CN106317519A - 一种耐老化、阻燃型电力电缆护套材料 - Google Patents

一种耐老化、阻燃型电力电缆护套材料 Download PDF

Info

Publication number
CN106317519A
CN106317519A CN201610652974.7A CN201610652974A CN106317519A CN 106317519 A CN106317519 A CN 106317519A CN 201610652974 A CN201610652974 A CN 201610652974A CN 106317519 A CN106317519 A CN 106317519A
Authority
CN
China
Prior art keywords
parts
cable sheath
sheath material
power cable
flame retardant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610652974.7A
Other languages
English (en)
Inventor
邵斌斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Chengtong Automation Equipment Co Ltd
Original Assignee
Wuhu Chengtong Automation Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Chengtong Automation Equipment Co Ltd filed Critical Wuhu Chengtong Automation Equipment Co Ltd
Priority to CN201610652974.7A priority Critical patent/CN106317519A/zh
Publication of CN106317519A publication Critical patent/CN106317519A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐老化、阻燃型电力电缆护套材料，包括如下质量份数的组分：低密度聚乙烯30‑40份、PVC树脂15‑20份、乙烯基三甲氧基硅烷2‑4份、偏苯三甲酸三异辛酯1‑2份、硫化剂0.8‑1.2份、阻燃剂3‑5份、氢氧化铝2‑4份、丁睛胶1.2‑1.6份、活性碳酸钙2‑4份、稳定剂0.6‑0.8份、丁苯橡胶60‑80份、环氧化天然橡胶20‑40份、乙烯‑醋酸乙烯酯共聚物5‑10份、纳米白炭黑10‑30份等。本发明的电缆护套材料，其具有优异的耐老化性能和阻燃性能，且强度高，材料环保，制作的电缆护套综合性能好，使用寿命长。

