CN106349787A - Warehousing shelf for supermarkets - Google Patents
Warehousing shelf for supermarkets Download PDFInfo
- Publication number
- CN106349787A CN106349787A CN201610743038.7A CN201610743038A CN106349787A CN 106349787 A CN106349787 A CN 106349787A CN 201610743038 A CN201610743038 A CN 201610743038A CN 106349787 A CN106349787 A CN 106349787A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- weight
- parts
- main body
- treatment liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a warehousing shelf for supermarkets, comprising a metal shelf body; the metal shelf body is subjected to laminating treatment; the laminating treatment includes the steps of 1) adding 1-2 parts by weight of tri(2-ethylhexyl)acetocitrate, 1.5 parts by weight of sorbitol, 1.9 parts by weight of Upsilon-methacryloxypropyltrimethoxysilane and 0.9 part by weight of dimethyldistearylammonium chloride sequentially into 43 parts by weight of deionized water, and stirring well; 2) adding 8.9 parts by weight of ethanol, 9.7 parts by weight of dipropylene glycol, 2.2 parts by weight of fatty alcohol polyoxyethylene ether and 3.8 parts by weight of dibutyl succinate, and continuing to stir until full mixing to obtain a laminating liquid; 3) soaking the metal shelf body in the laminating liquid, removing, and drying. The metal shelf body of the warehousing shelf for supermarkets has the surface coated with a protective film, the good properties are provided, and the surface is highly glossy.
Description
Technical field
The present invention relates to supermarket's storage rack.
Background technology
Existing supermarket storage rack, heat-resisting, abrasion-resistant, the antioxidation of its metal shelf main body, corrosion-resistant, antirust, resistance to
Cold, weather resistance has much room for improvement, and surface smoothness is also not ideal enough.
Content of the invention
It is an object of the invention to provide a kind of supermarket storage rack, its metal shelf main body is through aluminum coated steel, gold
Belong to shelf body surface and be covered with protecting film, there is excellent heat-resisting, abrasion-resistant, antioxidation, corrosion-resistant, antirust, cold-resistant, weatherability
Can, and surface smoothness is good.
For achieving the above object, the technical scheme is that a kind of supermarket of design storage rack, it includes metal goods
Frame body, through aluminum coated steel, described aluminum coated steel comprises the steps: this metal shelf main body
1) by 1～2 weight portion tri(2-ethylhexyl)acetocitrate, 1.5 weight portion Sorbitol, 1.9 weight portion γ-
(methacryloxypropyl) propyl trimethoxy silicane, 0.9 weight portion chloro distearyl dimethyl ammonium put into 43 weight portions successively
In deionized water, stir；
2) 8.9 parts by weight of ethanol, 9.7 weight portion dipropylene glycol, 2.2 weight portion aliphatic alcohol polyethenoxies are put into again successively
Ether, 3.8 weight portion di-n-butyl succinates, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Preferably, supermarket's storage rack, it includes metal shelf main body, this metal shelf main body through aluminum coated steel,
Described aluminum coated steel comprises the steps:
1) by 1 weight portion tri(2-ethylhexyl)acetocitrate, 1.5 weight portion Sorbitol, 1.9 weight portion γ-(methyl
Acryloyl-oxy) propyl trimethoxy silicane, 0.9 weight portion chloro distearyl dimethyl ammonium put into 43 weight portion deionizations successively
In water, stir；
2) 8.9 parts by weight of ethanol, 9.7 weight portion dipropylene glycol, 2.2 weight portion aliphatic alcohol polyethenoxies are put into again successively
Ether, 3.8 weight portion di-n-butyl succinates, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Preferably, supermarket's storage rack, it includes metal shelf main body, this metal shelf main body through aluminum coated steel,
Described aluminum coated steel comprises the steps:
1) by 2 weight portion tri(2-ethylhexyl)acetocitrates, 1.5 weight portion Sorbitol, 1.9 weight portion γ-(methyl
Acryloyl-oxy) propyl trimethoxy silicane, 0.9 weight portion chloro distearyl dimethyl ammonium put into 43 weight portion deionizations successively
In water, stir；
