CN106349788A - Cam for textile equipment - Google Patents
Cam for textile equipment Download PDFInfo
- Publication number
- CN106349788A CN106349788A CN201610748252.1A CN201610748252A CN106349788A CN 106349788 A CN106349788 A CN 106349788A CN 201610748252 A CN201610748252 A CN 201610748252A CN 106349788 A CN106349788 A CN 106349788A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- weight portion
- metal master
- treatment liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cam for textile equipment, including a metal body. The metal body is film mulched by the steps of 1, adding, by weight, 1-2 parts of polyethylene glycol, 1.9 parts of mediate octyl alcohol polyoxyethylene ether, 2.2 parts of hydroxyethyl cellulose and 0.9 part of alkyl glycoside into 41 parts of deionized water successively and stirring evenly; 2, obtaining the tectorial solution prepared from adding, by weight, 3.3 parts of chitosan, 7.9 parts of vinyl acetate, 3.1 parts of tributyl phosphate and 1.8 parts of trihexyl O-acetyl citrate into the solution and stirring evenly; 3, stoving the metal body after being soakaged in the tectorial solution. The metal body of the cam for textile equipment is provided with a protecting film on the surface. The metal body has the advantages of good performance and good surface finish.
Description
Technical field
The present invention relates to Weaving device cam.
Background technology
Existing Weaving device cam, antirust, heat-resisting, cold-resistant, abrasion-resistant, the antioxidation of its metal master, corrosion-resistant, resistance to
Wait performance to have much room for improvement, and surface smoothness is also not ideal enough.
Content of the invention
It is an object of the invention to provide a kind of Weaving device cam, its metal master is through aluminum coated steel, metal master
Body surface face is covered with protecting film, has excellent antirust, heat-resisting, cold-resistant, abrasion-resistant, antioxidation, corrosion-resistant, weather resistance, and table
Face fineness is good.
For achieving the above object, the technical scheme is that a kind of Weaving device cam of design, it includes metal master
Body, through aluminum coated steel, described aluminum coated steel comprises the steps: this metal master
1) by 1～2 weight portion Polyethylene Glycol, 1.9 weight portion sec-octyl alcohol polyoxyethylene ether, 2.2 weight portion hydroxy ethyl fibers
Element, 0.9 part by weight of alkylglycoside put in 41 parts by weight of deionized water successively, stir；
2) put into successively again 3.3 weight portion shitosans, 7.9 parts by weight acetic acid vinyl acetate, 3.1 parts by weight of phosphoric acid tributyls,
1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal master is inserted dipping in coating treatment liquid, take out post-drying.
Preferably, Weaving device cam, it includes metal master, this metal master through aluminum coated steel, described overlay film
Process comprises the steps:
1) by 1 weight portion Polyethylene Glycol, 1.9 weight portion sec-octyl alcohol polyoxyethylene ether, 2.2 weight portion hydroxyethyl celluloses,
0.9 part by weight of alkylglycoside puts in 41 parts by weight of deionized water successively, stirs；
2) put into successively again 3.3 weight portion shitosans, 7.9 parts by weight acetic acid vinyl acetate, 3.1 parts by weight of phosphoric acid tributyls,
1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal master is inserted dipping in coating treatment liquid, take out post-drying.
Preferably, Weaving device cam, it includes metal master, this metal master through aluminum coated steel, described overlay film
Process comprises the steps:
1) by 2 weight portion Polyethylene Glycol, 1.9 weight portion sec-octyl alcohol polyoxyethylene ether, 2.2 weight portion hydroxyethyl celluloses,
0.9 part by weight of alkylglycoside puts in 41 parts by weight of deionized water successively, stirs；
2) put into successively again 3.3 weight portion shitosans, 7.9 parts by weight acetic acid vinyl acetate, 3.1 parts by weight of phosphoric acid tributyls,
1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal master is inserted dipping in coating treatment liquid, take out post-drying.
Preferably, Weaving device cam, it includes metal master, this metal master through aluminum coated steel, described overlay film
Process comprises the steps:
1) by 1.2 weight portion Polyethylene Glycol, 1.9 weight portion sec-octyl alcohol polyoxyethylene ether, 2.2 weight portion hydroxy ethyl fibers
Element, 0.9 part by weight of alkylglycoside put in 41 parts by weight of deionized water successively, stir；
2) put into successively again 3.3 weight portion shitosans, 7.9 parts by weight acetic acid vinyl acetate, 3.1 parts by weight of phosphoric acid tributyls,
1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal master is inserted dipping in coating treatment liquid, take out post-drying.
Advantages of the present invention and having the beneficial effects that: provide a kind of Weaving device cam, its metal master is through overlay film
Process, metal body surface is covered with protecting film, there is excellent antirust, heat-resisting, cold-resistant, abrasion-resistant, antioxidation, corrosion-resistant, resistance to
Wait performance, and surface smoothness is good.
The performance of " coating treatment liquid " and purposes are determined by its component and proportioning, and in " coating treatment liquid " not
With group, branch influences each other, and component and its proportioning can determine the final performance of " coating treatment liquid ", such as fruit component and its proportioning not
Mutually coordinated, the beneficial effect that single component is brought, even can be eliminated by other components abatement, when serious, different groups
Split-phase is mutually conflicted, and does not have whole synthesis effect, produces negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly
Checking, obtain the optimal component of " coating treatment liquid " and proportioning so that multiple component combine, mutually coordinated and produce
Positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Weaving device cam, it includes metal master, and through aluminum coated steel, described aluminum coated steel includes this metal master
Following steps:
1) by 1～2 weight portion Polyethylene Glycol, 1.9 weight portion sec-octyl alcohol polyoxyethylene ether, 2.2 weight portion hydroxy ethyl fibers
Element, 0.9 part by weight of alkylglycoside put in 41 parts by weight of deionized water successively, stir；
2) put into successively again 3.3 weight portion shitosans, 7.9 parts by weight acetic acid vinyl acetate, 3.1 parts by weight of phosphoric acid tributyls,
1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal master is inserted dipping in coating treatment liquid, take out post-drying.
