CN106118203A - A kind of putty powder for exterior wall and preparation method thereof - Google Patents
A kind of putty powder for exterior wall and preparation method thereof Download PDFInfo
- Publication number
- CN106118203A CN106118203A CN201610680900.4A CN201610680900A CN106118203A CN 106118203 A CN106118203 A CN 106118203A CN 201610680900 A CN201610680900 A CN 201610680900A CN 106118203 A CN106118203 A CN 106118203A
- Authority
- CN
- China
- Prior art keywords
- parts
- exterior wall
- putty
- putty powder
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of putty powder for exterior wall and preparation method thereof, belong to building material technical field, be made up of the raw material of following weight portion: cement 22 30 parts, 5 10 parts of flyash, ground calcium carbonate 20 35 parts, 20 30 parts of kieselguhr, polypropylene fibre 8 15 parts, carboxymethyl cellulose 39 parts, penetrating agent 0.1 0.8 parts, antimitotic agent 5 12 parts, latex powder 5 10 parts, pigment 0.2 2 parts, defoamer 0.1 1.2 parts；The putty powder for exterior wall of the present invention has protection against the tide, the resistance of water-fast and cracking resistance is split the advantage such as effective and has superior adhesion strength.Being added in of carboxymethyl cellulose improves the adhesion strength of putty to a certain extent and improves workability；Polypropylene fibre can be good with cement slurry bonding, and when putty is by ectocine strain crackings such as wet temps, polypropylene fibre can play resistance and split and refine the effect in crack so that the contractility of putty is improved.
Description
Technical field
The invention belongs to building material technical field, be specifically related to a kind of putty powder for exterior wall and preparation method thereof.
Background technology
Along with developing rapidly of building trade, various building coatings emerge like the mushrooms after rain, meet each rank
The consumer need of layer different levels.Can improving constantly along with the development of coating and living standards of the people, people are to coating tradition
Construction method and coating quality require more and more higher.
Putty is a part for building decoration and fitment, levelling for wall-surface patching, and the decoration for next step does basis.Putty
Being again batch ash or filler, dry-powder putty is mainly made up of base material, filler and auxiliary agent three part, criticizes to scrape being watered into soft paste before
Thing.Hole on body of wall, crack and other defect can be filled and led up by wall surface putty, make surfacing smooth, have texture, putty material
Can be used for the pretreatment before metal finish coatings, it is possible to coagulation is stopped, the surface leveling of the nonmetallic materials such as cement mortar,
The surface being widely used in various buildings or structures in the industries such as furniture, car and boat, machinery, lathe and building field processes, and is
The functional material of significant research and development.Putty is various in style, and the sorting technique of putty is also had difference, common classification side
Method has by using position, dividing and by composition form classification etc. by function.Conventional putty can be that exterior wall is with greasy by using position to divide
Son and putty for interior wall, dividing by state can be powdery, paste, double-constituent putty.Exterior wall putty to be resisted and to expose to the weather so glue
Property is big, intensity is high, and environmental protection index is slightly lower.Existing powder of lacquer putty for use on, the water resistance having under the long-term corrosion of steam in atmosphere
Peeling poor, easy, hollowing and cracking, some unstable chemcial properties, easily by acid and alkali corrosion with go mouldy.
Summary of the invention
For above-mentioned deficiency, in order to overcome the defect of prior art, the present invention provides a kind of protection against the tide, cracking resistance resistance to split effective
Putty powder for exterior wall and preparation method thereof.
In order to realize the purpose of the present invention, adopt the following technical scheme that
A kind of putty powder for exterior wall, is made up of the raw material of following weight portion:
Preferably, it is made up of the raw material of following weight portion:
Preferably, it is made up of the raw material of following weight portion:
Preferably, the one during pigment is iron oxide red, white carbon black, chrome yellow or phenol cyanines basket.
Further, the preparation method of a kind of putty powder for exterior wall, specifically include following steps:
(1) weigh each raw material of corresponding weight portion respectively, cement, flyash, ground calcium carbonate and kieselguhr are joined
In batch mixer, mix and blend obtains the first compound, and rotating speed is 80-150r/min, and mixing time is 30min；
(2) in the first compound, polypropylene fibre, carboxymethyl cellulose, penetrating agent, latex powder, antimitotic agent, face are added
Material and defoamer, the rotating speed keeping batch mixer is constant, and mixing time is 50-80min, obtains the second compound；
(3) being dried by the second compound and i.e. obtain putty powder for exterior wall, wherein baking temperature is 70-110 DEG C, drying time
For 30-50min.
