CN103351132A - Environmentally-friendly interior wall putty powder - Google Patents
Environmentally-friendly interior wall putty powder Download PDFInfo
- Publication number
- CN103351132A CN103351132A CN2013102546400A CN201310254640A CN103351132A CN 103351132 A CN103351132 A CN 103351132A CN 2013102546400 A CN2013102546400 A CN 2013102546400A CN 201310254640 A CN201310254640 A CN 201310254640A CN 103351132 A CN103351132 A CN 103351132A
- Authority
- CN
- China
- Prior art keywords
- parts
- putty powder
- powder
- sodium
- order
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses environmentally-friendly interior wall putty powder, wherein the putty powder is composed of the following ingredients in parts by weight: 15-18 parts of white cement, 3-5 parts of sierozem powder, 6-8 parts of gelatinized cassava starch, 22-26 parts of heavy calcium carbonate powder (-320 meshes), 3-5 parts of expanded perlite (-200 meshes), 1.5-2.5 parts of polypropylene fiber (3-5mm), 2-4 parts of polyvinyl alcohol, 2-3 parts of sodium carboxymethyl cellulose, 2.5-3.5 parts of three-grade fly ash, 5-7 parts of sodium bentonite, 1-2 parts of sodium fluosilicate, 2-4 parts of dispersing agent, 0.4-0.6 parts of antifoaming agent and 0.2-0.4 parts of parts of mildew preventive.
Description
Technical field
The present invention relates to building material technical field, relate in particular to a kind of environmental protection inner wall putty powder.
Background technology
The structure of modern architecture is an organic whole, bearing wall, functional thermal insulation layer, waterproof layer, ornament layer, and materials at different levels complement each other, and are indispensable.Putty is between body of wall leveling mortar and the dope layer, plays the booster action of further levelling and the ornamental textured pattern of formation.The accumulating of putty powder packing is convenient, and the scene adds water and stirs and can directly construct.Putty powder common on the market is main component mainly with white cement, inert filler, chemical additive, by evenly being mixed to get, after this dry powder material is transported to the working-yard, directly adds on request water and stirs into paste and get final product knife-coat application, and is very convenient.Yet the defectives such as there is the easy shrinkage cracking of cement-based material inevitably in the traditional putty take cement as agglutinate, flake, peel off, and with the putty of gypsum as main gelling material preparation, can effectively avoid above-mentioned shortcoming, and the construction of being more convenient for.Be the preparation method that the Chinese invention patent of CN101037557 disclosed preparing powder wall mastic with desullfurization gypsum on September 19th, 2007 such as notification number, notification number is that the Chinese invention patent of CN1454945 discloses environmental-protection type gypsum-based putty powder for building on November 12nd, 2003, and notification number is the admixture that the Chinese invention patent of CN101423679 discloses anti-crack putty production by fluorgypsum on May 6th, 2009.These patents prepare putty with plaster of Paris and desulfurated plaster, fluorgypsum as base-material, but still not good, the intensity of existence and stability and hardness do not reach the shortcomings such as Specific construction requirement to above-mentioned prior art.
The leading indicator of existing putty powder is freedom from cracking, non-scale, does not come off, and has certain hardness and water tolerance.Along with social progress, people also improve gradually to the functional requirement of putty powder, except general requirement, also need consider the demand of energy-conserving and environment-protective.How developing a kind of is environmental protection, energy-conservation, construction facility, and the putty powder that can satisfy again the specific function demand has become the trend of from now on putty development.
Summary of the invention
The object of the invention is to propose a kind of environmental protection inner wall putty powder, this putty powder freedom from cracking, non-scale, do not peel off, self does not have hazardous and noxious substances, and can appropriateness improve environmental quality.
A kind of environmental protection inner wall putty powder, this putty powder is comprised of following component in weight part: white cement 15-18 part, ash calcium powder 3-5 part, cassava pasted starch 6-8 part,-320 order heavy calcium carbonate 22-26 parts,-200 order pearlstone 3-5 parts, 3-5mm polypropylene fibre 1.5-2.5 part, polyvinyl alcohol 2-4 part, carboxymethyl cellulose 2-3 part, three grades of flyash 2.5-3.5 parts, sodium bentonite 5-7 part, Sodium Silicofluoride 1-2 part, dispersion agent 2-4 part, defoamer 0.4-0.6 part, mould inhibitor 0.2-0.4 part.
Preferably, this putty powder is comprised of following component in weight part: white cement 16-17 part, ash calcium powder 3.5-4.5 part, cassava pasted starch 6.5-7.5 part,-320 order heavy calcium carbonate 23-25 parts,-200 order pearlstone 3.5-4.5 parts, 3-5mm polypropylene fibre 1.8-2.2 part, polyvinyl alcohol 2.5-3.5 part, carboxymethyl cellulose 2.3-2.7 part, three grades of flyash 2.8-3.2 parts, sodium bentonite 5.5-6.5 part, Sodium Silicofluoride 1.3-1.7 part, dispersion agent 2.5-3.5 part, defoamer 0.45-0.55 part, mould inhibitor 0.25-0.35 part.
