CN106084970A - A kind of environmental protection cracking resistance antiseptical inner wall putty powder and preparation method thereof - Google Patents
A kind of environmental protection cracking resistance antiseptical inner wall putty powder and preparation method thereof Download PDFInfo
- Publication number
- CN106084970A CN106084970A CN201610676440.8A CN201610676440A CN106084970A CN 106084970 A CN106084970 A CN 106084970A CN 201610676440 A CN201610676440 A CN 201610676440A CN 106084970 A CN106084970 A CN 106084970A
- Authority
- CN
- China
- Prior art keywords
- parts
- environmental protection
- antiseptical
- wall putty
- chinese medicine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of environmental protection cracking resistance antiseptical inner wall putty powder and preparation method thereof, belong to building material technical field, be made up of the raw material of following weight portion: white cement 50 parts, ground calcium carbonate 42 50 parts, Pulvis Talci 60 80 parts, wollastonite 30 55 parts, 35 47 parts of tourmaline anion powder, redispersable latex powder 18 30 parts, lignin 17 28 parts, bentonite 22 35 parts, carboxymethyl starch sodium 10 15 parts, polypropylene fibre 8 12 parts, lubricant 7 15 parts, Chinese medicine extract 12 25 parts, antifungus agent 59 parts；The inner wall putty powder of the present invention has the adhesion strength of excellence, resistance to corrosion, protection against the tide, wear-resisting and wash durability, can purify the air of a room；The raw material of the present invention is easy to get, and nontoxic compared with environmental protection and with low cost, production technology and equipment are simple, it is simple to large-scale production.
Description
Technical field
The invention belongs to building material technical field, be specifically related to a kind of environmental protection cracking resistance antiseptical inner wall putty powder and system thereof
Preparation Method.
Background technology
Along with developing rapidly of building trade, various building coatings emerge like the mushrooms after rain, meet each rank
The consumer need of layer different levels.Can improving constantly along with the development of coating and living standards of the people, people are to coating tradition
Construction method and coating quality require more and more higher.
Putty is a part for building decoration and fitment, levelling for wall-surface patching, and the decoration for next step does basis.Putty
Being again batch ash or filler, dry-powder putty is mainly made up of base material, filler and auxiliary agent three part, criticizes to scrape being watered into soft paste before
Thing.Hole on body of wall, crack and other defect can be filled and led up by wall surface putty, make surfacing smooth, have texture, putty material
Can be used for the pretreatment before metal finish coatings, it is possible to coagulation is stopped, the surface leveling of the nonmetallic materials such as cement mortar,
The surface being widely used in various buildings or structures in the industries such as furniture, car and boat, machinery, lathe and building field processes, and is
The functional material of significant research and development.Putty is various in style, and the sorting technique of putty is also had difference, common classification side
Method has by using position, dividing and by composition form classification etc. by function.Conventional putty can be that exterior wall is with greasy by using position to divide
Son and putty for interior wall, dividing by state can be powdery, paste, double-constituent putty.The leading indicator of existing powder of lacquer putty for use on be freedom from cracking,
Non-scale, do not fall off, there is certain hardness and resistance to water.Along with social progress, people to the functional requirement of powder of lacquer putty for use on also by
Gradually improve, especially inner wall putty powder, in addition to general requirement, also need to consider the demand of energy-conserving and environment-protective.How to develop one
Kind i.e. environmental protection, energy-conservation, convenient construction, the powder of lacquer putty for use on that can meet again specific function demand has become the trend of putty development from now on.
Summary of the invention
It is an object of the invention to provide a kind of environmental protection, water-fast, cracking resistance, antiseptical inner wall putty powder and preparation method thereof.
In order to realize the purpose of the present invention, adopt the following technical scheme that
A kind of environmental protection cracking resistance antiseptical inner wall putty powder, is made up of the raw material of following weight portion:
Wherein, Chinese medicine extract is made up of the raw material of following weight portion:
Flos Caryophylli 18-25 part, Herba Houttuyniae 22-30 part, Herba Pogostemonis 15-22 part, Radix Sophorae Flavescentis 8-13 part, Folium Artemisiae Argyi 16-24 part, Fructus Cnidii
12-20 part, Rhizoma Coptidis 6-15 part, Flos Chrysanthemi stem stalk 9-16 part, Herba Menthae 5-10 part.
