CN106832150A - Modified Nano SiO2/ epoxy acrylate latex and its preparation method and application - Google Patents
Modified Nano SiO2/ epoxy acrylate latex and its preparation method and application Download PDFInfo
- Publication number
- CN106832150A CN106832150A CN201710024424.5A CN201710024424A CN106832150A CN 106832150 A CN106832150 A CN 106832150A CN 201710024424 A CN201710024424 A CN 201710024424A CN 106832150 A CN106832150 A CN 106832150A
- Authority
- CN
- China
- Prior art keywords
- modified nano
- acrylate
- epoxy
- sio
- latex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of modified Nano SiO2The preparation method of/epoxy acrylate latex, including prepare modified Nano SiO2With the preparation of latex, the method that water-based anticorrosive paint is prepared with the latex is also disclosed, the present invention is by oleic acid to Nano-meter SiO_22It is modified, by modified Nano SiO2, epoxy resin and acrylate be sufficiently mixed uniformly, modified Nano SiO is obtained after reaction2/ epoxy acrylate latex.With modified Nano SiO2/ epoxy acrylate is film forming matter, and epoxy resin is 1: 1 with the mol ratio of acrylate, and optimizes acid-base value with 0.15%NaOH, and a kind of new modified Nano-meter SiO_2 is obtained2/ epoxy acrylate watery anti-corrosion paint, the adhesive force of coating reaches 1 grade, and impact resistance reaches 50cm, and pencil hardness reaches 2H, and can good, weather resistance and the excellent characteristic of physical and mechanical properties with bin stability.
Description
Technical field
The present invention relates to a kind of preparation method of composite, and in particular to a kind of modified Nano SiO2/ epoxy-acrylic
The preparation method of ester latex.
Background technology
Water paint is with water as solvent or makees the coating of decentralized medium.It has nontoxic, tasteless, cheap, money
The features such as source is enriched, can greatly reduce the pollution that organic solvent volatilization is caused to air in coating, and using water as solvent,
Can greatly improve security of the coating in storage, transport and work progress.At present, water-based anticorrosive paint successful Application
In building decoration, automobile making, ship and Production Container, railway locomotive, Aero-Space, traffic bridge and woodwork coating etc..
Exist during water-based anticorrosive paint use bin stability can it is poor, be demulsified, flocculate and medium-resistance difference etc. is asked
Topic, the technical difficulty in watery anti-corrosion paint development process is larger in addition, causes industrial applications level relatively low.
The content of the invention
Goal of the invention:The invention aims to overcome water-based anticorrosive paint bin stability can it is poor, be demulsified, flocculate and
A kind of problem of medium-resistance difference, there is provided modified Nano SiO2The preparation method of/epoxy-acrylate latex.
Technical scheme:A kind of modified Nano SiO2The preparation method of/epoxy-acrylate latex, comprises the following steps:
1) modified Nano SiO2Preparation:By 20~30g oleic acid and 5~10g Nano-meter SiO_2s2It is sufficiently mixed, addition 40~
50mL acetone, regulation pH value is to disperse 30~50min, temperature on high speed homogenization dispersion machine after 8~9,40KHz ultrasonic waves disperse
110~120 DEG C are risen to, drying is obtained modified Nano SiO2, it is stand-by;
2) by 18~20g epoxy resin and 2~3g modified Nanos SiO2It is sufficiently mixed, adds 40~50mL of acetone, propylene
8~10g of acid esters and dibutyl tin laurate 3~5 are dripped, and after ultrasonic wave dispersion 30min, are warming up to 90 DEG C, are incubated 3h, and addition is gone
Ionized water 10~15g, it is to be emulsified fully after, remove acetone, curing agent 3~5g of triethylene tetramine is added after cooling, stir
Modified Nano SiO is obtained afterwards2/ epoxy-acrylate latex.
Preferably, described epoxy resin is 1: 1 with the mol ratio of acrylate.
The invention also discloses the modified Nano SiO made by above-mentioned preparation method2/ epoxy-acrylate latex.
As third object of the present invention, modified Nano SiO is also disclosed2/ epoxy-acrylate latex is preparing water
Application in property anticorrosive coating.