Description

一种耐老化、阻燃型电力电缆护套材料
技术领域
本发明属于电力电缆生产技术领域，具体涉及一种耐老化、阻燃型电力电缆护套材料。
背景技术
随着电力电缆埋地敷设工程的迅速发展，对电缆保护提出的更高要求，电缆保护套管是采用聚乙烯 PE 和优质钢管经过喷砂抛丸前处理、浸塑或涂装、加温固化工艺制作而 成。它是保护电线和电缆最常用的一种电绝缘管。因为具有绝缘性能良好、化学稳定性高、 不生锈、不老化、可适应苛刻环境而被广泛得以应用。
电线电缆行业是中国仅次于汽车行业的第二大行业，产品品种满足率和国内市场占有率均超过 90%。在世界范围内，中国电线电缆总产值已超过美国，成为世界上第一大电线电缆生产国。伴随着中国电线电缆行业高速发展，新增企业数量不断上升，行业整体技术水平得到大幅提高。随着中国电力工业、数据通信业、城市轨道交通业、汽车业以及造船等行业规模的不断扩大，对电线电缆的需求也将迅速增长，未来电线电缆业还有巨大的发展潜力。
聚乙烯以其质轻、价廉、优异的电绝缘性及耐化学性等诸多优点而广泛应用于各个行业，但其阻燃性差，在制作电线电缆时容易引起火灾。因此，如何生产一种环保阻燃的电缆材料，具有重要的现实意义。
丁苯橡胶是 1,3- 丁二烯和苯乙烯经共聚而制得的弹性体，与一般的通用橡胶相比，具有以下优点 ：硫化曲线平坦，胶料不易烧焦和过硫 ；耐磨性、耐热性、耐油性和耐老化 性好 ；在加工过程中相对分子质量降低到一定程度不再降低，因而不易过炼，可塑度均匀， 硫化橡胶硬度变化小 ；提高相对分子质量可以实现高填充性，充油橡胶的加工性能好；容 易与其他高不饱和通用橡胶并用。但是纯丁苯橡胶强度低，与配合剂的相容性差，用作电缆 材料不能满足社会的需要，需要进行改性。
发明内容
发明目的：本发明针对现有技术中的不足，提出一种具有优异的耐老化性能和阻燃性能，且强度高，材料环保，制作的电缆护套综合性能好，使用寿命长的电力电缆护套材料。
技术方案：本发明所述的一种耐老化、阻燃型电力电缆护套材料，包括如下质量份数的组分：
低密度聚乙烯 30-40 份、PVC 树脂 15-20 份、乙烯基三甲氧基硅烷 2-4 份、偏苯三甲酸三异辛酯 1-2 份、硫化剂 0.8-1.2 份、阻燃剂 3-5 份、氢氧化铝 2-4 份、丁睛胶1.2-1.6 份、 活性碳酸钙 2-4 份、稳定剂 0.6-0.8 份、丁苯橡胶 60-80 份、 环氧化天然橡胶 20-40 份、乙烯-醋酸乙烯酯共聚物 5-10 份、纳米白炭黑 10-30 份、活性硅酸钙 5-20 份、纳米二氧化硅 5-15 份、硬脂酸 5-10 份、氧化锌 3-8 份、生物碳 15-30 份、菜籽油 5-13 份、椰子油 3-8 份、橄榄油 4-10 份、过氧化苯甲酰 3-7 份、丙三醇 0.5-1.3份、三羟甲基丙烷 0.2-1 份、季戊四醇 0.2-1.3 份、促进剂 1-3 份、防老剂 5-8 份。
进一步的，包括如下质量份数的组分：
低密度聚乙烯 35-40 份、PVC 树脂 16-20 份、乙烯基三甲氧基硅烷 3-4 份、偏苯三甲酸三异辛酯 1.5-2 份、硫化剂 1-1.2 份、阻燃剂 4-5 份、氢氧化铝 3-4 份、丁睛胶1.4-1.6 份、 活性碳酸钙 3-4 份、稳定剂 0.6-0.8 份、丁苯橡胶 70-80 份、环氧化天然橡胶 30-40 份、乙烯-醋酸乙烯酯共聚物 8-10 份、纳米白炭黑 20-30 份、活性硅酸钙10-20 份、纳米二氧化硅 10-15 份、硬脂酸 8-10 份、氧化锌 5-8 份、生物碳20-30 份、菜籽油 10-13 份、椰子油5-8 份、橄榄油 6-10 份、过氧化苯甲酰 5-7 份、丙三醇 1-1.3 份、三羟甲基丙烷 0.6-1 份、季戊四醇 0.8-1.3 份、促进剂 2-3 份、防老剂 6-8 份。
进一步的，包括如下质量份数的组分：
低密度聚乙烯 38 份、PVC 树脂 18 份、乙烯基三甲氧基硅烷 3.5份、偏苯三甲酸三异辛酯 1.7份、硫化剂 1.1份、阻燃剂 4.5份、氢氧化铝 3.5份、丁睛胶 1.5份、 活性碳酸钙3.5份、稳定剂 0.7份、丁苯橡胶 75份、环氧化天然橡胶 35 份、乙烯-醋酸乙烯酯共聚物9份、纳米白炭黑 25份、活性硅酸钙15份、纳米二氧化硅 12份、硬脂酸9份、氧化锌7份、生物碳25份、菜籽油 12份、椰子油6份、橄榄油 8 份、过氧化苯甲酰 6份、丙三醇 1.2份、三羟甲基丙烷 0.8份、季戊四醇 1 份、促进剂 2.5份、防老剂7份。
进一步的，所述的硫化剂为过氧化二异丙苯和硫磺按照重量比 1-2 ：1 组成的混合物。
