CN106149163A - A kind of cool feeling yarn and the dyeing and finishing method of spandex plain fabric thereof - Google Patents
A kind of cool feeling yarn and the dyeing and finishing method of spandex plain fabric thereof Download PDFInfo
- Publication number
- CN106149163A CN106149163A CN201610726437.2A CN201610726437A CN106149163A CN 106149163 A CN106149163 A CN 106149163A CN 201610726437 A CN201610726437 A CN 201610726437A CN 106149163 A CN106149163 A CN 106149163A
- Authority
- CN
- China
- Prior art keywords
- cool feeling
- silk
- nylon
- yarn
- dyeing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Present invention is disclosed a kind of cool feeling yarn, using nylon and artificial silk is raw material, and in spinning liquid, interpolation nano mica powder end obtains nylon cool feeling silk and artificial silk cool feeling silk, described nylon cool feeling silk and the network doubling again of artificial silk cool feeling silk and obtains cool feeling yarn.The present invention not only has high pyroconductivity, also has high humidity absorption and release effect, obtains special fiber crops ash effect by double dyes, and color fastness is high, cool feeling consistency of performance, and Moisture absorbing & quick drying property is excellent.
Description
Technical field
The invention belongs to field of textile, particularly to a kind of cool feeling yarn and the dyeing and finishing side of spandex plain fabric thereof
Method.
Background technology
Existing cool feeling yarn, mainly adds the material of high thermal conductivity such as nanoscale jade, Muscovitum in spinning liquid.Female
Body material commonly uses terylene and nylon, is called terylene cool feeling fabric and nylon cool feeling fabric.Terylene and nylon self hygroscopicity
Difference, have impact on the humidity absorption and release effect of cool feeling fabric, and color effects is single.Also have and conventional fabric is carried out at cool feeling dyeing and finishing
Reason, adds cool feeling auxiliary agent, but cool feeling performance is the most water-fastness, and effect is also not as the thread fabric of cool feeling yarn.
Summary of the invention
It is an object of the invention to provide and a kind of not only there is high pyroconductivity, also there is high humidity absorption and release effect,
Obtaining special fiber crops ash effect by double dyes, color fastness is high, cool feeling consistency of performance, cool feeling yarn that Moisture absorbing & quick drying property is excellent and
The dyeing and finishing method of its spandex plain fabric.
The technical scheme is that, it is provided that a kind of cool feeling yarn, using nylon and artificial silk is raw material, in spinning liquid
Adding nano mica powder end and obtain nylon cool feeling silk and artificial silk cool feeling silk, described nylon cool feeling silk and artificial silk cool feeling silk are again
Network doubling obtains cool feeling yarn.
In a preferred embodiment of the present invention, the content at described nano mica powder end is 0.08-1.2%.
In a preferred embodiment of the present invention, described nylon cool feeling silk is the nylon full-dull drafting silk of 40D/34F, institute
Stating the bright rayon that artificial silk is 50D/30F, described cool feeling yarn is the cool feeling yarn of 90D/64F.
In a preferred embodiment of the present invention, the network number of described network silk is that 90-100 twists with the fingers/100 meters.
The dyeing and finishing technology of the spandex plain of a kind of cool feeling yarn, weaves shape by 90D/64F cool feeling yarn plaiting 30D spandex
Become spandex calicut, then carry out dyeing and finishing processing, comprise the steps:
1) pre-treatment: the grey cloth low-tension of open-width is sent in Full-width rinsing machine and washes, and add the soda of 2.5g/l,
The detergent of 1.2g/l, bath raio is 1:10, and treatment temperature is 80 DEG C, and the process time is 30min；
2) pre-setting: being fixed on forming machine by the semi-finished product after washing and feed cloth, setting temperature is 180 DEG C, feeding cloth speed is
18m/s, and overfeeding 30%；
3) two-bath process: first contaminate nylon with acid stain, and add the levelling agent of 1.2g/l, the glacial acetic acid of 1g/l, bath raio is
1:15, dyeing temperature is 98 DEG C, and temperature retention time is 60min, cleans with room temperature washing afterwards, carries out nylon fixation treatment, add
Color fixing agent 1%, the glacial acetic acid of 0.5g/l, temperature is 65 DEG C, and the time is 20min, contaminates artificial silk with reactive dye afterwards, at room temperature
Lower addition reactive dye, add the sodium sulfate of 22g/l after 10min, the sodium carbonate of 12g/l, and bath raio is 1:18, with 1 DEG C/min's
Programming rate rises to 60 DEG C, and temperature retention time is 60min, cleans with room temperature washing afterwards, then carries out artificial silk pickling processes, adds
The glacial acetic acid of 0.5g/l, pickling temperature is 30 DEG C, and pickling time is 10min；
It is 4) upper soft: the cloth after dyeing to be carried out upper soft process at normal temperatures, adds the Hydrophilic nonionic softening agent of 1.5g/l,
Bath raio is 1:8；
5) sizing: by upper soft after cloth put into forming machine heat treatment, setting temperature is 140 DEG C, and the forming machine speed of service is
20m/min。
In a preferred embodiment of the present invention, the loop length of described spandex plain is 26cm/100 piece.
