CN106242464A - Composite inner wall putty and preparation method thereof - Google Patents
Composite inner wall putty and preparation method thereof Download PDFInfo
- Publication number
- CN106242464A CN106242464A CN201610601634.1A CN201610601634A CN106242464A CN 106242464 A CN106242464 A CN 106242464A CN 201610601634 A CN201610601634 A CN 201610601634A CN 106242464 A CN106242464 A CN 106242464A
- Authority
- CN
- China
- Prior art keywords
- composite inner
- wall putty
- powder
- putty
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of composite inner wall putty and preparation method thereof；Described composite inner wall putty includes each component of following weight content: cement 21 29%, kieselguhr 29 39%, Gypsum Fibrosum powder 14 21%, sierozem power 13 19%, activated carbon 1 5%, initiator 0.2 0.8%, solid dispersion 0.3 1%, anti-crack fiber 0.5 1%, special rubber powder 0.5 1.5%.Described preparation method: by described cement, kieselguhr, Gypsum Fibrosum powder, sierozem power, activated carbon, anti-crack fiber, special rubber powder mix homogeneously；Add initiator, solid dispersion mixes 5 10 minutes, obtains described composite inner wall putty.Owing to prior art is compared, the present invention permanently effective absorption harmful substance of energy and abnormal flavour, purify the air of a room.
Description
Technical field
The present invention relates to a kind of composite inner wall putty and preparation method thereof.
Background technology
Putty, also known as fillering, is a kind of thick slurry coating material.Painting imposes on priming paint or is directly coated with and imposes on object, in order to clearly
Except defect rugged on coated article surface.Its major function is: 1) make up Defect Base, levelling: with floating rule at metope or
Scratch on end face, be allowed to meet the requirement decorated flatness；Do light: fill said minuscule hole and gap, be allowed to meet surface
The requirement of smoothness；Cover crackle: bouncing putty can cover the segmentation crack of below 0.5mm.2) performance variation texture or decorative pattern.
Through retrieval, earlier application CN104927463A discloses a kind of purgeable inner wall putty, although possess clean room
Interior air, the effect of absorption noxious substance, but composition relates to a large amount of Radix Rhodiolae, Radix Et Rhizoma Nardostachyos, Chinese torreya, lavandula angustifolia etc., and not only price is held high
Expensive, and its essence is not absorption, purifies, but play the effect being capped with poisonous gas.Earlier application CN105198322A
Disclose a kind of inner wall putty powder, although there is extremely strong wearability, after being made moist by water without hollowing, peeling, chap, coming off shows
As, also without jaundice, mouldy, a black speck phenomenon, aesthetic property is good, and the poisonous and harmful substance in energy adsorption chamber, safety and environmental protection, but
Its its prepare raw material and relate to substantial amounts of Semen oryzae sativae, starch, cost is of a relatively high.Although earlier application CN104403399A discloses one
Planting inner wall putty, product is pollution-free, and Diamond Search discharges, and may act as the bottom of emulsion paint, also can be separately as interior decoration material
Material, but its major function is regulation humidity, and non-regulated air quality.
Summary of the invention
For defect of the prior art, it is an object of the invention to provide a kind of composite inner wall putty and preparation side thereof
Method, a kind of high absorption, the putty of purification function, and cost is relatively low, is not related to any organic component, health environment-friendly.
The present invention is achieved by the following technical solutions:
The present invention provides a kind of composite inner wall putty, including each component of following weight content:
Preferably, described cement is 42.5 common cement.
Preferably, described kieselguhr is the one in kieselguhr CD10 (slightly), CD09 (slightly), CD08 (slightly) or two kinds,
Produced by Shengzhou Hua Li diatomite product company limited.
Preferably, described Gypsum Fibrosum powder mesh number is 500-1000 mesh；Described Gypsum Fibrosum powder i.e. plaster of Paris, also known as Gypsum Fibrosum preparata,
Plaster, by natural dihydrate gypsum (CaSO4·2H2O) through calcining, levigate beta-type semi-hydrated gypsum (2CaSO4·H2O)。
Preferably, described sierozem power mesh number is 300-1000 mesh；Main component is Ca (OH)2, CaO and a small amount of CaCO3's
Mixture, is the intensely processed products of Calx.
Preferably, described activated carbon is coal mass active carbon HC-ML002, purchased from Shanghai Xi Tan Environmental Protection Technology Co., Ltd.
Preferably, described initiator is the one in aluminium powder, aluminium oxide, magnesium hydroxide, iron powder, sodium peroxydisulfate or two
Kind.
Preferably, described solid dispersion is mesh polypropylene-fibre, lignin fibre, polyacrylonitrile fibre, powdery
How one or both in based water reducer, powdery polycarboxylic acid water reducer, pH value 5-6.In order to retain the part of polycarboxylate water-reducer
Activity present invention defines pH value, and it is amount of activated that mistake conference makes water reducer lose, it is impossible to participates in the chemisorbed of compound putty
Reaction, too small, make water reducer itself unstable, and lost efficacy.
Preferably, described anti-crack fiber is in mesh polypropylene-fibre, polyacrylonitrile fibre, propylene reticular fiber
Plant or two kinds.
