CN106381040A - Supermarket adjustment type shelf - Google Patents

Supermarket adjustment type shelf Download PDF

Info

Publication number
CN106381040A
CN106381040A CN201610742511.XA CN201610742511A CN106381040A CN 106381040 A CN106381040 A CN 106381040A CN 201610742511 A CN201610742511 A CN 201610742511A CN 106381040 A CN106381040 A CN 106381040A
Authority
CN
China
Prior art keywords
weight
weight portion
main body
parts
shelf main
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610742511.XA
Other languages
Chinese (zh)
Inventor
邵俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changshu City Guli Town Miaoquan Daguang Metal Product Factory
Original Assignee
Changshu City Guli Town Miaoquan Daguang Metal Product Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changshu City Guli Town Miaoquan Daguang Metal Product Factory filed Critical Changshu City Guli Town Miaoquan Daguang Metal Product Factory
Priority to CN201610742511.XA priority Critical patent/CN106381040A/en
Publication of CN106381040A publication Critical patent/CN106381040A/en
Pending legal-status Critical Current

Abstract

The present invention discloses a supermarket adjustment type shelf, which comprises a metal shelf main body. The metal shelf main body is subjected to the coating treatment. The coating treatment comprises the following steps: 1) sequentially adding 1-2 parts by weight of potassium persulphate, 1.2 parts by weight of mercaptobenzothiazole, 0.5 parts by weight of sodium hexametaphosphate and 1.6 parts by weight of castor oil polyoxyethylene ether into 43 parts by weight of deionized water, and stirring uniformly; 2) sequentially adding 6.5 parts by weight of acrylic resin polyurethane co-polymerized resin, 7.6 parts by weight of butyl ether acetate, 1.3 weight parts of dodecyl betaine and 4.1 parts by weight of polyvinyl alcohol into the above obtained material, continuously stirring till the obtained material is fully and uniformly mixed, and preparing a coating conditioning fluid; 3) placing and dipping the metal shelf main body into the coating conditioning fluid, taking the metal shelf main body out of the coating conditioning fluid, and drying the metal shelf main body. The surface of the metal shelf main body of the supermarket adjustment type shelf is coated with a protective film, so that the supermarket adjustment type shelf is good in performance and excellent in surface fineness.

