CN106280838A - A kind of air purifying coating for automobile collection box and preparation method thereof - Google Patents
A kind of air purifying coating for automobile collection box and preparation method thereof Download PDFInfo
- Publication number
- CN106280838A CN106280838A CN201610665404.1A CN201610665404A CN106280838A CN 106280838 A CN106280838 A CN 106280838A CN 201610665404 A CN201610665404 A CN 201610665404A CN 106280838 A CN106280838 A CN 106280838A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- collection box
- air purifying
- automobile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of air purifying coating for automobile collection box, be made up of following raw materials according: Hydroxylated acrylic resin, pure-acrylic emulsion, celluosic resin, lignocellulose, nano zine oxide, wetting agent, catalyst, thickening agent, Pulvis Talci, kieselguhr, hexone, propylene glycol monomethyl ether, deionized water, tetramethylolmethane；Its preparation method in turn includes the following steps: (1) is by uniform for corresponding raw material stirring；(2) mixed solution is prepared；(3) coating mixed liquor is prepared；(4) coating mixed liquor is ground, filter to obtain finished product.Excellent product performance of the present invention, having good purification air performance, its coating surface is smooth, fine and smooth, smooth, and gloss retention is good, hot strength and elongation at break are superior to common coating, can meet automobile collection box and the anticorrosion of casing application, weather-proof etc. is used requirement；Preparation method of the present invention is simple, and cost is relatively low, is suitable to industrialized mass production.
Description
Technical field
The present invention relates to coating industry field, particularly relate to a kind of air purifying coating for automobile collection box and system thereof
Preparation Method.
Background technology
Along with the development of social life level, nowadays increasing people have the private car of oneself, Automobile Products
Motor Maintenance articles for use have the most just become the essential part of vehicle maintenance in other words, as three macroplates in market after automobile
One of, Automobile Products market is also one of industry the most with fastest developing speed, that prospect is best.Blowout along with Domestic Automotive Industry
Formula develops, and Automobile Products industry development speed is at a tremendous pace, and according to statistics, 2011, China's Automobile Products series products gross output value was just
430,000,000,000 yuans are reached, family more than ten thousand more than more than 10 of Automobile Products industry distributing business of current China.Along with Chinese Government
Gradually pay attention to Automobile Products industry, actively push forward the industrialization of Automobile Products, encourage the technological innovation of Automobile Products industry, government
Also in relevant laws and regulations and the standard of gradual perfection Automobile Products industry, for the competition ring that the development offer of Automobile Products enterprise is orderly
Border.Simultaneously Automobile Products enterprise also should constantly autonomous innovation, introduce and cultivate professional, catching the good of Automobile Products industry
Opportunity to develop.
Containing box in Automobile Products is mainly placed in automobile trunk, is used for depositing article.At present, people are for vapour
Article in the interior material of car and automobile are increasingly paid attention to, to the requirement of the aspects such as the coating property of Automobile Products, environmental protection more
Come the highest, but can't be met, in the face of the huge market demand and the ever-increasing application of Automobile Products coating
Prospect, need to develop technically, on cost, more show the coating of powerful competitive advantage in performance so that it is to automobile
Articles for use have well protection and decoration.
Summary of the invention
The invention aims to overcome the deficiencies in the prior art, it is provided that a kind of clean for automobile collection box
Change air coating and preparation method thereof, this coating products excellent performance, there is good purification air performance, and meet environmental protection and want
Ask.