Preferably, it is made up of the raw material of following weight portion:
Wherein, Chinese medicine extract is made up of the raw material of following weight portion:
Flos Caryophylli 20-24 part, Herba Houttuyniae 25-28 part, Herba Pogostemonis 18-21 part, Radix Sophorae Flavescentis 10-12 part, Folium Artemisiae Argyi 19-22 part, Fructus Cnidii
15-18 part, Rhizoma Coptidis 8-12 part, Flos Chrysanthemi stem stalk 12-15 part, Herba Menthae 5-8 part.
Preferably, it is made up of the raw material of following weight portion:
Wherein, Chinese medicine extract is made up of the raw material of following weight portion:
Flos Caryophylli 22 parts, Herba Houttuyniae 25 parts, Herba Pogostemonis 20 parts, Radix Sophorae Flavescentis 11 parts, Folium Artemisiae Argyi 20 parts, Fructus Cnidii 16 parts, Rhizoma Coptidis 10 parts, chrysanthemum
Scape stalk 15 parts, Herba Menthae 8 parts.
Preferably, 350 mesh standard sieves crossed by wollastonite.
Preferably, Pulvis Talci and ground calcium carbonate all cross 200-300 mesh standard sieve.
Further, a kind of environmental protection cracking resistance antiseptical inner wall putty powder, the preparation method of Chinese medicine extract is:
Weigh each Chinese herb of corresponding weight portion respectively, join in the water of Chinese medicine gross weight 3-5 times, decoct 3 times, often
Secondary 30-80min, filters, and three filtrates is merged, cooling, concentrates and i.e. obtain Chinese medicine extract.
Further, the preparation method of a kind of environmental protection cracking resistance antiseptical inner wall putty powder, specifically include following steps:
(1) weigh each raw material of corresponding weight portion respectively, white cement and polymer dispersion powder are joined in batch mixer, mixed
The first compound is stirred to obtain in conjunction, and its medium speed is 60-120r/min, mixing time 20-40min；
(2) in the first compound, add wollastonite, Pulvis Talci, ground calcium carbonate and bentonite, keep turning of batch mixer
Speed is constant, and mixing time is 40-60min, obtains the second compound；
(3) in the second compound, tourmaline anion powder, carboxymethyl starch sodium, polypropylene fibre, lignin, profit are added
Lubrication prescription, Chinese medicine extract and antifungus agent, mix and blend, rotating speed is 50r/min, and mixing time 30min obtains the 3rd compound；
(4) being dried by the 3rd compound and i.e. obtain inner wall putty powder, wherein baking temperature is 60-90 DEG C, drying time
For 30-50min.
Beneficial effects of the present invention:
The inner wall putty powder white cement of the present invention and redispersable latex powder, make powder of lacquer putty for use on have excellent bonding strong to basic unit
Degree, adds wollastonite, can keep powder of lacquer putty for use on surfacing and good glossiness, have resistance to corrosion and increasing in powder of lacquer putty for use on
Add adhesive force；Putty adds lignin and carboxymethyl starch sodium, putty cracking can be prevented, improve the conjunction of its water-retaining property and construction
Yi Xing, and increase intensity and the viscosity of putty；The tourmaline anion powder added, is possible not only to eliminate foreign flavor indoors and various have
Evil gas, purifies the air of a room, and the negative oxygen ion that produces of anion powder body weight have higher active time, have the strongest oxygen
Change reduction, cell membrane or the activity of cellular plasm organized enzyme of antibacterial can be destroyed, reach the purpose of antibiotic and sterilizing；Add
Bentonite have excellence protection against the tide, wear-resisting and wash durability；The raw material of the present invention is easy to get, nontoxic relatively environmental protection and one-tenth
This is cheap, and production technology and equipment are simple, it is simple to large-scale production.
Detailed description of the invention
Elaborating embodiments of the invention below, the present embodiment is carried out under premised on technical solution of the present invention
Implement, give detailed embodiment and concrete operating process, but protection scope of the present invention is not limited to following enforcement
Example.
