CN106336776A - Tank box - Google Patents
Tank box Download PDFInfo
- Publication number
- CN106336776A CN106336776A CN201610783056.8A CN201610783056A CN106336776A CN 106336776 A CN106336776 A CN 106336776A CN 201610783056 A CN201610783056 A CN 201610783056A CN 106336776 A CN106336776 A CN 106336776A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- weight
- parts
- protective paint
- metal cabinet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a tank box. The surface of a metal box body of the tank box is coated with protective paint. The protective paint is prepared by the following steps: 1) putting 1 to 2 parts by weight of diethylenetriamine, 0.7 part by weight of cobalt naphthenate, 1.5 parts by weight of fatty alcohol-polyoxyethylene ether, 1.2 parts by weight of gamma-epoxy propyl ether trimethoxy silane and 11 parts by weight of E-12 epoxy resin into 26 parts by weight of deionized water sequentially and stirring uniformly; and 2) putting 9 parts by weight of acrylic resin, 0.6 part by weight of aluminium triphosphate, 0.9 part by weight of tetramethyl ammonium bromide, 1.3 parts by weight of sodium citrate and 1.8 parts by weight of acetyl citric acid tri(2-ethyl hexyl)ester sequentially and continuously stirring until the materials are mixed completely and uniformly to prepare the protective paint. According to the tank box provided by the invention, the surface of the metal box body of the tank box is coated with the protective paint, so that long-term use of the tank box can be guaranteed.
Description
Technical field
The present invention relates to a kind of tank case.
Background technology
Existing tank case, antirust, corrosion-resistant, anti-oxidant, the weather resistance of its metal cabinet have much room for improvement, the length of impact tank case
Phase uses.
Content of the invention
It is an object of the invention to provide a kind of tank case, its metal cabinet surface is coated with protective paint, so that metal cabinet is had
There is excellent antirust, corrosion-resistant, anti-oxidant, weather resistance, thus ensureing tank case energy Long-Time Service.
For achieving the above object, the technical scheme is that a kind of tank case of design, including metal cabinet, this metal cabinet
Surface is covered with protective paint, and described protective paint is made by the steps:
1) by 1～2 weight portion diethylenetriamine, 0.7 weight portion cobalt naphthenate, 1.5 weight portion AEOs,
1.2 weight portion γ-glycidyl ether trimethoxy silane, 11 weight portion e-12 epoxy resin put into successively 26 weight portions go from
In sub- water, stir；
2) 9 parts by weight propylene acid resins, 0.6 weight portion aluminium triphosphate, 0.9 weight portion tetramethyl bromination are put into again successively
Ammonium, 1.3 parts by weight of lemon acid sodium, 1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, equal to being sufficiently mixed
Even, prepared protective paint.
Preferably, tank case, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint passes through such as
Lower step preparation:
1) by 1 weight portion diethylenetriamine, 0.7 weight portion cobalt naphthenate, 1.5 weight portion AEOs, 1.2
Weight portion γ-glycidyl ether trimethoxy silane, 11 weight portion e-12 epoxy resin put into 26 weight portion deionizations successively
In water, stir；
2) 9 parts by weight propylene acid resins, 0.6 weight portion aluminium triphosphate, 0.9 weight portion tetramethyl bromination are put into again successively
Ammonium, 1.3 parts by weight of lemon acid sodium, 1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, equal to being sufficiently mixed
Even, prepared protective paint.
Preferably, tank case, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint passes through such as
Lower step preparation:
1) by 2 weight portion diethylenetriamines, 0.7 weight portion cobalt naphthenate, 1.5 weight portion AEOs, 1.2
Weight portion γ-glycidyl ether trimethoxy silane, 11 weight portion e-12 epoxy resin put into 26 weight portion deionizations successively
In water, stir；
2) 9 parts by weight propylene acid resins, 0.6 weight portion aluminium triphosphate, 0.9 weight portion tetramethyl bromination are put into again successively
Ammonium, 1.3 parts by weight of lemon acid sodium, 1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, equal to being sufficiently mixed
Even, prepared protective paint.
Preferably, tank case, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint passes through such as
Lower step preparation:
1) by 1.2 weight portion diethylenetriamines, 0.7 weight portion cobalt naphthenate, 1.5 weight portion AEOs,
1.2 weight portion γ-glycidyl ether trimethoxy silane, 11 weight portion e-12 epoxy resin put into successively 26 weight portions go from
In sub- water, stir；
2) 9 parts by weight propylene acid resins, 0.6 weight portion aluminium triphosphate, 0.9 weight portion tetramethyl bromination are put into again successively
Ammonium, 1.3 parts by weight of lemon acid sodium, 1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, equal to being sufficiently mixed
Even, prepared protective paint.
Advantages of the present invention and having the beneficial effects that: provide a kind of tank case, its metal cabinet surface is coated with protective paint, makes
Metal cabinet has excellent antirust, corrosion-resistant, anti-oxidant, weather resistance, thus ensureing tank case energy Long-Time Service.
The performance of " protective paint " and purposes are determined by its component and proportioning, and the different component meeting in " protective paint "
Influence each other, component and its proportioning can determine the final performance of " protective paint ", such as fruit component and its proportioning be not mutually coordinated, single
The beneficial effect that component is brought, even can be eliminated by other components abatement, when serious, different component is mutually conflicted, and rises
Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " protection
The optimal component of paint " and proportioning so that multiple component combine, mutually coordinated and produce positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Tank case, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint is made as follows
Standby:
1) by 1～2 weight portion diethylenetriamine, 0.7 weight portion cobalt naphthenate, 1.5 weight portion AEOs,
1.2 weight portion γ-glycidyl ether trimethoxy silane, 11 weight portion e-12 epoxy resin put into successively 26 weight portions go from
In sub- water, stir；
2) 9 parts by weight propylene acid resins, 0.6 weight portion aluminium triphosphate, 0.9 weight portion tetramethyl bromination are put into again successively
Ammonium, 1.3 parts by weight of lemon acid sodium, 1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, equal to being sufficiently mixed
Even, prepared protective paint.
