CN106349786A - Goods shelf for supermarket storehouses - Google Patents

Goods shelf for supermarket storehouses Download PDF

Info

Publication number
CN106349786A
CN106349786A CN201610742558.6A CN201610742558A CN106349786A CN 106349786 A CN106349786 A CN 106349786A CN 201610742558 A CN201610742558 A CN 201610742558A CN 106349786 A CN106349786 A CN 106349786A
Authority
CN
China
Prior art keywords
weight portion
weight
parts
main body
treatment liquid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610742558.6A
Other languages
Chinese (zh)
Inventor
邵俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changshu City Guli Town Miaoquan Daguang Metal Product Factory
Original Assignee
Changshu City Guli Town Miaoquan Daguang Metal Product Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changshu City Guli Town Miaoquan Daguang Metal Product Factory filed Critical Changshu City Guli Town Miaoquan Daguang Metal Product Factory
Priority to CN201610742558.6A priority Critical patent/CN106349786A/en
Publication of CN106349786A publication Critical patent/CN106349786A/en
Pending legal-status Critical Current

Abstract

The invention discloses a goods shelf for supermarket storehouses, comprising a metal shelf body; the metal shelf body is subjected to laminating treatment; the laminating treatment includes the steps of 1) adding 1-2 parts by weight of acrylic acid, 1.1 parts by weight of sodium carboxymethyl cellulose, 2.6 parts by weight of Upsilon-glycidoxypropyltrimethoxysilane and 1.7 parts by weight of dodecyltrimethylammonium chloride sequentially into 43 parts by weight of deionized water, and stirring well; 2) adding 5.2 parts by weight of polytetrafluoroethylene, 4.8 parts by weight of diethylene glycol, 1.8 parts by weight of alkylphenol ethoxylates and 1.1 parts by weight of 2-aminoethylheptadecenylimidazoline sequentially, and continuing to stir until full mixing to obtain a laminating liquid; 3) soaking the metal shelf body in the laminating liquid, removing, and drying. The metal shelf body of the goods shelf for supermarket storehouses has the surface coated with a protective film, good properties are provided, and the surface is highly glossy.

