CN106398492A - Taper sleeve for wire rod rolling mill - Google Patents
Taper sleeve for wire rod rolling mill Download PDFInfo
- Publication number
- CN106398492A CN106398492A CN201610783061.9A CN201610783061A CN106398492A CN 106398492 A CN106398492 A CN 106398492A CN 201610783061 A CN201610783061 A CN 201610783061A CN 106398492 A CN106398492 A CN 106398492A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- protective paint
- weight portion
- rolling mill
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a taper sleeve for a wire rod rolling mill. The surface of the metal main body is coated by protective paint. The protective paint is prepared by the following steps: (1) 1-2 parts by weight of xylene, 1.3 parts by weight of calcium carbonate, 1.9 parts by weight of sodium alkyl sulfate, 0.7 parts by weight of sodium tripolyphosphate, and 13 parts by weight of aqueous alkyd resin are added into 20 parts by weight of deionized water in order with uniform stirring; (2) 11 parts by weight of modified water-soluble phenolic resin, 2.3 parts by weight of hexanediol butyl ether acetate, 1.6 parts by weight of block polyoxyethylene-polyoxypropylene ether, 2.3 parts by weight of polyvinyl alcohol, and 2.6 parts by weight of 1,2-diethoxy estersil ethane are added in order, stirring is carried out continuously till uniform mixing, and the protective paint is prepared. The surface of the metal main body is coated by the protective paint, and long-term usage of the taper sleeve for the wire rod rolling mill is guaranteed.
Description
Technical field
The present invention relates to a kind of rod-rolling mill tapered sleeve.
Background technology
Existing rod-rolling mill tapered sleeve, heat-resisting, anti-oxidant, antirust, the decay resistance of its metal master have much room for improvement, shadow
Ring the Long-Time Service of rod-rolling mill tapered sleeve.
Content of the invention
It is an object of the invention to provide a kind of rod-rolling mill tapered sleeve, its metal body surface is coated with protective paint, makes
Metal master has excellent heat-resisting, anti-oxidant, antirust, decay resistance, thus ensureing that rod-rolling mill tapered sleeve can make for a long time
With.
For achieving the above object, the technical scheme is that a kind of rod-rolling mill tapered sleeve of design, including metal master,
This metal body surface is covered with protective paint, and described protective paint is made by the steps：
1) by 1～2 parts by weight of xylene, 1.3 weight parts of calcium carbonate, 1.9 weight portion alkyl sulfate sodium, 0.7 weight portion
Sodium tripolyphosphate, 13 weight portion aqueous alkide resins put in 20 parts by weight of deionized water successively, stir；
2) more successively put into 11 part by weight modified water soluble phenol resins, 2.3 weight portion hexylene glycol monobutyl ether acetates, 1.6
Weight parts of block polyoxyethylene polyoxypropylene ether, 2.3 weight account polyethylene alcohol, 2.6 weight portion 1,2- diethoxy estersil base second
Alkane, continues stirring, uniform to being sufficiently mixed, prepared protective paint.
Preferably, rod-rolling mill tapered sleeve, including metal master, this metal body surface is covered with protective paint, described anti-
Vernix is made by the steps：
1) by 1 parts by weight of xylene, 1.3 weight parts of calcium carbonate, 1.9 weight portion alkyl sulfate sodium, 0.7 weight portion trimerization
Sodium phosphate, 13 weight portion aqueous alkide resins put in 20 parts by weight of deionized water successively, stir；
2) more successively put into 11 part by weight modified water soluble phenol resins, 2.3 weight portion hexylene glycol monobutyl ether acetates, 1.6
Weight parts of block polyoxyethylene polyoxypropylene ether, 2.3 weight account polyethylene alcohol, 2.6 weight portion 1,2- diethoxy estersil base second
Alkane, continues stirring, uniform to being sufficiently mixed, prepared protective paint.
Preferably, rod-rolling mill tapered sleeve, including metal master, this metal body surface is covered with protective paint, described anti-
Vernix is made by the steps：
1) by 2 parts by weight of xylene, 1.3 weight parts of calcium carbonate, 1.9 weight portion alkyl sulfate sodium, 0.7 weight portion trimerization
Sodium phosphate, 13 weight portion aqueous alkide resins put in 20 parts by weight of deionized water successively, stir；
2) more successively put into 11 part by weight modified water soluble phenol resins, 2.3 weight portion hexylene glycol monobutyl ether acetates, 1.6
Weight parts of block polyoxyethylene polyoxypropylene ether, 2.3 weight account polyethylene alcohol, 2.6 weight portion 1,2- diethoxy estersil base second
Alkane, continues stirring, uniform to being sufficiently mixed, prepared protective paint.
