CN108997804A - A kind of anti-static and anti-corrosive paint - Google Patents
A kind of anti-static and anti-corrosive paint Download PDFInfo
- Publication number
- CN108997804A CN108997804A CN201810977178.XA CN201810977178A CN108997804A CN 108997804 A CN108997804 A CN 108997804A CN 201810977178 A CN201810977178 A CN 201810977178A CN 108997804 A CN108997804 A CN 108997804A
- Authority
- CN
- China
- Prior art keywords
- parts
- static
- corrosive paint
- methyltriethoxysilane
- styrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to anti-static and anti-corrosive paints, the anti-static and anti-corrosive paint is by following mass fraction at being grouped as: 57-67 parts of polyethyleneglycol diglycidylether, 3-7 parts of defoaming agent, 10-16 parts of titanium dioxide, 3-8 parts of methyl methacrylate, 10-16 parts of styrene, 22-28 parts of precipitated calcium carbonate, 33-39 parts of ethyl orthosilicate, 3.3-5 parts of methyltriethoxysilane.The method in constituent by selecting the conductive auxiliary agents of a variety of interior cations, realize the low solvation of coating, coating surface is formed by by the way that static conductive auxiliary agent is connected to anticorrosive paint simultaneously, to make the static conductive component of coating not to be lost with dampening or the discharge of organic solvent, long-acting antistatic, etch-proof effect are reached.
Description
Technical field
The present invention relates to chemical products production field, specifically a kind of anti-static and anti-corrosive paint.
Background technique
Anticorrosive paint has become the important fresh combatants of paint field, and anticorrosive paint plays increasing effect, hair
Exhibition prospect is considerable.But traditional product gradually improves perfect, new product and constantly researches and develops appearance, to adapt to anticorrosion market and environmental law
New standard and requirement in rule development, it is still necessary to proactive, Continuous Innovation.Existing anti-corrosion material cannot it is effective it is antistatic,
Anti- spontaneous combustion, especially for the antistatic anti-corrosion of metallic oil tank inner wall, there are no better solutions, therefore give the life of people
It generates work and brings many inconvenience, therefore be badly in need of the new coating of one kind and emerge to fill a hole in the market, meet needed for people's production.
Summary of the invention
The present invention exactly for the technical problems in the prior art, provides a kind of anti-static and anti-corrosive paint.The method is logical
The conductive auxiliary agent for selecting a variety of interior cations in constituent is crossed, realizes the low solvation of coating, while quiet by that will lead
Electric auxiliary agent is connected to anticorrosive paint and is formed by coating surface, to make the static conductive component of coating will not be with dampening or organic molten
The discharge of agent and be lost, reach long-acting antistatic, etch-proof effect.
To achieve the goals above, technical scheme is as follows, a kind of anti-static and anti-corrosive paint, described antistatic anti-
Rotten coating is by following mass fraction at being grouped as: 57-67 parts of polyethyleneglycol diglycidylether, 3-7 parts of defoaming agent, and titanium white
10-16 parts of powder, 3-8 parts of methyl methacrylate, 10-16 parts of styrene, 22-28 parts of precipitated calcium carbonate, ethyl orthosilicate
33-39 parts, 3.3-5 parts of methyltriethoxysilane.
As an improvement of the present invention, the anti-static and anti-corrosive paint is by following mass fraction at being grouped as: poly- second
58-67 parts of Hexanediol diglycidyl ether, 4-7 parts of defoaming agent, 10-15 parts of titanium dioxide, 4-8 parts of methyl methacrylate, benzene
11-16 parts of ethylene, 23-28 parts of precipitated calcium carbonate, 34-39 parts of ethyl orthosilicate, methyltriethoxysilane 3.3-4.9
Part.
As an improvement of the present invention, the anti-static and anti-corrosive paint is by following mass fraction at being grouped as: poly- second
58 parts of Hexanediol diglycidyl ether, 4 parts of defoaming agent, 13 parts of titanium dioxide, 7 parts of methyl methacrylate, 14 parts of styrene, lightweight carbon
25 parts of sour calcium, 37 parts of ethyl orthosilicate, 3.5 parts of methyltriethoxysilane.