Embodiment 2
Tank case, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint is made as follows
Standby:
1) by 1 weight portion diethylenetriamine, 0.7 weight portion cobalt naphthenate, 1.5 weight portion AEOs, 1.2
Weight portion γ-glycidyl ether trimethoxy silane, 11 weight portion e-12 epoxy resin put into 26 weight portion deionizations successively
In water, stir；
2) 9 parts by weight propylene acid resins, 0.6 weight portion aluminium triphosphate, 0.9 weight portion tetramethyl bromination are put into again successively
Ammonium, 1.3 parts by weight of lemon acid sodium, 1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, equal to being sufficiently mixed
Even, prepared protective paint.
Embodiment 3
Tank case, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint is made as follows
Standby:
1) by 2 weight portion diethylenetriamines, 0.7 weight portion cobalt naphthenate, 1.5 weight portion AEOs, 1.2
Weight portion γ-glycidyl ether trimethoxy silane, 11 weight portion e-12 epoxy resin put into 26 weight portion deionizations successively
In water, stir；
2) 9 parts by weight propylene acid resins, 0.6 weight portion aluminium triphosphate, 0.9 weight portion tetramethyl bromination are put into again successively
Ammonium, 1.3 parts by weight of lemon acid sodium, 1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, equal to being sufficiently mixed
Even, prepared protective paint.
Embodiment 4
Tank case, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint is made as follows
Standby:
1) by 1.2 weight portion diethylenetriamines, 0.7 weight portion cobalt naphthenate, 1.5 weight portion AEOs,
1.2 weight portion γ-glycidyl ether trimethoxy silane, 11 weight portion e-12 epoxy resin put into successively 26 weight portions go from
In sub- water, stir；
2) 9 parts by weight propylene acid resins, 0.6 weight portion aluminium triphosphate, 0.9 weight portion tetramethyl bromination are put into again successively
Ammonium, 1.3 parts by weight of lemon acid sodium, 1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, equal to being sufficiently mixed
Even, prepared protective paint.
The tank case of the various embodiments described above, its metal cabinet surface is coated with protective paint, makes metal cabinet have excellent preventing
Rust, corrosion-resistant, anti-oxidant, weather resistance, thus ensure tank case energy Long-Time Service.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. it is characterised in that including metal cabinet, this metal cabinet surface is covered with protective paint to a kind of tank case, described protective paint
It is made by the steps:
1) by 1～2 weight portion diethylenetriamine, 0.7 weight portion cobalt naphthenate, 1.5 weight portion AEOs, 1.2
Weight portion γ-glycidyl ether trimethoxy silane, 11 weight portion e-12 epoxy resin put into 26 weight portion deionizations successively
In water, stir；
2) put into successively again 9 parts by weight propylene acid resins, 0.6 weight portion aluminium triphosphate, 0.9 weight portion 4 bromide,
1.3 parts by weight of lemon acid sodium, 1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, uniform to being sufficiently mixed,
Prepared protective paint.
2. tank case according to claim 1 is it is characterised in that include metal cabinet, this metal cabinet surface is covered with anti-
Vernix, described protective paint is made by the steps:
1) by 1 weight portion diethylenetriamine, 0.7 weight portion cobalt naphthenate, 1.5 weight portion AEOs, 1.2 weight
Part γ-glycidyl ether trimethoxy silane, 11 weight portion e-12 epoxy resin put in 26 parts by weight of deionized water successively,
Stir；
2) put into successively again 9 parts by weight propylene acid resins, 0.6 weight portion aluminium triphosphate, 0.9 weight portion 4 bromide,
1.3 parts by weight of lemon acid sodium, 1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, uniform to being sufficiently mixed,
Prepared protective paint.
3. tank case according to claim 1 is it is characterised in that include metal cabinet, this metal cabinet surface is covered with anti-
Vernix, described protective paint is made by the steps:
1) by 2 weight portion diethylenetriamines, 0.7 weight portion cobalt naphthenate, 1.5 weight portion AEOs, 1.2 weight
Part γ-glycidyl ether trimethoxy silane, 11 weight portion e-12 epoxy resin put in 26 parts by weight of deionized water successively,
Stir；
2) put into successively again 9 parts by weight propylene acid resins, 0.6 weight portion aluminium triphosphate, 0.9 weight portion 4 bromide,
1.3 parts by weight of lemon acid sodium, 1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, uniform to being sufficiently mixed,
Prepared protective paint.
4. tank case according to claim 1 is it is characterised in that include metal cabinet, this metal cabinet surface is covered with anti-
Vernix, described protective paint is made by the steps:
1) by 1.2 weight portion diethylenetriamines, 0.7 weight portion cobalt naphthenate, 1.5 weight portion AEOs, 1.2 weights
Amount part γ-glycidyl ether trimethoxy silane, 11 weight portion e-12 epoxy resin put into 26 parts by weight of deionized water successively
In, stir；
2) put into successively again 9 parts by weight propylene acid resins, 0.6 weight portion aluminium triphosphate, 0.9 weight portion 4 bromide,
1.3 parts by weight of lemon acid sodium, 1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, uniform to being sufficiently mixed,
Prepared protective paint.