CN106221383A - A kind of fastening iron hoop - Google Patents
A kind of fastening iron hoop Download PDFInfo
- Publication number
- CN106221383A CN106221383A CN201610782964.5A CN201610782964A CN106221383A CN 106221383 A CN106221383 A CN 106221383A CN 201610782964 A CN201610782964 A CN 201610782964A CN 106221383 A CN106221383 A CN 106221383A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- iron hoop
- protective paint
- weight
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fastening iron hoop, its iron hoop body surfaces is covered with protective paint, protective paint is made by the steps: 1) 1～2 weight portion iron oxide reds, 0.5 weight portion kieselguhr, 0.7 weight portion dodecyl sodium sulfate, 2.3 weight portion sodium silicate, 9 weight portion amino resins is put into successively in 22 parts by weight of deionized water, stirs；2) 14 parts of EVA emulsions, 2.9 weight portion butadiene-styrene latexes, 1.8 weight portion ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 0.8 weight portion tetrasodium ethylenediamine tetraacetate, 1.3 weight portion amine molybdates are put into the most successively, continue stirring, to being sufficiently mixed uniformly, prepare protective paint.The present invention fastens and uses iron hoop, and its iron hoop body surfaces is coated with protective paint, can ensure fastening iron hoop life-time service.
Description
Technical field
The present invention relates to a kind of fastening iron hoop.
Background technology
Existing fastening iron hoop, the antioxidation of its iron hoop main body, antirust, decay resistance have much room for improvement, and impact fastening is used
The life-time service of iron hoop.
Summary of the invention
It is an object of the invention to provide a kind of fastening iron hoop, its iron hoop body surfaces is coated with protective paint, makes iron hoop
Main body has the antioxidation of excellence, antirust, decay resistance, thus ensures fastening iron hoop energy life-time service.
For achieving the above object, the technical scheme is that a kind of fastening iron hoop of design, including iron hoop main body, this ferrum
Hoop body surfaces is covered with protective paint, and described protective paint is made by the steps:
1) by 1～2 weight portion iron oxide reds, 0.5 weight portion kieselguhr, 0.7 weight portion dodecyl sodium sulfate, 2.3 weights
Amount part sodium silicate, 9 weight portion amino resins put in 22 parts by weight of deionized water successively, stir；
2) 14 parts of EVA emulsions, 2.9 weight portion butadiene-styrene latexes, 1.8 weight portion ethylenediamine polyoxyethylene are put into the most successively
Oxypropylene block formula polyethers, 0.8 weight portion tetrasodium ethylenediamine tetraacetate, 1.3 weight portion amine molybdates, continue stirring, to fully
Mix homogeneously, prepares protective paint.
Preferably, fastening iron hoop, including iron hoop main body, this iron hoop body surfaces is covered with protective paint, described protective paint
It is made by the steps:
1) by 1 weight portion iron oxide red, 0.5 weight portion kieselguhr, 0.7 weight portion dodecyl sodium sulfate, 2.3 weight portions
Sodium silicate, 9 weight portion amino resins put in 22 parts by weight of deionized water successively, stir；
2) 14 parts of EVA emulsions, 2.9 weight portion butadiene-styrene latexes, 1.8 weight portion ethylenediamine polyoxyethylene are put into the most successively
Oxypropylene block formula polyethers, 0.8 weight portion tetrasodium ethylenediamine tetraacetate, 1.3 weight portion amine molybdates, continue stirring, to fully
Mix homogeneously, prepares protective paint.
Preferably, fastening iron hoop, including iron hoop main body, this iron hoop body surfaces is covered with protective paint, described protective paint
It is made by the steps:
1) by 2 weight portion iron oxide reds, 0.5 weight portion kieselguhr, 0.7 weight portion dodecyl sodium sulfate, 2.3 weight portions
Sodium silicate, 9 weight portion amino resins put in 22 parts by weight of deionized water successively, stir；
2) 14 parts of EVA emulsions, 2.9 weight portion butadiene-styrene latexes, 1.8 weight portion ethylenediamine polyoxyethylene are put into the most successively
Oxypropylene block formula polyethers, 0.8 weight portion tetrasodium ethylenediamine tetraacetate, 1.3 weight portion amine molybdates, continue stirring, to fully
Mix homogeneously, prepares protective paint.