As fourth object of the present invention, a kind of watery anti-corrosion paint is disclosed, by each group of following masses number
Part composition:
Slurrying component:1~2g of wetting agent, 2~3g of defoamer, 5~7g of dispersant, 1~2g of bactericide, multifunctional assistant 1
~2g, 5~8g of coalescents, 31~35g of mica powder, 31~35g of talcum powder, 20~22g of iron oxide red, 75~80g of trbasic zinc phosphate,
20~23g of aluminium triphosphate, 110~130g of titanium dioxide, 21~25g of ethylene glycol, 47~50g of wollastonite, hydroxyethyl cellulose 1
~2g, 130~150g of barium sulfate, 1~2g of NaOH, 200~220g of water;
Paint component:350~360g of latex, 2~3g of thickener, 2~3g of levelling agent, 5~7g of butyl glycol ether, defoamer
1~2g.
As the 5th purpose of the invention, the preparation method of above-mentioned watery anti-corrosion paint, including following step are disclosed
Suddenly:
1) anti-corrosive pulp is prepared:Water intaking, bactericide are added in stirred tank, and 500r/min stirs, and is subsequently adding into
Film auxiliary agent, ethylene glycol, dispersant, wetting agent, hydroxyethyl cellulose, defoamer and multifunctional assistant, 500r/min stir,
Obtain dispersion liquid;
In above-mentioned dispersion liquid whipping process, trbasic zinc phosphate, aluminium triphosphate, mica powder and iron oxide red, cunning are slowly added to
Stone flour, wollastonite, titanium dioxide, barium sulfate, 1800~2000r/min is adjusted to by stir speed (S.S.), disperses 16~18min, is added
NaOH is ground to granularity less than 40um to adjust pH value as 7, obtains final product anti-corrosive pulp, stand-by;
2) paint:Be slowly added to step 1 toward stirred tank) in ground anti-corrosive pulp, under 400r/min stirring at low speed,
Latex and thickener, levelling agent, butyl glycol ether and the defoamer being gradually added into claim 2, stir, that is, be obtained and change
Property Nano-meter SiO_22/ epoxy-acrylate watery anti-corrosion paint.
Preferably, step 1) in, the mass fraction that NaOH accounts for anti-corrosive pulp is 0.15%.
The present invention is by oleic acid to Nano-meter SiO_22It is modified, by modified Nano SiO2, epoxy resin and acrylate it is abundant
It is well mixed, wherein, epoxy resin is 1: 1 with the mol ratio of acrylate, and modified Nano SiO is obtained after reaction2/ epoxy-
Acrylic emulsion.With modified Nano SiO2/ epoxy-acrylate is film forming matter, adds face, filler and multifunctional assistant
Deng, and optimize acid-base value with 0.15%NaOH, a kind of new modified Nano-meter SiO_2 is obtained2/ epoxy-acrylate watery anti-corrosion
Coating, the adhesive force of coating reaches 1 grade, and impact resistance reaches 50cm, and pencil hardness reaches 2H, and with bin stability energy
Good, weather resistance and the excellent characteristic of physical and mechanical properties.
Specific embodiment
In the present invention:Each raw material model and source:Nano-meter SiO_22, oleic acid, Nanjing Shuguang Chemical General Plant;Epoxy resin (E-
51), Yueyang Petro-Chemical Corporation;Acetone (technical grade), Xi'an chemical reagent factory;Coalescents (CS-12, technical grade), Jiangsu is auspicious
Safe chemical company;Dispersant (SN-5040, technical grade), Pu Nuoke companies;Multifunctional assistant (AMP-95, technical grade), break Thailandization
Work company;PE-100 wetting agents (PE-100), talcum powder (1250 mesh), are technical grade, You Chang chemical companies;Defoamer (CF-
555, technical grade), Hai Chuan chemical companies;Bactericide (981, technical grade), auxiliary agent company of China;NaOH (NaOH, industry
Level), Tianjin Peng Kun chemical companies;Trbasic zinc phosphate (45%), aluminium triphosphate (APZ-99), iron oxide red (190), are technical grade, on
Hai Nuocheng chemical companies;Mica powder (800 mesh, technical grade), stag chemical company;Thickener (3116), levelling agent (3322),
It is technical grade, Guan Zhi chemical companies.
Laboratory apparatus:Ultrasonic cleaner (SK1200H types), Shanghai High Kudos Science Instrument Co., Ltd.;High speed homogenization point
Dissipate machine (FJ-200 types), Shanghai Sample Model Factory;Lacquer painting shock machine (QCJ types), Cangzhou City Ou Pu detecting instruments Co., Ltd.
