CN106381028A - Electrical cabinet - Google Patents
Electrical cabinet Download PDFInfo
- Publication number
- CN106381028A CN106381028A CN201610777070.7A CN201610777070A CN106381028A CN 106381028 A CN106381028 A CN 106381028A CN 201610777070 A CN201610777070 A CN 201610777070A CN 106381028 A CN106381028 A CN 106381028A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- weight portion
- metal cabinet
- weight parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an electrical cabinet. The surface of a metal cabinet body is coated with a protection paint, the protection paint comprises the following steps: 1) placing 1-2 weight parts of amounts by weight, 0.5 weight parts of aluminium triphosphate, 1.1 weight parts of Igepon T, 1.3 weight parts of vinyltrimethoxy silane, and 9 weight parts of alkyd resin in 26 weight parts of deionized water in order, uniformly stirring the raw materials; and 2) placing 7 weight parts of isobutanol etherified urea-formaldehyde, 0.6 weight parts of hydrated magnesium silicate, 1.6 weight parts of dodecyl trimethyl ammonium chloride, 1.5 weight parts of sodium borate, and 1.1 weight parts of urea, continuously stirring the raw materials, and fully and uniformly mixing the materials to obtain the protection paint. According to the electrical cabinet, the surface of the metal cabinet body is coated with the protection paint, so that long-term usage of the electrical cabinet can be guaranteed.
Description
Technical field
The present invention relates to a kind of electric box.
Background technology
Existing electric box, antirust, corrosion-resistant, anti-oxidant, the weather resistance of its metal cabinet have much room for improvement, and affect electric box
Long-Time Service.
Content of the invention
It is an object of the invention to provide a kind of electric box, its metal cabinet surface is coated with protective paint, makes metal cabinet
There is excellent antirust, corrosion-resistant, anti-oxidant, weather resistance, thus ensureing electric box energy Long-Time Service.
For achieving the above object, the technical scheme is that a kind of electric box of design, including metal cabinet, this metal box
Body surface face is covered with protective paint, and described protective paint is made by the steps：
1) by 1～2 parts by weight of acrylonitrile, 0.5 weight portion aluminium triphosphate, 1.1 weight portion Igepon Ts, 1.3 weight portion second
Thiazolinyl trimethoxy silane, 9 weight portion alkyd resins put in 26 parts by weight of deionized water successively, stir；
2) 7 parts by weight of isobutanol etherificate Lauxites, 0.6 weight portion hydrated magnesium silicate, 1.6 weight portions ten are put into again successively
Dialkyl group trimethyl ammonium chloride, 1.5 part by weight of boric acid sodium, 1.1 parts by weight of urea, continue stirring, to being sufficiently mixed uniformly, are obtained
Protective paint.
Preferably, electric box, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint passes through
Prepared by following steps：
1) by 1 parts by weight of acrylonitrile, 0.5 weight portion aluminium triphosphate, 1.1 weight portion Igepon Ts, 1.3 parts by weight of ethylene
Base trimethoxy silane, 9 weight portion alkyd resins put in 26 parts by weight of deionized water successively, stir；
2) 7 parts by weight of isobutanol etherificate Lauxites, 0.6 weight portion hydrated magnesium silicate, 1.6 weight portions ten are put into again successively
Dialkyl group trimethyl ammonium chloride, 1.5 part by weight of boric acid sodium, 1.1 parts by weight of urea, continue stirring, to being sufficiently mixed uniformly, are obtained
Protective paint.
Preferably, electric box, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint passes through
Prepared by following steps：
1) by 2 parts by weight of acrylonitrile, 0.5 weight portion aluminium triphosphate, 1.1 weight portion Igepon Ts, 1.3 parts by weight of ethylene
Base trimethoxy silane, 9 weight portion alkyd resins put in 26 parts by weight of deionized water successively, stir；
2) 7 parts by weight of isobutanol etherificate Lauxites, 0.6 weight portion hydrated magnesium silicate, 1.6 weight portions ten are put into again successively
Dialkyl group trimethyl ammonium chloride, 1.5 part by weight of boric acid sodium, 1.1 parts by weight of urea, continue stirring, to being sufficiently mixed uniformly, are obtained
Protective paint.
