CN107674580A - A kind of spinneret - Google Patents
A kind of spinneret Download PDFInfo
- Publication number
- CN107674580A CN107674580A CN201711088601.2A CN201711088601A CN107674580A CN 107674580 A CN107674580 A CN 107674580A CN 201711088601 A CN201711088601 A CN 201711088601A CN 107674580 A CN107674580 A CN 107674580A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- protective paint
- spinneret
- body surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of spinneret, its metal body surface Tu is covered with protective paint, and protective paint is made by the steps：1）1~2 parts by weight aluminum paste, 2.1 parts by weight maleic anhydrides, 2.3 parts by weight heterogeneous ten alcohol polyoxyethylene ethers, 4.1 parts by weight polyethylene glycol, 12 parts by weight silicones are put into 20 parts by weight of deionized water successively, stirred；2）Put into 8 parts by weight aniline-formaldehyde resins, 1.3 parts by weight MEKs, 1.8 parts by weight castor oil polyoxyethylene ethers, 2.3 parts by weight polyisobutene, 0.9 parts by weight morpholine successively again, continue to stir, to being sufficiently mixed uniformly, protective paint is made.Spinneret of the present invention, its metal body surface are coated with protective paint, can ensure spinneret long-term use.
Description
Technical field
The present invention relates to a kind of spinneret.
Background technology
Existing spinneret, the heat-resisting, anti-oxidant of its metal master, antirust, decay resistance have much room for improvement, and influence spinneret
Long-term use.
The content of the invention
It is an object of the invention to provide a kind of spinneret, its metal body surface is coated with protective paint, makes metal master
With excellent heat-resisting, anti-oxidant, antirust, decay resistance, so as to ensure that spinneret can be long-term use of.
To achieve the above object, the technical scheme is that designing a kind of spinneret, including metal master, metal master
Body surface face Tu is covered with protective paint, and the protective paint is made by the steps：
1）By 1~2 parts by weight aluminum paste, 2.1 parts by weight maleic anhydrides, 2.3 parts by weight heterogeneous ten alcohol polyoxyethylene ethers,
4.1 parts by weight polyethylene glycol, 12 parts by weight silicones are put into 20 parts by weight of deionized water successively, are stirred；
2）Put into 8 parts by weight aniline-formaldehyde resins, 1.3 parts by weight MEKs, 1.8 parts by weight castor oil polyoxyethylenes successively again
Ether, 2.3 parts by weight polyisobutene, 0.9 parts by weight morpholine, continue to stir, and to being sufficiently mixed uniformly, protective paint is made.
Preferably, spinneret, including metal master, the metal body surface Tu are covered with protective paint, and the protective paint passes through
It is prepared by following steps：
1）By 1 parts by weight aluminum paste, 2.1 parts by weight maleic anhydrides, 2.3 parts by weight heterogeneous ten alcohol polyoxyethylene ethers, 4.1 weights
Amount part polyethylene glycol, 12 parts by weight silicones are put into 20 parts by weight of deionized water successively, are stirred；
2）Put into 8 parts by weight aniline-formaldehyde resins, 1.3 parts by weight MEKs, 1.8 parts by weight castor oil polyoxyethylenes successively again
Ether, 2.3 parts by weight polyisobutene, 0.9 parts by weight morpholine, continue to stir, and to being sufficiently mixed uniformly, protective paint is made.
Preferably, spinneret, including metal master, the metal body surface Tu are covered with protective paint, and the protective paint passes through
It is prepared by following steps：
1）By 2 parts by weight aluminum pastes, 2.1 parts by weight maleic anhydrides, 2.3 parts by weight heterogeneous ten alcohol polyoxyethylene ethers, 4.1 weights
Amount part polyethylene glycol, 12 parts by weight silicones are put into 20 parts by weight of deionized water successively, are stirred；
2）Put into 8 parts by weight aniline-formaldehyde resins, 1.3 parts by weight MEKs, 1.8 parts by weight castor oil polyoxyethylenes successively again
Ether, 2.3 parts by weight polyisobutene, 0.9 parts by weight morpholine, continue to stir, and to being sufficiently mixed uniformly, protective paint is made.