进一步的，所述的阻燃剂为聚磷酸铵和二氧化锑按照重量比 3 ：1-2 组成的混合物。
进一步的，所述的稳定剂是硬脂酸钙和硬脂酸锌按照摩尔比 1-2 ：1 组成的混合物。
进一步的，所述促进剂为促进剂 DM、促进剂 D、促进剂 CZ 中的一种或者多种的组合。
进一步的，所述防老剂为防老剂 4010NA、防老剂 RD、防老剂 BZ、防老剂 MBZ、防老剂 NBC、防老剂 4020、防老剂 A、防老 剂 DFC-34 中的一种或者多种的组合。
有益效果：本发明的电缆护套材料，其具有优异的耐老化性能和阻燃性能，且强度高，材料环保，制作的电缆护套综合性能好，使用寿命长。
具体实施方式
下面结合具体实施例对本发明作进一步说明：
实施例1
一种耐老化、阻燃型电力电缆护套材料，包括如下质量份数的组分：
低密度聚乙烯 30份、PVC 树脂 15份、乙烯基三甲氧基硅烷 2份、偏苯三甲酸三异辛酯1份、硫化剂 0.8份、阻燃剂 3 份、氢氧化铝 2份、丁睛胶 1.2份、 活性碳酸钙 2份、稳定剂0.6 份、丁苯橡胶 60 份、 环氧化天然橡胶 20份、乙烯-醋酸乙烯酯共聚物 5份、纳米白炭黑 10份、活性硅酸钙 5份、纳米二氧化硅 5-份、硬脂酸 5份、氧化锌 3份、生物碳 15份、菜籽油 5份、椰子油 3份、橄榄油 4 份、过氧化苯甲酰 3份、丙三醇 0.5份、三羟甲基丙烷0.2份、季戊四醇 0.2份、促进剂 1份、防老剂 5份。
所述的硫化剂为过氧化二异丙苯和硫磺按照重量比 1：1 组成的混合物。
所述的阻燃剂为聚磷酸铵和二氧化锑按照重量比 3 ：1组成的混合物。
所述的稳定剂是硬脂酸钙和硬脂酸锌按照摩尔比 1 ：1 组成的混合物。
所述促进剂为促进剂 DM。
所述防老剂为防老剂 4010NA。
实施例2
一种耐老化、阻燃型电力电缆护套材料，包括如下质量份数的组分：
低密度聚乙烯40 份、PVC 树脂20 份、乙烯基三甲氧基硅烷 4 份、偏苯三甲酸三异辛酯 2 份、硫化剂 1.2 份、阻燃剂 5 份、氢氧化铝 4 份、丁睛胶 1.6 份、 活性碳酸钙 4份、稳定剂 0.8 份、丁苯橡胶 80 份、 环氧化天然橡胶 40 份、乙烯-醋酸乙烯酯共聚物10 份、纳米白炭黑 30 份、活性硅酸钙 20 份、纳米二氧化硅 15 份、硬脂酸 10 份、氧化锌 8 份、生物碳 30 份、菜籽油 13 份、椰子油 8 份、橄榄油 10 份、过氧化苯甲酰 7 份、丙三醇1.3 份、三羟甲基丙烷 1 份、季戊四醇 1.3 份、促进剂 3 份、防老剂 8 份。
所述的硫化剂为过氧化二异丙苯和硫磺按照重量比 2 ：1 组成的混合物。
所述的阻燃剂为聚磷酸铵和二氧化锑按照重量比 3 ：2 组成的混合物。
所述的稳定剂是硬脂酸钙和硬脂酸锌按照摩尔比 2 ：1 组成的混合物。
所述促进剂为促进剂 DM、促进剂 D两者的组合。
所述防老剂为防老剂 4010NA与防老剂 DFC-34 两者的组合。
实施例3
一种耐老化、阻燃型电力电缆护套材料，包括如下质量份数的组分：
低密度聚乙烯 38 份、PVC 树脂 18 份、乙烯基三甲氧基硅烷 3.5份、偏苯三甲酸三异辛酯 1.7份、硫化剂 1.1份、阻燃剂 4.5份、氢氧化铝 3.5份、丁睛胶 1.5份、 活性碳酸钙3.5份、稳定剂 0.7份、丁苯橡胶 75份、环氧化天然橡胶 35 份、乙烯-醋酸乙烯酯共聚物9份、纳米白炭黑 25份、活性硅酸钙15份、纳米二氧化硅 12份、硬脂酸9份、氧化锌7份、生物碳25份、菜籽油 12份、椰子油6份、橄榄油 8 份、过氧化苯甲酰 6份、丙三醇 1.2份、三羟甲基丙烷 0.8份、季戊四醇 1 份、促进剂 2.5份、防老剂7份。
所述的硫化剂为过氧化二异丙苯和硫磺按照重量比 1：1 组成的混合物。
所述的阻燃剂为聚磷酸铵和二氧化锑按照重量比 3 ：1 组成的混合物。
所述的稳定剂是硬脂酸钙和硬脂酸锌按照摩尔比 2 ：1 组成的混合物。
所述促进剂为促进剂 CZ。
进一步的，所述防老剂为防老剂 RD与防老剂 BZ两者的组合。
本发明的电缆护套材料，其具有优异的耐老化性能和阻燃性能，且强度高，材料环保，制作的电缆护套综合性能好，使用寿命长。
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，虽然本发明已以较佳实施例揭露如上，然而并非用以限定本发明，任何熟悉本专业的技术人员，在不脱离本发明技术方案范围内，当可利用上述揭示的技术内容作出些许更动或修饰为等同变化的等效实施例，但凡是未脱离本发明技术方案的内容，依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。

