CN106283006A - Measurer calibration equipment - Google Patents
Measurer calibration equipment Download PDFInfo
- Publication number
- CN106283006A CN106283006A CN201610717209.9A CN201610717209A CN106283006A CN 106283006 A CN106283006 A CN 106283006A CN 201610717209 A CN201610717209 A CN 201610717209A CN 106283006 A CN106283006 A CN 106283006A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- weight portion
- metal shell
- treatment liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of measurer calibration equipment, it includes metal shell, this metal shell is through aluminum coated steel, described aluminum coated steel comprises the steps: 1) 1~2 weight portion amine molybdates, 1.1 parts by weight sodium, 1.8 weight portion sodium silicate, 0.7 weight portion ethylenediamine polyoxyethylene oxypropylene block formula polyethers are put in 48 parts by weight of deionized water successively, stir;2) put into 11.7 parts by weight of bisphenol A type epoxy resin, 5.7 parts by weight of acrylic acid methyl ester, 0.8 weight portion dodecyl sodium sulfate, 1.3 part by weight of boric acid morpholines the most successively, continue stirring, to being sufficiently mixed uniformly, prepare coating treatment liquid;3) metal shell is inserted in coating treatment liquid and impregnate, take out post-drying.Measurer calibration equipment of the present invention, its metal housing surface is covered with protecting film, and performance is good, and surface smoothness is good.
Description
Technical field
The present invention relates to measurer calibration equipment.
Background technology
Existing measurer calibration equipment, the antioxidation of its metal shell, abrasion-resistant, corrosion-resistant, antirust, heat-resisting, cold-resistant, weather-proof
Performance has much room for improvement, and surface smoothness is the most not ideal enough.
Summary of the invention
It is an object of the invention to provide a kind of measurer calibration equipment, its metal shell is through aluminum coated steel, metal shell
Surface is covered with protecting film, has the antioxidation of excellence, abrasion-resistant, corrosion-resistant, antirust, heat-resisting, cold-resistant, weather resistance, and surface
Fineness is good.
For achieving the above object, the technical scheme is that a kind of measurer calibration equipment of design, it includes metal shell,
This metal shell is through aluminum coated steel, and described aluminum coated steel comprises the steps:
1) by 1~2 weight portion amine molybdates, 1.1 parts by weight sodium, 1.8 weight portion sodium silicate, 0.7 weight portion second two
Amine polyoxyethylene polyoxypropylene blocked polyethers puts in 48 parts by weight of deionized water successively, stirs;
2) 11.7 parts by weight of bisphenol A type epoxy resin, 5.7 parts by weight of acrylic acid methyl ester, 0.8 weight portion ten are put into the most successively
Dialkyl sulfonates, 1.3 part by weight of boric acid morpholines, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) metal shell is inserted in coating treatment liquid and impregnate, take out post-drying.
Preferably, measurer calibration equipment, it includes metal shell, and this metal shell is through aluminum coated steel, at described overlay film
Reason comprises the steps:
1) 1 weight portion amine molybdate, 1.1 parts by weight sodium, 1.8 weight portion sodium silicate, 0.7 weight portion ethylenediamine are gathered
Oxygen ethylene oxypropylene block formula polyethers puts in 48 parts by weight of deionized water successively, stirs;
2) 11.7 parts by weight of bisphenol A type epoxy resin, 5.7 parts by weight of acrylic acid methyl ester, 0.8 weight portion ten are put into the most successively
Dialkyl sulfonates, 1.3 part by weight of boric acid morpholines, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) metal shell is inserted in coating treatment liquid and impregnate, take out post-drying.
Preferably, measurer calibration equipment, it includes metal shell, and this metal shell is through aluminum coated steel, at described overlay film
Reason comprises the steps:
1) 2 weight portion amine molybdates, 1.1 parts by weight sodium, 1.8 weight portion sodium silicate, 0.7 weight portion ethylenediamine are gathered
Oxygen ethylene oxypropylene block formula polyethers puts in 48 parts by weight of deionized water successively, stirs;
2) 11.7 parts by weight of bisphenol A type epoxy resin, 5.7 parts by weight of acrylic acid methyl ester, 0.8 weight portion ten are put into the most successively
Dialkyl sulfonates, 1.3 part by weight of boric acid morpholines, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) metal shell is inserted in coating treatment liquid and impregnate, take out post-drying.
