CN106269959A - 一种殷钢带坯的生产方法 - Google Patents

一种殷钢带坯的生产方法 Download PDF

Info

Publication number
CN106269959A
CN106269959A CN201510307928.9A CN201510307928A CN106269959A CN 106269959 A CN106269959 A CN 106269959A CN 201510307928 A CN201510307928 A CN 201510307928A CN 106269959 A CN106269959 A CN 106269959A
Authority
CN
China
Prior art keywords
slab
invar
hot
belt
rolling
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510307928.9A
Other languages
English (en)
Inventor
荆正伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Danyang Kaixin Alloy Material Co Ltd
Original Assignee
Danyang Kaixin Alloy Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Danyang Kaixin Alloy Material Co Ltd filed Critical Danyang Kaixin Alloy Material Co Ltd
Priority to CN201510307928.9A priority Critical patent/CN106269959A/zh
Publication of CN106269959A publication Critical patent/CN106269959A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种制作殷钢冷轧带坯的方法,其包括如下步骤:(1)采用纯镍板、纯铁作为原料,经真空中频感应炉熔炼;(2)然后采用真空下浇注扁锭工艺,得到扁锭;(3)将下注的扁钢锭直接热轧开坯,直接热轧冷轧带坯;其中,将下浇注出来的扁钢锭用砂轮机将钢锭的麻点,翘皮修磨后,加热到1050-1100℃,保温0.5-1.0小时,即可进行热轧;所述纯镍板、纯铁的质量比为0.45:1至0.60:1,本发明由于没有经过热锻,所以不需要担心热轧前方坯的表面问题,不需要热轧带坯前对轧钢的扁状方坯进行一系列加工处理,例如刨铣扁坯,修磨扁坯,故而本发明的工艺较简单、成本较低且生产效率较高。