Embodiment 1:
A kind of modified Nano SiO2The preparation method of/epoxy-acrylate latex, comprises the following steps:
1) modified Nano SiO2Preparation:By 20g oleic acid and 5g Nano-meter SiO_2s2It is sufficiently mixed, adds 40ml acetone, adjusts pH
It is to disperse 30min after 8,40KHz ultrasonic waves disperse on high speed homogenization dispersion machine to be worth, and temperature rises to 110 DEG C, and drying is obtained and changes
Property Nano-meter SiO_22, it is stand-by;
2) by 18g epoxy resin and 2g modified Nanos SiO2It is sufficiently mixed, adds acetone 40mL, acrylate 8g and February
Dilaurylate 3~5 drips, and after ultrasonic wave dispersion 30min, is warming up to 90 DEG C, is incubated 3h, adds deionized water 10g, to be emulsified
After fully, acetone is removed, curing agent 3~5g of triethylene tetramine is added after cooling, modified Nano SiO is obtained after stirring2/ ring
Oxygen-Acrylic emulsion, in the present embodiment, epoxy resin is 1: 1 with the mol ratio of acrylate.
In modifying process, the influence of the selection of resin to coating property
The advantage and disadvantage of epoxy resin and acrylate are shown in Table 1.Epoxy resin and acrylate respectively have it as film forming matter
Advantage and disadvantage, respective deficiency can be made up from acrylated epoxy, can effectively play both advantages.Cause
This, acrylated epoxy latex is to prepare the comparatively ideal film forming matter of watery anti-corrosion paint.
The advantage and disadvantage of the epoxy resin of table 1 and acrylate
Watery anti-corrosion paint is prepared using above-mentioned latex, is made up of each component of following masses number:
Slurrying component:Wetting agent 1g, defoamer 2g, dispersant 5g, bactericide 1g, multifunctional assistant 1g, coalescents 5g,
Mica powder 31g, talcum powder 31g, iron oxide red 20g, trbasic zinc phosphate 75g, aluminium triphosphate 20g, titanium dioxide 110g, ethylene glycol
21g, wollastonite 47g, hydroxyethyl cellulose 1g, barium sulfate 130g, NaOH 1g, water 220g;
Paint component:Above-mentioned latex 350g, thickener 2g, levelling agent 2g, butyl glycol ether 5g, defoamer 1g.
The preparation method of above-mentioned water paint, comprises the following steps:
1) anti-corrosive pulp is prepared:Water intaking, bactericide are added in stirred tank, and 500r/min stirs, and is subsequently adding into
Film auxiliary agent, ethylene glycol, dispersant, wetting agent, hydroxyethyl cellulose, defoamer and multifunctional assistant, 500r/min stir;
In above-mentioned dispersion liquid whipping process, trbasic zinc phosphate, aluminium triphosphate, mica powder and iron oxide red, cunning are slowly added to
Stone flour, wollastonite, titanium dioxide, barium sulfate, 1800~2000r/min is adjusted to by stir speed (S.S.), disperses 16~18min, is added
NaOH is ground to granularity less than 40um to adjust pH value as 7, obtains final product anti-corrosive pulp, stand-by;
2) paint:Be slowly added to step 1 toward stirred tank) in ground anti-corrosive pulp, under 400r/min stirring at low speed,
Above-mentioned latex and thickener, levelling agent, butyl glycol ether and defoamer are gradually added into, are stirred, that is, modified Nano is obtained
SiO2/ epoxy-acrylate watery anti-corrosion paint.
In the present embodiment, step 1) in, the mass fraction that NaOH accounts for anti-corrosive pulp is 0.15%.
Influence of the pH value to coating stabilization performance
Because the slurry prepared is in stronger acidity, therefore slurry must be adjusted to neutrality with NaOH in pulping process, it is no
Then in the preparation process of water paint, easily there is neutralization reaction in Acid Slurry, each in influence water paint with the latex of alkalescence
The dispersity of component, and there are the wild effects such as be demulsified, harden.
Influence of the NaOH consumptions to coating stabilization performance is shown in Table 2.As known from Table 2, the addition of NaOH be 0.15% (wt,
Mass fraction, similarly hereinafter) when, the stability of coating is optimal.Too low NaOH additions can make coating occur demulsification, it is tacky and hard
Change phenomenon, excessive NaOH is both unnecessary while or can increase alkali to corrosion of metal.