Preferably, fastening iron hoop, including iron hoop main body, this iron hoop body surfaces is covered with protective paint, described protective paint
It is made by the steps:
1) by 1.2 weight portion iron oxide reds, 0.5 weight portion kieselguhr, 0.7 weight portion dodecyl sodium sulfate, 2.3 weight
Part sodium silicate, 9 weight portion amino resins put in 22 parts by weight of deionized water successively, stir；
2) 14 parts of EVA emulsions, 2.9 weight portion butadiene-styrene latexes, 1.8 weight portion ethylenediamine polyoxyethylene are put into the most successively
Oxypropylene block formula polyethers, 0.8 weight portion tetrasodium ethylenediamine tetraacetate, 1.3 weight portion amine molybdates, continue stirring, to fully
Mix homogeneously, prepares protective paint.
Advantages of the present invention and having the beneficial effects that: providing a kind of fastening iron hoop, its iron hoop body surfaces is coated with anti-
Vernix, makes iron hoop main body have the antioxidation of excellence, antirust, decay resistance, thus ensures fastening iron hoop energy life-time service.
Performance and the purposes of " protective paint " are determined by its component and proportioning, and the different component meeting in " protective paint "
Influencing each other, component and proportioning thereof can determine the final performance of " protective paint ", as the most mutually coordinated in fruit component and proportioning thereof, single
The beneficial effect that component is brought, even can be eliminated by other components abatement, and the when of serious, different component is mutually conflicted, and rises
Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " protection
Paint " optimal component and proportioning so that multiple components combine, mutually coordinated and produce forward comprehensive effect.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.Following example are only used for more
Add and clearly demonstrate technical scheme, and can not limit the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Fastening iron hoop, including iron hoop main body, this iron hoop body surfaces is covered with protective paint, and described protective paint is by as follows
Prepared by step:
1) by 1～2 weight portion iron oxide reds, 0.5 weight portion kieselguhr, 0.7 weight portion dodecyl sodium sulfate, 2.3 weights
Amount part sodium silicate, 9 weight portion amino resins put in 22 parts by weight of deionized water successively, stir；
2) 14 parts of EVA emulsions, 2.9 weight portion butadiene-styrene latexes, 1.8 weight portion ethylenediamine polyoxyethylene are put into the most successively
Oxypropylene block formula polyethers, 0.8 weight portion tetrasodium ethylenediamine tetraacetate, 1.3 weight portion amine molybdates, continue stirring, to fully
Mix homogeneously, prepares protective paint.
Embodiment 2
Fastening iron hoop, including iron hoop main body, this iron hoop body surfaces is covered with protective paint, and described protective paint is by as follows
Prepared by step:
1) by 1 weight portion iron oxide red, 0.5 weight portion kieselguhr, 0.7 weight portion dodecyl sodium sulfate, 2.3 weight portions
Sodium silicate, 9 weight portion amino resins put in 22 parts by weight of deionized water successively, stir；
2) 14 parts of EVA emulsions, 2.9 weight portion butadiene-styrene latexes, 1.8 weight portion ethylenediamine polyoxyethylene are put into the most successively
Oxypropylene block formula polyethers, 0.8 weight portion tetrasodium ethylenediamine tetraacetate, 1.3 weight portion amine molybdates, continue stirring, to fully
Mix homogeneously, prepares protective paint.
Embodiment 3
Fastening iron hoop, including iron hoop main body, this iron hoop body surfaces is covered with protective paint, and described protective paint is by as follows
Prepared by step:
1) by 2 weight portion iron oxide reds, 0.5 weight portion kieselguhr, 0.7 weight portion dodecyl sodium sulfate, 2.3 weight portions
Sodium silicate, 9 weight portion amino resins put in 22 parts by weight of deionized water successively, stir；
2) 14 parts of EVA emulsions, 2.9 weight portion butadiene-styrene latexes, 1.8 weight portion ethylenediamine polyoxyethylene are put into the most successively
Oxypropylene block formula polyethers, 0.8 weight portion tetrasodium ethylenediamine tetraacetate, 1.3 weight portion amine molybdates, continue stirring, to fully
Mix homogeneously, prepares protective paint.