Description

一种殷钢带坯的生产方法
技术领域
本发明涉及制作殷钢扁锭直接热轧带坯方法,尤其是真空下浇注1支扁锭直接热轧殷钢带坯的新工艺。
背景技术
殷钢属于铁基高镍合金,通常含有32-36wt%的Ni,还含有少量的S、P、C等元素,其余为60wt%左右的Fe,由于镍为扩大奥氏体元素,故高镍使奥氏体转为马氏体的相变降至室温以下,-100℃~-120℃,因而经退火后,殷钢在室温及室温以下一定温度范围内,均具有面心晶格结构的奥氏体组织,也是镍溶于γ-Fe中形成的固溶体,因而殷钢具有膨胀系数小,强度、硬度不高,导热系数低,塑性、韧性高等优良的性能。
殷钢的用途:由于殷钢具有膨胀系数小,强度、硬度不高,导热系数低,塑性、韧性高等优良的性能,所以殷钢适合用于制作对温度变形有严格要求的精密零件膜式框架、荫罩、航空工业的CRP部件回火模具,低于-200℃的人造卫星和导弹电子控制单元框架,激光控制装置电磁镜头中的辅助电子管。液化气的生产、贮存和运输;工作温度低于+200℃以下的测量和控制仪器,如温度调节装置.金属和其他材料间的螺旋连接器衬套、双金属和温控双金属。目前4G网络的迅速发展,殷钢在4G网络上也得到了广泛的应用比如滤波器,谐振杆,波导管等都需要用到殷钢的材料。殷钢在各领域的广泛应用导致殷钢的需求量日益增大,出现这种情况需要进行量产。
传统殷钢冷轧带坯的生产工艺:目前国内对于殷钢冷轧带坯的生产采用的是中频炉熔炼,电渣重熔,这样就会导致气体杂质含量高,熔炼之后进行热锻,修磨方坯,刨铣方坯,然后进行热轧带坯,这样热锻后的方坯材料非常容易出现裂纹,氧化皮、麻点、毛刺,起皮等缺陷,为了消除这些热锻带来的缺陷,需要花大力气对方坯进行一系列的铣刨磨的工序,以便消除缺陷,但这样做的同时,也增加了殷钢带坯的生产成本和无形损耗,导致产品的生产成本的上涨,降低产品的市场竞争力,同时由于工序繁多,影响产量和生产周期,导致旺季殷钢带坯市场供应短缺。
发明内容
本发明所要解决的技术问题是提供一种工艺较简单、成本较低且效率较高的殷钢带坯的生产方法。
为了解决上述问题,本发明提供了一种殷钢带坯的生产方法:滚锻热轧工艺:殷钢下注扁锭直接开坯,直接热轧殷钢带坯。
具体的殷钢带坯的生产方法,包括如下步骤:
(1)采用纯镍板、纯铁作为原料,经真空中频感应炉熔炼;
(2)然后采用真空下浇注扁锭工艺,得到殷钢扁状钢锭;
(3)将殷钢扁状钢锭热轧开坯,直接热轧殷钢冷轧带坯。
其中,将下浇注出来的钢锭用砂轮机将钢锭的麻点,翘皮修磨后,加热到1050-1100℃,保温0.5-1.1小时,即可进行开坯热轧。
进一步,所述纯镍板、纯铁的质量比为0.45:1至0.6:1。
本发明的技术效果:
1)本发明由于没有经过热锻(即相对于现有技术,省略电渣锻造的步骤),所以不需要担心热轧前方坯的表面问题,不需要热轧殷钢带坯前对轧钢的扁坯进行一系列加工处理,例如刨铣扁坯,修磨扁坯,这样可以大大节约殷钢的制造和加工的成本,每公斤大约可以节约成本8-10元;
2)本发明由于省去了热锻和铣床加工的中间环节,反而增加了产品的10%-15%的成材率,减少了3-4%的无形损耗;
3)本发明由于没有热锻,修磨,铣刨扁坯的的生产环节,生产周期大大缩减,生产效率大大提高,并且能满足了殷钢后续大批量量产的需求;现有技术中,采用的是中频炉熔炼,电渣重熔,(注:电渣的加工价格5元/Kg)这样就会导致气体含量比真空冶炼要高,熔炼电渣之后进行热锻热锻(注:热锻的加工价格5元/Kg),修磨方坯,刨铣方坯(注:方坯铣刨的加工费3-4元/kg),然后进行热轧盘圆,这样热锻后的方坯材料非常容易出现裂纹,氧化皮、麻点、毛刺,起皮等缺陷,为了消除这些热锻带来的缺陷,需要花大力气对方坯进行一系列的铣刨磨的工序,以便消除缺陷,但这样做的同时,也增加了殷钢的生产成本和无形损耗,导致产品的生产成本的上涨,一般锻造后刨铣方坯的成材率是85-90%,无形损耗是3-4%,生产加工费是3-4元/公斤,另外还需要浸酸检查,由锻造产生的裂纹,氧化皮、麻点、毛刺,起皮等缺陷,是否已经清除干净,费工费钱。
具体实施方式
实施例1
本实施例的殷钢带坯的生产方法,包括如下步骤:
1)真空中频感应炉熔炼:选择金川牌纯镍板,太原钢厂低碳、低硫磷的纯铁作为原料进行殷钢的熔炼,这样气体杂质等方面大大减少并且增加了殷钢的塑性,韧性,延长了殷钢的使用寿命。所述纯镍板、纯铁的质量比为0.5:1。
2)采用真空下浇注扁锭工艺,使得到的扁状殷钢扁锭表面质量大大提高。
3)将殷钢扁钢锭进行热轧开坯、热轧殷钢冷轧带坯。
其中,根据热轧加工的孔型设计钢锭的尺寸为大头200x110mm,小头190x100mm,长度在1200mm左右的大小头扁锭,下浇注出来的扁钢锭只需用砂轮机将扁钢锭的表面麻点,翘皮简单修磨一下,然后经煤气发生炉或者天然气炉加热到1100℃,保温1小时,即可热轧到所需要殷钢冷轧带坯的尺寸,然后酸洗抛光到所需坯料的尺寸,这样省去了电渣和热锻这两个成本非常高的环节和避免了热锻后方坯表面出现裂纹,氧化皮、麻点、毛刺,起皮等缺陷,从而省却了一系列高成本、高难度的后续对扁坯铣、刨、磨的处理。
实施例2
在实施例1的基础上,本实施例的殷钢带坯的生产方法,存在如下变型:所述纯镍板、纯铁的质量比为0.59:1。对下浇注出来的钢锭加热到1110℃,保温1.1小时。
实施例3
在实施例1的基础上,本实施例的殷钢带坯的生产方法,存在如下变型:所述纯镍板、纯铁的质量比为0.45:1,对下浇注出来的钢锭加热到1150℃,保温0.9小时。
以上所述,仅是本发明的较佳实施例而已,并非是对本发明作其它形式的限制,任何熟悉本专业的技术人员可能利用上述揭示的技术内容加以变更或改型为等同变化的等效实施例。但是凡是未脱离本发明技术方案内容,依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与改型,仍属于本发明技术方案的保护范围。

Claims (4)

1.一种殷钢带坯的生产方法,其特征在于包括,滚轧工艺:殷钢扁锭直接开坯热轧带坯。
2.一种殷钢带坯的生产方法,其特征在于包括,
采用纯镍板、纯铁作为原料,经真空中频感应炉熔炼;
然后采用真空下浇注扁锭工艺,得到下注的扁钢锭;
将扁钢锭热轧开坯,直接热轧带坯。
3.根据权利要求2所述的方法,其特征在于,将下浇注出来的扁钢锭用砂轮机将钢锭的麻点,翘皮修磨后,加热到1050-1100℃,保温0.50-1.1小时,即可进行热轧带坯。
4.根据权利要求2所述的方法,其特征在于,所述纯镍板、纯铁的质量比为0.45:1至0.6:1。
CN201510307928.9A 2015-06-08 2015-06-08 一种殷钢带坯的生产方法 Pending CN106269959A (zh)