For solve above-mentioned technical problem, the present invention by the following technical solutions:
A kind of air purifying coating for automobile collection box, it is characterised in that be prepared by the raw materials in: hydroxyl
Base acrylic resin 15～35 parts, pure-acrylic emulsion 5～20 parts, celluosic resin 5～20 parts, lignocellulose 2～10 parts, nanometer
Zinc oxide 1～5 parts, wetting agent 0.2～1 part, catalyst 1～5 parts, thickening agent 0.2～1.5 parts, Pulvis Talci 1～5 parts, kieselguhr
1～5 part, hexone 0.2～1 part, propylene glycol monomethyl ether 0.3～2 parts, deionized water 20～50 parts, tetramethylolmethane 2～
10 parts；
Its preparation method in turn includes the following steps:
(1) by Hydroxylated acrylic resin, pure-acrylic emulsion, celluosic resin, lignocellulose, nano zine oxide and deionization
Water is put in reaction vessel, and controlling temperature is 50～60 DEG C, stirs and makes mixture dispersed in 15～30 minutes；
(2) again Pulvis Talci, kieselguhr, hexone and propylene glycol monomethyl ether are joined in reaction vessel, constantly
Temperature, until mix homogeneously, is risen to 70～75 DEG C and carries out being heated at reflux 1～1.5 hour, be finally slowly added to Ji Wusi by stirring
Alcohol, and stirring and dissolving 0.5～1 hour, obtain mixed solution；
(3) mixed solution that step (2) prepares is cooled to 20～30 DEG C, then is separately added into wetting agent, catalyst and increasing
Thick dose, it is kept stirring for 20～50 minutes, obtains coating mixed liquor；
(4) the coating mixed liquor that step (3) prepares is entered sand mill to grind 4～6 times, filter to obtain finished product.
Preferably, described wetting agent is polyether modified siloxane.
Preferably, described catalyst is sodium sulfonate.
Preferably, described thickening agent is carboxymethyl cellulose.
The present invention is had advantageous effect in that compared with prior art:
The present invention mostly is plastic material in view of automobile collection box, and its lower hardness, the feature of surface not scratch resistance, by adopting
With combination property preferably high-molecular organic material and carry out optimum organization, improve the purification air performance of compositions, use
The coating surface that the present invention obtains is smooth, fine and smooth, smooth, and gloss retention is good, and hot strength and elongation at break are superior to commonly be coated with
Material, can meet automobile collection box and the anticorrosion of casing application, weather-proof etc. is used requirement；Present invention achieves filling of resource and the energy
Dividing and utilize, production process is environment friendly and pollution-free, and its preparation method is simple, and cost is relatively low, with short production cycle, has convenient transportation, easily
In storage, the feature such as easy to use, be suitable to industrialized mass production.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1:
A kind of air purifying coating for automobile collection box, it is characterised in that be prepared by the raw materials in: hydroxyl
Base acrylic resin 15 parts, pure-acrylic emulsion 5 parts, celluosic resin 5 parts, lignocellulose 2 parts, nano zine oxide 1 part, wetting agent
0.2 part, catalyst 1 part, thickening agent 0.2 part, Pulvis Talci 1 part, 1 part of kieselguhr, hexone 0.2 part, propylene glycol first
0.3 part of ether, deionized water 20 parts, tetramethylolmethane 2 parts；
Its preparation method in turn includes the following steps:
(1) by Hydroxylated acrylic resin, pure-acrylic emulsion, celluosic resin, lignocellulose, nano zine oxide and deionization
Water is put in reaction vessel, and controlling temperature is 50～60 DEG C, stirs and makes mixture dispersed in 15 minutes；
(2) again Pulvis Talci, kieselguhr, hexone and propylene glycol monomethyl ether are joined in reaction vessel, constantly
Temperature, until mix homogeneously, is risen to 70～75 DEG C and carries out being heated at reflux 1 hour, be finally slowly added to tetramethylolmethane by stirring, and
Stirring and dissolving 0.5 hour, obtains mixed solution；
(3) mixed solution that step (2) prepares is cooled to 20～30 DEG C, then is separately added into wetting agent, catalyst and increasing
Thick dose, it is kept stirring for 20 minutes, obtains coating mixed liquor；
(4) the coating mixed liquor that step (3) prepares is entered sand mill to grind 4 times, filter to obtain finished product.
Preferably, described wetting agent is polyether modified siloxane.
Preferably, described catalyst is sodium sulfonate.
Preferably, described thickening agent is carboxymethyl cellulose.
