CN106243845A - A kind of transparent rapid hardening environment-friendly type building water-repellent paint - Google Patents
A kind of transparent rapid hardening environment-friendly type building water-repellent paint Download PDFInfo
- Publication number
- CN106243845A CN106243845A CN201610620214.8A CN201610620214A CN106243845A CN 106243845 A CN106243845 A CN 106243845A CN 201610620214 A CN201610620214 A CN 201610620214A CN 106243845 A CN106243845 A CN 106243845A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- water
- accelerator
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of transparent rapid hardening environment-friendly type building water-repellent paint, including component A and B component, described component A is prepared from by the raw material of following parts by weight: EVA emulsion 85～96 parts, transparency silica glass powder 12～18 parts, Lauryl Alcohol ester 0.24～0.6 part, stabilizer 0.6～1.2 parts, dispersant 0.24～0.36 part, defoamer 0.24～0.36 part, antibacterial 0.18～0.3 part, water 6～18 parts, described B component is prepared from by the raw material of following parts by weight: accelerator 18～30 parts, accelerator 3～9.6 parts, water 5～15 parts.The present invention use transparent EVA emulsion be main film forming matter be component A, with alkali-free liquid setting accelerator, nanometer film forming accelerating for firming agent B component, component A contacts with B component after reacting, rapid condensation generates the waterproof layer of layer of transparent, environmental protection, and the healthy injury to workmen is little, there are higher hot strength and elongation percentage, spraying application can be used, improve efficiency of construction, and film forming thickness is more uniform.
Description
[technical field]
The present invention relates to the technical field of building water-proof paint, particularly to a kind of transparent waterproof painting of rapid hardening environment-friendly type building
Material.
[background technology]
Building water-proof paint is a kind of important construction material, is called for short water-repellent paint, is amorphous materials (shape aqueous, thick
Thing, powder add water job mix, liquid and powder job mix), brush by scene, scrape, smear, spray etc. is constructed, can be on works surface
It solidify to form the film material with water-proof function.Water-repellent paint is mainly used in building, and some may be by the structure of water erosion
Position or structural elements, such as roofing, basement, toilet bath room, water tower, pond, water tank be isostructural waterproof, moistureproof and antiseepage
Deng.
Along with variation, the enhancing of people's aesthetic consciousness and the raising to architectural appearance pursuit of modern building design,
Existing conventional polyurethane water-proof paint, polymer cement waterproof paint etc. can not be expired owing to color is relatively deep or hides the reasons such as the end
Some particular/special requirements of foot people, and when the safe and environment-friendly human survival that becomes is with when developing primary need, and environment-friendly type building is waterproof
Coating is increasingly welcome by user, but current environment-friendly type building water-repellent paint in work progress still with blade coating, roller
The forms of construction work such as painting are main, waste time and energy, and also can cause the problem that coating thickness is uneven, and in order to solve the problems referred to above, having must
Propose a kind of transparent rapid hardening environment-friendly type building water-repellent paint, can construct in the way of using spraying, reduce work strong
Degree, improves efficiency of construction, improves the suitability of coating simultaneously, meet some particular/special requirements of people.
[summary of the invention]
It is an object of the invention to overcome above-mentioned the deficiencies in the prior art, it is provided that a kind of transparent rapid hardening environment-friendly type building is waterproof
Coating, it aims to solve the problem that technical problem of the prior art.
For achieving the above object, the present invention proposes a kind of transparent rapid hardening environment-friendly type building water-repellent paint, including component A and
B component, described component A is prepared from by the raw material of following parts by weight: EVA emulsion 85～96 parts, transparency silica glass powder
12～18 parts, Lauryl Alcohol ester 0.24～0.6 part, stabilizer 0.6～1.2 parts, dispersant 0.24～0.36 part, defoamer 0.24
～0.36 part, antibacterial 0.18～0.3 part, water 6～18 parts, described B component is prepared from by the raw material of following parts by weight:
Accelerator 18～30 parts, accelerator 3～9.6 parts, water 5～15 parts.
As preferably, described component A is prepared from by the raw material of following parts by weight: EVA emulsion 85 parts, suprasil
12 parts of glass dust, Lauryl Alcohol ester 0.24 part, stabilizer 0.6 part, dispersant 0.24 part, defoamer 0.24 part, antibacterial 0.18
Part, 6 parts of water, described B component is prepared from by the raw material of following parts by weight: accelerator 18.2 parts, accelerator 3 parts, water 5
Part.
As preferably, described component A is prepared from by the raw material of following parts by weight: EVA emulsion 90.5 parts, transparent stone
15 parts of English glass dust, Lauryl Alcohol ester 0.42 part, stabilizer 0.9 part, dispersant 0.3 part, defoamer 0.3 part, antibacterial 0.24
Part, 12 parts of water, described B component is prepared from by the raw material of following parts by weight: accelerator 22 parts, accelerator 4.8 parts, water 9
Part.