As an improvement of the present invention, the anti-static and anti-corrosive paint is by following mass fraction at being grouped as: poly- second
60 parts of Hexanediol diglycidyl ether, 5 parts of defoaming agent, 11 parts of titanium dioxide, 6 parts of methyl methacrylate, 13 parts of styrene, lightweight carbon
24 parts of sour calcium, 36 parts of ethyl orthosilicate, 4.2 parts of methyltriethoxysilane.
As an improvement of the present invention, the anti-static and anti-corrosive paint is by following mass fraction at being grouped as: poly- second
67 parts of Hexanediol diglycidyl ether, 7 parts of defoaming agent, 14 parts of titanium dioxide, 5 parts of methyl methacrylate, 12 parts of styrene, lightweight carbon
27 parts of sour calcium, 37 parts of ethyl orthosilicate, 3.8 parts of methyltriethoxysilane.
As an improvement of the present invention, the anti-static and anti-corrosive paint is by following mass fraction at being grouped as: poly- second
63 parts of Hexanediol diglycidyl ether, 6 parts of defoaming agent, 10 parts of titanium dioxide, 4 parts of methyl methacrylate, 16 parts of styrene, lightweight carbon
28 parts of sour calcium, 38 parts of ethyl orthosilicate, 4.1 parts of methyltriethoxysilane.
As an improvement of the present invention, the method comprises the following steps: 1) first by polyethyleneglycol diglycidylether, disappear
Infusion and titanium dioxide stir 22-30min, it is to be mixed uniformly after, base-material is made.Then by methyl methacrylate, styrene,
Precipitated calcium carbonate, ethyl orthosilicate and methyltriethoxysilane are put into pulverizer and are crushed, and smashed mixture is put into
Continue 77-89min of stirring in base-material, is thoroughly mixed to ingredient and obtains finished product.
The opposite and prior art, the invention has the advantages that, 1) operation is simple and reliable for entire technical solution, cost compared with
Low, being conducive to enterprise reduces production cost;2) method is real by selecting the conductive auxiliary agents of a variety of interior cations in constituent
The low solvation of coating is showed, while being formed by coating surface by the way that static conductive auxiliary agent is connected to anticorrosive paint, to make
The static conductive component of coating will not be lost with dampening or the discharge of organic solvent, reach long-acting antistatic, etch-proof effect.
Specific embodiment:
Embodiment 1: a kind of anti-static and anti-corrosive paint is by following mass fraction at being grouped as: polyethyleneglycol diglycidylether 58
Part, 4 parts of defoaming agent, 13 parts of titanium dioxide, 7 parts of methyl methacrylate, 14 parts of styrene, 25 parts of precipitated calcium carbonate, positive silicic acid second
37 parts of ester, 3.5 parts of methyltriethoxysilane.
Embodiment 2: a kind of anti-static and anti-corrosive paint, the anti-static and anti-corrosive paint is by following mass fraction at grouping
At: 60 parts of polyethyleneglycol diglycidylether, 5 parts of defoaming agent, 11 parts of titanium dioxide, 6 parts of methyl methacrylate, styrene 13
Part, 24 parts of precipitated calcium carbonate, 36 parts of ethyl orthosilicate, 4.2 parts of methyltriethoxysilane.
Embodiment 3: a kind of anti-static and anti-corrosive paint, the anti-static and anti-corrosive paint is by following mass fraction at grouping
At: 67 parts of polyethyleneglycol diglycidylether, 7 parts of defoaming agent, 14 parts of titanium dioxide, 5 parts of methyl methacrylate, styrene 12
Part, 27 parts of precipitated calcium carbonate, 37 parts of ethyl orthosilicate, 3.8 parts of methyltriethoxysilane.
Embodiment 4: a kind of anti-static and anti-corrosive paint, the anti-static and anti-corrosive paint is by following mass fraction at grouping
At: 63 parts of polyethyleneglycol diglycidylether, 6 parts of defoaming agent, 10 parts of titanium dioxide, 4 parts of methyl methacrylate, styrene 16
Part, 28 parts of precipitated calcium carbonate, 38 parts of ethyl orthosilicate, 4.1 parts of methyltriethoxysilane.
