CN106243816A - A kind of multifunctional putty cream for simulated tile coating and preparation method thereof - Google Patents
A kind of multifunctional putty cream for simulated tile coating and preparation method thereof Download PDFInfo
- Publication number
- CN106243816A CN106243816A CN201610848204.XA CN201610848204A CN106243816A CN 106243816 A CN106243816 A CN 106243816A CN 201610848204 A CN201610848204 A CN 201610848204A CN 106243816 A CN106243816 A CN 106243816A
- Authority
- CN
- China
- Prior art keywords
- tile coating
- simulated tile
- putty cream
- multifunctional putty
- putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of multifunctional putty cream for simulated tile coating disclosed by the invention, is prepared from by water, antibacterial, dispersant, defoamer, coalescents, hydroxypropyl methyl cellulose, acrylic emulsion, titanium dioxide, ground calcium carbonate, quartz sand, polypropene staple, aqueous color paste.The invention also discloses this preparation method for the multifunctional putty cream of simulated tile coating.The present invention has the Comprehensive Characteristics of putty, priming paint and intermediate layer paint, original three process is condensed into one procedure, and is an effective cracking resistance material.It is applicable to the matching operation of simulated tile coating technique, color-adjustable, the putty priming paint in alternative original system and imitative brick lines paint.Pliability is good, can effectively shield the blind crack of basic unit, saves man-hour cost-effective.
Description
Technical field
The present invention relates to a kind of multifunctional putty cream, for imitating the supplementary material of brick effect coating, belong to construction material neck
Territory, particularly to a kind of multifunctional putty cream for simulated tile coating and preparation method thereof
Background technology
The coating of imitative brick effect is a kind of trailing common on current metope, conventional construction technique be leveling putty,
Alkali-resistant primer, roller coating lines color intermediate layer paint, imitative brick texture coating.Putty be mainly composed of inorganic gel materials-cement, inorganic
After Binder Materials meets water, hydration reaction starts, and aqua calcis reaches saturated and separates out crystal, causes basic unit's table after construction
Face shows high alkalinity (pH value ＞ 12), and the excessive mill base easily causing surface layer emulsion paint of alkalescence decomposes, and causes irregular colour, because of
This, need brushing alkali-resistant primer after putty construction and maintenance, after priming paint construction and maintenance, according to lines color brushing middle level needed for imitative brick effect
Paint, simulated tile coating of finally constructing.
From above traditional construction technique it can be seen that needed construct putty, priming paint, intermediate layer paint three before construction simulated tile coating
Planting material, time-consuming feed consumption consumption is artificial.And the putty rigidity of inorganic coagulation material is strong, easy to crack.
Summary of the invention
An object of the present invention is to provide a kind of multifunctional putty cream for simulated tile coating, have putty, priming paint and
The Comprehensive Characteristics of intermediate layer paint, is condensed into one procedure original three process, and is an effective cracking resistance material.It is suitable for
In the matching operation of simulated tile coating technique, color-adjustable, the putty priming paint in alternative original system and imitative brick lines paint.Pliability
Good, can effectively shield the blind crack of basic unit, save man-hour cost-effective.
The two of the purpose of the present invention are to provide the preparation method of the above-mentioned multifunctional putty cream for simulated tile coating.
The present invention is to be realized by following technical scheme:
A kind of multifunctional putty cream for simulated tile coating, is prepared from by the raw material of above percentage by weight:
Described antibacterial is preferably isothiazolinone biocide agent.
Described dispersant is equal polycarboxylate salt dispersant.
Described defoamer is preferably mineral oil type antifoaming agent.
Described coalescents is preferably alcohol ester 12.
Described hydroxypropyl methyl cellulose preferably viscosity is 5～100,000.
Described acrylic emulsion, as film forming matter, parcel filler and mill base, realizes intensity and the pH of putty layer after film forming
Neutral feature.Described acrylic emulsion is preferably elastomeric propylene yogurt liquid, and vitrification point is less than 5 DEG C.
Described titanium dioxide is Rutile type titanium dioxide.
Described ground calcium carbonate fineness is at 200-800 mesh.