Preferably, measurer calibration equipment, it includes metal shell, and this metal shell is through aluminum coated steel, at described overlay film
Reason comprises the steps:
1) by 1.2 weight portion amine molybdates, 1.1 parts by weight sodium, 1.8 weight portion sodium silicate, 0.7 weight portion ethylenediamine
Polyoxyethylene polyoxypropylene blocked polyethers puts in 48 parts by weight of deionized water successively, stirs;
2) 11.7 parts by weight of bisphenol A type epoxy resin, 5.7 parts by weight of acrylic acid methyl ester, 0.8 weight portion ten are put into the most successively
Dialkyl sulfonates, 1.3 part by weight of boric acid morpholines, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) metal shell is inserted in coating treatment liquid and impregnate, take out post-drying.
Advantages of the present invention and having the beneficial effects that: providing a kind of measurer calibration equipment, its metal shell is at overlay film
Reason, metal housing surface is covered with protecting film, has the antioxidation of excellence, abrasion-resistant, corrosion-resistant, antirust, heat-resisting, cold-resistant, weather-proof
Performance, and surface smoothness is good.
Performance and the purposes of " coating treatment liquid " are determined by its component and proportioning, and in " coating treatment liquid " not
Can influence each other with component, component and proportioning thereof can determine the final performance of " coating treatment liquid ", such as fruit component and proportioning thereof not
Mutually coordinated, that single component is brought beneficial effect, even can be eliminated by other components abatement, the when of serious, and different groups
Split-phase is conflicted mutually, does not has whole synthesis effect, produces negative interaction and substandard products.The present invention is by a large amount of creative works, repeatedly
Checking, obtains optimal component and the proportioning of " coating treatment liquid " so that multiple components combine, mutually coordinated and produce
Forward comprehensive effect.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.Following example are only used for more
Add and clearly demonstrate technical scheme, and can not limit the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Measurer calibration equipment, it includes metal shell, this metal shell through aluminum coated steel, described aluminum coated steel include as
Lower step:
1) by 1~2 weight portion amine molybdates, 1.1 parts by weight sodium, 1.8 weight portion sodium silicate, 0.7 weight portion second two
Amine polyoxyethylene polyoxypropylene blocked polyethers puts in 48 parts by weight of deionized water successively, stirs;
2) 11.7 parts by weight of bisphenol A type epoxy resin, 5.7 parts by weight of acrylic acid methyl ester, 0.8 weight portion ten are put into the most successively
Dialkyl sulfonates, 1.3 part by weight of boric acid morpholines, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) metal shell is inserted in coating treatment liquid and impregnate, take out post-drying.
Embodiment 2
Measurer calibration equipment, it includes metal shell, this metal shell through aluminum coated steel, described aluminum coated steel include as
Lower step:
1) 1 weight portion amine molybdate, 1.1 parts by weight sodium, 1.8 weight portion sodium silicate, 0.7 weight portion ethylenediamine are gathered
Oxygen ethylene oxypropylene block formula polyethers puts in 48 parts by weight of deionized water successively, stirs;
2) 11.7 parts by weight of bisphenol A type epoxy resin, 5.7 parts by weight of acrylic acid methyl ester, 0.8 weight portion ten are put into the most successively
Dialkyl sulfonates, 1.3 part by weight of boric acid morpholines, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) metal shell is inserted in coating treatment liquid and impregnate, take out post-drying.
Embodiment 3
Measurer calibration equipment, it includes metal shell, this metal shell through aluminum coated steel, described aluminum coated steel include as
Lower step:
1) 2 weight portion amine molybdates, 1.1 parts by weight sodium, 1.8 weight portion sodium silicate, 0.7 weight portion ethylenediamine are gathered
Oxygen ethylene oxypropylene block formula polyethers puts in 48 parts by weight of deionized water successively, stirs;
2) 11.7 parts by weight of bisphenol A type epoxy resin, 5.7 parts by weight of acrylic acid methyl ester, 0.8 weight portion ten are put into the most successively
Dialkyl sulfonates, 1.3 part by weight of boric acid morpholines, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) metal shell is inserted in coating treatment liquid and impregnate, take out post-drying.