Embodiment 1
A kind of environmental protection cracking resistance antiseptical inner wall putty powder, is made up of the raw material of following weight portion: white cement 50 parts, heavy carbon
Acid calcium 42 parts, Pulvis Talci 60 parts, wollastonite 30 parts, 35 parts of tourmaline anion powder, redispersable latex powder 18 parts, lignin 17
Part, bentonite 22 parts, carboxymethyl starch sodium 10 parts, polypropylene fibre 8 parts, lubricant 7 parts, Chinese medicine extract 12 parts, antifungus agent 5
Part；
Wherein, Chinese medicine extract is made up of the raw material of following weight portion:
Flos Caryophylli 18 parts, Herba Houttuyniae 22 parts, Herba Pogostemonis 15 parts, Radix Sophorae Flavescentis 8 parts, Folium Artemisiae Argyi 16 parts, Fructus Cnidii 12 parts, Rhizoma Coptidis 6 parts, Flos Chrysanthemi
Stem stalk 9 parts, Herba Menthae 5 parts；350 mesh standard sieves crossed by wollastonite；Pulvis Talci and ground calcium carbonate all cross 250 mesh standard sieves.
A kind of environmental protection cracking resistance antiseptical inner wall putty powder, the preparation method of Chinese medicine extract is:
Weigh each Chinese herb of corresponding weight portion respectively, join in the water of Chinese medicine gross weight 3 times, decoct 3 times, every time
40min, filters, and three filtrates is merged, cooling, concentrates and i.e. obtain Chinese medicine extract.
The preparation method of a kind of environmental protection cracking resistance antiseptical inner wall putty powder, specifically includes following steps:
(1) weigh each raw material of corresponding weight portion respectively, white cement and polymer dispersion powder are joined in batch mixer, mixed
The first compound is stirred to obtain in conjunction, and its medium speed is 80r/min, mixing time 30min；
(2) in the first compound, add wollastonite, Pulvis Talci, ground calcium carbonate and bentonite, keep turning of batch mixer
Speed is constant, and mixing time is 50min, obtains the second compound；
(3) in the second compound, tourmaline anion powder, carboxymethyl starch sodium, polypropylene fibre, lignin, profit are added
Lubrication prescription, Chinese medicine extract and antifungus agent, mix and blend, rotating speed is 50r/min, and mixing time 30min obtains the 3rd compound；
(4) being dried by the 3rd compound and i.e. obtain inner wall putty powder, wherein baking temperature is 70 DEG C, and drying time is
40min。
Embodiment 2
A kind of environmental protection cracking resistance antiseptical inner wall putty powder, is made up of the raw material of following weight portion: white cement 65 parts, heavy carbon
Acid calcium 50 parts, Pulvis Talci 80 parts, wollastonite 55 parts, 47 parts of tourmaline anion powder, redispersable latex powder 30 parts, lignin 28
Part, bentonite 35 parts, carboxymethyl starch sodium 15 parts, polypropylene fibre 12 parts, lubricant 15 parts, Chinese medicine extract 25 parts, mildew-resistant
Agent 9 parts；
Wherein, Chinese medicine extract is made up of the raw material of following weight portion:
Flos Caryophylli 25 parts, Herba Houttuyniae 30 parts, Herba Pogostemonis 22 parts, Radix Sophorae Flavescentis 13 parts, Folium Artemisiae Argyi 24 parts, Fructus Cnidii 20 parts, Rhizoma Coptidis 15 parts, chrysanthemum
Scape stalk 16 parts, Herba Menthae 10 parts；350 mesh standard sieves crossed by wollastonite；Pulvis Talci and ground calcium carbonate all cross 200 mesh standard sieves.
A kind of environmental protection cracking resistance antiseptical inner wall putty powder, the preparation method of Chinese medicine extract is:
Weigh each Chinese herb of corresponding weight portion respectively, join in the water of Chinese medicine gross weight 4 times, decoct 3 times, every time
60min, filters, and three filtrates is merged, cooling, concentrates and i.e. obtain Chinese medicine extract.