Embodiment 5: a kind of preparation method of anti-static and anti-corrosive paint, the method comprises the following steps: 1) first by poly- second two
Alcohol diglycidyl ether, defoaming agent and titanium dioxide stir 22-30min, it is to be mixed uniformly after, base-material is made.Then by methyl-prop
E pioic acid methyl ester, styrene, precipitated calcium carbonate, ethyl orthosilicate and methyltriethoxysilane are put into pulverizer and are crushed, powder
Mixture after broken, which is put into, continues 77-89min of stirring in base-material, be thoroughly mixed to ingredient and obtain finished product.
It should be noted that above-described embodiment, is not intended to limit the scope of protection of the present invention, in above-mentioned technical proposal
On the basis of made equivalents or substitution each fall within the range that the claims in the present invention are protected.
Claims (7)
1. a kind of anti-static and anti-corrosive paint, which is characterized in that the anti-static and anti-corrosive paint is by following mass fraction at grouping
At: 57-67 parts of polyethyleneglycol diglycidylether, 3-7 parts of defoaming agent, 10-16 parts of titanium dioxide, methyl methacrylate 3-
8 parts, 10-16 parts of styrene, 22-28 parts of precipitated calcium carbonate, 33-39 parts of ethyl orthosilicate, methyltriethoxysilane
3.3-5 parts.
2. a kind of anti-static and anti-corrosive paint according to claim 1, which is characterized in that the anti-static and anti-corrosive paint by with
Lower mass fraction at being grouped as: 58-67 parts of polyethyleneglycol diglycidylether, 4-7 parts of defoaming agent, titanium dioxide 10-15
Part, 4-8 parts of methyl methacrylate, 11-16 parts of styrene, 23-28 parts of precipitated calcium carbonate, 34-39 parts of ethyl orthosilicate,
3.3-4.9 parts of methyltriethoxysilane.
3. a kind of anti-static and anti-corrosive paint according to claim 1 or 2, which is characterized in that the anti-static and anti-corrosive paint
By following mass fraction at being grouped as: 58 parts of polyethyleneglycol diglycidylether, 4 parts of defoaming agent, 13 parts of titanium dioxide, methyl-prop
7 parts of e pioic acid methyl ester, 14 parts of styrene, 25 parts of precipitated calcium carbonate, 37 parts of ethyl orthosilicate, 3.5 parts of methyltriethoxysilane.
4. a kind of anti-static and anti-corrosive paint according to claim 1, which is characterized in that the anti-static and anti-corrosive paint by with
Lower mass fraction at being grouped as: 60 parts of polyethyleneglycol diglycidylether, 5 parts of defoaming agent, 11 parts of titanium dioxide, methacrylic acid
6 parts of methyl esters, 13 parts of styrene, 24 parts of precipitated calcium carbonate, 36 parts of ethyl orthosilicate, 4.2 parts of methyltriethoxysilane.
5. a kind of anti-static and anti-corrosive paint according to claim 1, which is characterized in that the anti-static and anti-corrosive paint by with
Lower mass fraction at being grouped as: 67 parts of polyethyleneglycol diglycidylether, 7 parts of defoaming agent, 14 parts of titanium dioxide, methacrylic acid
5 parts of methyl esters, 12 parts of styrene, 27 parts of precipitated calcium carbonate, 37 parts of ethyl orthosilicate, 3.8 parts of methyltriethoxysilane.
6. a kind of anti-static and anti-corrosive paint according to claim 1, which is characterized in that the anti-static and anti-corrosive paint by with
Lower mass fraction at being grouped as: 63 parts of polyethyleneglycol diglycidylether, 6 parts of defoaming agent, 10 parts of titanium dioxide, methacrylic acid
4 parts of methyl esters, 16 parts of styrene, 28 parts of precipitated calcium carbonate, 38 parts of ethyl orthosilicate, 4.1 parts of methyltriethoxysilane.
7. the preparation method of claim 1-6 anti-static and anti-corrosive paint, which is characterized in that the method comprises the following steps: 1)
First by polyethyleneglycol diglycidylether, defoaming agent and titanium dioxide stir 22-30min, it is to be mixed uniformly after, base-material is made;
Then methyl methacrylate, styrene, precipitated calcium carbonate, ethyl orthosilicate and methyltriethoxysilane are put into pulverizer
It is crushed, smashed mixture, which is put into, continues 77-89min of stirring in base-material, be thoroughly mixed to ingredient and obtain finished product.