Preferably, electric box, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint passes through
Prepared by following steps：
1) by 1.2 parts by weight of acrylonitrile, 0.5 weight portion aluminium triphosphate, 1.1 weight portion Igepon Ts, 1.3 weight portion second
Thiazolinyl trimethoxy silane, 9 weight portion alkyd resins put in 26 parts by weight of deionized water successively, stir；
2) 7 parts by weight of isobutanol etherificate Lauxites, 0.6 weight portion hydrated magnesium silicate, 1.6 weight portions ten are put into again successively
Dialkyl group trimethyl ammonium chloride, 1.5 part by weight of boric acid sodium, 1.1 parts by weight of urea, continue stirring, to being sufficiently mixed uniformly, are obtained
Protective paint.
Advantages of the present invention and having the beneficial effects that：There is provided a kind of electric box, its metal cabinet surface is coated with protective paint,
Metal cabinet is made to have excellent antirust, corrosion-resistant, anti-oxidant, weather resistance, thus ensureing electric box energy Long-Time Service.
The performance of " protective paint " and purposes are determined by its component and proportioning, and the different component meeting in " protective paint "
Influence each other, component and its proportioning can determine the final performance of " protective paint ", such as fruit component and its proportioning be not mutually coordinated, single
The beneficial effect that component is brought, even can be eliminated by other components abatement, when serious, different component is mutually conflicted, and rises
Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " protection
The optimal component of paint " and proportioning so that multiple component combine, mutually coordinated and produce positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is：
Embodiment 1
Electric box, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint is as follows
Preparation：
1) by 1～2 parts by weight of acrylonitrile, 0.5 weight portion aluminium triphosphate, 1.1 weight portion Igepon Ts, 1.3 weight portion second
Thiazolinyl trimethoxy silane, 9 weight portion alkyd resins put in 26 parts by weight of deionized water successively, stir；
2) 7 parts by weight of isobutanol etherificate Lauxites, 0.6 weight portion hydrated magnesium silicate, 1.6 weight portions ten are put into again successively
Dialkyl group trimethyl ammonium chloride, 1.5 part by weight of boric acid sodium, 1.1 parts by weight of urea, continue stirring, to being sufficiently mixed uniformly, are obtained
Protective paint.
Embodiment 2
Electric box, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint is as follows
Preparation：
1) by 1 parts by weight of acrylonitrile, 0.5 weight portion aluminium triphosphate, 1.1 weight portion Igepon Ts, 1.3 parts by weight of ethylene
Base trimethoxy silane, 9 weight portion alkyd resins put in 26 parts by weight of deionized water successively, stir；
2) 7 parts by weight of isobutanol etherificate Lauxites, 0.6 weight portion hydrated magnesium silicate, 1.6 weight portions ten are put into again successively
Dialkyl group trimethyl ammonium chloride, 1.5 part by weight of boric acid sodium, 1.1 parts by weight of urea, continue stirring, to being sufficiently mixed uniformly, are obtained
Protective paint.
Embodiment 3
Electric box, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint is as follows
Preparation：
1) by 2 parts by weight of acrylonitrile, 0.5 weight portion aluminium triphosphate, 1.1 weight portion Igepon Ts, 1.3 parts by weight of ethylene
Base trimethoxy silane, 9 weight portion alkyd resins put in 26 parts by weight of deionized water successively, stir；
2) 7 parts by weight of isobutanol etherificate Lauxites, 0.6 weight portion hydrated magnesium silicate, 1.6 weight portions ten are put into again successively
Dialkyl group trimethyl ammonium chloride, 1.5 part by weight of boric acid sodium, 1.1 parts by weight of urea, continue stirring, to being sufficiently mixed uniformly, are obtained
Protective paint.