Preferably, spinneret, including metal master, the metal body surface Tu are covered with protective paint, and the protective paint passes through
It is prepared by following steps：
1）By 1.2 parts by weight aluminum pastes, 2.1 parts by weight maleic anhydrides, 2.3 parts by weight heterogeneous ten alcohol polyoxyethylene ethers, 4.1
Parts by weight polyethylene glycol, 12 parts by weight silicones are put into 20 parts by weight of deionized water successively, are stirred；
2）Put into 8 parts by weight aniline-formaldehyde resins, 1.3 parts by weight MEKs, 1.8 parts by weight castor oil polyoxyethylenes successively again
Ether, 2.3 parts by weight polyisobutene, 0.9 parts by weight morpholine, continue to stir, and to being sufficiently mixed uniformly, protective paint is made.
The advantages of the present invention are：A kind of spinneret is provided, its metal body surface is coated with protective paint,
Make metal master that there is excellent heat-resisting, anti-oxidant, antirust, decay resistance, so as to ensure that spinneret can be long-term use of.
The performance and purposes of " protective paint " are determined by its component and proportioning, and the different component meeting in " protective paint "
Influence each other, component and its proportioning can determine the final performance of " protective paint ", single such as fruit component and its proportioning be not mutually coordinated
Beneficial effect caused by component, it can be cut down by other components and even eliminate, when serious, different component mutually contradicts, and rises
Acted on less than whole synthesis, produce negative interaction and substandard products.The present invention obtains " protection by a large amount of creative works, verify repeatedly
The optimal component and proportioning of paint " so that multiple components combine, mutually coordinated and produce positive comprehensive effect.
Embodiment
With reference to embodiment, the embodiment of the present invention is further described.Following examples are only used for more
Add and clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied is：
Embodiment 1
Spinneret, including metal master, the metal body surface Tu are covered with protective paint, and the protective paint is made as follows
It is standby：
1）By 1~2 parts by weight aluminum paste, 2.1 parts by weight maleic anhydrides, 2.3 parts by weight heterogeneous ten alcohol polyoxyethylene ethers,
4.1 parts by weight polyethylene glycol, 12 parts by weight silicones are put into 20 parts by weight of deionized water successively, are stirred；
2）Put into 8 parts by weight aniline-formaldehyde resins, 1.3 parts by weight MEKs, 1.8 parts by weight castor oil polyoxyethylenes successively again
Ether, 2.3 parts by weight polyisobutene, 0.9 parts by weight morpholine, continue to stir, and to being sufficiently mixed uniformly, protective paint is made.
Embodiment 2
Spinneret, including metal master, the metal body surface Tu are covered with protective paint, and the protective paint is made as follows
It is standby：
1）By 1 parts by weight aluminum paste, 2.1 parts by weight maleic anhydrides, 2.3 parts by weight heterogeneous ten alcohol polyoxyethylene ethers, 4.1 weights
Amount part polyethylene glycol, 12 parts by weight silicones are put into 20 parts by weight of deionized water successively, are stirred；
2）Put into 8 parts by weight aniline-formaldehyde resins, 1.3 parts by weight MEKs, 1.8 parts by weight castor oil polyoxyethylenes successively again
Ether, 2.3 parts by weight polyisobutene, 0.9 parts by weight morpholine, continue to stir, and to being sufficiently mixed uniformly, protective paint is made.
Embodiment 3
Spinneret, including metal master, the metal body surface Tu are covered with protective paint, and the protective paint is made as follows
It is standby：
1）By 2 parts by weight aluminum pastes, 2.1 parts by weight maleic anhydrides, 2.3 parts by weight heterogeneous ten alcohol polyoxyethylene ethers, 4.1 weights
Amount part polyethylene glycol, 12 parts by weight silicones are put into 20 parts by weight of deionized water successively, are stirred；
2）Put into 8 parts by weight aniline-formaldehyde resins, 1.3 parts by weight MEKs, 1.8 parts by weight castor oil polyoxyethylenes successively again
Ether, 2.3 parts by weight polyisobutene, 0.9 parts by weight morpholine, continue to stir, and to being sufficiently mixed uniformly, protective paint is made.