Described quartz sand fineness is at 50-180 mesh
Described polypropene staple fibre length is 1.0～3.0mm
Described aqueous color paste is the mill bases such as carbon black, iron oxide yellow, iron oxide red according to color demand.
The preparation method of the above-mentioned multifunctional putty cream for simulated tile coating, be in water add antibacterial, dispersant, disappear
After infusion, coalescents, add hydroxypropyl methyl cellulose, titanium dioxide and ground calcium carbonate, high-speed stirred under agitation
15 minutes, it is subsequently adding acrylic emulsion, quartz sand and polypropene staple, stirs 5-10 minute, be eventually adding aqueous color paste,
Discharging is got final product after mix homogeneously.
The present invention compared with prior art has the advantage that
(1) due to do not use inorganic coagulation material to realize resistance to water, thus construction after putty layer show as neutrality,
Occur without tradition putty accumulation of salt in the surface soil problem, can be in order to avoid using alkali-resistant primer when therefore using this product.
(2) relative to tradition putty simply white or Lycoperdon polymorphum Vitt, the present invention can directly arbitrarily need with aqueous color paste furnishing
The color wanted, can be in order to avoid using intermediate layer paint when therefore using this product.
(3) elastic emulsion wraps up quartz sand and the powder of thickness collocation so that the present invention can criticize to scrape and reach certain thickness
And intensity, playing the levelling effect of basic unit, adhesion strength also can meet industry standard " JGT157-2009 putty for exterior use " and refer to
Mark.
(4) owing to using elastic emulsion and polypropene staple, the putty paste of the present invention has certain pliability and resists thin
Gap.
(5) easy construction, paste putty can directly be criticized and scrape, without adding water compared with tradition putty.
Comprehensive above feature, the product of the present invention can substitute for the leveling putty in building coating system, alkali-resistant primer and
Intermediate layer paint, reduces operation during construction, cost-effective.Properties of product meet industry relevant criterion requirement simultaneously.
Detailed description of the invention:
Embodiment 1
The multifunctional putty cream for simulated tile coating of this embodiment is a black putty paste, and filler each component particle diameter is big
Little answering rationally, easily batch scrape and levelling basic unit, color is black, can use in black line simulated tile coating system.Construction work
Skill is kept to 2 roads from 4 original roads.
Preparation method:
After adding antibacterial, dispersant, defoamer, alcohol ester 12 in water, add hydroxypropyl methyl under agitation
Cellulose, titanium dioxide and 300 mesh ground calcium carbonate, high-speed stirred 15 minutes, it is subsequently adding elastomeric propylene yogurt liquid, 80-120 mesh
Quartz sand and 2mm polypropene staple, stir 5-10 minute, be eventually adding carbon black color slurry, get final product discharging after mix homogeneously.
Construction method for simulated tile coating:
Directly criticize at metope and scrape construction, can construct together or two roads, make degree of plainness for wall surface reach necessary requirement.Then line is pasted
U.S. stricture of vagina paper, finally construction texture simulated tile coating needed for bar, take U.S. stricture of vagina paper off and can form imitative brick effect coating decoration.
Embodiment 2
The multifunctional putty cream for simulated tile coating of this embodiment is a yellow putty paste, and filler each component particle diameter is relatively
Greatly, easily batch scrape and for the poor basic unit of flatness, color is yellow, can use in yellow line bar simulated tile coating system.
Preparation method:
After adding antibacterial, dispersant, defoamer, alcohol ester 12 in water, add hydroxypropyl methyl under agitation
Cellulose, titanium dioxide and 200 mesh ground calcium carbonate, high-speed stirred 15 minutes, it is subsequently adding elastomeric propylene yogurt liquid, 50-80 mesh
Quartz sand and 3mm polypropene staple, stir 5-10 minute, be eventually adding iron oxide yellow mill base, get final product discharging after mix homogeneously.
Construction method for simulated tile coating:
Directly criticize at metope and scrape construction, can construct together or two roads, make degree of plainness for wall surface reach necessary requirement.Then line is pasted
U.S. stricture of vagina paper, finally construction texture simulated tile coating needed for bar, take U.S. stricture of vagina paper off and can form imitative brick effect coating decoration.