Description

Supermarket's warehouse shelf
Technical field
The present invention relates to supermarket's warehouse shelf.
Background technology
Existing supermarket warehouse shelf, heat-resisting, abrasion-resistant, the antioxidation of its metal shelf main body, corrosion-resistant, antirust, resistance to Cold, weather resistance has much room for improvement, and surface smoothness is also not ideal enough.
Content of the invention
It is an object of the invention to provide a kind of supermarket warehouse shelf, its metal shelf main body is through aluminum coated steel, gold Belong to shelf body surface and be covered with protecting film, there is excellent heat-resisting, abrasion-resistant, antioxidation, corrosion-resistant, antirust, cold-resistant, weatherability Can, and surface smoothness is good.
For achieving the above object, the technical scheme is that a kind of supermarket of design warehouse shelf, it includes metal goods Frame body, through aluminum coated steel, described aluminum coated steel comprises the steps: this metal shelf main body
1) by 1~2 parts by weight of acrylic acid, 1.1 weight portion sodium carboxymethyl cellulose, 2.6 weight portion γ-glycidyl ether Trimethoxy silane, 1.7 weight portion Trimethyllaurylammonium chlorides put in 43 parts by weight of deionized water successively, stir;
2) 5.2 weight portion politef, 4.8 weight portion diethylene glycol, 1.8 weight portion alkyl phenol polyoxy second are put into again successively Alkene ether, 1.1 weight portion 2- aminoethyl 17 alkenyl imidazoline, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Preferably, supermarket warehouse shelf, it includes metal shelf main body, this metal shelf main body through aluminum coated steel, Described aluminum coated steel comprises the steps:
1) by 1 parts by weight of acrylic acid, 1.1 weight portion sodium carboxymethyl cellulose, 2.6 weight portion γ-glycidyl ether three Methoxy silane, 1.7 weight portion Trimethyllaurylammonium chlorides put in 43 parts by weight of deionized water successively, stir;
2) 5.2 weight portion politef, 4.8 weight portion diethylene glycol, 1.8 weight portion alkyl phenol polyoxy second are put into again successively Alkene ether, 1.1 weight portion 2- aminoethyl 17 alkenyl imidazoline, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Preferably, supermarket warehouse shelf, it includes metal shelf main body, this metal shelf main body through aluminum coated steel, Described aluminum coated steel comprises the steps:
1) by 2 parts by weight of acrylic acid, 1.1 weight portion sodium carboxymethyl cellulose, 2.6 weight portion γ-glycidyl ether three Methoxy silane, 1.7 weight portion Trimethyllaurylammonium chlorides put in 43 parts by weight of deionized water successively, stir;
2) 5.2 weight portion politef, 4.8 weight portion diethylene glycol, 1.8 weight portion alkyl phenol polyoxy second are put into again successively Alkene ether, 1.1 weight portion 2- aminoethyl 17 alkenyl imidazoline, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Preferably, supermarket warehouse shelf, it includes metal shelf main body, this metal shelf main body through aluminum coated steel, Described aluminum coated steel comprises the steps:
1) by 1.2 parts by weight of acrylic acid, 1.1 weight portion sodium carboxymethyl cellulose, 2.6 weight portion γ-glycidyl ether Trimethoxy silane, 1.7 weight portion Trimethyllaurylammonium chlorides put in 43 parts by weight of deionized water successively, stir;
2) 5.2 weight portion politef, 4.8 weight portion diethylene glycol, 1.8 weight portion alkyl phenol polyoxy second are put into again successively Alkene ether, 1.1 weight portion 2- aminoethyl 17 alkenyl imidazoline, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Advantages of the present invention and having the beneficial effects that: provide a kind of supermarket warehouse shelf, its metal shelf main body is passed through Aluminum coated steel, metal shelf body surfaces are covered with protecting film, have excellent heat-resisting, abrasion-resistant, antioxidation, corrosion-resistant, antirust, Cold-resistant, weather resistance, and surface smoothness is good.
The performance of " coating treatment liquid " and purposes are determined by its component and proportioning, and in " coating treatment liquid " not With group, branch influences each other, and component and its proportioning can determine the final performance of " coating treatment liquid ", such as fruit component and its proportioning not Mutually coordinated, the beneficial effect that single component is brought, even can be eliminated by other components abatement, when serious, different groups Split-phase is mutually conflicted, and does not have whole synthesis effect, produces negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly Checking, obtain the optimal component of " coating treatment liquid " and proportioning so that multiple component combine, mutually coordinated and produce Positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Supermarket's warehouse shelf, it includes metal shelf main body, this metal shelf main body through aluminum coated steel, described overlay film Process comprises the steps:
1) by 1~2 parts by weight of acrylic acid, 1.1 weight portion sodium carboxymethyl cellulose, 2.6 weight portion γ-glycidyl ether Trimethoxy silane, 1.7 weight portion Trimethyllaurylammonium chlorides put in 43 parts by weight of deionized water successively, stir;
2) 5.2 weight portion politef, 4.8 weight portion diethylene glycol, 1.8 weight portion alkyl phenol polyoxy second are put into again successively Alkene ether, 1.1 weight portion 2- aminoethyl 17 alkenyl imidazoline, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Embodiment 2
Supermarket's warehouse shelf, it includes metal shelf main body, this metal shelf main body through aluminum coated steel, described overlay film Process comprises the steps:
1) by 1 parts by weight of acrylic acid, 1.1 weight portion sodium carboxymethyl cellulose, 2.6 weight portion γ-glycidyl ether three Methoxy silane, 1.7 weight portion Trimethyllaurylammonium chlorides put in 43 parts by weight of deionized water successively, stir;
2) 5.2 weight portion politef, 4.8 weight portion diethylene glycol, 1.8 weight portion alkyl phenol polyoxy second are put into again successively Alkene ether, 1.1 weight portion 2- aminoethyl 17 alkenyl imidazoline, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Embodiment 3
Supermarket's warehouse shelf, it includes metal shelf main body, this metal shelf main body through aluminum coated steel, described overlay film Process comprises the steps:
1) by 2 parts by weight of acrylic acid, 1.1 weight portion sodium carboxymethyl cellulose, 2.6 weight portion γ-glycidyl ether three Methoxy silane, 1.7 weight portion Trimethyllaurylammonium chlorides put in 43 parts by weight of deionized water successively, stir;
2) 5.2 weight portion politef, 4.8 weight portion diethylene glycol, 1.8 weight portion alkyl phenol polyoxy second are put into again successively Alkene ether, 1.1 weight portion 2- aminoethyl 17 alkenyl imidazoline, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Embodiment 4
Supermarket's warehouse shelf, it includes metal shelf main body, this metal shelf main body through aluminum coated steel, described overlay film Process comprises the steps:
1) by 1.2 parts by weight of acrylic acid, 1.1 weight portion sodium carboxymethyl cellulose, 2.6 weight portion γ-glycidyl ether Trimethoxy silane, 1.7 weight portion Trimethyllaurylammonium chlorides put in 43 parts by weight of deionized water successively, stir;
2) 5.2 weight portion politef, 4.8 weight portion diethylene glycol, 1.8 weight portion alkyl phenol polyoxy second are put into again successively Alkene ether, 1.1 weight portion 2- aminoethyl 17 alkenyl imidazoline, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
Surface through metal shelf main body in the various embodiments described above is covered with protecting film, has excellent heat-resisting, abrasion-resistant, anti- Oxidation, corrosion-resistant, antirust, cold-resistant, weather resistance, and surface smoothness is good.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications Also should be regarded as protection scope of the present invention.

