CN102852315A - Carbon-plastic composite floor and manufacturing method thereof - Google Patents
Carbon-plastic composite floor and manufacturing method thereof Download PDFInfo
- Publication number
- CN102852315A CN102852315A CN2012103387159A CN201210338715A CN102852315A CN 102852315 A CN102852315 A CN 102852315A CN 2012103387159 A CN2012103387159 A CN 2012103387159A CN 201210338715 A CN201210338715 A CN 201210338715A CN 102852315 A CN102852315 A CN 102852315A
- Authority
- CN
- China
- Prior art keywords
- active carbon
- composite floor
- plastic composite
- floor
- charcoal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a carbon-plastic composite floor and a manufacturing method thereof. The manufacturing method includes filling formable activated carbon materials in holes of various plastic hollow floors which are commercially available, and drilling a plurality of small holes on seams or backs of the floors to improve breathability of the composite floor. Performances of original hollow floors are retained while functions of activated carbon such as adsorption, deodorization and moisture proofing are added, so that the carbon-plastic composite floor has effects such as air purification and pollution elimination. The manufacturing method is simple, easy to implement and low in cost, and has important environmental benefits and excellent market prospects.
Description
Technical field
The present invention relates to the wood-based plate technical field of floor, particularly relate to a kind of charcoal plastic composite floor and manufacture method thereof with environment-friendly function.
Background technology
Along with the fast development of realty industry, various artificial decoration finishing materials emerge in multitude, and room air pollution is very serious, and people pay attention to discharging and the elimination of the poisonous and harmful substances such as PARA FORMALDEHYDE PRILLS(91,95) and various strange stinks especially.Active carbon is as a kind of carbonaceous material of hole prosperity, and the aspect such as air purification and water treatment is widely used.Common way is to put use after active carbon is wired up with nonwoven, can affect to a certain extent indoor attractive in appearance and health cleaning.
Summary of the invention
The object of the present invention is to provide a kind of charcoal plastic composite floor and manufacture method thereof with environment-friendly function.The present invention takes full advantage of the special construction of Hollow floor, and active carbon and floor are assembled dexterously, gives the floor new environment-friendly function.Charcoal plastic composite floor of the present invention has kept on the one hand the various characteristics of original Hollow floor and has used function; Given on the other hand the function such as absorption, deodorizing, protection against the tide of active carbon, have purify air, the effect such as pollution abatement.This method is simple, and cost is low.
For achieving the above object, the present invention adopts following technical scheme to be:
A kind of charcoal plastic composite floor, in the hole on plastic hollow floor, the filling active carbon obtains the charcoal plastic composite floor.
Described plastic hollow floor comprises commercially available Vybak, polyvinyl resin and rock quartz, microlite, color spar Hollow floor.
Described active carbon is plastic active carbon.
For improving the gas permeability of composite floor board, bore some apertures at seam or the back side on floor.
A kind of method of making aforesaid charcoal plastic composite floor, to mix after the pressed active carbon raw material weighing, progressively add again entry and mix well pulp, the floor is erect, slurry is injected the cavity to leave standstill 24 hours, in indoor maintenance more than 7 days, wait removing surface is regular behind the slurry curing, totally get final product.
Described pressed active carbon raw material and quality proportioning thereof are 7 parts of active carbon powders, 3 parts of ordinary Portland cements; Add the water of 30-35%.
A kind of method of making aforesaid charcoal plastic composite floor, to mix after the pressed active carbon raw material weighing, progressively add again entry and mix well pulp, the floor is erect, slurry is injected the cavity left standstill 24 hours, wait removing surface is regular behind the slurry curing, totally get final product.
Described pressed active carbon raw material and quality proportioning thereof are 6 parts of active carbon powders, 4 parts of plaster of paris; Add the water of 30-35%.