Influence of the NaOH consumptions of the table 2 (accounting for the weight fraction of slurry) to coating stabilization performance
Influence of the epoxy/acrylic acid ester mol ratio to coating property
Influence of the epoxy/acrylic acid ester mol ratio to coating property is shown in Table 3.As known from Table 3, epoxy/acrylic acid ester rubs
Your proportioning for 1: 1 when, the decay resistance of water paint, adhesion property and weather resistance are preferable.Because both mole
Match for 1: 1 when, molecule is engaged must be compared closely, modified best results.Any one of epoxy resin and acrylate
It is excessive, can influence the combination property of coating.Epoxy resin excess, the weather resistance of coating is poor;Acrylate excess, coating
Corrosion resistance, adhesion property it is general.
Influence of the epoxy/acrylic acid ester mol ratio of table 3 to coating property
Face filler to coating antiseptic corrosion can influence
Ferric oxide red colorant has superior high temperature resistant, alkaline-resisting, fast light and salt spray resistance, mica powder, wollastonite, talcum
The sheet inert filler such as powder, the stable in physicochemical property of themselves can prevent wearing for corrosive medium after filling with stacked together
Thoroughly, so as to play initial physical shielding effect.Trbasic zinc phosphate and aluminium triphosphate are added as filler, the ion of their hydrolysis
Can be reacted with ferrous ion, the protection thin layer of densification be formed in metal surface, so as to blocked corrosive medium enter to metal
One step is corroded.
Result shows, in the coating while adding iron oxide red, mica powder, wollastonite, talcum powder, trbasic zinc phosphate and trimerization phosphorus
Sour aluminium is combined as color stuffing by physical shielding and chemical preservation, can greatly enhance the Corrosion Protection of coating.
Embodiment 2:
A kind of modified Nano SiO2The preparation method of/epoxy-acrylate latex, comprises the following steps:
1) modified Nano SiO2Preparation:By 30g oleic acid and 10g Nano-meter SiO_2s2It is sufficiently mixed, adds 50ml acetone, regulation
PH value is to disperse 50min after 9,40KHz ultrasonic waves disperse on high speed homogenization dispersion machine, and temperature rises to 110 DEG C, and drying is obtained
Modified Nano SiO2, it is stand-by;
2) by 20g epoxy resin and 3g modified Nanos SiO2It is sufficiently mixed, adds acetone 50mL, acrylate 10g and two
Dibutyl tin laurate 3~5 drips, and after ultrasonic wave dispersion 30min, is warming up to 90 DEG C, is incubated 3h, adds deionized water 15g, treats breast
After changing fully, acetone is removed, curing agent triethylene tetramine 5g is added after cooling, modified Nano SiO is obtained after stirring2/ ring
Oxygen-Acrylic emulsion, in the present embodiment, epoxy resin is 1: 1 with the mol ratio of acrylate.
Watery anti-corrosion paint is prepared using above-mentioned latex, is made up of each component of following masses number:
Slurrying component:Wetting agent 2g, defoamer 3g, dispersant 7g, bactericide 2g, multifunctional assistant 2g, coalescents 8g,
Mica powder 35g, talcum powder 35g, iron oxide red 22g, trbasic zinc phosphate 80g, aluminium triphosphate 23g, titanium dioxide 130g, ethylene glycol
25g, wollastonite 50g, hydroxyethyl cellulose 2g, barium sulfate 150g, NaOH 2g, water 220g;
Paint component:Above-mentioned self-control latex 360g, thickener 3g, levelling agent 3g, butyl glycol ether 7g, defoamer 2g.
The preparation method of above-mentioned water paint, comprises the following steps:
1) anti-corrosive pulp is prepared:Water intaking, bactericide are added in stirred tank, and 500r/min stirs, and is subsequently adding into
Film auxiliary agent, ethylene glycol, dispersant, wetting agent, hydroxyethyl cellulose, defoamer and multifunctional assistant are added to above-mentioned dispersion liquid
In, 500r/min stirs;
In above-mentioned dispersion liquid whipping process, trbasic zinc phosphate, aluminium triphosphate, mica powder and iron oxide red, cunning are slowly added to
Stone flour, wollastonite, titanium dioxide, barium sulfate, 1800~2000r/min is adjusted to by stir speed (S.S.), disperses 16~18min, is added
NaOH is ground to granularity less than 40um to adjust pH value as 7, obtains final product anti-corrosive pulp, stand-by;
2) paint:Be slowly added to step 1 toward stirred tank) in ground anti-corrosive pulp, under 400r/min stirring at low speed,
Above-mentioned latex and thickener, levelling agent, butyl glycol ether and defoamer are gradually added into, are stirred, that is, modified Nano is obtained
SiO2/ epoxy-acrylate watery anti-corrosion paint.
