CN106243845B - A kind of transparent rapid hardening environment-friendly type building water-repellent paint - Google Patents
A kind of transparent rapid hardening environment-friendly type building water-repellent paint Download PDFInfo
- Publication number
- CN106243845B CN106243845B CN201610620214.8A CN201610620214A CN106243845B CN 106243845 B CN106243845 B CN 106243845B CN 201610620214 A CN201610620214 A CN 201610620214A CN 106243845 B CN106243845 B CN 106243845B
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- water
- raw material
- prepared
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of transparent rapid hardening environment-friendly type building water-repellent paints, including component A and B component, the component A to be prepared by following raw material in parts by weight：85~96 parts of EVA lotions, 12~18 parts of transparency silica glass powder, 0.24~0.6 part of Lauryl Alcohol ester, 0.6~1.2 part of stabilizer, 0.24~0.36 part of dispersant, 0.24~0.36 part of antifoaming agent, 0.18~0.3 part of fungicide, 6~18 parts of water, the B component is prepared by following raw material in parts by weight：18~30 parts of accelerator, 3~9.6 parts of accelerating agent, 5~15 parts of water.It for main film forming matter is component A that the present invention, which uses transparent EVA lotions, using alkali-free liquid setting accelerator, nanometer film forming accelerating as curing agent B component, component A is contacted with B component react after, rapid condensation generates the waterproof layer of layer of transparent, environmentally protective, small to the health injury of construction personnel, there are higher tensile strength and elongation percentage, spraying application can be used, improve construction efficiency, and film forming thickness is more uniform.
Description
【Technical field】
The present invention relates to the technical field of building water-proof paint, more particularly to a kind of transparent rapid hardening environment-friendly type building waterproof applies
Material.
【Background technology】
Building water-proof paint is a kind of important construction material, and abbreviation water-repellent paint is amorphous materials (liquid, thick shape
Object, pulvis add water job mix, liquid and powder job mix), the constructions such as brush, scrape, smear, spray by scene, it can be on works surface
It is formed by curing the film material with water-proof function.Water-repellent paint is mainly used for that building is certain may be by the structure of water erosion
Position or structural elements, such as roofing, basement, toilet bath room, water tower, pond, the isostructural waterproof of water tank, moisture-proof and antiseepage
Deng.
With the diversification of modern building design, the enhancing of people's aesthetic consciousness and to architectural appearance pursue raising,
Existing common polyurethane water-proof paint, polymer cement waterproof paint etc. cannot be expired due to color relatively depth or screening bottom etc.
Some particular/special requirements of sufficient people, and when it is safe and environment-friendly become human survival with development primary need when, environment-friendly type building waterproof
Coating is increasingly welcome by user, but current environment-friendly type building water-repellent paint is in the construction process still with blade coating, roller
It is time-consuming and laborious based on the forms of construction work such as painting, the non-uniform problem of coating thickness can be also caused, to solve the above-mentioned problems, having must
It is proposed a kind of transparent rapid hardening environment-friendly type building water-repellent paint, the mode that spraying may be used is constructed, strong to reduce work
Degree improves construction efficiency, while improving the applicability of coating, meets some particular/special requirements of people.
【Invention content】
It is an object of the invention to overcome above-mentioned the deficiencies in the prior art, a kind of transparent rapid hardening environment-friendly type building waterproof is provided
Coating, the technical issues of aiming to solve the problem that in the prior art.
To achieve the above object, the present invention proposes a kind of transparent rapid hardening environment-friendly type building water-repellent paint, including component A and
B component, the component A are prepared by following raw material in parts by weight：85~96 parts of EVA lotions, transparency silica glass powder
12~18 parts, 0.24~0.6 part of Lauryl Alcohol ester, 0.6~1.2 part of stabilizer, 0.24~0.36 part of dispersant, antifoaming agent 0.24
~0.36 part, 0.18~0.3 part of fungicide, 6~18 parts of water, the B component is prepared by following raw material in parts by weight：
18~30 parts of accelerator, 3~9.6 parts of accelerating agent, 5~15 parts of water.
Preferably, the component A is prepared by following raw material in parts by weight：85 parts of EVA lotions, suprasil
12 parts of glass powder, 0.24 part of Lauryl Alcohol ester, 0.6 part of stabilizer, 0.24 part of dispersant, 0.24 part of antifoaming agent, fungicide 0.18
Part, 6 parts of water, the B component is prepared by following raw material in parts by weight：18.2 parts of accelerator, 3 parts of accelerating agent, water 5
Part.