Embodiment 4
Spinneret, including metal master, the metal body surface Tu are covered with protective paint, and the protective paint is made as follows
It is standby：
1）By 1.2 parts by weight aluminum pastes, 2.1 parts by weight maleic anhydrides, 2.3 parts by weight heterogeneous ten alcohol polyoxyethylene ethers, 4.1
Parts by weight polyethylene glycol, 12 parts by weight silicones are put into 20 parts by weight of deionized water successively, are stirred；
2）Put into 8 parts by weight aniline-formaldehyde resins, 1.3 parts by weight MEKs, 1.8 parts by weight castor oil polyoxyethylenes successively again
Ether, 2.3 parts by weight polyisobutene, 0.9 parts by weight morpholine, continue to stir, and to being sufficiently mixed uniformly, protective paint is made.
The spinneret of the various embodiments described above, its metal body surface are coated with protective paint, have metal master excellent
Heat-resisting, anti-oxidant, antirust, decay resistance, so as to ensure that spinneret can be long-term use of.
Described above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, some improvements and modifications can also be made, these improvements and modifications
Also it should be regarded as protection scope of the present invention.
Claims (4)
1. a kind of spinneret, it is characterised in that including metal master, the metal body surface Tu is covered with protective paint, the protection
Paint is made by the steps：
1）By 1~2 parts by weight aluminum paste, 2.1 parts by weight maleic anhydrides, 2.3 parts by weight heterogeneous ten alcohol polyoxyethylene ethers,
4.1 parts by weight polyethylene glycol, 12 parts by weight silicones are put into 20 parts by weight of deionized water successively, are stirred；
2）Put into 8 parts by weight aniline-formaldehyde resins, 1.3 parts by weight MEKs, 1.8 parts by weight castor oil polyoxyethylenes successively again
Ether, 2.3 parts by weight polyisobutene, 0.9 parts by weight morpholine, continue to stir, and to being sufficiently mixed uniformly, protective paint is made.
2. spinneret according to claim 1, it is characterised in that including metal master, the metal body surface Tu is covered with
Protective paint, the protective paint are made by the steps：
1）By 1 parts by weight aluminum paste, 2.1 parts by weight maleic anhydrides, 2.3 parts by weight heterogeneous ten alcohol polyoxyethylene ethers, 4.1 weights
Amount part polyethylene glycol, 12 parts by weight silicones are put into 20 parts by weight of deionized water successively, are stirred；
2）Put into 8 parts by weight aniline-formaldehyde resins, 1.3 parts by weight MEKs, 1.8 parts by weight castor oil polyoxyethylenes successively again
Ether, 2.3 parts by weight polyisobutene, 0.9 parts by weight morpholine, continue to stir, and to being sufficiently mixed uniformly, protective paint is made.
3. spinneret according to claim 1, it is characterised in that including metal master, the metal body surface Tu is covered with
Protective paint, the protective paint are made by the steps：
1）By 2 parts by weight aluminum pastes, 2.1 parts by weight maleic anhydrides, 2.3 parts by weight heterogeneous ten alcohol polyoxyethylene ethers, 4.1 weights
Amount part polyethylene glycol, 12 parts by weight silicones are put into 20 parts by weight of deionized water successively, are stirred；
2）Put into 8 parts by weight aniline-formaldehyde resins, 1.3 parts by weight MEKs, 1.8 parts by weight castor oil polyoxyethylenes successively again
Ether, 2.3 parts by weight polyisobutene, 0.9 parts by weight morpholine, continue to stir, and to being sufficiently mixed uniformly, protective paint is made.
4. spinneret according to claim 1, it is characterised in that including metal master, the metal body surface Tu is covered with
Protective paint, the protective paint are made by the steps：
1）By 1.2 parts by weight aluminum pastes, 2.1 parts by weight maleic anhydrides, 2.3 parts by weight heterogeneous ten alcohol polyoxyethylene ethers, 4.1
Parts by weight polyethylene glycol, 12 parts by weight silicones are put into 20 parts by weight of deionized water successively, are stirred；
2）Put into 8 parts by weight aniline-formaldehyde resins, 1.3 parts by weight MEKs, 1.8 parts by weight castor oil polyoxyethylenes successively again
Ether, 2.3 parts by weight polyisobutene, 0.9 parts by weight morpholine, continue to stir, and to being sufficiently mixed uniformly, protective paint is made.