Embodiment 4
Electric box, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint is as follows
Preparation：
1) by 1.2 parts by weight of acrylonitrile, 0.5 weight portion aluminium triphosphate, 1.1 weight portion Igepon Ts, 1.3 weight portion second
Thiazolinyl trimethoxy silane, 9 weight portion alkyd resins put in 26 parts by weight of deionized water successively, stir；
2) 7 parts by weight of isobutanol etherificate Lauxites, 0.6 weight portion hydrated magnesium silicate, 1.6 weight portions ten are put into again successively
Dialkyl group trimethyl ammonium chloride, 1.5 part by weight of boric acid sodium, 1.1 parts by weight of urea, continue stirring, to being sufficiently mixed uniformly, are obtained
Protective paint.
The electric box of the various embodiments described above, its metal cabinet surface is coated with protective paint, so that metal cabinet is had excellent
Antirust, corrosion-resistant, anti-oxidant, weather resistance, thus ensure electric box energy Long-Time Service.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. it is characterised in that including metal cabinet, this metal cabinet surface is covered with protective paint to a kind of electric box, described protection
Paint is made by the steps：
1) by 1～2 parts by weight of acrylonitrile, 0.5 weight portion aluminium triphosphate, 1.1 weight portion Igepon Ts, 1.3 parts by weight of ethylene bases
Trimethoxy silane, 9 weight portion alkyd resins put in 26 parts by weight of deionized water successively, stir；
2) 7 parts by weight of isobutanol etherificate Lauxites, 0.6 weight portion hydrated magnesium silicate, 1.6 weight portion dodecanes are put into again successively
Base trimethyl ammonium chloride, 1.5 part by weight of boric acid sodium, 1.1 parts by weight of urea, continue stirring, to being sufficiently mixed uniformly, protection are obtained
Paint.
2. electric box according to claim 1 is it is characterised in that include metal cabinet, this metal cabinet surface is covered with
Protective paint, described protective paint is made by the steps：
1) by 1 parts by weight of acrylonitrile, 0.5 weight portion aluminium triphosphate, 1.1 weight portion Igepon Ts, 1.3 parts by weight of ethylene bases three
Methoxy silane, 9 weight portion alkyd resins put in 26 parts by weight of deionized water successively, stir；
2) 7 parts by weight of isobutanol etherificate Lauxites, 0.6 weight portion hydrated magnesium silicate, 1.6 weight portion dodecanes are put into again successively
Base trimethyl ammonium chloride, 1.5 part by weight of boric acid sodium, 1.1 parts by weight of urea, continue stirring, to being sufficiently mixed uniformly, protection are obtained
Paint.
3. electric box according to claim 1 is it is characterised in that include metal cabinet, this metal cabinet surface is covered with
Protective paint, described protective paint is made by the steps：
1) by 2 parts by weight of acrylonitrile, 0.5 weight portion aluminium triphosphate, 1.1 weight portion Igepon Ts, 1.3 parts by weight of ethylene bases three
Methoxy silane, 9 weight portion alkyd resins put in 26 parts by weight of deionized water successively, stir；
2) 7 parts by weight of isobutanol etherificate Lauxites, 0.6 weight portion hydrated magnesium silicate, 1.6 weight portion dodecanes are put into again successively
Base trimethyl ammonium chloride, 1.5 part by weight of boric acid sodium, 1.1 parts by weight of urea, continue stirring, to being sufficiently mixed uniformly, protection are obtained
Paint.
4. electric box according to claim 1 is it is characterised in that include metal cabinet, this metal cabinet surface is covered with
Protective paint, described protective paint is made by the steps：
1) by 1.2 parts by weight of acrylonitrile, 0.5 weight portion aluminium triphosphate, 1.1 weight portion Igepon Ts, 1.3 parts by weight of ethylene bases
Trimethoxy silane, 9 weight portion alkyd resins put in 26 parts by weight of deionized water successively, stir；
2) 7 parts by weight of isobutanol etherificate Lauxites, 0.6 weight portion hydrated magnesium silicate, 1.6 weight portion dodecanes are put into again successively
Base trimethyl ammonium chloride, 1.5 part by weight of boric acid sodium, 1.1 parts by weight of urea, continue stirring, to being sufficiently mixed uniformly, protection are obtained
Paint.