2) 8.9 parts by weight of ethanol, 9.7 weight portion dipropylene glycol, 2.2 weight portion aliphatic alcohol polyethenoxies are put into again successively
Ether, 3.8 weight portion di-n-butyl succinates, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Preferably, supermarket's storage rack, it includes metal shelf main body, this metal shelf main body through aluminum coated steel,
Described aluminum coated steel comprises the steps:
1) by 1.2 weight portion tri(2-ethylhexyl)acetocitrates, 1.5 weight portion Sorbitol, 1.9 weight portion γ-(first
Base acryloyl-oxy) propyl trimethoxy silicane, 0.9 weight portion chloro distearyl dimethyl ammonium put into successively 43 weight portions go from
In sub- water, stir；
2) 8.9 parts by weight of ethanol, 9.7 weight portion dipropylene glycol, 2.2 weight portion aliphatic alcohol polyethenoxies are put into again successively
Ether, 3.8 weight portion di-n-butyl succinates, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Advantages of the present invention and having the beneficial effects that: provide a kind of supermarket storage rack, its metal shelf main body is passed through
Aluminum coated steel, metal shelf body surfaces are covered with protecting film, have excellent heat-resisting, abrasion-resistant, antioxidation, corrosion-resistant, antirust,
Cold-resistant, weather resistance, and surface smoothness is good.
The performance of " coating treatment liquid " and purposes are determined by its component and proportioning, and in " coating treatment liquid " not
With group, branch influences each other, and component and its proportioning can determine the final performance of " coating treatment liquid ", such as fruit component and its proportioning not
Mutually coordinated, the beneficial effect that single component is brought, even can be eliminated by other components abatement, when serious, different groups
Split-phase is mutually conflicted, and does not have whole synthesis effect, produces negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly
Checking, obtain the optimal component of " coating treatment liquid " and proportioning so that multiple component combine, mutually coordinated and produce
Positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Supermarket's storage rack, it includes metal shelf main body, this metal shelf main body through aluminum coated steel, described overlay film
Process comprises the steps:
1) by 1～2 weight portion tri(2-ethylhexyl)acetocitrate, 1.5 weight portion Sorbitol, 1.9 weight portion γ-
(methacryloxypropyl) propyl trimethoxy silicane, 0.9 weight portion chloro distearyl dimethyl ammonium put into 43 weight portions successively
In deionized water, stir；
2) 8.9 parts by weight of ethanol, 9.7 weight portion dipropylene glycol, 2.2 weight portion aliphatic alcohol polyethenoxies are put into again successively
Ether, 3.8 weight portion di-n-butyl succinates, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Embodiment 2
Supermarket's storage rack, it includes metal shelf main body, this metal shelf main body through aluminum coated steel, described overlay film
Process comprises the steps:
1) by 1 weight portion tri(2-ethylhexyl)acetocitrate, 1.5 weight portion Sorbitol, 1.9 weight portion γ-(methyl
Acryloyl-oxy) propyl trimethoxy silicane, 0.9 weight portion chloro distearyl dimethyl ammonium put into 43 weight portion deionizations successively
In water, stir；
2) 8.9 parts by weight of ethanol, 9.7 weight portion dipropylene glycol, 2.2 weight portion aliphatic alcohol polyethenoxies are put into again successively
Ether, 3.8 weight portion di-n-butyl succinates, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Embodiment 3
Supermarket's storage rack, it includes metal shelf main body, this metal shelf main body through aluminum coated steel, described overlay film
Process comprises the steps:
1) by 2 weight portion tri(2-ethylhexyl)acetocitrates, 1.5 weight portion Sorbitol, 1.9 weight portion γ-(methyl
Acryloyl-oxy) propyl trimethoxy silicane, 0.9 weight portion chloro distearyl dimethyl ammonium put into 43 weight portion deionizations successively
In water, stir；
2) 8.9 parts by weight of ethanol, 9.7 weight portion dipropylene glycol, 2.2 weight portion aliphatic alcohol polyethenoxies are put into again successively