Preferably, rod-rolling mill tapered sleeve, including metal master, this metal body surface is covered with protective paint, described anti-
Vernix is made by the steps：
1) by 1.2 parts by weight of xylene, 1.3 weight parts of calcium carbonate, 1.9 weight portion alkyl sulfate sodium, 0.7 weight portion three
Polyphosphate sodium, 13 weight portion aqueous alkide resins put in 20 parts by weight of deionized water successively, stir；
2) more successively put into 11 part by weight modified water soluble phenol resins, 2.3 weight portion hexylene glycol monobutyl ether acetates, 1.6
Weight parts of block polyoxyethylene polyoxypropylene ether, 2.3 weight account polyethylene alcohol, 2.6 weight portion 1,2- diethoxy estersil base second
Alkane, continues stirring, uniform to being sufficiently mixed, prepared protective paint.
Advantages of the present invention and having the beneficial effects that：There is provided a kind of rod-rolling mill tapered sleeve, its metal body surface coats
There is protective paint, make metal master have excellent heat-resisting, anti-oxidant, antirust, decay resistance, thus ensureing that rod-rolling mill is bored
Set can Long-Time Service.
The performance of " protective paint " and purposes are determined by its component and proportioning, and the different component meeting in " protective paint "
Influence each other, component and its proportioning can determine the final performance of " protective paint ", such as fruit component and its proportioning be not mutually coordinated, single
The beneficial effect that component is brought, even can be eliminated by other components abatement, when serious, different component is mutually conflicted, and rises
Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " protection
The optimal component of paint " and proportioning so that multiple component combine, mutually coordinated and produce positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is：
Embodiment 1
Rod-rolling mill tapered sleeve, including metal master, this metal body surface is covered with protective paint, and described protective paint passes through
Prepared by following steps：
1) by 1～2 parts by weight of xylene, 1.3 weight parts of calcium carbonate, 1.9 weight portion alkyl sulfate sodium, 0.7 weight portion
Sodium tripolyphosphate, 13 weight portion aqueous alkide resins put in 20 parts by weight of deionized water successively, stir；
2) more successively put into 11 part by weight modified water soluble phenol resins, 2.3 weight portion hexylene glycol monobutyl ether acetates, 1.6
Weight parts of block polyoxyethylene polyoxypropylene ether, 2.3 weight account polyethylene alcohol, 2.6 weight portion 1,2- diethoxy estersil base second
Alkane, continues stirring, uniform to being sufficiently mixed, prepared protective paint.
Embodiment 2
Rod-rolling mill tapered sleeve, including metal master, this metal body surface is covered with protective paint, and described protective paint passes through
Prepared by following steps：
1) by 1 parts by weight of xylene, 1.3 weight parts of calcium carbonate, 1.9 weight portion alkyl sulfate sodium, 0.7 weight portion trimerization
Sodium phosphate, 13 weight portion aqueous alkide resins put in 20 parts by weight of deionized water successively, stir；
2) more successively put into 11 part by weight modified water soluble phenol resins, 2.3 weight portion hexylene glycol monobutyl ether acetates, 1.6
Weight parts of block polyoxyethylene polyoxypropylene ether, 2.3 weight account polyethylene alcohol, 2.6 weight portion 1,2- diethoxy estersil base second
Alkane, continues stirring, uniform to being sufficiently mixed, prepared protective paint.
Embodiment 3
Rod-rolling mill tapered sleeve, including metal master, this metal body surface is covered with protective paint, and described protective paint passes through
Prepared by following steps：
1) by 2 parts by weight of xylene, 1.3 weight parts of calcium carbonate, 1.9 weight portion alkyl sulfate sodium, 0.7 weight portion trimerization
Sodium phosphate, 13 weight portion aqueous alkide resins put in 20 parts by weight of deionized water successively, stir；
2) more successively put into 11 part by weight modified water soluble phenol resins, 2.3 weight portion hexylene glycol monobutyl ether acetates, 1.6
Weight parts of block polyoxyethylene polyoxypropylene ether, 2.3 weight account polyethylene alcohol, 2.6 weight portion 1,2- diethoxy estersil base second
Alkane, continues stirring, uniform to being sufficiently mixed, prepared protective paint.