Claims (8)

1.一种耐老化、阻燃型电力电缆护套材料，其特征在于：包括如下质量份数的组分：
低密度聚乙烯 30-40 份、PVC 树脂 15-20 份、乙烯基三甲氧基硅烷 2-4 份、偏苯三甲酸三异辛酯 1-2 份、硫化剂 0.8-1.2 份、阻燃剂 3-5 份、氢氧化铝 2-4 份、丁睛胶1.2-1.6 份、 活性碳酸钙 2-4 份、稳定剂 0.6-0.8 份、丁苯橡胶 60-80 份、 环氧化天然橡胶 20-40 份、乙烯-醋酸乙烯酯共聚物 5-10 份、纳米白炭黑 10-30 份、活性硅酸钙 5-20 份、纳米二氧化硅 5-15 份、硬脂酸 5-10 份、氧化锌 3-8 份、生物碳 15-30 份、菜籽油 5-13 份、椰子油 3-8 份、橄榄油 4-10 份、过氧化苯甲酰 3-7 份、丙三醇 0.5-1.3份、三羟甲基丙烷 0.2-1 份、季戊四醇 0.2-1.3 份、促进剂 1-3 份、防老剂 5-8 份。
2.根据权利要求1所述的一种耐老化、阻燃型电力电缆护套材料，其特征在于：包括如下质量份数的组分：
低密度聚乙烯 35-40 份、PVC 树脂 16-20 份、乙烯基三甲氧基硅烷 3-4 份、偏苯三甲酸三异辛酯 1.5-2 份、硫化剂 1-1.2 份、阻燃剂 4-5 份、氢氧化铝 3-4 份、丁睛胶1.4-1.6 份、 活性碳酸钙 3-4 份、稳定剂 0.6-0.8 份、丁苯橡胶 70-80 份、环氧化天然橡胶 30-40 份、乙烯-醋酸乙烯酯共聚物 8-10 份、纳米白炭黑 20-30 份、活性硅酸钙10-20 份、纳米二氧化硅 10-15 份、硬脂酸 8-10 份、氧化锌 5-8 份、生物碳20-30 份、菜籽油 10-13 份、椰子油5-8 份、橄榄油 6-10 份、过氧化苯甲酰 5-7 份、丙三醇 1-1.3 份、三羟甲基丙烷 0.6-1 份、季戊四醇 0.8-1.3 份、促进剂 2-3 份、防老剂 6-8 份。
3.根据权利要求1或2所述的一种耐老化、阻燃型电力电缆护套材料，其特征在于：包括如下质量份数的组分：
低密度聚乙烯 38 份、PVC 树脂 18 份、乙烯基三甲氧基硅烷 3.5份、偏苯三甲酸三异辛酯 1.7份、硫化剂 1.1份、阻燃剂 4.5份、氢氧化铝 3.5份、丁睛胶 1.5份、 活性碳酸钙3.5份、稳定剂 0.7份、丁苯橡胶 75份、环氧化天然橡胶 35 份、乙烯-醋酸乙烯酯共聚物9份、纳米白炭黑 25份、活性硅酸钙15份、纳米二氧化硅 12份、硬脂酸9份、氧化锌7份、生物碳25份、菜籽油 12份、椰子油6份、橄榄油 8 份、过氧化苯甲酰 6份、丙三醇 1.2份、三羟甲基丙烷 0.8份、季戊四醇 1 份、促进剂 2.5份、防老剂7份。
4.根据权利要求1-3任一一项所述的一种耐老化、阻燃型电力电缆护套材料，其特征在于：所述的硫化剂为过氧化二异丙苯和硫磺按照重量比 1-2 ：1 组成的混合物。
5.根据权利要求1-3任一一项所述的一种耐老化、阻燃型电力电缆护套材料，其特征在于：所述的阻燃剂为聚磷酸铵和二氧化锑按照重量比 3 ：1-2 组成的混合物。
6.根据权利要求1-3任一一项所述的一种耐老化、阻燃型电力电缆护套材料，其特征在于：所述的稳定剂是硬脂酸钙和硬脂酸锌按照摩尔比 1-2 ：1 组成的混合物。
7.根据权利要求1-3任一一项所述的一种耐老化、阻燃型电力电缆护套材料，其特征在于：所述促进剂为促进剂 DM、促进剂 D、促进剂 CZ 中的一种或者多种的组合。
8.根据权利要求1-3任一一项所述的一种耐老化、阻燃型电力电缆护套材料，其特征在于：所述防老剂为防老剂 4010NA、防老剂 RD、防老剂 BZ、防老剂 MBZ、防老剂 NBC、防老剂4020、防老剂 A、防老 剂 DFC-34 中的一种或者多种的组合。
CN201610652974.7A 2016-08-11 2016-08-11 一种耐老化、阻燃型电力电缆护套材料 Pending CN106317519A (zh)