CN106010052A - Heat-insulation paint used for automobile containing box and preparation method thereof - Google Patents
Heat-insulation paint used for automobile containing box and preparation method thereof Download PDFInfo
- Publication number
- CN106010052A CN106010052A CN201610665282.6A CN201610665282A CN106010052A CN 106010052 A CN106010052 A CN 106010052A CN 201610665282 A CN201610665282 A CN 201610665282A CN 106010052 A CN106010052 A CN 106010052A
- Authority
- CN
- China
- Prior art keywords
- parts
- automobile
- mixed liquor
- preparation
- collection box
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a heat-insulation paint used for an automobile containing box. The heat-insulation paint comprises the following raw materials: hydroxy acrylic resin, a pure acrylic emulsion, cellulose resin, ethene resin, alumina, a leveling agent, a catalyst, a thickening agent, powdered steatile, silica, methyl isobutyl ketone, dimethyl carbonate, deionized water and pentaerythritol. The preparation method comprises the following steps: 1) uniformly stirring the corresponding raw materials; 2) preparing a mixing solution; 3) preparing paint mixed liquor; and 4) grinding the paint mixed liquor, filtering the paint mixed liquor to obtain the finished product. The product has excellent performance, and has advantages of good high temperature resistance, flat and fine coating surface, and good light retention, tensile strength and breaking elongation are better than that of the common paint, the usage requirements of anticorrosion and weatherability of the automobile containing box on coating can be satisfied; and the preparation method has the advantages of simple process and low cost, and is adapted to industrial batch production.
Description
Technical field
The present invention relates to coating industry field, particularly relate to a kind of heat insulating coatings for automobile collection box and preparation method thereof.
Background technology
Along with the development of social life level, nowadays increasing people have the private car of oneself, and Automobile Products are in other words
Motor Maintenance articles for use have the most just become the essential part of vehicle maintenance, as one of three macroplates in market, vapour after automobile
Automobile-used product market is also one of industry the most with fastest developing speed, that prospect is best.Along with the eruptive growth of Domestic Automotive Industry,
Automobile Products industry development speed is at a tremendous pace, and according to statistics, 2011, China's Automobile Products series products gross output value reached 4300 the most
Hundred million yuans, family more than ten thousand more than more than 10 of Automobile Products industry distributing business of current China.Automobile is gradually paid attention to along with Chinese Government
Articles for use industry, actively pushes forward the industrialization of Automobile Products, encourages the technological innovation of Automobile Products industry, and government is also at gradual perfection
The relevant laws and regulations of Automobile Products industry and standard, for the competitive environment that the development offer of Automobile Products enterprise is orderly.Automobile is used simultaneously
Product enterprise also should constantly autonomous innovation, introduce and cultivate professional, catching the good opportunity to develop of Automobile Products industry.
Containing box in Automobile Products is mainly placed in automobile trunk, is used for depositing article.At present, people are for automobile
Article in interior material and automobile are increasingly paid attention to, and the requirement to aspects such as the coating property of Automobile Products, environmental protection is more and more higher,
But can't be met, in the face of the huge market demand and the ever-increasing application prospect of Automobile Products coating, need
Develop technically, on cost, more show the coating of powerful competitive advantage in performance so that it is Automobile Products are had very
Good protection and decoration.
Summary of the invention
The invention aims to overcome the deficiencies in the prior art, it is provided that a kind of heat-insulation and heat-preservation for automobile collection box
Coating and preparation method thereof, this coating products excellent performance, there is good heat preservation and insulation, and meet environmental requirement.
