CN106297955A - 一种纳米银导体浆料 - Google Patents
一种纳米银导体浆料 Download PDFInfo
- Publication number
- CN106297955A CN106297955A CN201610879015.9A CN201610879015A CN106297955A CN 106297955 A CN106297955 A CN 106297955A CN 201610879015 A CN201610879015 A CN 201610879015A CN 106297955 A CN106297955 A CN 106297955A
- Authority
- CN
- China
- Prior art keywords
- conductive paste
- nano silver
- silver conductive
- nano
- organic carrier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明是一种纳米银导体浆料,由以下质量百分比的原料组成:纳米银线0.1‑1%、玻璃粉0.5‑14%、有机载体5‑28%、分散剂1‑2%、流平剂1‑5%、消泡剂0.3‑0.8%、无机添加剂0.1‑6%、溶剂加至100%。本发明提供一种纳米银导体浆料,通过添加分散剂,使得浆料分散均匀,添加消泡剂和流平剂,有效解决了纳米银导体浆料的电阻稳定性差及导电性差的问题,加入有机载体,有效避免了纳米银线易脱落的问题。
Description
技术领域
本发明涉及一种电子浆料制备技术领域,尤其涉及一种纳米银导体浆料。
背景技术
随着导体浆料广泛的应用于各种高性能电子产品中,对导体浆料性能的要求也越来越高。粒径在微米、亚微米、纳米级的银颗粒被广泛用作导体浆料,采用纳米银制备导体浆料,具有很大的优势,然而传统的纳米银导体浆料存在浆料分散不均匀,电阻稳定性差,导电性差,易脱落等问题。
发明内容
本发明旨在解决现有技术的不足,而提供一种纳米银导体浆料。
本发明为实现上述目的,采用以下技术方案:一种纳米银导体浆料,其特征在于,由以下质量百分比的原料组成:
纳米银线0.1-1%;
玻璃粉0.5-14%;
有机载体5-28%;
分散剂1-2%;
流平剂1-5%;
消泡剂0.3-0.8%;
无机添加剂0.1-6%;
溶剂加至100%。
作为优选,所述纳米银线的长度范围在15-30μm内。
作为优选,所述的玻璃粉是指硼铝硅酸钛玻璃粉末。
作为优选,所述的有机载体由以下质量百分比的原料组成:
乙基纤维素树脂10-60%;
丙烯酸树脂20-60%;
丁基卡必醇醋酸酯13-35%。
作为优选,所述的分散剂为聚乙烯吡咯烷酮。
作为优选,所述的流平剂是指有机硅油或乙二醇丁醚中的任意一种。
作为优选,所述的消泡剂为聚硅氧烷。
作为优选,所述的溶剂为磷酸三丁酯、柠檬酸三丁酯和二甘醇乙醚醋酸酯中的一种或多种。
本发明的有益效果是:本发明提供一种纳米银导体浆料,通过添加分散剂,使得浆料分散均匀,添加消泡剂和流平剂,有效解决了纳米银导体浆料的电阻稳定性差及导电性差的问题,加入有机载体,有效避免了纳米银线易脱落的问题。
具体实施方式
下面结合实施例对本发明作进一步说明:
实施例1
一种纳米银导体浆料,由以下质量百分比的原料组成:
纳米银线0.1%;
硼铝硅酸钛玻璃粉末0.5%;
有机载体5%;
聚乙烯吡咯烷酮1%;
有机硅油1%;
聚硅氧烷0.3%;
无机添加剂0.1%;
磷酸三丁酯92%。
所述纳米银线的长度为15μm。
所述的有机载体由以下质量百分比的原料组成:
乙基纤维素树脂40%;
丙烯酸树脂40%;
丁基卡必醇醋酸酯20%。
实施例2
一种纳米银导体浆料,由以下质量百分比的原料组成:
纳米银线1%;
硼铝硅酸钛玻璃粉末14%;
有机载体28%;
聚乙烯吡咯烷酮2%;
乙二醇丁醚5%;
聚硅氧烷0.8%;
无机添加剂6%;
二甘醇乙醚醋酸酯43.2%。
所述纳米银线的长度为30μm。
所述的有机载体由以下质量百分比的原料组成:
乙基纤维素树脂30%;
丙烯酸树脂55%;
丁基卡必醇醋酸酯15%。
上面对本发明进行了示例性描述,显然本发明具体实现并不受上述方式的限制,只要采用了本发明的方法构思和技术方案进行的各种改进,或未经改进直接应用于其它场合的,均在本发明的保护范围之内。
Claims (8)
1.一种纳米银导体浆料,其特征在于,由以下质量百分比的原料组成:
纳米银线 0.1-1%;
玻璃粉 0.5-14%;
有机载体 5-28%;
分散剂 1-2%;
流平剂 1-5%;
消泡剂 0.3-0.8%;
无机添加剂 0.1-6%;
溶剂加至 100%。
2.根据权利要求1所述的一种纳米银导体浆料,其特征在于,所述纳米银线的长度范围在15-30μm内。
3.根据权利要求1所述的一种纳米银导体浆料,其特征在于,所述的玻璃粉是指硼铝硅酸钛玻璃粉末。
4.根据权利要求1所述的一种纳米银导体浆料,其特征在于,所述的有机载体由以下质量百分比的原料组成:
乙基纤维素树脂 10-60%;
丙烯酸树脂 20-60%;
丁基卡必醇醋酸酯 13-35%。
5.根据权利要求1所述的一种纳米银导体浆料,其特征在于,所述的分散剂为聚乙烯吡咯烷酮。
6.根据权利要求1所述的一种纳米银导体浆料,其特征在于,所述的流平剂是指有机硅油或乙二醇丁醚中的任意一种。
7.根据权利要求1所述的一种纳米银导体浆料,其特征在于,所述的消泡剂为聚硅氧烷。
8.根据权利要求1所述的一种纳米银导体浆料,其特征在于,所述的溶剂为磷酸三丁酯、柠檬酸三丁酯和二甘醇乙醚醋酸酯中的一种或多种。