Claims (4)

1., it is characterised in that it includes metal shelf main body, this metal shelf main body is at overlay film for supermarket warehouse shelf Reason, described aluminum coated steel comprises the steps:
1) by 1~2 parts by weight of acrylic acid, 1.1 weight portion sodium carboxymethyl cellulose, 2.6 weight portion γ-glycidyl ether front three TMOS, 1.7 weight portion Trimethyllaurylammonium chlorides put in 43 parts by weight of deionized water successively, stir;
2) 5.2 weight portion politef, 4.8 weight portion diethylene glycol, 1.8 weight portion alkylphenol-polyethenoxies are put into again successively Ether, 1.1 weight portion 2- aminoethyl 17 alkenyl imidazoline, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
2. supermarket according to claim 1 warehouse shelf are it is characterised in that it includes metal shelf main body, this metal Through aluminum coated steel, described aluminum coated steel comprises the steps: shelf body
1) by 1 parts by weight of acrylic acid, 1.1 weight portion sodium carboxymethyl cellulose, 2.6 weight portion γ-glycidyl ether trimethoxy Base silane, 1.7 weight portion Trimethyllaurylammonium chlorides put in 43 parts by weight of deionized water successively, stir;
2) 5.2 weight portion politef, 4.8 weight portion diethylene glycol, 1.8 weight portion alkylphenol-polyethenoxies are put into again successively Ether, 1.1 weight portion 2- aminoethyl 17 alkenyl imidazoline, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
3. supermarket according to claim 1 warehouse shelf are it is characterised in that it includes metal shelf main body, this metal Through aluminum coated steel, described aluminum coated steel comprises the steps: shelf body
1) by 2 parts by weight of acrylic acid, 1.1 weight portion sodium carboxymethyl cellulose, 2.6 weight portion γ-glycidyl ether trimethoxy Base silane, 1.7 weight portion Trimethyllaurylammonium chlorides put in 43 parts by weight of deionized water successively, stir;
2) 5.2 weight portion politef, 4.8 weight portion diethylene glycol, 1.8 weight portion alkylphenol-polyethenoxies are put into again successively Ether, 1.1 weight portion 2- aminoethyl 17 alkenyl imidazoline, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
4. supermarket according to claim 1 warehouse shelf are it is characterised in that it includes metal shelf main body, this metal Through aluminum coated steel, described aluminum coated steel comprises the steps: shelf body
1) by 1.2 parts by weight of acrylic acid, 1.1 weight portion sodium carboxymethyl cellulose, 2.6 weight portion γ-glycidyl ether front three TMOS, 1.7 weight portion Trimethyllaurylammonium chlorides put in 43 parts by weight of deionized water successively, stir;
2) 5.2 weight portion politef, 4.8 weight portion diethylene glycol, 1.8 weight portion alkylphenol-polyethenoxies are put into again successively Ether, 1.1 weight portion 2- aminoethyl 17 alkenyl imidazoline, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal shelf main body is inserted dipping in coating treatment liquid, take out post-drying.
CN201610742558.6A 2016-08-29 2016-08-29 Goods shelf for supermarket storehouses Pending CN106349786A (en)