As preferably, described component A is prepared from by the raw material of following parts by weight: EVA emulsion 96 parts, suprasil
18 parts of glass dust, Lauryl Alcohol ester 0.6 part, stabilizer 1.2 parts, dispersant 0.36 part, defoamer 0.36 part, antibacterial 0.3 part,
18 parts of water, described B component is prepared from by the raw material of following parts by weight: accelerator 30 parts, accelerator 9 parts, 15 parts of water.
As preferably, described component A is 0.25～0.4 with the ratio of the parts by weight of B component.
As preferably, the described stabilizer in component A is lignocellulose stabilizer or lignocellulose and glass
The mixed stabilizer of fiber, dispersant is the mixture of stearmide and higher alcohol, and defoamer is silicone defoamer, sterilization
Agent is Kathon LX antibacterial, and water is deionized water.
As preferably, described and in B component accelerator is alkali-free liquid setting accelerator, and accelerator is that nanometer film forming promotes
Agent, water is deionized water.
As preferably, described component A also includes the Muscovitum powder of trace.
Beneficial effects of the present invention: compared with prior art, the one transparent rapid hardening environment-friendly type building that the present invention provides is prevented
Water paint, use transparent EVA emulsion be main film forming matter be component A, with alkali-free liquid setting accelerator, nanometer film forming promote
Agent is firming agent B component, and component A contacts with B component after reacting, and rapid condensation generates the waterproof layer of layer of transparent, green
Environmental protection, had both had higher hot strength and elongation percentage to the waterproof layer that the healthy injury of workmen is little and transparent, also
Original architectural appearance will not be covered, during construction application, use the mode of spraying to construct, improve water-repellent paint
Based on forms of construction work such as blade coating, roller coat in work progress, waste time and energy and easily cause the problem that coating thickness is uneven, fall
Low construction intensity, improves efficiency of construction, and film forming thickness is more uniform.
Inventive feature and advantage will be described in detail by embodiment.
[detailed description of the invention]
For making the object, technical solutions and advantages of the present invention of greater clarity, below by embodiment, the present invention is entered
Row further describes.However, it should be understood that specific embodiment described herein is only in order to explain the present invention, and need not
In limiting the scope of the present invention.Additionally, in the following description, eliminate the description to known features and technology, so that avoid need not
Idea of the invention is obscured in strategic point.
The embodiment of the present invention provides a kind of transparent rapid hardening environment-friendly type building water-repellent paint, including component A and B component, described
Component A be prepared from by the raw material of following parts by weight: EVA emulsion 85～96 parts, transparency silica glass powder 12～18 parts, ten
Two carbon alcohol esters 0.24～0.6 part, stabilizer 0.6～1.2 parts, dispersant 0.24～0.36 part, defoamer 0.24～0.36 part, kill
Microbial inoculum 0.18～0.3 part, water 6～18 parts, described B component is prepared from by the raw material of following parts by weight: accelerator 18～
30 parts, accelerator 3～9.6 parts, water 5～15 parts.
Wherein, described component A is 0.25～0.4 with the ratio of the parts by weight of B component, stablizing in described component A
Agent is the mixed stabilizer of lignocellulose stabilizer or lignocellulose and glass fibre, and dispersant is that stearmide is with high
The mixture of level alcohol, defoamer is silicone defoamer, and antibacterial is Kathon LX antibacterial, and water is deionized water, described
And B component in accelerator be alkali-free liquid setting accelerator, accelerator is nanometer film forming accelerating, and water is deionized water, described
Component A in also include the Muscovitum powder of trace.
Embodiment one,
Described component A is prepared from by the raw material of following parts by weight: EVA emulsion 85 parts, transparency silica glass powder 12
Part, Lauryl Alcohol ester 0.24 part, stabilizer 0.6 part, dispersant 0.24 part, defoamer 0.24 part, antibacterial 0.18 part, 6 parts of water,
Described B component is prepared from by the raw material of following parts by weight: accelerator 18.2 parts, accelerator 3 parts, 5 parts of water.
Embodiment two,
Described component A is prepared from by the raw material of following parts by weight: EVA emulsion 90.5 parts, transparency silica glass powder
15 parts, Lauryl Alcohol ester 0.42 part, stabilizer 0.9 part, dispersant 0.3 part, defoamer 0.3 part, antibacterial 0.24 part, water 12
Part, described B component is prepared from by the raw material of following parts by weight: accelerator 22 parts, accelerator 4.8 parts, 9 parts of water.