For solve above-mentioned technical problem, the present invention by the following technical solutions:
A kind of heat insulating coatings for automobile collection box, it is characterised in that be prepared by the raw materials in: hydroxyl third
Olefin(e) acid resin 15～35 parts, pure-acrylic emulsion 5～20 parts, celluosic resin 5～20 parts, vinyl 2～10 parts, aluminium oxide
1～5 part, levelling agent 0.2～1 part, catalyst 1～5 parts, thickening agent 0.2～1.5 parts, Pulvis Talci 1～5 parts, silicon dioxide
1～5 part, hexone 0.2～1 part, dimethyl carbonate 0.3～2 parts, deionized water 20～50 parts, tetramethylolmethane
2～10 parts；
Its preparation method in turn includes the following steps:
(1) Hydroxylated acrylic resin, pure-acrylic emulsion, celluosic resin, vinyl, aluminium oxide and deionized water are put into instead
Answering in container, controlling temperature is 50～60 DEG C, stirs and makes mixture dispersed in 15～30 minutes；
(2) again Pulvis Talci, silicon dioxide, hexone and dimethyl carbonate are joined in reaction vessel, constantly stir
Mix until mix homogeneously, temperature risen to 70～75 DEG C and carries out being heated at reflux 1～1.5 hour, be finally slowly added to tetramethylolmethane,
And stirring and dissolving 0.5～1 hour, obtain mixed solution；
(3) mixed solution that step (2) prepares is cooled to 20～30 DEG C, then is separately added into levelling agent, catalyst and thickening
Agent, is kept stirring for 20～50 minutes, obtains coating mixed liquor；
(4) the coating mixed liquor that step (3) prepares is entered sand mill to grind 4～6 times, filter to obtain finished product.
Preferably, described levelling agent is polyester modification siloxanes.
Preferably, described catalyst is sodium sulfonate.
Preferably, described thickening agent is carboxymethyl cellulose.
The present invention is had advantageous effect in that compared with prior art:
The present invention mostly is plastic material in view of automobile collection box, its lower hardness, the feature of surface not scratch resistance, combines by using
Close performance preferably high-molecular organic material and carry out optimum organization, improve the heat preservation and insulation of compositions, using the present invention
The coating surface obtained is smooth, fine and smooth, smooth, and gloss retention is good, and hot strength and elongation at break are superior to common coating, energy
Meet automobile collection box and the anticorrosion of casing application, weather-proof etc. is used requirement；Present invention achieves making full use of of resource and the energy,
Production process is environment friendly and pollution-free, and its preparation method is simple, and cost is relatively low, with short production cycle, has convenient transportation, it is easy to store,
The feature such as easy to use, is suitable to industrialized mass production.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1:
A kind of heat insulating coatings for automobile collection box, it is characterised in that be prepared by the raw materials in: hydroxyl third
Olefin(e) acid resin 15 parts, pure-acrylic emulsion 5 parts, celluosic resin 5 parts, vinyl 2 parts, aluminium oxide 1 part, levelling agent 0.2
Part, catalyst 1 part, thickening agent 0.2 part, Pulvis Talci 1 part, silica 1 part, hexone 0.2 part, carbonic acid
Dimethyl ester 0.3 part, deionized water 20 parts, tetramethylolmethane 2 parts；
Its preparation method in turn includes the following steps:
(1) Hydroxylated acrylic resin, pure-acrylic emulsion, celluosic resin, vinyl, aluminium oxide and deionized water are put into instead
Answering in container, controlling temperature is 50～60 DEG C, stirs and makes mixture dispersed in 15 minutes；
(2) again Pulvis Talci, silicon dioxide, hexone and dimethyl carbonate are joined in reaction vessel, constantly stir
Mix until mix homogeneously, temperature is risen to 70～75 DEG C and carries out being heated at reflux 1 hour, be finally slowly added to tetramethylolmethane, and stir
Mix dissolving 0.5 hour, obtain mixed solution；
(3) mixed solution that step (2) prepares is cooled to 20～30 DEG C, then is separately added into levelling agent, catalyst and thickening
Agent, is kept stirring for 20 minutes, obtains coating mixed liquor；
(4) the coating mixed liquor that step (3) prepares is entered sand mill to grind 4 times, filter to obtain finished product.
Preferably, described levelling agent is polyester modification siloxanes.
Preferably, described catalyst is sodium sulfonate.
Preferably, described thickening agent is carboxymethyl cellulose.