Most preferably, step 1) in, the mass fraction that NaOH accounts for anti-corrosive pulp is 0.15%.
Embodiment 3:
A kind of modified Nano SiO2The preparation method of/epoxy-acrylate latex, comprises the following steps:
1) modified Nano SiO2Preparation:By 25g oleic acid and 8g Nano-meter SiO_2s2It is sufficiently mixed, adds 45ml acetone, adjusts pH
It is to disperse 40min after 8,40KHz ultrasonic waves disperse on high speed homogenization dispersion machine to be worth, and temperature rises to 120 DEG C, and drying is obtained and changes
Property Nano-meter SiO_22, it is stand-by;
2) by 18g epoxy resin and 2g modified Nanos SiO2It is sufficiently mixed, adds acetone 40mL, acrylate 8g and February
Dilaurylate 3~5 drips, and after ultrasonic wave dispersion 30min, is warming up to 90 DEG C, is incubated 3h, adds deionized water 10g, to be emulsified
After fully, acetone is removed, curing agent triethylene tetramine 5g is added after cooling, modified Nano SiO is obtained after stirring2/ epoxy-
Acrylic emulsion, in the present embodiment, epoxy resin is 1: 1 with the mol ratio of acrylate.Acrylate can be acrylic acid
Monomer.
Watery anti-corrosion paint is prepared using above-mentioned latex, is made up of each component of following masses number:
Slurrying component:Wetting agent 1g, defoamer 2g, dispersant 6g, bactericide 1g, multifunctional assistant 1g, coalescents 7g,
Mica powder 34g, talcum powder 33g, iron oxide red 20g, trbasic zinc phosphate 75g, aluminium triphosphate 20g, titanium dioxide 120g, ethylene glycol
24g, wollastonite 47g, hydroxyethyl cellulose 1g, barium sulfate 140g, NaOH 1g, water 210g;
Paint component:Above-mentioned latex 360g, thickener 2g, levelling agent 2g, butyl glycol ether 6g, defoamer 1g.
The preparation method of above-mentioned water paint, comprises the following steps:
1) anti-corrosive pulp is prepared:Water intaking, bactericide are added in stirred tank, and 500r/min stirs, and is subsequently adding into
Film auxiliary agent, ethylene glycol, dispersant, wetting agent, hydroxyethyl cellulose, defoamer and multifunctional assistant are added to above-mentioned dispersion liquid
In, 500r/min stirs;
In above-mentioned dispersion liquid whipping process, trbasic zinc phosphate, aluminium triphosphate, mica powder and iron oxide red, cunning are slowly added to
Stone flour, wollastonite, titanium dioxide, barium sulfate, 1800~2000r/min is adjusted to by stir speed (S.S.), disperses 16~18min, is added
NaOH is ground to granularity less than 40um to adjust pH value as 7, obtains final product anti-corrosive pulp, stand-by;
2) paint:Be slowly added to step 1 toward stirred tank) in ground anti-corrosive pulp, under 400r/min stirring at low speed,
Above-mentioned latex and thickener, levelling agent, butyl glycol ether and defoamer are gradually added into, are stirred, that is, modified Nano is obtained
SiO2/ epoxy-acrylate watery anti-corrosion paint.
In order to further embody beneficial effects of the present invention, spy enumerates following test example:
The combination property of water-based anticorrosive paint:
Impact resistance is tested according to GB/T 1732-1993;Adhesive force is tested according to GB/T 1720-1979;Pencil is hard
Degree is tested according to GB/T 6739-1996;Water resistance is tested according to GB/T 1733-1993;Salt fog resistance is according to GB/T
1771-2007 tests.
The water-based anticorrosive paint coating in the 2 roads present invention is sprayed on tinplate after treatment, spraying 1 road after 1d again should
Coating, under the conditions of humidity 60%, 25 DEG C of temperature, dries 150h, and it is the corrosion-inhibiting coating of 110um, test that total thickness of dry film is obtained
The results are shown in Table 4.