Preferably, the component A is prepared by following raw material in parts by weight：90.5 parts of EVA lotions, transparent stone
15 parts of English glass powder, 0.42 part of Lauryl Alcohol ester, 0.9 part of stabilizer, 0.3 part of dispersant, 0.3 part of antifoaming agent, fungicide 0.24
Part, 12 parts of water, the B component is prepared by following raw material in parts by weight：22 parts of accelerator, 4.8 parts of accelerating agent, water 9
Part.
Preferably, the component A is prepared by following raw material in parts by weight：96 parts of EVA lotions, suprasil
18 parts of glass powder, 0.6 part of Lauryl Alcohol ester, 1.2 parts of stabilizer, 0.36 part of dispersant, 0.36 part of antifoaming agent, 0.3 part of fungicide,
18 parts of water, the B component is prepared by following raw material in parts by weight：30 parts of accelerator, 9 parts of accelerating agent, 15 parts of water.
Preferably, the ratio between described parts by weight of component A and B component are 0.25~0.4.
Preferably, the stabilizer in the component A is lignocellulosic stabilizer or lignocellulosic and glass
The mixed stabilizer of fiber, dispersant are the mixture of stearmide and higher alcohol, and antifoaming agent is organic silicon antifoaming agent, sterilization
Agent is Kathon LX fungicide, and water is deionized water.
Preferably, the accelerator in described and B component is alkali-free liquid setting accelerator, accelerating agent is that nanometer film forming promotes
Agent, water are deionized water.
Preferably, further including micro mica powder in the component A.
Beneficial effects of the present invention：Compared with prior art, a kind of transparent rapid hardening environment-friendly type building provided by the invention is anti-
Water paint, it for main film forming matter is component A to use transparent EVA lotions, is promoted with alkali-free liquid setting accelerator, nanometer film forming
Agent is curing agent B component, component A contact with B component react after, the waterproof layer of rapid condensation generation layer of transparent is green
Environmental protection, injuring small and transparent waterproof layer to the health of construction personnel both has higher tensile strength and elongation percentage, also
Original architectural appearance will not be covered, during construction application, is constructed by the way of spraying, improves water-repellent paint
It is time-consuming and laborious and easily cause the non-uniform problem of coating thickness in the construction process based on the forms of construction work such as blade coating, roller coating, it drops
Low construction intensity, improves construction efficiency, and film forming thickness is more uniform.
The feature and advantage of the present invention will be described in detail by embodiment.
【Specific implementation mode】
In order to make the objectives, technical solutions and advantages of the present invention clearer, below by embodiment, to the present invention into
Row is further described.However, it should be understood that the specific embodiments described herein are merely illustrative of the present invention, and do not have to
In limiting the scope of the invention.In addition, in the following description, descriptions of well-known structures and technologies are omitted, to avoid need not
Obscure idea of the invention in strategic point.
The embodiment of the present invention provides a kind of transparent rapid hardening environment-friendly type building water-repellent paint, including component A and B component, described
Component A be prepared by following raw material in parts by weight：85~96 parts of EVA lotions, 12~18 parts of transparency silica glass powder, ten
Two 0.24~0.6 part of carbon alcohol esters, 0.6~1.2 part of stabilizer, 0.24~0.36 part of dispersant, 0.24~0.36 part of antifoaming agent kill
0.18~0.3 part of microbial inoculum, 6~18 parts of water, the B component is prepared by following raw material in parts by weight：Accelerator 18~
30 parts, 3~9.6 parts of accelerating agent, 5~15 parts of water.
Wherein, the ratio between parts by weight of the component A and B component are 0.25~0.4, the stabilization in the component A
Agent is the mixed stabilizer of lignocellulosic stabilizer or lignocellulosic and glass fibre, and dispersant is stearmide and height
The mixture of grade alcohol, antifoaming agent are organic silicon antifoaming agent, and fungicide is Kathon LX fungicide, and water is deionized water, described
And B component in accelerator be alkali-free liquid setting accelerator, accelerating agent be nanometer film forming accelerating, water is deionized water, described
Component A in further include micro mica powder.
Embodiment one,
The component A is prepared by following raw material in parts by weight：85 parts of EVA lotions, transparency silica glass powder 12
Part, 0.24 part of Lauryl Alcohol ester, 0.6 part of stabilizer, 0.24 part of dispersant, 0.24 part of antifoaming agent, 0.18 part of fungicide, 6 parts of water,
The B component is prepared by following raw material in parts by weight：18.2 parts of accelerator, 3 parts of accelerating agent, 5 parts of water.
