CN101628795A - Environment-friendly active carbon decorating material - Google Patents
Environment-friendly active carbon decorating material Download PDFInfo
- Publication number
- CN101628795A CN101628795A CN200810140698A CN200810140698A CN101628795A CN 101628795 A CN101628795 A CN 101628795A CN 200810140698 A CN200810140698 A CN 200810140698A CN 200810140698 A CN200810140698 A CN 200810140698A CN 101628795 A CN101628795 A CN 101628795A
- Authority
- CN
- China
- Prior art keywords
- portions
- powder
- decorating material
- active carbon
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to an environment-friendly active carbon decorating material, which is prepared from the following raw materials in portion by weight: 0.5 to 0.7 portion of active carbon, 12 to 13 portions of sierozem power, 23 to 26 portions of heavy calcium carbonate (calcium carbonate), 9 to 11 portions of talcum powder, 7 to 8 portions of light calcium powder, 1.5 portions of polyvinyl alcohol (PVA glue), 1.1 portions of rubber powder, 1.8 portions of modifier, 1.0 portion of color retention agent, and 0.7 portion of brightening agent (VBL). The decorating material can be used by mixing with any one of cement, paint and gypsum to carry out indoor decoration. The decorating material can thoroughly adsorb and clean indoor harmful substances completely and three-dimensionally, and the effective time of the decorating material can be as long as over 20 to 30 years.
Description
Technical field:
The present invention relates to decoration material field, particularly a kind of environment-friendly type active carbon decorating material.
Technical background:
In each side such as at present conventional family residence, office space, public place, public places of entertainment, interior decoration all is to use whitewashes that cement is floating, gesso is criticized and scraped, coating surface is handled the method for plasterboard, lines, dress furred ceiling.Adopt the part chemical feedstocks as tackiness agent, carry out interior decoration.Adopt painting, electroplated decoration product, practical product, decorative plastic product, wall tile, floor tile, electric equipment products etc. to decorate again to indoor.The use of these products plays effects such as attractive in appearance, generous, civilized, practicality in indoor and each place.For people's work, rest, study, amusement and all normal activities provide good activity space.But, the use of these finishing materials has also increased obnoxious flavour (as benzene, formaldehyde, ether, methyl alcohol etc.), harmful ion (as argon, radon, ammonia, aluminium, lead, chromium, molybdenum etc.), harmful radiation (as light, electricity, magnetic, sound etc.), harmful element (as carbon monoxide, tetracol phenixin, plastics volatile matter etc.) that finishing product, utility, furniture etc. are produced simultaneously.These obnoxious flavoures, harmful ion, harmful element etc. directly affect human physical and mental health.So interior decoration with decorate the source of pollution also just become indoor maximum.These pollutions cause bigger harm to the people, and more weak patient or child's harm are more serious to resistibility especially, as: septicemia, respiratory tract disease, heavy metal poisoning etc.Therefore, be also referred to as " decorating the killer " in interior decoration at present.
Summary of the invention:
Defective in the objective of the invention is to use at above technology discloses a kind ofly on the basis of not losing original finishing effect, and can reach environmental protection, a kind of environment-friendly type active carbon decorating material of health effect.
The objective of the invention is to realize by the following technical solutions:
A kind of environment-friendly type active carbon decorating material is making by following raw material (weight part) proportioning:
Gac 0.5～0.7
Ash calcium powder 12～13
Water-ground limestone (dry powder) 23～26
Talcum powder 9～11
Light calcium carbonate powder 7～8
Polyvinyl alcohol (PVA glue) 1.5
Rubber powder 1.1
Properties-correcting agent 1.8
Color preserving agent 1.0
Whitening agent (VBL) 0.7
Described gac: fineness≤200 orders, iodine sorption value 〉=1000mg/g, tetracol phenixin adsorptive value 〉=90%, benzene adsorptive value 〉=45%.
Any mixing that product of the present invention can be arranged in pairs or groups in cement, coating, the gypsum is used.
Product of the present invention is when using with cement mixing, and the ratio in 7% joins in the cement of GB No. 200 to No. 500, by even stirring, be mainly used in wall floating.Its main absorption index is: iodine sorption value 〉=200mg/g, tetracol phenixin adsorptive value 〉=80mg/g, benzene adsorptive value 〉=40mg/g.
Product of the present invention is when mixing use with coating, the ratio in 1% joins in the coating, through even stirring, be mainly used in wall floating.Its main absorption index is: iodine sorption value 〉=100mg/g, and tetracol phenixin adsorptive value 〉=70mg/g, benzene adsorptive value 〉=35mg/g.
Product of the present invention is when mixing use with gypsum, the ratio in 7% joins in the gypsum, makes through evenly stirring, and is mainly used in indoor furred ceiling and floating putty.Its main absorption index is: iodine sorption value 〉=70mg/g, tetracol phenixin adsorptive value 〉=60mg/g, benzene adsorptive value 〉=30mg/g.