The performance test results of the water-based anticorrosive paint of table 4
To sum up, the present invention passes through oleic acid to Nano-meter SiO_22It is modified, by modified Nano SiO2, epoxy resin and acrylic acid
Ester is sufficiently mixed uniformly, and modified Nano SiO is obtained after reaction2/ epoxy-acrylate latex.With modified Nano SiO2/ epoxy-the third
Olefin(e) acid ester is film forming matter, and epoxy resin is 1: 1 with the mol ratio of acrylate, and optimizes acid-base value with 0.15%NaOH,
A kind of new modified Nano-meter SiO_2 is obtained2/ epoxy-acrylate watery anti-corrosion paint, the adhesive force of coating reaches 1 grade, resistance to punching
Hitting property reaches 50cm, and pencil hardness reaches 2H, and excellent with the bin stability good, weather resistance of energy and physical and mechanical properties
Characteristic.
Claims (7)
1. a kind of modified Nano SiO2The preparation method of/epoxy-acrylate latex, it is characterised in that:Comprise the following steps:
1) modified Nano SiO2Preparation:By 20~30g oleic acid and 5~10g Nano-meter SiO_2s2It is sufficiently mixed, adds 40~50mL third
Ketone, regulation pH value is to disperse 30~50min on high speed homogenization dispersion machine after 8~9,40KHz ultrasonic waves disperse, and temperature rises to
110~120 DEG C, drying is obtained modified Nano SiO2, it is stand-by;
2) by 18~20g epoxy resin and 2~3g modified Nanos SiO2It is sufficiently mixed, adds 40~50mL of acetone, acrylate 8
~10g and dibutyl tin laurate 3~5 drip, and after ultrasonic wave dispersion 30min, are warming up to 90 DEG C, are incubated 3h, add deionization
Water 10~15g, it is to be emulsified fully after, remove acetone, curing agent 3~5g of triethylene tetramine is added after cooling, made after stirring
Obtain modified Nano SiO2/ epoxy-acrylate latex.
2. modified Nano SiO as claimed in claim 12The preparation method of/epoxy-acrylate latex, it is characterised in that:Institute
The epoxy resin stated is 1: 1 with the mol ratio of acrylate.
3. the modified Nano SiO made by a kind of preparation method as described in claim 1 or 22/ epoxy-acrylate breast
Glue.
4. the modified Nano SiO in claim 32Application of/epoxy-acrylate the latex in watery anti-corrosion paint is prepared.
5. a kind of watery anti-corrosion paint, it is characterised in that:It is made up of each component of following masses number:
Slurrying component:1~2g of wetting agent, 2~3g of defoamer, 5~7g of dispersant, 1~2g of bactericide, 1~2g of multifunctional assistant,
5~8g of coalescents, 31~35g of mica powder, 31~35g of talcum powder, 20~22g of iron oxide red, 75~80g of trbasic zinc phosphate, trimerization
20~23g of aluminum phosphate, 110~130g of titanium dioxide, 21~25g of ethylene glycol, 47~50g of wollastonite, hydroxyethyl cellulose 1~
2g, 130~150g of barium sulfate, 1~2g of NaOH, 200~220g of water;
Paint component:350~360g of latex in claim 3,2~3g of thickener, 2~3g of levelling agent, butyl glycol ether 5~
7g, 1~2g of defoamer.
6. the preparation method of the watery anti-corrosion paint in a kind of claim 5, it is characterised in that:Comprise the following steps:
1) anti-corrosive pulp is prepared:Water intaking, bactericide are added in stirred tank, and 500r/min stirs, and is subsequently adding film forming and helps
Agent, ethylene glycol, dispersant, wetting agent, hydroxyethyl cellulose, defoamer and multifunctional assistant, 500r/min stir;
In above-mentioned dispersion liquid whipping process, be slowly added to trbasic zinc phosphate, aluminium triphosphate, mica powder and iron oxide red, talcum powder,
Wollastonite, titanium dioxide, barium sulfate, 1800~2000r/min is adjusted to by stir speed (S.S.), disperses 16~18min, adds hydroxide
Sodium is ground to granularity less than 40um to adjust pH value as 7, obtains final product anti-corrosive pulp, stand-by;
2) paint:Be slowly added to step 1 toward stirred tank) in ground anti-corrosive pulp, under 400r/min stirring at low speed, gradually
The latex and thickener, levelling agent, butyl glycol ether and defoamer in claim 2 are added, is stirred, that is, modified receiving is obtained
Rice SiO2/ epoxy-acrylate watery anti-corrosion paint.
7. the preparation method of watery anti-corrosion paint as claimed in claim 6, it is characterised in that:Step 1) in, NaOH
The mass fraction for accounting for anti-corrosive pulp is 0.15%.