Embodiment two,
The component A is prepared by following raw material in parts by weight：90.5 parts of EVA lotions, transparency silica glass powder
15 parts, 0.42 part of Lauryl Alcohol ester, 0.9 part of stabilizer, 0.3 part of dispersant, 0.3 part of antifoaming agent, 0.24 part of fungicide, water 12
Part, the B component is prepared by following raw material in parts by weight：22 parts of accelerator, 4.8 parts of accelerating agent, 9 parts of water.
Embodiment three,
The component A is prepared by following raw material in parts by weight：96 parts of EVA lotions, transparency silica glass powder 18
Part, 0.6 part of Lauryl Alcohol ester, 1.2 parts of stabilizer, 0.36 part of dispersant, 0.36 part of antifoaming agent, 0.3 part of fungicide, 18 parts of water,
The B component is prepared by following raw material in parts by weight：30 parts of accelerator, 9 parts of accelerating agent, 15 parts of water.
Test：
Respectively to a kind of transparent rapid hardening environment-friendly type building water-repellent paint of embodiment one to embodiment three, using double spray guns pair
Component A and B component in each embodiment are carried out at the same time atomizing spraying, setting time are then tested, to embodiment one to implementation
The transparent watertight coating that a kind of transparent rapid hardening environment-friendly type building water-repellent paint of example three is obtained is tested for the property.
The result shows that the setting time in embodiment two is most short；The transparent watertight coating that embodiment three is obtained stretches strong
Degree relatively applies example one and the transparent watertight of embodiment two applies floor height；The fracture elongation of waterproof coating in embodiment one is compared with embodiment
Two and three transparent watertight applies floor height, and the comprehensive performance for the transparent watertight coating that embodiment two is obtained is compared with embodiment one and three
It is good.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
Any modification, equivalent replacement or improvement etc., should all be included in the protection scope of the present invention made by within refreshing and principle.
Claims (4)
1. a kind of transparent rapid hardening environment-friendly type building water-repellent paint, it is characterised in that：Including component A and B component, the component A
It is prepared by following raw material in parts by weight：85~96 parts of EVA lotions, 12~18 parts of transparency silica glass powder, Lauryl Alcohol
0.24~0.6 part of ester, 0.6~1.2 part of stabilizer, 0.24~0.36 part of dispersant, 0.24~0.36 part of antifoaming agent, fungicide
0.18~0.3 part, 6~18 parts of water, the B component is prepared by following raw material in parts by weight：18~30 parts of accelerator,
3~9.6 parts of accelerating agent, 5~15 parts of water；The ratio between described parts by weight of component A and B component are 0.25~0.4, the A
Stabilizer in component is the mixed stabilizer of lignocellulosic stabilizer or lignocellulosic and glass fibre, and dispersant is
The mixture of stearmide and higher alcohol, antifoaming agent are organic silicon antifoaming agent, and fungicide is Kathon LX fungicide, and water is
Deionized water；Accelerator in the B component is alkali-free liquid setting accelerator, and accelerating agent is nanometer film forming accelerating, and water is to go
Ionized water further includes micro mica powder in the component A.
2. a kind of transparent rapid hardening environment-friendly type building water-repellent paint as described in claim 1, it is characterised in that：The component A
It is prepared by following raw material in parts by weight：85 parts of EVA lotions, 12 parts of transparency silica glass powder, 0.24 part of Lauryl Alcohol ester,
0.6 part of stabilizer, 0.24 part of dispersant, 0.24 part of antifoaming agent, 0.18 part of fungicide, 6 parts of water, the B component is by following heavy
The raw material of amount number is prepared：18.2 parts of accelerator, 3 parts of accelerating agent, 5 parts of water.
3. a kind of transparent rapid hardening environment-friendly type building water-repellent paint as described in claim 1, it is characterised in that：The component A
It is prepared by following raw material in parts by weight：90.5 parts of EVA lotions, 15 parts of transparency silica glass powder, Lauryl Alcohol ester 0.42
Part, 0.9 part of stabilizer, 0.3 part of dispersant, 0.3 part of antifoaming agent, 0.24 part of fungicide, 12 parts of water, the B component is by following
The raw material of parts by weight is prepared：22 parts of accelerator, 4.8 parts of accelerating agent, 9 parts of water.
4. a kind of transparent rapid hardening environment-friendly type building water-repellent paint as described in claim 1, it is characterised in that：The component A
It is prepared by following raw material in parts by weight：96 parts of EVA lotions, 18 parts of transparency silica glass powder, 0.6 part of Lauryl Alcohol ester,
1.2 parts of stabilizer, 0.36 part of dispersant, 0.36 part of antifoaming agent, 0.3 part of fungicide, 18 parts of water, the B component is by following heavy
The raw material of amount number is prepared：30 parts of accelerator, 9 parts of accelerating agent, 15 parts of water.