Preferably, before weighing weight, flyash crosses 300 mesh standard sieves.
Preferably, before weighing weight, ground calcium carbonate crosses 250-300 mesh standard sieve.
Beneficial effects of the present invention:
The putty powder for exterior wall of the present invention has protection against the tide, the resistance of water-fast and cracking resistance is split the advantage such as effective and has superior bonding
Intensity.Being added in of carboxymethyl cellulose improves the adhesion strength of putty to a certain extent and improves workability；Poly-third
Alkene fiber can be good with cement slurry bonding, when putty is by ectocine strain crackings such as wet temps, and polypropylene fibre energy
Play resistance and split and refine the effect in crack so that the contractility of putty is improved.
Detailed description of the invention
Elaborating embodiments of the invention below, the present embodiment is carried out under premised on technical solution of the present invention
Implement, give detailed embodiment and concrete operating process, but protection scope of the present invention is not limited to following enforcement
Example.
Embodiment 1
A kind of putty powder for exterior wall, is made up of the raw material of following weight portion: cement 22 parts, 5 parts of flyash, ground calcium carbonate 20
Part, 20 parts of kieselguhr, polypropylene fibre 8 parts, carboxymethyl cellulose 3 parts, penetrating agent 0.1 part, antimitotic agent 5 parts, latex powder 5 parts,
Pigment 0.2 part, defoamer 0.1 part；One during wherein pigment is iron oxide red, white carbon black, chrome yellow or phenol cyanines basket.
The preparation method of a kind of putty powder for exterior wall, specifically includes following steps:
(1) weigh each raw material of corresponding weight portion respectively, cement, flyash, ground calcium carbonate and kieselguhr are joined
In batch mixer, mix and blend obtains the first compound, and rotating speed is 80r/min, and mixing time is 30min；
(2) in the first compound, polypropylene fibre, carboxymethyl cellulose, penetrating agent, latex powder, antimitotic agent, face are added
Material and defoamer, the rotating speed keeping batch mixer is constant, and mixing time is 60min, obtains the second compound；
(3) being dried by the second compound and i.e. obtain putty powder for exterior wall, wherein baking temperature is 70 DEG C, and drying time is
50min。
Further, before weighing weight, flyash crosses 300 mesh standard sieves.
Further, before weighing weight, ground calcium carbonate crosses 250 mesh standard sieves.
Embodiment 2
A kind of putty powder for exterior wall, is made up of the raw material of following weight portion: cement 30 parts, 10 parts of flyash, ground calcium carbonate
35 parts, 30 parts of kieselguhr, polypropylene fibre 15 parts, carboxymethyl cellulose 9 parts, penetrating agent 0.8 part, antimitotic agent 12 parts, latex powder
10 parts, pigment 2 parts, defoamer 0.5 part；One during wherein pigment is iron oxide red, white carbon black, chrome yellow or phenol cyanines basket.
The preparation method of a kind of putty powder for exterior wall, specifically includes following steps:
(1) weigh each raw material of corresponding weight portion respectively, cement, flyash, ground calcium carbonate and kieselguhr are joined
In batch mixer, mix and blend obtains the first compound, and rotating speed is 100r/min, and mixing time is 30min；
(2) in the first compound, polypropylene fibre, carboxymethyl cellulose, penetrating agent, latex powder, antimitotic agent, face are added
Material and defoamer, the rotating speed keeping batch mixer is constant, and mixing time is 60min, obtains the second compound；
(3) being dried by the second compound and i.e. obtain putty powder for exterior wall, wherein baking temperature is 80 DEG C, and drying time is
40min。
Further, before weighing weight, flyash crosses 300 mesh standard sieves.
Further, before weighing weight, ground calcium carbonate crosses 280 mesh standard sieves.
Embodiment 3
A kind of putty powder for exterior wall, is made up of the raw material of following weight portion: cement 27 parts, 5 parts of flyash, ground calcium carbonate 35
Part, 23 parts of kieselguhr, polypropylene fibre 10 parts, carboxymethyl cellulose 7 parts, penetrating agent 0.5 part, antimitotic agent 8 parts, latex powder 7 parts,
Pigment 0.5 part, defoamer 0.4 part；One during wherein pigment is iron oxide red, white carbon black, chrome yellow or phenol cyanines basket.