The preparation method of a kind of environmental protection cracking resistance antiseptical inner wall putty powder, specifically includes following steps:
(1) weigh each raw material of corresponding weight portion respectively, white cement and polymer dispersion powder are joined in batch mixer, mixed
The first compound is stirred to obtain in conjunction, and its medium speed is 80r/min, mixing time 40min；
(2) in the first compound, add wollastonite, Pulvis Talci, ground calcium carbonate and bentonite, keep turning of batch mixer
Speed is constant, and mixing time is 40min, obtains the second compound；
(3) in the second compound, tourmaline anion powder, carboxymethyl starch sodium, polypropylene fibre, lignin, profit are added
Lubrication prescription, Chinese medicine extract and antifungus agent, mix and blend, rotating speed is 50r/min, and mixing time 30min obtains the 3rd compound；
(4) being dried by the 3rd compound and i.e. obtain inner wall putty powder, wherein baking temperature is 90 DEG C, and drying time is
50min。
Embodiment 3
A kind of environmental protection cracking resistance antiseptical inner wall putty powder, is made up of the raw material of following weight portion: white cement 55 parts, heavy carbon
Acid calcium 48 parts, Pulvis Talci 67 parts, wollastonite 34 parts, 38 parts of tourmaline anion powder, redispersable latex powder 22 parts, lignin 25
Part, bentonite 30 parts, carboxymethyl starch sodium 13 parts, polypropylene fibre 10 parts, lubricant 9 parts, Chinese medicine extract 20 parts, antifungus agent
7 parts；
Wherein, Chinese medicine extract is made up of the raw material of following weight portion:
Flos Caryophylli 20 parts, Herba Houttuyniae 25 parts, Herba Pogostemonis 18 parts, Radix Sophorae Flavescentis 10 parts, Folium Artemisiae Argyi 18 parts, Fructus Cnidii 18 parts, Rhizoma Coptidis 7 parts, chrysanthemum
Scape stalk 12 parts, Herba Menthae 7 parts；350 mesh standard sieves crossed by wollastonite；Pulvis Talci and ground calcium carbonate all cross 280 mesh standard sieves.
A kind of environmental protection cracking resistance antiseptical inner wall putty powder, the preparation method of Chinese medicine extract is:
Weigh each Chinese herb of corresponding weight portion respectively, join in the water of Chinese medicine gross weight 5 times, decoct 3 times, every time
40min, filters, and three filtrates is merged, cooling, concentrates and i.e. obtain Chinese medicine extract.
The preparation method of a kind of environmental protection cracking resistance antiseptical inner wall putty powder, specifically includes following steps:
(1) weigh each raw material of corresponding weight portion respectively, white cement and polymer dispersion powder are joined in batch mixer, mixed
The first compound is stirred to obtain in conjunction, and its medium speed is 120r/min, mixing time 20min；
(2) in the first compound, add wollastonite, Pulvis Talci, ground calcium carbonate and bentonite, keep turning of batch mixer
Speed is constant, and mixing time is 60min, obtains the second compound；
(3) in the second compound, tourmaline anion powder, carboxymethyl starch sodium, polypropylene fibre, lignin, profit are added
Lubrication prescription, Chinese medicine extract and antifungus agent, mix and blend, rotating speed is 50r/min, and mixing time 30min obtains the 3rd compound；
(4) being dried by the 3rd compound and i.e. obtain inner wall putty powder, wherein baking temperature is 90 DEG C, and drying time is
40min。
Embodiment 4
A kind of environmental protection cracking resistance antiseptical inner wall putty powder, is made up of the raw material of following weight portion: white cement 60 parts, heavy carbon
Acid Ca45 part, Pulvis Talci 75 parts, wollastonite 50 parts, 42 parts of tourmaline anion powder, redispersable latex powder 25 parts, lignin 22
Part, bentonite 30 parts, carboxymethyl starch sodium 14 parts, polypropylene fibre 11 parts, lubricant 13 parts, Chinese medicine extract 21 parts, mildew-resistant
Agent 6 parts；
Wherein, Chinese medicine extract is made up of the raw material of following weight portion:
Flos Caryophylli 20 parts, Herba Houttuyniae 25 parts, Herba Pogostemonis 20 parts, Radix Sophorae Flavescentis 11 parts, Folium Artemisiae Argyi 17 parts, Fructus Cnidii 18 parts, Rhizoma Coptidis 9 parts, chrysanthemum
Scape stalk 15 parts, Herba Menthae 6 parts；350 mesh standard sieves crossed by wollastonite；Pulvis Talci and ground calcium carbonate all cross 300 mesh standard sieves.
A kind of environmental protection cracking resistance antiseptical inner wall putty powder, the preparation method of Chinese medicine extract is:
Weigh each Chinese herb of corresponding weight portion respectively, join in the water of Chinese medicine gross weight 5 times, decoct 3 times, every time
80min, filters, and three filtrates is merged, cooling, concentrates and i.e. obtain Chinese medicine extract.
