triethylene tetramine, 1.2 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 0.7 weight
Part sodium tripolyphosphate, 9 weight portion E-42 epoxy resin put in 26 parts by weight of deionized water successively, stir；
2) 13 parts of EVA emulsions, 2.2 weight portion chlorinated polyethylenees, 0.7 weight portion cetylpyridinium chloride, 0.7 weight are put into again successively
Part disodium hydrogen phosphate, 0.4 weight portion potassium peroxydisulfate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
3. movable gas filling station container according to claim 1 is it is characterised in that include metal cabinet, this metal box
Body surface face is covered with protective paint, and described protective paint is made by the steps：
1) by 2 weight portion iron oxide reds, 0.8 weight portion triethylene tetramine, 1.2 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 0.7 weight
Part sodium tripolyphosphate, 9 weight portion E-42 epoxy resin put in 26 parts by weight of deionized water successively, stir；
2) 13 parts of EVA emulsions, 2.2 weight portion chlorinated polyethylenees, 0.7 weight portion cetylpyridinium chloride, 0.7 weight are put into again successively
Part disodium hydrogen phosphate, 0.4 weight portion potassium peroxydisulfate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
4. movable gas filling station container according to claim 1 is it is characterised in that include metal cabinet, this metal box
Body surface face is covered with protective paint, and described protective paint is made by the steps：
1) by 1.2 weight portion iron oxide reds, 0.8 weight portion triethylene tetramine, 1.2 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 0.7 weight
Amount part sodium tripolyphosphate, 9 weight portion E-42 epoxy resin put in 26 parts by weight of deionized water successively, stir；
2) 13 parts of EVA emulsions, 2.2 weight portion chlorinated polyethylenees, 0.7 weight portion cetylpyridinium chloride, 0.7 weight are put into again successively
Part disodium hydrogen phosphate, 0.4 weight portion potassium peroxydisulfate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.