The preparation method of a kind of putty powder for exterior wall, specifically includes following steps:
(1) weigh each raw material of corresponding weight portion respectively, cement, flyash, ground calcium carbonate and kieselguhr are joined
In batch mixer, mix and blend obtains the first compound, and rotating speed is 120r/min, and mixing time is 30min；
(2) in the first compound, polypropylene fibre, carboxymethyl cellulose, penetrating agent, latex powder, antimitotic agent, face are added
Material and defoamer, the rotating speed keeping batch mixer is constant, and mixing time is 80min, obtains the second compound；
(3) being dried by the second compound and i.e. obtain putty powder for exterior wall, wherein baking temperature is 100 DEG C, and drying time is
40min。
Further, before weighing weight, flyash crosses 300 mesh standard sieves.
Further, before weighing weight, ground calcium carbonate crosses 250 mesh standard sieves.
Embodiment 4
A kind of putty powder for exterior wall, is made up of the raw material of following weight portion: cement 26 parts, 8 parts of flyash, ground calcium carbonate 25
Part, 30 parts of kieselguhr, polypropylene fibre 12 parts, carboxymethyl cellulose 6 parts, penetrating agent 0.3 part, antimitotic agent 9 parts, latex powder 6 parts,
Pigment 0.6 part, defoamer 0.5 part；One during wherein pigment is iron oxide red, white carbon black, chrome yellow or phenol cyanines basket.
The preparation method of a kind of putty powder for exterior wall, specifically includes following steps:
(1) weigh each raw material of corresponding weight portion respectively, cement, flyash, ground calcium carbonate and kieselguhr are joined
In batch mixer, mix and blend obtains the first compound, and rotating speed is 150r/min, and mixing time is 30min；
(2) in the first compound, polypropylene fibre, carboxymethyl cellulose, penetrating agent, latex powder, antimitotic agent, face are added
Material and defoamer, the rotating speed keeping batch mixer is constant, and mixing time is 80min, obtains the second compound；
(3) being dried by the second compound and i.e. obtain putty powder for exterior wall, wherein baking temperature is 110 DEG C, and drying time is
30min。
Further, before weighing weight, flyash crosses 300 mesh standard sieves.
Further, before weighing weight, ground calcium carbonate crosses 300 mesh standard sieves.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all essences in the present invention
Any amendment, equivalent and the improvement etc. made within god and principle, should be included within the scope of the present invention.
Claims (7)
1. a putty powder for exterior wall, it is characterised in that be made up of the raw material of following weight portion:
A kind of putty powder for exterior wall the most according to claim 1, it is characterised in that be made up of the raw material of following weight portion:
A kind of putty powder for exterior wall the most according to claim 1, it is characterised in that be made up of the raw material of following weight portion:
4. according to a kind of putty powder for exterior wall described in claim 1 or 2 or 3, it is characterised in that pigment is iron oxide red, white carbon black, chrome yellow
Or the one in phenol cyanines basket.
5. the preparation method of a putty powder for exterior wall, it is characterised in that specifically include following steps:
(1) weigh each raw material of corresponding weight portion respectively, cement, flyash, ground calcium carbonate and kieselguhr are joined batch mixing
In machine, mix and blend obtains the first compound, and rotating speed is 80-150r/min, and mixing time is 30min；
(2) in the first compound add polypropylene fibre, carboxymethyl cellulose, penetrating agent, latex powder, antimitotic agent, pigment and
Defoamer, the rotating speed keeping batch mixer is constant, and mixing time is 50-80min, obtains the second compound；
(3) being dried by the second compound and i.e. obtain putty powder for exterior wall, wherein baking temperature is 70-110 DEG C, and drying time is
30-50min。
The preparation method of a kind of putty powder for exterior wall the most according to claim 5, it is characterised in that weigh flyash before weight
Cross 300 mesh standard sieves.
The preparation method of a kind of putty powder for exterior wall the most according to claim 5, it is characterised in that weigh heavy carbon before weight
Acid calcium crosses 250-300 mesh standard sieve.