Description

Supermarket's adjustable type shelf
Technical field
The present invention relates to supermarket's adjustable type shelf.
Background technology
Existing supermarket adjustable type shelf, the heat-resisting, abrasion-resistant of its metal shelf main body, anti-oxidant, corrosion-resistant, antirust, Cold-resistant, weather resistance has much room for improvement, and surface smoothness is also not ideal enough.
Content of the invention
It is an object of the invention to provide a kind of supermarket adjustable type shelf, its metal shelf main body through aluminum coated steel, Metal shelf body surfaces are covered with protecting film, have excellent heat-resisting, abrasion-resistant, anti-oxidant, corrosion-resistant, antirust, cold-resistant, weather-proof Performance, and surface smoothness is good.
For achieving the above object, the technical scheme is that a kind of supermarket of design adjustable type shelf, it includes metal Shelf body, through aluminum coated steel, described aluminum coated steel comprises the steps this metal shelf main body：
1) by 1～2 weight portion potassium peroxydisulfate, 1.2 weight portion mercaptobenzothiazolers, 0.5 weight portion calgon, 1.6 Weight portion castor oil polyoxyethylene ether puts in 43 parts by weight of deionized water successively, stirs；
2) put into successively again 6.5 parts by weight propylene acid resin polyurethane copolymerization resins, 7.6 weight portion monobutyl ether acetates, 1.3 Weight portion empgen BB, 4.1 weight account polyethylene alcohol, continue stirring, uniform to being sufficiently mixed, prepared aluminum coated steel Liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Preferably, supermarket's adjustable type shelf, it includes metal shelf main body, and this metal shelf main body is at overlay film Reason, described aluminum coated steel comprises the steps：
1) by 1 weight portion potassium peroxydisulfate, 1.2 weight portion mercaptobenzothiazolers, 0.5 weight portion calgon, 1.6 weight Part castor oil polyoxyethylene ether puts in 43 parts by weight of deionized water successively, stirs；
2) put into successively again 6.5 parts by weight propylene acid resin polyurethane copolymerization resins, 7.6 weight portion monobutyl ether acetates, 1.3 Weight portion empgen BB, 4.1 weight account polyethylene alcohol, continue stirring, uniform to being sufficiently mixed, prepared aluminum coated steel Liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Preferably, supermarket's adjustable type shelf, it includes metal shelf main body, and this metal shelf main body is at overlay film Reason, described aluminum coated steel comprises the steps：
1) by 2 weight portion potassium peroxydisulfates, 1.2 weight portion mercaptobenzothiazolers, 0.5 weight portion calgon, 1.6 weight Part castor oil polyoxyethylene ether puts in 43 parts by weight of deionized water successively, stirs；
2) put into successively again 6.5 parts by weight propylene acid resin polyurethane copolymerization resins, 7.6 weight portion monobutyl ether acetates, 1.3 Weight portion empgen BB, 4.1 weight account polyethylene alcohol, continue stirring, uniform to being sufficiently mixed, prepared aluminum coated steel Liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Preferably, supermarket's adjustable type shelf, it includes metal shelf main body, and this metal shelf main body is at overlay film Reason, described aluminum coated steel comprises the steps：
1) by 1.2 weight portion potassium peroxydisulfates, 1.2 weight portion mercaptobenzothiazolers, 0.5 weight portion calgon, 1.6 weights Amount part castor oil polyoxyethylene ether puts in 43 parts by weight of deionized water successively, stirs；
2) put into successively again 6.5 parts by weight propylene acid resin polyurethane copolymerization resins, 7.6 weight portion monobutyl ether acetates, 1.3 Weight portion empgen BB, 4.1 weight account polyethylene alcohol, continue stirring, uniform to being sufficiently mixed, prepared aluminum coated steel Liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Advantages of the present invention and having the beneficial effects that：There is provided a kind of supermarket adjustable type shelf, its metal shelf main body warp Cross aluminum coated steel, metal shelf body surfaces are covered with protecting film, there is excellent heat-resisting, abrasion-resistant, anti-oxidant, corrosion-resistant, anti- Rust, cold-resistant, weather resistance, and surface smoothness is good.
The performance of " coating treatment liquid " and purposes are determined by its component and proportioning, and in " coating treatment liquid " not With group, branch influences each other, and component and its proportioning can determine the final performance of " coating treatment liquid ", such as fruit component and its proportioning not Mutually coordinated, the beneficial effect that single component is brought, even can be eliminated by other components abatement, when serious, different groups Split-phase is mutually conflicted, and does not have whole synthesis effect, produces negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly Checking, obtain the optimal component of " coating treatment liquid " and proportioning so that multiple component combine, mutually coordinated and produce Positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is：
Embodiment 1
Supermarket's adjustable type shelf, it includes metal shelf main body, and this metal shelf main body, through aluminum coated steel, described is covered Film process comprises the steps：
1) by 1～2 weight portion potassium peroxydisulfate, 1.2 weight portion mercaptobenzothiazolers, 0.5 weight portion calgon, 1.6 Weight portion castor oil polyoxyethylene ether puts in 43 parts by weight of deionized water successively, stirs；
2) put into successively again 6.5 parts by weight propylene acid resin polyurethane copolymerization resins, 7.6 weight portion monobutyl ether acetates, 1.3 Weight portion empgen BB, 4.1 weight account polyethylene alcohol, continue stirring, uniform to being sufficiently mixed, prepared aluminum coated steel Liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Embodiment 2
Supermarket's adjustable type shelf, it includes metal shelf main body, and this metal shelf main body, through aluminum coated steel, described is covered Film process comprises the steps：
1) by 1 weight portion potassium peroxydisulfate, 1.2 weight portion mercaptobenzothiazolers, 0.5 weight portion calgon, 1.6 weight Part castor oil polyoxyethylene ether puts in 43 parts by weight of deionized water successively, stirs；
2) put into successively again 6.5 parts by weight propylene acid resin polyurethane copolymerization resins, 7.6 weight portion monobutyl ether acetates, 1.3 Weight portion empgen BB, 4.1 weight account polyethylene alcohol, continue stirring, uniform to being sufficiently mixed, prepared aluminum coated steel Liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Embodiment 3
Supermarket's adjustable type shelf, it includes metal shelf main body, and this metal shelf main body, through aluminum coated steel, described is covered Film process comprises the steps：
1) by 2 weight portion potassium peroxydisulfates, 1.2 weight portion mercaptobenzothiazolers, 0.5 weight portion calgon, 1.6 weight Part castor oil polyoxyethylene ether puts in 43 parts by weight of deionized water successively, stirs；
2) put into successively again 6.5 parts by weight propylene acid resin polyurethane copolymerization resins, 7.6 weight portion monobutyl ether acetates, 1.3 Weight portion empgen BB, 4.1 weight account polyethylene alcohol, continue stirring, uniform to being sufficiently mixed, prepared aluminum coated steel Liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Embodiment 4
Supermarket's adjustable type shelf, it includes metal shelf main body, and this metal shelf main body, through aluminum coated steel, described is covered Film process comprises the steps：
1) by 1.2 weight portion potassium peroxydisulfates, 1.2 weight portion mercaptobenzothiazolers, 0.5 weight portion calgon, 1.6 weights Amount part castor oil polyoxyethylene ether puts in 43 parts by weight of deionized water successively, stirs；
2) put into successively again 6.5 parts by weight propylene acid resin polyurethane copolymerization resins, 7.6 weight portion monobutyl ether acetates, 1.3 Weight portion empgen BB, 4.1 weight account polyethylene alcohol, continue stirring, uniform to being sufficiently mixed, prepared aluminum coated steel Liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Surface through metal shelf main body in the various embodiments described above is covered with protecting film, has excellent heat-resisting, abrasion-resistant, anti- Oxidation, corrosion-resistant, antirust, cold-resistant, weather resistance, and surface smoothness is good.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications Also should be regarded as protection scope of the present invention.