Embodiment 2:
A kind of air purifying coating for automobile collection box, it is characterised in that be prepared by the raw materials in: hydroxyl
Base acrylic resin 35 parts, pure-acrylic emulsion 20 parts, celluosic resin 20 parts, lignocellulose 10 parts, nano zine oxide 5 parts, profit
Humectant 1 part, catalyst 5 parts, thickening agent 1.5 parts, Pulvis Talci 5 parts, 5 parts of kieselguhr, hexone 1 part, propylene glycol first
2 parts of ether, deionized water 50 parts, tetramethylolmethane 10 parts；
Its preparation method in turn includes the following steps:
(1) by Hydroxylated acrylic resin, pure-acrylic emulsion, celluosic resin, lignocellulose, nano zine oxide and deionization
Water is put in reaction vessel, and controlling temperature is 50～60 DEG C, stirs and makes mixture dispersed in 30 minutes；
(2) again Pulvis Talci, kieselguhr, hexone and propylene glycol monomethyl ether are joined in reaction vessel, constantly
Temperature, until mix homogeneously, is risen to 70～75 DEG C and carries out being heated at reflux 1.5 hours, be finally slowly added to tetramethylolmethane by stirring,
And stirring and dissolving 1 hour, obtain mixed solution；
(3) mixed solution that step (2) prepares is cooled to 20～30 DEG C, then is separately added into wetting agent, catalyst and increasing
Thick dose, it is kept stirring for 50 minutes, obtains coating mixed liquor；
(4) the coating mixed liquor that step (3) prepares is entered sand mill to grind 6 times, filter to obtain finished product.
In the above embodiment of the present invention:
Described wetting agent is polyether modified siloxane；
Described catalyst is sodium sulfonate；
Described thickening agent is carboxymethyl cellulose.
The present invention mostly is plastic material in view of automobile collection box, and its lower hardness, the feature of surface not scratch resistance, by adopting
With combination property preferably high-molecular organic material and carry out optimum organization, improve the purification air performance of compositions, use
The coating surface that the present invention obtains is smooth, fine and smooth, smooth, and gloss retention is good, and hot strength and elongation at break are superior to commonly be coated with
Material, can meet automobile collection box and the anticorrosion of casing application, weather-proof etc. is used requirement；Present invention achieves filling of resource and the energy
Dividing and utilize, production process is environment friendly and pollution-free, and its preparation method is simple, and cost is relatively low, with short production cycle, has convenient transportation, easily
In storage, the feature such as easy to use, be suitable to industrialized mass production.
Finally it should be noted that above example only in order to illustrative not limiting technical scheme, although reference
The present invention has been described in detail by above-described embodiment, it will be appreciated by those skilled in the art that and still can carry out the present invention
Amendment or equivalent, any modification or partial replacement without departing from the spirit and scope of the present invention, it all should be contained
In scope of the presently claimed invention.
Claims (4)
1. the air purifying coating for automobile collection box, it is characterised in that be prepared by the raw materials in: hydroxyl
Acrylic resin 15～35 parts, pure-acrylic emulsion 5～20 parts, celluosic resin 5～20 parts, lignocellulose 2～10 parts, nano oxygen
Change zinc 1～5 parts, wetting agent 0.2～1 part, catalyst 1～5 parts, thickening agent 0.2～1.5 parts, Pulvis Talci 1～5 parts, kieselguhr 1
～5 parts, hexone 0.2～1 part, propylene glycol monomethyl ether 0.3～2 parts, deionized water 20～50 parts, tetramethylolmethane 2～
10 parts；
Its preparation method in turn includes the following steps:
(1) Hydroxylated acrylic resin, pure-acrylic emulsion, celluosic resin, lignocellulose, nano zine oxide and deionized water are put
Entering in reaction vessel, controlling temperature is 50～60 DEG C, stirs and makes mixture dispersed in 15～30 minutes；
(2) again Pulvis Talci, kieselguhr, hexone and propylene glycol monomethyl ether are joined in reaction vessel, be stirred continuously
Until mix homogeneously, temperature is risen to 70～75 DEG C and carries out being heated at reflux 1～1.5 hour, be finally slowly added to tetramethylolmethane, and
Stirring and dissolving 0.5～1 hour, obtain mixed solution；
(3) mixed solution that step (2) prepares is cooled to 20～30 DEG C, then is separately added into wetting agent, catalyst and thickening agent,
It is kept stirring for 20～50 minutes, obtains coating mixed liquor；
(4) the coating mixed liquor that step (3) prepares is entered sand mill to grind 4～6 times, filter to obtain finished product.
Air purifying coating for automobile collection box the most according to claim 1, it is characterised in that described wetting agent is
Polyether modified siloxane.
Air purifying coating for automobile collection box the most according to claim 1, it is characterised in that described catalyst is
Sodium sulfonate.
Air purifying coating for automobile collection box the most according to claim 1, it is characterised in that described thickening agent is
Carboxymethyl cellulose.