In a preferred embodiment of the present invention, in described spandex plain, the content of ammonia wheel is 10%, grammes per square metre 185g/m2。
Of the present invention for a kind of cool feeling yarn and the dyeing and finishing method of spandex plain fabric thereof, the present invention not only has high
Pyroconductivity, also has high humidity absorption and release effect, obtains special fiber crops ash effect by double dyes, and color fastness is high, cool feeling performance
Persistently, Moisture absorbing & quick drying property is excellent.
Detailed description of the invention
Below presently preferred embodiments of the present invention is described in detail so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that thus protection scope of the present invention is made apparent clear and definite defining.
Embodiment one
A kind of cool feeling yarn, using nylon and artificial silk is raw material, adds nano mica powder end and obtain nylon in spinning liquid
Cool feeling silk and artificial silk cool feeling silk, described nylon cool feeling silk and the network doubling again of artificial silk cool feeling silk obtain cool feeling yarn.
The content at described nano mica powder end is 0.08-1.2%.
Described nylon cool feeling silk is the nylon full-dull drafting silk of 40D/34F, described artificial silk be 50D/30F have light people
Making silk, described cool feeling yarn is the cool feeling yarn of 90D/64F.
The network number of described network silk is that 90-100 twists with the fingers/100 meters.
The dyeing and finishing technology of the spandex plain of a kind of cool feeling yarn, weaves shape by 90D/64F cool feeling yarn plaiting 30D spandex
Become spandex calicut, then carry out dyeing and finishing processing, comprise the steps:
1) pre-treatment: the grey cloth low-tension of open-width is sent in Full-width rinsing machine and washes, and add the soda of 2.5g/l,
The detergent of 1.2g/l, bath raio is 1:10, and treatment temperature is 80 DEG C, and the process time is 30min；
2) pre-setting: being fixed on forming machine by the semi-finished product after washing and feed cloth, setting temperature is 180 DEG C, feeding cloth speed is
18m/s, and overfeeding 30%；
3) two-bath process: first contaminate nylon with acid stain, and add the levelling agent of 1.2g/l, the glacial acetic acid of 1g/l, bath raio is
1:15, dyeing temperature is 98 DEG C, and temperature retention time is 60min, cleans with room temperature washing afterwards, carries out nylon fixation treatment, add
Color fixing agent 1%, the glacial acetic acid of 0.5g/l, temperature is 65 DEG C, and the time is 20min, contaminates artificial silk with reactive dye afterwards, at room temperature
Lower addition reactive dye, add the sodium sulfate of 22g/l after 10min, the sodium carbonate of 12g/l, and bath raio is 1:18, with 1 DEG C/min's
Programming rate rises to 60 DEG C, and temperature retention time is 60min, cleans with room temperature washing afterwards, then carries out artificial silk pickling processes, adds
The glacial acetic acid of 0.5g/l, pickling temperature is 30 DEG C, and pickling time is 10min；
It is 4) upper soft: the cloth after dyeing to be carried out upper soft process at normal temperatures, adds the Hydrophilic nonionic softening agent of 1.5g/l,
Bath raio is 1:8；
5) sizing: by upper soft after cloth put into forming machine heat treatment, setting temperature is 140 DEG C, and the forming machine speed of service is
20m/min。
The loop length of described spandex plain is 26cm/100 piece.