In cement, coating, gypsum, mix and use product of the present invention indoor wall to be whitewashed finishing, a 15-20m
2Indoor, can use about the about 150-200kg of cement, about coating 20kg-50kg, about gypsum (being mainly used in batch Puttying, plasterboard, line, bar etc.) 100kg.Net effect can reach: absorption obnoxious flavour 15kg-20kg, harmful ion 30kg-40kg.Can remove completely indoor objectionable impurities and external objectionable impurities.If to a 100m
2The student fits up in the classroom, approximately can use about above raw material 2000kg.Can inhale about harmful ion 200kg, about obnoxious flavour 120kg, can guarantee student's health study.If to a 300-500m
2Meeting room, office, public place of entertainment fit up, approximately can use above raw material 5000kg.It can active adsorption harmful ion 500kg about, about obnoxious flavour 3000kg, can guarantee staff, amusement crowd's health.
Mix with cement, gypsum with product of the present invention and can also make various protective shields, infrared rays, ultraviolet ray, X-ray are effectively protected.
Inject mould with product of the present invention and gypsum, the coating back of can sizing mixing, make the various artworks that adsorption effect arranged, ornamental article, combination calligraphy and painting, various suspension members etc.Fit up indoor, to increase attractive in appearance, generous sensation.
Beneficial effect:
Because gac has the good adsorption performance to light, electricity, magnetic, radiation, so being added in cement, coating, gypsum with product material of the present invention fits up indoor, can carry out active adsorption to light, electricity, magnetic, radiation that household electrical appliance, office appliance, amusement electrical appliance, teaching consuming energy device etc. give out, to reduce these radiation to the human injury.Compare with present on the market environmental friendly indoor product, the present invention has adsorptive capacity height, absorption is wide, price is low characteristics, can be comprehensive, stereoscopic thoroughly removes indoor objectionable impurities.The absorption validity period is more than the 20-30.
Embodiment:
A kind of environment-friendly type active carbon decorating material of the present invention is to be made by following raw material (weight part) proportioning:
Gac 0.5～0.7
Ash calcium powder 12～13
Water-ground limestone (dry powder) 23～26
Talcum powder 9～11
Light calcium carbonate powder 7～8
Polyvinyl alcohol (PVA glue) 1.5
Rubber powder 1.1
Properties-correcting agent 1.8
Color preserving agent 1.0
Whitening agent (VBL) 0.7
Described gac: fineness≤200 orders, iodine sorption value 〉=1000mg/g, tetracol phenixin adsorptive value 〉=90%, benzene adsorptive value 〉=45%.
Any mixing that product of the present invention can be arranged in pairs or groups in cement, coating, the gypsum is used.
Embodiment 1:
A kind of environment-friendly type active carbon decorating material, when itself and cement mixing were used, it was to be made by following raw material (weight part) proportioning:
Gac 0.7
Ash calcium powder 13
Water-ground limestone (dry powder) 26
Talcum powder 11
Light calcium carbonate powder 9
Polyvinyl alcohol (PVA glue) 1.5
Rubber powder 1.1
Properties-correcting agent 1.8
Color preserving agent 1.0
Whitening agent (VBL) 0.7
Above-mentioned raw materials is joined in 7% ratio in the cement of GB No. 200 to No. 500, by even stirring, be mainly used in wall floating.
Embodiment 2:
A kind of environment-friendly type active carbon decorating material, when it was mixed use with coating, it was to be made by following raw material (weight part) proportioning:
Gac 0.6
Ash calcium powder 12.5
Water-ground limestone (dry powder) 25
Talcum powder 10
Light calcium carbonate powder 8
Polyvinyl alcohol (PVA glue) 1.5
Rubber powder 1.1
Properties-correcting agent 1.8
Color preserving agent 1.0
Whitening agent (VBL) 0.7
Above-mentioned raw materials is joined in the coating in 1% ratio, make, be mainly used in wall floating through evenly stirring.
Embodiment 3:
A kind of environment-friendly type active carbon decorating material, when it was mixed use with gypsum, it was to be made by following raw material (weight part) proportioning:
Gac 0.5
Ash calcium powder 12
Water-ground limestone (dry powder) 23
Talcum powder 9
Light calcium carbonate powder 7
Polyvinyl alcohol (PVA glue) 1.5
Rubber powder 1.1
Properties-correcting agent 1.8
Color preserving agent 1.0
Whitening agent (VBL) 0.7
Above-mentioned raw materials is joined in the gypsum in 7% ratio, make, be mainly used in indoor furred ceiling and floating putty through evenly stirring.
Claims (2)
1, a kind of environment-friendly type active carbon decorating material is characterized in that: it is making by following raw material (weight part) proportioning:
Gac 0.5～0.7, grey calcium powder 12～13, water-ground limestone (dry powder) 23～26, talcum powder 9～11, light calcium carbonate powder 7～8, polyvinyl alcohol (PVA glue) 1.5, rubber powder 1.1, properties-correcting agent 1.8, color preserving agent 1.0, whitening agent (VBL) 0.7.
2, according to a kind of environment-friendly type active carbon decorating material described in the claim 1, it is characterized in that: described gac: fineness≤200 orders, iodine sorption value 〉=1000mg/g, tetracol phenixin adsorptive value 〉=90%, benzene adsorptive value 〉=45%.