Embodiment 2
Weaving device cam, it includes metal master, and through aluminum coated steel, described aluminum coated steel includes this metal master
Following steps:
1) by 1 weight portion Polyethylene Glycol, 1.9 weight portion sec-octyl alcohol polyoxyethylene ether, 2.2 weight portion hydroxyethyl celluloses,
0.9 part by weight of alkylglycoside puts in 41 parts by weight of deionized water successively, stirs；
2) put into successively again 3.3 weight portion shitosans, 7.9 parts by weight acetic acid vinyl acetate, 3.1 parts by weight of phosphoric acid tributyls,
1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal master is inserted dipping in coating treatment liquid, take out post-drying.
Embodiment 3
Weaving device cam, it includes metal master, and through aluminum coated steel, described aluminum coated steel includes this metal master
Following steps:
1) by 2 weight portion Polyethylene Glycol, 1.9 weight portion sec-octyl alcohol polyoxyethylene ether, 2.2 weight portion hydroxyethyl celluloses,
0.9 part by weight of alkylglycoside puts in 41 parts by weight of deionized water successively, stirs；
2) put into successively again 3.3 weight portion shitosans, 7.9 parts by weight acetic acid vinyl acetate, 3.1 parts by weight of phosphoric acid tributyls,
1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal master is inserted dipping in coating treatment liquid, take out post-drying.
Embodiment 4
Weaving device cam, it includes metal master, and through aluminum coated steel, described aluminum coated steel includes this metal master
Following steps:
1) by 1.2 weight portion Polyethylene Glycol, 1.9 weight portion sec-octyl alcohol polyoxyethylene ether, 2.2 weight portion hydroxy ethyl fibers
Element, 0.9 part by weight of alkylglycoside put in 41 parts by weight of deionized water successively, stir；
2) put into successively again 3.3 weight portion shitosans, 7.9 parts by weight acetic acid vinyl acetate, 3.1 parts by weight of phosphoric acid tributyls,
1.8 weight portion tri(2-ethylhexyl)acetocitrates, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal master is inserted dipping in coating treatment liquid, take out post-drying.
Surface through metal master in the various embodiments described above is covered with protecting film, has excellent antirust, heat-resisting, cold-resistant, resistance to
Friction, antioxidation, corrosion-resistant, weather resistance, and surface smoothness is good.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. Weaving device cam is it is characterised in that it includes metal master, and this metal master, through aluminum coated steel, described covers
Film process comprises the steps:
1) by 1～2 weight portion Polyethylene Glycol, 1.9 weight portion sec-octyl alcohol polyoxyethylene ether, 2.2 weight portion hydroxyethyl celluloses,
0.9 part by weight of alkylglycoside puts in 41 parts by weight of deionized water successively, stirs；
2) 3.3 weight portion shitosans, 7.9 parts by weight acetic acid vinyl acetate, 3.1 parts by weight of phosphoric acid tributyls, 1.8 weights are put into again successively
Amount part tri(2-ethylhexyl)acetocitrate, continues stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal master is inserted dipping in coating treatment liquid, take out post-drying.
2. Weaving device cam according to claim 1 is it is characterised in that it includes metal master, this metal master
Through aluminum coated steel, described aluminum coated steel comprises the steps:
1) by 1 weight portion Polyethylene Glycol, 1.9 weight portion sec-octyl alcohol polyoxyethylene ether, 2.2 weight portion hydroxyethyl celluloses, 0.9 weight
Amount part alkyl polyglucoside puts in 41 parts by weight of deionized water successively, stirs；
2) 3.3 weight portion shitosans, 7.9 parts by weight acetic acid vinyl acetate, 3.1 parts by weight of phosphoric acid tributyls, 1.8 weights are put into again successively
Amount part tri(2-ethylhexyl)acetocitrate, continues stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal master is inserted dipping in coating treatment liquid, take out post-drying.
3. Weaving device cam according to claim 1 is it is characterised in that it includes metal master, this metal master
Through aluminum coated steel, described aluminum coated steel comprises the steps:
1) by 2 weight portion Polyethylene Glycol, 1.9 weight portion sec-octyl alcohol polyoxyethylene ether, 2.2 weight portion hydroxyethyl celluloses, 0.9 weight
Amount part alkyl polyglucoside puts in 41 parts by weight of deionized water successively, stirs；
2) 3.3 weight portion shitosans, 7.9 parts by weight acetic acid vinyl acetate, 3.1 parts by weight of phosphoric acid tributyls, 1.8 weights are put into again successively
Amount part tri(2-ethylhexyl)acetocitrate, continues stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal master is inserted dipping in coating treatment liquid, take out post-drying.
4. Weaving device cam according to claim 1 is it is characterised in that it includes metal master, this metal master
Through aluminum coated steel, described aluminum coated steel comprises the steps:
1) by 1.2 weight portion Polyethylene Glycol, 1.9 weight portion sec-octyl alcohol polyoxyethylene ether, 2.2 weight portion hydroxyethyl celluloses, 0.9
Part by weight of alkylglycoside puts in 41 parts by weight of deionized water successively, stirs；
2) 3.3 weight portion shitosans, 7.9 parts by weight acetic acid vinyl acetate, 3.1 parts by weight of phosphoric acid tributyls, 1.8 weights are put into again successively
Amount part tri(2-ethylhexyl)acetocitrate, continues stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal master is inserted dipping in coating treatment liquid, take out post-drying.