In described spandex plain, the content of ammonia wheel is 10%, grammes per square metre 185g/m2.
Wherein, Q-max value reaches 0.25J/c sec, and moment cool feeling value reaches 1.9 DEG C.
Of the present invention for a kind of cool feeling yarn and the dyeing and finishing method of spandex plain fabric thereof, the present invention not only has high
Pyroconductivity, also has high humidity absorption and release effect, obtains special fiber crops ash effect by double dyes, and color fastness is high, cool feeling performance
Persistently, Moisture absorbing & quick drying property is excellent.
The foregoing is only the detailed description of the invention of the present invention, but protection scope of the present invention is not limited thereto, any
Those of ordinary skill in the art in the technical scope that disclosed herein, the change that can expect without creative work or
Replace, all should contain within protection scope of the present invention.Therefore, protection scope of the present invention should be limited with claims
Fixed protection domain is as the criterion.
Claims (7)
1. a cool feeling yarn, it is characterised in that: using nylon and artificial silk is raw material, adds nanoscale Muscovitum in spinning liquid
Powder obtains nylon cool feeling silk and artificial silk cool feeling silk, described nylon cool feeling silk and the network doubling again of artificial silk cool feeling silk and obtains cool
Sense yarn.
Cool feeling yarn the most according to claim 1, it is characterised in that: the content at described nano mica powder end is 0.08-
1.2%。
Cool feeling yarn the most according to claim 1, it is characterised in that: described nylon cool feeling silk is that the nylon of 40D/34F is complete
Delustring drafting silk, described artificial silk is the bright rayon of 50D/30F, and described cool feeling yarn is the cool feeling yarn of 90D/64F.
Cool feeling yarn the most according to claim 1, it is characterised in that: the network number of described network silk be 90-100 twist with the fingers/
100 meters.
5. a dyeing and finishing technology for the spandex plain of cool feeling yarn, is knitted to form 90D/64F cool feeling yarn plaiting 30D spandex
Spandex calicut, then carry out dyeing and finishing processing, it is characterised in that: comprise the steps:
1) pre-treatment: the grey cloth low-tension of open-width is sent in Full-width rinsing machine and washes, and add the soda of 2.5g/l,
The detergent of 1.2g/l, bath raio is 1:10, and treatment temperature is 80 DEG C, and the process time is 30min；
2) pre-setting: being fixed on forming machine by the semi-finished product after washing and feed cloth, setting temperature is 180 DEG C, feeding cloth speed is
18m/s, and overfeeding 30%；
3) two-bath process: first contaminate nylon with acid stain, and add the levelling agent of 1.2g/l, the glacial acetic acid of 1g/l, bath raio is
1:15, dyeing temperature is 98 DEG C, and temperature retention time is 60min, cleans with room temperature washing afterwards, carries out nylon fixation treatment, add
Color fixing agent 1%, the glacial acetic acid of 0.5g/l, temperature is 65 DEG C, and the time is 20min, contaminates artificial silk with reactive dye afterwards, at room temperature
Lower addition reactive dye, add the sodium sulfate of 22g/l after 10min, the sodium carbonate of 12g/l, and bath raio is 1:18, with 1 DEG C/min's
Programming rate rises to 60 DEG C, and temperature retention time is 60min, cleans with room temperature washing afterwards, then carries out artificial silk pickling processes, adds
The glacial acetic acid of 0.5g/l, pickling temperature is 30 DEG C, and pickling time is 10min；
It is 4) upper soft: the cloth after dyeing to be carried out upper soft process at normal temperatures, adds the Hydrophilic nonionic softening agent of 1.5g/l,
Bath raio is 1:8；
5) sizing: by upper soft after cloth put into forming machine heat treatment, setting temperature is 140 DEG C, and the forming machine speed of service is
20m/min。
The dyeing and finishing technology of the spandex plain of cool feeling yarn the most according to claim 5, it is characterised in that: described spandex is put down
The loop length of stricture of vagina cloth is 26cm/100 piece.
The dyeing and finishing technology of the spandex plain of cool feeling yarn the most according to claim 5, it is characterised in that: described spandex is put down
In stricture of vagina cloth, the content of ammonia wheel is 10%, grammes per square metre 185g/m2。