Embodiment three,
Described component A is prepared from by the raw material of following parts by weight: EVA emulsion 96 parts, transparency silica glass powder 18
Part, Lauryl Alcohol ester 0.6 part, stabilizer 1.2 parts, dispersant 0.36 part, defoamer 0.36 part, antibacterial 0.3 part, 18 parts of water,
Described B component is prepared from by the raw material of following parts by weight: accelerator 30 parts, accelerator 9 parts, 15 parts of water.
Test:
One transparent rapid hardening environment-friendly type building water-repellent paint to embodiment one to embodiment three respectively, uses double spray gun pair
Component A and B component in each embodiment carry out atomizing spraying simultaneously, then test setting time, to embodiment one to enforcement
The transparent watertight coating that a kind of transparent rapid hardening environment-friendly type building water-repellent paint of example three is obtained carries out performance test.
Result shows, the setting time in embodiment two is the shortest；The transparent watertight coating stretching that embodiment three is obtained is strong
Degree is relatively executed the transparent watertight of example one and embodiment two and is coated with floor height；The fracture elongation of the waterproof coating in embodiment one relatively embodiment
The transparent watertight of two and three is coated with floor height, the combination property of the transparent watertight coating that embodiment two is obtained relatively embodiment one and three
Good.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all essences in the present invention
Any amendment, equivalent or the improvement etc. made within god and principle, should be included within the scope of the present invention.
Claims (8)
1. a transparent rapid hardening environment-friendly type building water-repellent paint, it is characterised in that: include component A and B component, described component A
It is prepared from by the raw material of following parts by weight: EVA emulsion 85～96 parts, transparency silica glass powder 12～18 parts, Lauryl Alcohol
Ester 0.24～0.6 part, stabilizer 0.6～1.2 parts, dispersant 0.24～0.36 part, defoamer 0.24～0.36 part, antibacterial
0.18～0.3 part, water 6～18 parts, described B component is prepared from by the raw material of following parts by weight: accelerator 18～30 parts,
Accelerator 3～9.6 parts, water 5～15 parts.
A kind of transparent rapid hardening environment-friendly type building water-repellent paint the most as claimed in claim 1, it is characterised in that: described component A
It is prepared from by the raw material of following parts by weight: EVA emulsion 85 parts, 12 parts of transparency silica glass powder, Lauryl Alcohol ester 0.24 part,
Stabilizer 0.6 part, dispersant 0.24 part, defoamer 0.24 part, antibacterial 0.18 part, 6 parts of water, described B component is by following heavy
The raw material of amount number is prepared from: accelerator 18.2 parts, accelerator 3 parts, 5 parts of water.
A kind of transparent rapid hardening environment-friendly type building water-repellent paint the most as claimed in claim 1, it is characterised in that: described component A
It is prepared from by the raw material of following parts by weight: EVA emulsion 90.5 parts, 15 parts of transparency silica glass powder, Lauryl Alcohol ester 0.42
Part, stabilizer 0.9 part, dispersant 0.3 part, defoamer 0.3 part, antibacterial 0.24 part, 12 parts of water, described B component is by following
The raw material of parts by weight is prepared from: accelerator 22 parts, accelerator 4.8 parts, 9 parts of water.
A kind of transparent rapid hardening environment-friendly type building water-repellent paint the most as claimed in claim 1, it is characterised in that: described component A
It is prepared from by the raw material of following parts by weight: EVA emulsion 96 parts, 18 parts of transparency silica glass powder, Lauryl Alcohol ester 0.6 part,
Stabilizer 1.2 parts, dispersant 0.36 part, defoamer 0.36 part, antibacterial 0.3 part, 18 parts of water, described B component is by following heavy
The raw material of amount number is prepared from: accelerator 30 parts, accelerator 9 parts, 15 parts of water.
5. the one transparent rapid hardening environment-friendly type building water-repellent paint as described in any one in Claims 1-4, its feature exists
In: described component A is 0.25～0.4 with the ratio of the parts by weight of B component.
6. the one transparent rapid hardening environment-friendly type building water-repellent paint as described in any one in Claims 1-4, its feature exists
In the mixed stability that: the described stabilizer in component A is lignocellulose stabilizer or lignocellulose and glass fibre
Agent, dispersant is the mixture of stearmide and higher alcohol, and defoamer is silicone defoamer, and antibacterial is Kathon LX
Antibacterial, water is deionized water.
7. the one transparent rapid hardening environment-friendly type building water-repellent paint as described in any one in Claims 1-4, its feature exists
In: described and in B component accelerator is alkali-free liquid setting accelerator, and accelerator is nanometer film forming accelerating, and water is deionization
Water.
8. the one transparent rapid hardening environment-friendly type building water-repellent paint as described in any one in Claims 1-4, its feature exists
In: described component A also includes the Muscovitum powder of trace.