CN105385964A - Movable shear blade - Google Patents
Movable shear blade Download PDFInfo
- Publication number
- CN105385964A CN105385964A CN201510983474.7A CN201510983474A CN105385964A CN 105385964 A CN105385964 A CN 105385964A CN 201510983474 A CN201510983474 A CN 201510983474A CN 105385964 A CN105385964 A CN 105385964A
- Authority
- CN
- China
- Prior art keywords
- speed
- alloy material
- room temperature
- min again
- warming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a movable shear blade. The movable shear blade comprises a metal body made of an alloy material treated thermally. The alloy material is prepared from 1-2% of As, 0.5% of Se, 0.7% of N, 0.9% of Au, 0.9% of Tc, 0.7% of Ba and the balance Fe and unavoidable impurities. The alloy material is thermally heated through the following steps that firstly, the temperature is raised to 665 DEG C at the speed of 25 DEG C/min and is kept for 2.5 h; secondly, the temperature is lowered to the room temperature at the speed of 30 DEG C/min; thirdly, the temperature is raised to 765 DEG C at the speed of 15 DEG C/min and is kept for 3 h; fourthly, the temperature is lowered to the room temperature at the speed of 25 DEG C/min. The metal body of the movable shear blade is good in performance and long in service life.
Description
Technical field
The present invention relates to movable cutting edge.
Background technology
The work under bad environment of movable cutting edge, to its metal master performance requriements higher.
Summary of the invention
The object of the present invention is to provide a kind of movable cutting edge, its metal master is made by through heat treated alloy material, and metal master is lightweight, intensity is high, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, antioxidant property is good, and duration of service is long.
For achieving the above object, technical scheme of the present invention is a kind of movable cutting edge of design, and comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1~2%,
Se:0.5%,
N:0.7%,
Au:0.9%,
Tc:0.9%,
Ba:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 665 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 765 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Preferably, movable cutting edge, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1%,
Se:0.5%,
N:0.7%,
Au:0.9%,
Tc:0.9%,
Ba:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 665 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 765 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Preferably, movable cutting edge, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:2%,
Se:0.5%,
N:0.7%,
Au:0.9%,
Tc:0.9%,
Ba:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 665 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 765 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Advantage of the present invention and beneficial effect are: provide a kind of movable cutting edge, its metal master is made by through heat treated alloy material, and metal master is lightweight, intensity is high, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, antioxidant property is good, and duration of service is long.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of movable cutting edge, comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1~2%,
Se:0.5%,
N:0.7%,
Au:0.9%,
Tc:0.9%,
Ba:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 665 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 765 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Embodiment 2
Movable cutting edge, comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1%,
Se:0.5%,
N:0.7%,
Au:0.9%,
Tc:0.9%,
Ba:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 665 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 765 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
Embodiment 3
Movable cutting edge, comprise metal master, described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:2%,
Se:0.5%,
N:0.7%,
Au:0.9%,
Tc:0.9%,
Ba:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 665 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 765 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. movable cutting edge, is characterized in that, comprises metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1~2%,
Se:0.5%,
N:0.7%,
Au:0.9%,
Tc:0.9%,
Ba:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 665 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 765 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
2. movable cutting edge according to claim 1, is characterized in that, comprise metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:1%,
Se:0.5%,
N:0.7%,
Au:0.9%,
Tc:0.9%,
Ba:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 665 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 765 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.
3. movable cutting edge according to claim 1, is characterized in that, comprise metal master, and described metal master is made by through heat treated alloy material, and by weight percentage, the composition of this alloy material is:
As:2%,
Se:0.5%,
N:0.7%,
Au:0.9%,
Tc:0.9%,
Ba:0.7%,
Surplus is Fe and inevitable impurity;
Described alloy material is heat-treated as follows:
1) be warming up to 665 DEG C with the speed of 25 DEG C/min, be incubated 2.5 hours;
2) room temperature is cooled to the speed of 30 DEG C/min again;
3) be warming up to 765 DEG C with the speed of 15 DEG C/min again, be incubated 3 hours;
4) room temperature is cooled to the speed of 25 DEG C/min again.