The preparation method of a kind of environmental protection cracking resistance antiseptical inner wall putty powder, specifically includes following steps:
(1) weigh each raw material of corresponding weight portion respectively, white cement and polymer dispersion powder are joined in batch mixer, mixed
The first compound is stirred to obtain in conjunction, and its medium speed is 100r/min, mixing time 35min；
(2) in the first compound, add wollastonite, Pulvis Talci, ground calcium carbonate and bentonite, keep turning of batch mixer
Speed is constant, and mixing time is 60min, obtains the second compound；
(3) in the second compound, tourmaline anion powder, carboxymethyl starch sodium, polypropylene fibre, lignin, profit are added
Lubrication prescription, Chinese medicine extract and antifungus agent, mix and blend, rotating speed is 50r/min, and mixing time 30min obtains the 3rd compound；
(4) being dried by the 3rd compound and i.e. obtain inner wall putty powder, wherein baking temperature is 85 DEG C, and drying time is
45min。
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all essences in the present invention
Any amendment, equivalent and the improvement etc. made within god and principle, should be included within the scope of the present invention.
Claims (7)
1. an environmental protection cracking resistance antiseptical inner wall putty powder, it is characterised in that be made up of the raw material of following weight portion:
Wherein, Chinese medicine extract is made up of the raw material of following weight portion:
Flos Caryophylli 18-25 part, Herba Houttuyniae 22-30 part, Herba Pogostemonis 15-22 part, Radix Sophorae Flavescentis 8-13 part, Folium Artemisiae Argyi 16-24 part, Fructus Cnidii 12-20
Part, Rhizoma Coptidis 6-15 part, Flos Chrysanthemi stem stalk 9-16 part, Herba Menthae 5-10 part.
A kind of environmental protection cracking resistance antiseptical inner wall putty powder the most according to claim 1, it is characterised in that by following weight portion
Raw material composition:
Wherein, Chinese medicine extract is made up of the raw material of following weight portion:
Flos Caryophylli 20-24 part, Herba Houttuyniae 25-28 part, Herba Pogostemonis 18-21 part, Radix Sophorae Flavescentis 10-12 part, Folium Artemisiae Argyi 19-22 part, Fructus Cnidii 15-18
Part, Rhizoma Coptidis 8-12 part, Flos Chrysanthemi stem stalk 12-15 part, Herba Menthae 5-8 part.
A kind of environmental protection cracking resistance antiseptical inner wall putty powder the most according to claim 1, it is characterised in that by following weight portion
Raw material composition:
Wherein, Chinese medicine extract is made up of the raw material of following weight portion:
Flos Caryophylli 22 parts, Herba Houttuyniae 25 parts, Herba Pogostemonis 20 parts, Radix Sophorae Flavescentis 11 parts, Folium Artemisiae Argyi 20 parts, Fructus Cnidii 16 parts, Rhizoma Coptidis 10 parts, Flos Chrysanthemi stem
Stalk 15 parts, Herba Menthae 8 parts.
4. according to a kind of environmental protection cracking resistance antiseptical inner wall putty powder described in claim 1 or 2 or 3, it is characterised in that wollastonite
Cross 350 mesh standard sieves.
5. according to a kind of environmental protection cracking resistance antiseptical inner wall putty powder described in claim 1 or 2 or 3, it is characterised in that Pulvis Talci
200-300 mesh standard sieve is all crossed with ground calcium carbonate.
6. an environmental protection cracking resistance antiseptical inner wall putty powder, it is characterised in that the preparation method of Chinese medicine extract is:
Weigh each Chinese herb of corresponding weight portion respectively, join in the water of Chinese medicine gross weight 3-5 times, decoct 3 times, every time
30-80min, filters, and three filtrates is merged, cooling, concentrates and i.e. obtain Chinese medicine extract.
7. the preparation method of an environmental protection cracking resistance antiseptical inner wall putty powder, it is characterised in that specifically include following steps:
(1) weighing each raw material of corresponding weight portion respectively, join in batch mixer by white cement and polymer dispersion powder, mixing is stirred
Mixing to obtain the first compound, its medium speed is 60-120r/min, mixing time 20-40min；
(2) in the first compound, add wollastonite, Pulvis Talci, ground calcium carbonate and bentonite, keep the rotating speed of batch mixer not
Becoming, mixing time is 40-60min, obtains the second compound；
(3) in the second compound, tourmaline anion powder, carboxymethyl starch sodium, polypropylene fibre, lignin, lubrication are added
Agent, Chinese medicine extract and antifungus agent, mix and blend, rotating speed is 50r/min, and mixing time 30min obtains the 3rd compound；
(4) being dried by the 3rd compound and i.e. obtain inner wall putty powder, wherein baking temperature is 60-90 DEG C, and drying time is 30-
50min。