Embodiment 4
Measurer calibration equipment, it includes metal shell, this metal shell through aluminum coated steel, described aluminum coated steel include as
Lower step:
1) by 1.2 weight portion amine molybdates, 1.1 parts by weight sodium, 1.8 weight portion sodium silicate, 0.7 weight portion ethylenediamine
Polyoxyethylene polyoxypropylene blocked polyethers puts in 48 parts by weight of deionized water successively, stirs;
2) 11.7 parts by weight of bisphenol A type epoxy resin, 5.7 parts by weight of acrylic acid methyl ester, 0.8 weight portion ten are put into the most successively
Dialkyl sulfonates, 1.3 part by weight of boric acid morpholines, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) metal shell is inserted in coating treatment liquid and impregnate, take out post-drying.
In the various embodiments described above, the surface of metal shell is covered with protecting film, has the antioxidation of excellence, abrasion-resistant, corrosion resistant
Erosion, antirust, heat-resisting, cold-resistant, weather resistance, and surface smoothness is good.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvements and modifications, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. measurer calibration equipment, it is characterised in that it includes metal shell, this metal shell through aluminum coated steel, described overlay film
Process comprises the steps:
1) 1~2 weight portion amine molybdates, 1.1 parts by weight sodium, 1.8 weight portion sodium silicate, 0.7 weight portion ethylenediamine are gathered
Oxygen ethylene oxypropylene block formula polyethers puts in 48 parts by weight of deionized water successively, stirs;
2) 11.7 parts by weight of bisphenol A type epoxy resin, 5.7 parts by weight of acrylic acid methyl ester, 0.8 weight portion dodecane are put into the most successively
Base sodium sulfonate, 1.3 part by weight of boric acid morpholines, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) metal shell is inserted in coating treatment liquid and impregnate, take out post-drying.
Measurer calibration equipment the most according to claim 1, it is characterised in that it includes metal shell, this metal shell warp
Crossing aluminum coated steel, described aluminum coated steel comprises the steps:
1) by 1 weight portion amine molybdate, 1.1 parts by weight sodium, 1.8 weight portion sodium silicate, 0.7 weight portion ethylenediamine polyoxy second
Alkene oxypropylene block formula polyethers puts in 48 parts by weight of deionized water successively, stirs;
2) 11.7 parts by weight of bisphenol A type epoxy resin, 5.7 parts by weight of acrylic acid methyl ester, 0.8 weight portion dodecane are put into the most successively
Base sodium sulfonate, 1.3 part by weight of boric acid morpholines, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) metal shell is inserted in coating treatment liquid and impregnate, take out post-drying.
Measurer calibration equipment the most according to claim 1, it is characterised in that it includes metal shell, this metal shell warp
Crossing aluminum coated steel, described aluminum coated steel comprises the steps:
1) by 2 weight portion amine molybdates, 1.1 parts by weight sodium, 1.8 weight portion sodium silicate, 0.7 weight portion ethylenediamine polyoxy second
Alkene oxypropylene block formula polyethers puts in 48 parts by weight of deionized water successively, stirs;
2) 11.7 parts by weight of bisphenol A type epoxy resin, 5.7 parts by weight of acrylic acid methyl ester, 0.8 weight portion dodecane are put into the most successively
Base sodium sulfonate, 1.3 part by weight of boric acid morpholines, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) metal shell is inserted in coating treatment liquid and impregnate, take out post-drying.
Measurer calibration equipment the most according to claim 1, it is characterised in that it includes metal shell, this metal shell warp
Crossing aluminum coated steel, described aluminum coated steel comprises the steps:
1) by 1.2 weight portion amine molybdates, 1.1 parts by weight sodium, 1.8 weight portion sodium silicate, 0.7 weight portion ethylenediamine polyoxy
Ethylene oxypropylene block formula polyethers puts in 48 parts by weight of deionized water successively, stirs;
2) 11.7 parts by weight of bisphenol A type epoxy resin, 5.7 parts by weight of acrylic acid methyl ester, 0.8 weight portion dodecane are put into the most successively
Base sodium sulfonate, 1.3 part by weight of boric acid morpholines, continue stirring, to being sufficiently mixed uniformly, prepares coating treatment liquid;
3) metal shell is inserted in coating treatment liquid and impregnate, take out post-drying.