Beneficial effect of the present invention: take full advantage of the special construction of Hollow floor, active carbon and floor are assembled dexterously, give the floor new environment-friendly function.Charcoal plastic composite floor of the present invention has kept on the one hand the various characteristics of original Hollow floor and has used function; Given on the other hand the function such as absorption, deodorizing, protection against the tide of active carbon, have purify air, the effect such as pollution abatement.This method is simple, and cost is low.
Description of drawings
Fig. 1 is the schematic diagram of the charcoal plastic composite floor of embodiment 1.
Fig. 2 is the schematic diagram of the charcoal plastic composite floor of embodiment 2.
The specific embodiment
Describe the present invention below in conjunction with concrete accompanying drawing, but be to be understood that the description does not here consist of limiting the scope of the invention.
Embodiment 1:
Can see in conjunction with Fig. 1:
2 is the front on plastic hollow floor among the figure, and 5 is the back side on floor, and 3 and 4 is the interface on floor.1 place among the figure was some holes on plastic hollow floor originally, and blacking represents to clog has expired the pressed active carbon situation.
The charge ratio of pressed active carbon is: 7 parts of active carbon powder+3 part ordinary Portland cements add the water of 30-35%.Concrete steps are: mix after with active carbon and cement weighing by said ratio first, progressively add again entry and mix well pulp, the floor is erect, slurry is injected the cavity left standstill 24 hours, in indoor maintenance more than 7 days, wait removing surface is regular behind the slurry curing, totally get final product.
Embodiment 2:
Can see in conjunction with Fig. 2:
Similar to embodiment 1, in order to improve the aeration of charcoal plastic composite floor, can bore some apertures at floor gap 6 and the back side, communicate with active carbon in the hole.In order to raise the efficiency, also can select the plaster of paris to prepare pressed active carbon in addition, the charge ratio of pressed active carbon is: 6 parts of active carbon powder+4 part plaster of paris add the water of 30-35%.Concrete steps are: mix after with active carbon and plaster of paris weighing by said ratio first, progressively add again entry and mix well pulp, the floor is erect, slurry is injected the cavity left standstill 24 hours, wait removing surface is regular behind the slurry curing, totally get final product.
The above only is preferred embodiment of the present invention, and all equalizations of doing according to the present patent application claim change and modify, and all should belong to covering scope of the present invention.
Claims (8)
1. a charcoal plastic composite floor is characterized in that: in the hole on plastic hollow floor, clog active carbon and obtain the charcoal plastic composite floor.
2. charcoal plastic composite floor according to claim 1, it is characterized in that: described plastic hollow floor comprises commercially available Vybak, polyvinyl resin and rock quartz, microlite, color spar Hollow floor.
3. charcoal plastic composite floor according to claim 1, it is characterized in that: described active carbon is plastic active carbon.
4. charcoal plastic composite floor according to claim 1 is characterized in that: for improving the gas permeability of composite floor board, bore some apertures at seam or the back side on floor.
5. method of making charcoal plastic composite floor as claimed in claim 1, it is characterized in that: will mix after the pressed active carbon raw material weighing, progressively add again entry and mix well pulp, the floor is erect, slurry is injected the cavity to leave standstill 24 hours, in indoor maintenance more than 7 days, wait removing surface is regular behind the slurry curing, totally get final product.
6. the manufacture method of charcoal plastic composite floor according to claim 5, it is characterized in that: described pressed active carbon raw material and quality proportioning thereof are 7 parts of active carbon powders, 3 parts of ordinary Portland cements; Add the water of 30-35%.
7. method of making charcoal plastic composite floor as claimed in claim 1, it is characterized in that: will mix after the pressed active carbon raw material weighing, progressively add again entry and mix well pulp, the floor is erect, slurry is injected the cavity left standstill 24 hours, wait removing surface is regular behind the slurry curing, totally get final product.
8. the manufacture method of charcoal plastic composite floor according to claim 7, it is characterized in that: described pressed active carbon raw material and quality proportioning thereof are 6 parts of active carbon powders, 4 parts of plaster of paris; Add the water of 30-35%.