Embodiment 3
The multifunctional putty cream for simulated tile coating of this embodiment is a coffee-like putty paste, filler each component particle diameter
Less, pliability is good, easily criticizes and scrapes and for the preferable basic unit of flatness, and color is coffee-like, can imitate brick at coffee-like lines
Coating system uses.
Preparation method:
After adding antibacterial, dispersant, defoamer, alcohol ester 12 in water, add hydroxypropyl methyl under agitation
Cellulose, titanium dioxide and 800 mesh ground calcium carbonate, high-speed stirred 15 minutes, it is subsequently adding elastomeric propylene yogurt liquid, 120-180
Mesh quartz sand and 1mm polypropene staple, stir 5-10 minute, be eventually adding iron oxide yellow, iron oxide red, carbon black color slurry, after mix homogeneously
Get final product discharging.
Construction method for simulated tile coating:
Directly criticize at metope and scrape construction, can construct together or two roads, make degree of plainness for wall surface reach necessary requirement.Then line is pasted
U.S. stricture of vagina paper, finally construction texture simulated tile coating needed for bar, take U.S. stricture of vagina paper off and can form imitative brick effect coating decoration.
Comparative example:
Common exterior wall putty and construction method
Common exterior wall putty is mixed by weight percentage by following components:
Construction method for simulated tile coating:
The 30-40% that adds water in comparative example, batch scrapes metope together or two roads, makes degree of plainness for wall surface reach institute after stirring
Needs are asked.Then brushing alkali resistant wash coats, brushing lines color intermediate layer paint, U.S. stricture of vagina paper needed for pasting lines, finally construction texture is imitated
Brick coating, takes U.S. stricture of vagina paper off and forms imitative brick effect coating decoration.
Detection performance parameter:
Sum up: the product of embodiment 1,2,3, in neutral or alkalescence, can make directly as lines color after levelling basic unit
With, performance data meets JG/T 157-2009 " putty for exterior use standard ", and pliability meets flexible index.Comparative example
Product alkalescence is high, needs brushing alkali resistant wash coats, and can not mix colours after construction, still needs to brush middle level when simulated tile coating system
Paint.Therefore the product of embodiment can reduce technique, and cost-effective, performance meets industry standard.
Claims (9)
1. the multifunctional putty cream for simulated tile coating, it is characterised in that by the raw material preparation of above percentage by weight
Become:
A kind of multifunctional putty cream for simulated tile coating, it is characterised in that described antibacterial
It is preferably isothiazolinone biocide agent；Described dispersant is equal polycarboxylate salt dispersant；Described defoamer is preferably mineral
Oil type defoamer；Described coalescents is preferably alcohol ester 12.
A kind of multifunctional putty cream for simulated tile coating, it is characterised in that described hydroxypropyl
Methylcellulose be viscosity be 5～100,000.
A kind of multifunctional putty cream for simulated tile coating, it is characterised in that described propylene yogurt
Liquid is preferably elastic emulsion, and vitrification point is less than 5 DEG C.
A kind of multifunctional putty cream for simulated tile coating, it is characterised in that described titanium dioxide is
Rutile type titanium dioxide.
A kind of multifunctional putty cream for simulated tile coating, it is characterised in that described heavy carbon
Acid calcium fineness is at 200-800 mesh.
A kind of multifunctional putty cream for simulated tile coating, it is characterised in that described quartz sand
Fineness is at 50-180 mesh
A kind of multifunctional putty cream for simulated tile coating, it is characterised in that described polypropylene
Chopped fiber fibre length is 1.0～3.0mm
9. the preparation method of the multifunctional putty cream for simulated tile coating described in claim 1 to 8, is characterized in that adding in water
After entering antibacterial, dispersant, defoamer, coalescents, add hydroxypropyl methyl cellulose, titanium dioxide and weight under agitation
Matter calcium carbonate, high-speed stirred 15 minutes, it is subsequently adding acrylic emulsion, quartz sand and polypropene staple, stirs 5-10 minute,
It is eventually adding aqueous color paste, after mix homogeneously, gets final product discharging.