Ether, 3.8 weight portion di-n-butyl succinates, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Embodiment 4
Supermarket's storage rack, it includes metal shelf main body, this metal shelf main body through aluminum coated steel, described overlay film
Process comprises the steps:
1) by 1.2 weight portion tri(2-ethylhexyl)acetocitrates, 1.5 weight portion Sorbitol, 1.9 weight portion γ-(first
Base acryloyl-oxy) propyl trimethoxy silicane, 0.9 weight portion chloro distearyl dimethyl ammonium put into successively 43 weight portions go from
In sub- water, stir；
2) 8.9 parts by weight of ethanol, 9.7 weight portion dipropylene glycol, 2.2 weight portion aliphatic alcohol polyethenoxies are put into again successively
Ether, 3.8 weight portion di-n-butyl succinates, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Surface through metal shelf main body in the various embodiments described above is covered with protecting film, has excellent heat-resisting, abrasion-resistant, anti-
Oxidation, corrosion-resistant, antirust, cold-resistant, weather resistance, and surface smoothness is good.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1., it is characterised in that it includes metal shelf main body, this metal shelf main body is at overlay film for supermarket's storage rack
Reason, described aluminum coated steel comprises the steps:
1) by 1～2 weight portion tri(2-ethylhexyl)acetocitrate, 1.5 weight portion Sorbitol, 1.9 weight portion γ-(methyl
Acryloyl-oxy) propyl trimethoxy silicane, 0.9 weight portion chloro distearyl dimethyl ammonium put into 43 weight portion deionizations successively
In water, stir；
2) put into successively again 8.9 parts by weight of ethanol, 9.7 weight portion dipropylene glycol, 2.2 weight portion fatty alcohol-polyoxyethylene ether, 3.8
Weight portion di-n-butyl succinate, continues stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
2. supermarket according to claim 1 storage rack is it is characterised in that it includes metal shelf main body, this metal
Through aluminum coated steel, described aluminum coated steel comprises the steps: shelf body
1) by 1 weight portion tri(2-ethylhexyl)acetocitrate, 1.5 weight portion Sorbitol, 1.9 weight portion γ-(metering system
Acyl-oxygen) propyl trimethoxy silicane, 0.9 weight portion chloro distearyl dimethyl ammonium put into 43 parts by weight of deionized water successively
In, stir；
2) put into successively again 8.9 parts by weight of ethanol, 9.7 weight portion dipropylene glycol, 2.2 weight portion fatty alcohol-polyoxyethylene ether, 3.8
Weight portion di-n-butyl succinate, continues stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
3. supermarket according to claim 1 storage rack is it is characterised in that it includes metal shelf main body, this metal
Through aluminum coated steel, described aluminum coated steel comprises the steps: shelf body
1) by 2 weight portion tri(2-ethylhexyl)acetocitrates, 1.5 weight portion Sorbitol, 1.9 weight portion γ-(metering system
Acyl-oxygen) propyl trimethoxy silicane, 0.9 weight portion chloro distearyl dimethyl ammonium put into 43 parts by weight of deionized water successively
In, stir；
2) put into successively again 8.9 parts by weight of ethanol, 9.7 weight portion dipropylene glycol, 2.2 weight portion fatty alcohol-polyoxyethylene ether, 3.8
Weight portion di-n-butyl succinate, continues stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
4. supermarket according to claim 1 storage rack is it is characterised in that it includes metal shelf main body, this metal
Through aluminum coated steel, described aluminum coated steel comprises the steps: shelf body
1) by 1.2 weight portion tri(2-ethylhexyl)acetocitrates, 1.5 weight portion Sorbitol, 1.9 weight portion γ-(methyl-prop
Alkene acyl-oxygen) propyl trimethoxy silicane, 0.9 weight portion chloro distearyl dimethyl ammonium put into 43 parts by weight of deionized water successively
In, stir；
2) put into successively again 8.9 parts by weight of ethanol, 9.7 weight portion dipropylene glycol, 2.2 weight portion fatty alcohol-polyoxyethylene ether, 3.8
Weight portion di-n-butyl succinate, continues stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.