Claims (4)

1. supermarket with adjustable type shelf it is characterised in that it includes metal shelf main body, this metal shelf main body is at overlay film Reason, described aluminum coated steel comprises the steps：
1) by 1～2 weight portion potassium peroxydisulfate, 1.2 weight portion mercaptobenzothiazolers, 0.5 weight portion calgon, 1.6 weight Part castor oil polyoxyethylene ether puts in 43 parts by weight of deionized water successively, stirs；
2) 6.5 parts by weight propylene acid resin polyurethane copolymerization resins, 7.6 weight portion monobutyl ether acetates, 1.3 weight are put into again successively Part empgen BB, 4.1 weight account polyethylene alcohol, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
2. supermarket according to claim 1 with adjustable type shelf it is characterised in that it includes metal shelf main body, this gold Belong to shelf body through aluminum coated steel, described aluminum coated steel comprises the steps：
1) by 1 weight portion potassium peroxydisulfate, 1.2 weight portion mercaptobenzothiazolers, 0.5 weight portion calgon, 1.6 weight portion castors Sesame oil APEO puts in 43 parts by weight of deionized water successively, stirs；
2) 6.5 parts by weight propylene acid resin polyurethane copolymerization resins, 7.6 weight portion monobutyl ether acetates, 1.3 weight are put into again successively Part empgen BB, 4.1 weight account polyethylene alcohol, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
3. supermarket according to claim 1 with adjustable type shelf it is characterised in that it includes metal shelf main body, this gold Belong to shelf body through aluminum coated steel, described aluminum coated steel comprises the steps：
1) by 2 weight portion potassium peroxydisulfates, 1.2 weight portion mercaptobenzothiazolers, 0.5 weight portion calgon, 1.6 weight portion castors Sesame oil APEO puts in 43 parts by weight of deionized water successively, stirs；
2) 6.5 parts by weight propylene acid resin polyurethane copolymerization resins, 7.6 weight portion monobutyl ether acetates, 1.3 weight are put into again successively Part empgen BB, 4.1 weight account polyethylene alcohol, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
4. supermarket according to claim 1 with adjustable type shelf it is characterised in that it includes metal shelf main body, this gold Belong to shelf body through aluminum coated steel, described aluminum coated steel comprises the steps：
1) by 1.2 weight portion potassium peroxydisulfates, 1.2 weight portion mercaptobenzothiazolers, 0.5 weight portion calgon, 1.6 weight portions Castor oil polyoxyethylene ether puts in 43 parts by weight of deionized water successively, stirs；
2) 6.5 parts by weight propylene acid resin polyurethane copolymerization resins, 7.6 weight portion monobutyl ether acetates, 1.3 weight are put into again successively Part empgen BB, 4.1 weight account polyethylene alcohol, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid；
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
CN201610742511.XA 2016-08-29 2016-08-29 Supermarket adjustment type shelf Pending CN106381040A (en)