Embodiment 4
Rod-rolling mill tapered sleeve, including metal master, this metal body surface is covered with protective paint, and described protective paint passes through
Prepared by following steps：
1) by 1.2 parts by weight of xylene, 1.3 weight parts of calcium carbonate, 1.9 weight portion alkyl sulfate sodium, 0.7 weight portion three
Polyphosphate sodium, 13 weight portion aqueous alkide resins put in 20 parts by weight of deionized water successively, stir；
2) more successively put into 11 part by weight modified water soluble phenol resins, 2.3 weight portion hexylene glycol monobutyl ether acetates, 1.6
Weight parts of block polyoxyethylene polyoxypropylene ether, 2.3 weight account polyethylene alcohol, 2.6 weight portion 1,2- diethoxy estersil base second
Alkane, continues stirring, uniform to being sufficiently mixed, prepared protective paint.
The rod-rolling mill tapered sleeve of the various embodiments described above, its metal body surface is coated with protective paint, so that metal master is had
There is excellent heat-resisting, anti-oxidant, antirust, decay resistance, thus ensureing rod-rolling mill tapered sleeve energy Long-Time Service.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. it is characterised in that including metal master, this metal body surface is covered with protective paint to a kind of rod-rolling mill tapered sleeve,
Described protective paint is made by the steps：
1) by 1～2 parts by weight of xylene, 1.3 weight parts of calcium carbonate, 1.9 weight portion alkyl sulfate sodium, 0.7 weight portion trimerization
Sodium phosphate, 13 weight portion aqueous alkide resins put in 20 parts by weight of deionized water successively, stir；
2) 11 part by weight modified water soluble phenol resins, 2.3 weight portion hexylene glycol monobutyl ether acetates, 1.6 weight are put into again successively
Part Block polyoxyethylene-polyethenoxy ether, 2.3 weight account polyethylene alcohol, 2.6 weight portions 1,2- diethoxy estersil base ethane,
Continue stirring, prepared protective paint uniform to being sufficiently mixed.
2. rod-rolling mill tapered sleeve according to claim 1 is it is characterised in that include metal master, this metal master table
Face is covered with protective paint, and described protective paint is made by the steps：
1) by 1 parts by weight of xylene, 1.3 weight parts of calcium carbonate, 1.9 weight portion alkyl sulfate sodium, 0.7 weight portion tripolyphosphate
Sodium, 13 weight portion aqueous alkide resins put in 20 parts by weight of deionized water successively, stir；
2) 11 part by weight modified water soluble phenol resins, 2.3 weight portion hexylene glycol monobutyl ether acetates, 1.6 weight are put into again successively
Part Block polyoxyethylene-polyethenoxy ether, 2.3 weight account polyethylene alcohol, 2.6 weight portions 1,2- diethoxy estersil base ethane,
Continue stirring, prepared protective paint uniform to being sufficiently mixed.
3. rod-rolling mill tapered sleeve according to claim 1 is it is characterised in that include metal master, this metal master table
Face is covered with protective paint, and described protective paint is made by the steps：
1) by 2 parts by weight of xylene, 1.3 weight parts of calcium carbonate, 1.9 weight portion alkyl sulfate sodium, 0.7 weight portion tripolyphosphate
Sodium, 13 weight portion aqueous alkide resins put in 20 parts by weight of deionized water successively, stir；
2) 11 part by weight modified water soluble phenol resins, 2.3 weight portion hexylene glycol monobutyl ether acetates, 1.6 weight are put into again successively
Part Block polyoxyethylene-polyethenoxy ether, 2.3 weight account polyethylene alcohol, 2.6 weight portions 1,2- diethoxy estersil base ethane,
Continue stirring, prepared protective paint uniform to being sufficiently mixed.
4. rod-rolling mill tapered sleeve according to claim 1 is it is characterised in that include metal master, this metal master table
Face is covered with protective paint, and described protective paint is made by the steps：
1) by 1.2 parts by weight of xylene, 1.3 weight parts of calcium carbonate, 1.9 weight portion alkyl sulfate sodium, 0.7 weight portion trimerization phosphorus
Sour sodium, 13 weight portion aqueous alkide resins put in 20 parts by weight of deionized water successively, stir；
2) 11 part by weight modified water soluble phenol resins, 2.3 weight portion hexylene glycol monobutyl ether acetates, 1.6 weight are put into again successively
Part Block polyoxyethylene-polyethenoxy ether, 2.3 weight account polyethylene alcohol, 2.6 weight portions 1,2- diethoxy estersil base ethane,
Continue stirring, prepared protective paint uniform to being sufficiently mixed.