Preferably, described rubber powder be styrenic-acrylic latex powder, Acrylic emulsion powder one or both；PH value
5-7, number-average molecular weight 8-20 ten thousand.In order to retain, rubber powder is amount of activated present invention defines pH value, as pH value limits beyond the present invention
Fixed, crossing conference, that rubber powder is lost is amount of activated, it is impossible to participate in the Chemisorption of compound putty, too small, make rubber powder this
Body is unstable, and loses efficacy.
Second aspect, the present invention provides the preparation method of a kind of described composite inner wall putty, comprises the steps: preparation
Time, comprise the steps:
By described cement, kieselguhr, Gypsum Fibrosum powder, sierozem power, activated carbon, anti-crack fiber, special rubber powder mix homogeneously；Add again
Enter initiator, solid dispersion mixing 5-10 minute, obtain described composite inner wall putty.
Preferably, the mode of described mixing is stirring.
Compared with prior art, the present invention has a following beneficial effect:
Because kieselguhr possesses " molecular sieve " structure and the selective absorption performance of uniqueness, can effectively remove in air
Harmful substance and the abnormal flavour such as free formaldehyde, benzene, ammonia, purify the air of a room.Gypsum Fibrosum powder, sierozem power, activated carbon compound use also
Play the effect purified the air of a room.Use under the effect of initiator by the Organic substance of absorption slowly be transformed into producing high-molecular
Compound so that absorption harmful substance and the kieselguhr of abnormal flavour, Gypsum Fibrosum powder, sierozem power, the composition of activated carbon, the suction that energy is permanently effective
Attached harmful substance and abnormal flavour, purify the air of a room.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in detail.Following example will assist in the technology of this area
Personnel are further appreciated by the present invention, but limit the present invention the most in any form.It should be pointed out that, the ordinary skill to this area
For personnel, without departing from the inventive concept of the premise, it is also possible to make some deformation and improvement.These broadly fall into the present invention
Protection domain.
Composite inner wall putty provided by the present invention is prepared by step once: by described cement, kieselguhr, stone
Cream powder, sierozem power, activated carbon, anti-crack fiber, special rubber powder mix homogeneously；Add initiator, solid dispersion mixing 5-10
Minute, obtain described composite inner wall putty.
Embodiment 1-3
Embodiment 1-3 each provides a kind of composite inner wall putty, and concrete component and content are shown in Table 1:
Table 1
Comparative example 1-3
Comparative example 1-3 is the comparative example of embodiment 1, is shown in Table 2 in place of contrast:
Table 2
Performance detects
Testing the performance of embodiment 1-3 and comparative example 1-3, examination criteria is: JG/T 298-2010 " building room
Interior putty ", the results are shown in Table 3, table 4:
Table 3
Table 4
| Testing index | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 | Comparative example 2 | Comparative example 3 |
| Formaldehyde HCHO (mg/m3)≤0.08 | 0 | 0 | 0 | 0.05 | 0 | 0.09 |
| TVOC(mg/m3)≤0.5 | 0.01 | 0.02 | 0.01 | 0.03 | 0.01 | 0.06 |
Above the specific embodiment of the present invention is described.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformation or amendment within the scope of the claims, this not shadow
Ring the flesh and blood of the present invention.
Claims (10)
1. a composite inner wall putty, it is characterised in that include each component of following weight content:
Composite inner wall putty the most according to claim 1, it is characterised in that described cement is 42.5 common water
Mud.
Composite inner wall putty the most according to claim 1, it is characterised in that described kieselguhr be kieselguhr CD10,
One in CD09, CD08 or two kinds.
Composite inner wall putty the most according to claim 1, it is characterised in that described Gypsum Fibrosum powder mesh number is 500-1000
Mesh；
Described sierozem power mesh number is 300-1000 mesh.
Composite inner wall putty the most according to claim 1, it is characterised in that described activated carbon is coal mass active carbon
HC-ML002。
Composite inner wall putty the most according to claim 1, it is characterised in that described initiator be aluminium powder, aluminium oxide,
One or both in magnesium hydroxide, iron powder, sodium peroxydisulfate.
Composite inner wall putty the most according to claim 1, it is characterised in that described solid dispersion is polypropylene net
One or both in shape fiber, lignin fibre, polyacrylonitrile fibre, powdery how based water reducer, powdery polycarboxylic acid water reducer.
Composite inner wall putty the most according to claim 1, it is characterised in that described anti-crack fiber is polypropylene mesh
One or both in fiber, polyacrylonitrile fibre, propylene reticular fiber.
Composite inner wall putty the most according to claim 1, it is characterised in that described rubber powder is Styrene And Chloroalkyl Acrylates
Latex powder, Acrylic emulsion powder one or both.
10. the preparation method of a described composite inner wall putty, it is characterised in that comprise the steps: described cement, silicon
Diatomaceous earth, Gypsum Fibrosum powder, sierozem power, activated carbon, anti-crack fiber, rubber powder mix homogeneously；Add initiator, solid dispersion mixing 5-
10 minutes, obtain described composite inner wall putty.