Embodiment 2:
A kind of heat insulating coatings for automobile collection box, it is characterised in that be prepared by the raw materials in: hydroxyl third
Olefin(e) acid resin 35 parts, pure-acrylic emulsion 20 parts, celluosic resin 20 parts, vinyl 10 parts, aluminium oxide 5 parts, levelling agent
1 part, catalyst 5 parts, thickening agent 1.5 parts, Pulvis Talci 5 parts, silicon dioxide 5 parts, hexone 1 part, carbonic acid
Dimethyl ester 2 parts, deionized water 50 parts, tetramethylolmethane 10 parts；
Its preparation method in turn includes the following steps:
(1) Hydroxylated acrylic resin, pure-acrylic emulsion, celluosic resin, vinyl, aluminium oxide and deionized water are put into instead
Answering in container, controlling temperature is 50～60 DEG C, stirs and makes mixture dispersed in 30 minutes；
(2) again Pulvis Talci, silicon dioxide, hexone and dimethyl carbonate are joined in reaction vessel, constantly stir
Mix until mix homogeneously, temperature is risen to 70～75 DEG C and carries out being heated at reflux 1.5 hours, be finally slowly added to tetramethylolmethane, and
Stirring and dissolving 1 hour, obtains mixed solution；
(3) mixed solution that step (2) prepares is cooled to 20～30 DEG C, then is separately added into levelling agent, catalyst and thickening
Agent, is kept stirring for 50 minutes, obtains coating mixed liquor；
(4) the coating mixed liquor that step (3) prepares is entered sand mill to grind 6 times, filter to obtain finished product.
In the above embodiment of the present invention:
Described levelling agent is polyester modification siloxanes；
Described catalyst is sodium sulfonate；
Described thickening agent is carboxymethyl cellulose.
The present invention mostly is plastic material in view of automobile collection box, its lower hardness, the feature of surface not scratch resistance, combines by using
Close performance preferably high-molecular organic material and carry out optimum organization, improve the heat preservation and insulation of compositions, using the present invention
The coating surface obtained is smooth, fine and smooth, smooth, and gloss retention is good, and hot strength and elongation at break are superior to common coating, energy
Meet automobile collection box and the anticorrosion of casing application, weather-proof etc. is used requirement；Present invention achieves making full use of of resource and the energy,
Production process is environment friendly and pollution-free, and its preparation method is simple, and cost is relatively low, with short production cycle, has convenient transportation, it is easy to store,
The feature such as easy to use, is suitable to industrialized mass production.
Finally it should be noted that above example only in order to illustrative not limiting technical scheme, although with reference to above-mentioned reality
Execute example the present invention has been described in detail, it will be appreciated by those skilled in the art that still the present invention can be modified or
Equivalent, any modification or partial replacement without departing from the spirit and scope of the present invention, it all should contain the power in the present invention
In profit claimed range.
Claims (4)
1. the heat insulating coatings for automobile collection box, it is characterised in that be prepared by the raw materials in: hydroxyl
Acrylic resin 15～35 parts, pure-acrylic emulsion 5～20 parts, celluosic resin 5～20 parts, vinyl 2～10 parts, oxidation
Aluminum 1～5 parts, levelling agent 0.2～1 part, catalyst 1～5 parts, thickening agent 0.2～1.5 parts, Pulvis Talci 1～5 parts, dioxy
SiClx 1～5 parts, hexone 0.2～1 part, dimethyl carbonate 0.3～2 parts, deionized water 20～50 parts, season penta
Tetrol 2～10 parts；
Its preparation method in turn includes the following steps:
(1) Hydroxylated acrylic resin, pure-acrylic emulsion, celluosic resin, vinyl, aluminium oxide and deionized water are put into instead
Answering in container, controlling temperature is 50～60 DEG C, stirs and makes mixture dispersed in 15～30 minutes；
(2) again Pulvis Talci, silicon dioxide, hexone and dimethyl carbonate are joined in reaction vessel, constantly stir
Mix until mix homogeneously, temperature risen to 70～75 DEG C and carries out being heated at reflux 1～1.5 hour, be finally slowly added to tetramethylolmethane,
And stirring and dissolving 0.5～1 hour, obtain mixed solution；
(3) mixed solution that step (2) prepares is cooled to 20～30 DEG C, then is separately added into levelling agent, catalyst and thickening
Agent, is kept stirring for 20～50 minutes, obtains coating mixed liquor；
(4) the coating mixed liquor that step (3) prepares is entered sand mill to grind 4～6 times, filter to obtain finished product.
Heat insulating coatings for automobile collection box the most according to claim 1, it is characterised in that described levelling agent is
Polyester modification siloxanes.
Heat insulating coatings for automobile collection box the most according to claim 1, it is characterised in that described catalyst is
Sodium sulfonate.
Heat insulating coatings for automobile collection box the most according to claim 1, it is characterised in that described thickening agent is
Carboxymethyl cellulose.