Embodiment 4
Fastening iron hoop, including iron hoop main body, this iron hoop body surfaces is covered with protective paint, and described protective paint is by as follows
Prepared by step:
1) by 1.2 weight portion iron oxide reds, 0.5 weight portion kieselguhr, 0.7 weight portion dodecyl sodium sulfate, 2.3 weight
Part sodium silicate, 9 weight portion amino resins put in 22 parts by weight of deionized water successively, stir；
2) 14 parts of EVA emulsions, 2.9 weight portion butadiene-styrene latexes, 1.8 weight portion ethylenediamine polyoxyethylene are put into the most successively
Oxypropylene block formula polyethers, 0.8 weight portion tetrasodium ethylenediamine tetraacetate, 1.3 weight portion amine molybdates, continue stirring, to fully
Mix homogeneously, prepares protective paint.
The fastening iron hoop of the various embodiments described above, its iron hoop body surfaces is coated with protective paint, makes iron hoop main body have excellent
Different antioxidation, antirust, decay resistance, thus ensure fastening iron hoop energy life-time service.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvements and modifications, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. a fastening iron hoop, it is characterised in that include iron hoop main body, this iron hoop body surfaces is covered with protective paint, described
Protective paint is made by the steps:
1) by 1～2 weight portion iron oxide reds, 0.5 weight portion kieselguhr, 0.7 weight portion dodecyl sodium sulfate, 2.3 weight portions
Sodium silicate, 9 weight portion amino resins put in 22 parts by weight of deionized water successively, stir；
2) 14 parts of EVA emulsions, 2.9 weight portion butadiene-styrene latexes, 1.8 weight portion ethylenediamine polyoxyethylene polyoxies are put into the most successively
Polypropylene block formula polyethers, 0.8 weight portion tetrasodium ethylenediamine tetraacetate, 1.3 weight portion amine molybdates, continue stirring, to being sufficiently mixed
Uniformly, protective paint is prepared.
Fastening iron hoop the most according to claim 1, it is characterised in that include iron hoop main body, this iron hoop body surfaces
Being covered with protective paint, described protective paint is made by the steps:
1) by 1 weight portion iron oxide red, 0.5 weight portion kieselguhr, 0.7 weight portion dodecyl sodium sulfate, 2.3 weight portion flower bulbs
Alkali, 9 weight portion amino resins put in 22 parts by weight of deionized water successively, stir；
2) 14 parts of EVA emulsions, 2.9 weight portion butadiene-styrene latexes, 1.8 weight portion ethylenediamine polyoxyethylene polyoxies are put into the most successively
Polypropylene block formula polyethers, 0.8 weight portion tetrasodium ethylenediamine tetraacetate, 1.3 weight portion amine molybdates, continue stirring, to being sufficiently mixed
Uniformly, protective paint is prepared.
Fastening iron hoop the most according to claim 1, it is characterised in that include iron hoop main body, this iron hoop body surfaces
Being covered with protective paint, described protective paint is made by the steps:
1) by 2 weight portion iron oxide reds, 0.5 weight portion kieselguhr, 0.7 weight portion dodecyl sodium sulfate, 2.3 weight portion flower bulbs
Alkali, 9 weight portion amino resins put in 22 parts by weight of deionized water successively, stir；
2) 14 parts of EVA emulsions, 2.9 weight portion butadiene-styrene latexes, 1.8 weight portion ethylenediamine polyoxyethylene polyoxies are put into the most successively
Polypropylene block formula polyethers, 0.8 weight portion tetrasodium ethylenediamine tetraacetate, 1.3 weight portion amine molybdates, continue stirring, to being sufficiently mixed
Uniformly, protective paint is prepared.
Fastening iron hoop the most according to claim 1, it is characterised in that include iron hoop main body, this iron hoop body surfaces
Being covered with protective paint, described protective paint is made by the steps:
1) by 1.2 weight portion iron oxide reds, 0.5 weight portion kieselguhr, 0.7 weight portion dodecyl sodium sulfate, 2.3 weight portion bubbles
Flower alkali, 9 weight portion amino resins put in 22 parts by weight of deionized water successively, stir；
2) 14 parts of EVA emulsions, 2.9 weight portion butadiene-styrene latexes, 1.8 weight portion ethylenediamine polyoxyethylene polyoxies are put into the most successively
Polypropylene block formula polyethers, 0.8 weight portion tetrasodium ethylenediamine tetraacetate, 1.3 weight portion amine molybdates, continue stirring, to being sufficiently mixed
Uniformly, protective paint is prepared.