Most preferably, this putty powder is comprised of following component in weight part: 16.5 parts of white cements, 4 parts of grey calcium powders, 7 parts of cassava pasted starches, 24 parts of-320 order heavy calcium carbonates, 4 parts of-200 order pearlstones, 2.0 parts of 3-5mm polypropylene fibres, 3 parts of polyvinyl alcohol, 2.5 parts of carboxymethyl celluloses, 3.0 parts in three grades of flyash, 6 parts of sodium bentonites, 1.5 parts of Sodium Silicofluorides, 3 parts of dispersion agents, 0.5 part of defoamer, 0.3 part of mould inhibitor.
Wherein dispersion agent, defoamer and mould inhibitor all adopt the conventional material of prior art to get final product.
Compared with prior art, the present invention has following beneficial effect:
1, inner wall putty of the present invention has good water tolerance and bonding strength, basal plane after the wiping is hollowing not, do not ftracture dry linting not, simultaneously easy construction, putty layer compact structure behind the blade coating, keep ventilative again natural film forming, make metope more level and smooth, save the usage quantity of emulsion paint, and simple to operate, steady quality.
2, inner wall putty of the present invention has added the pearlstone with thermal insulation function, compares with traditional wall putty powder, and the putty powder that uses this prescription to produce has the functional performances such as insulation, heat insulation, sound-absorbing.
3, inner wall putty of the present invention itself is without hazardous and noxious substances, and because the effect that the component that adds also has the objectionable impurities in the appropriate absorbing air.
Embodiment
Embodiment one
A kind of environmental protection inner wall putty powder, this putty powder is comprised of following component in weight part: 15 parts of white cements, 5 parts of grey calcium powders, 6 parts of cassava pasted starches, 26 parts of-320 order heavy calcium carbonates, 3 parts of-200 order pearlstones, 2.5 parts of 3-5mm polypropylene fibres, 2 parts of polyvinyl alcohol, 3 parts of carboxymethyl celluloses, 2.5 parts in three grades of flyash, 7 parts of sodium bentonites, 1 part of Sodium Silicofluoride, 4 parts of dispersion agents, 0.4 part of defoamer, 0.4 part of mould inhibitor.
Embodiment two
A kind of environmental protection inner wall putty powder, this putty powder is comprised of following component in weight part: 18 parts of white cements, 3 parts of grey calcium powders, 8 parts of cassava pasted starches, 22 parts of-320 order heavy calcium carbonates, 5 parts of-200 order pearlstones, 1.5 parts of 3-5mm polypropylene fibres, 4 parts of polyvinyl alcohol, 2 parts of carboxymethyl celluloses, 3.5 parts in three grades of flyash, 5 parts of sodium bentonites, 2 parts of Sodium Silicofluorides, 2 parts of dispersion agents, 0.6 part of defoamer, 0.2 part of mould inhibitor.
Embodiment three
A kind of environmental protection inner wall putty powder, this putty powder is comprised of following component in weight part: 16 parts of white cements, 4.5 parts of grey calcium powders, 6.5 parts of cassava pasted starches, 25 parts of-320 order heavy calcium carbonates, 3.5 parts of-200 order pearlstones, 2.2 parts of 3-5mm polypropylene fibres, 2.5 parts of polyvinyl alcohol, 2.7 parts of carboxymethyl celluloses, 2.8 parts in three grades of flyash, 6.5 parts of sodium bentonites, 1.3 parts of Sodium Silicofluorides, 3.5 parts of dispersion agents, 0.45 part of defoamer, 0.35 part of mould inhibitor.
Embodiment four
A kind of environmental protection inner wall putty powder, this putty powder is comprised of following component in weight part: 17 parts of white cements, 3.5 parts of grey calcium powders, 7.5 parts of cassava pasted starches, 23 parts of-320 order heavy calcium carbonates, 4.5 parts of-200 order pearlstones, 1.8 parts of 3-5mm polypropylene fibres, 3.5 parts of polyvinyl alcohol, 2.3 parts of carboxymethyl celluloses, 3.2 parts in three grades of flyash, 5.5 parts of sodium bentonites, 1.7 parts of Sodium Silicofluorides, 2.5 parts of dispersion agents, 0.55 part of defoamer, 0.25 part of mould inhibitor.
Embodiment five
A kind of environmental protection inner wall putty powder, this putty powder is comprised of following component in weight part: 16.5 parts of white cements, 4 parts of grey calcium powders, 7 parts of cassava pasted starches, 24 parts of-320 order heavy calcium carbonates, 4 parts of-200 order pearlstones, 2.0 parts of 3-5mm polypropylene fibres, 3 parts of polyvinyl alcohol, 2.5 parts of carboxymethyl celluloses, 3.0 parts in three grades of flyash, 6 parts of sodium bentonites, 1.5 parts of Sodium Silicofluorides, 3 parts of dispersion agents, 0.5 part of defoamer, 0.3 part of mould inhibitor.
Inner wall putty of the present invention has good water tolerance and bonding strength, basal plane after the wiping is hollowing not, do not ftracture dry linting not, simultaneously easy construction, putty layer compact structure behind the blade coating, keep ventilative again natural film forming, make metope more level and smooth, save the usage quantity of emulsion paint, and simple to operate, steady quality.
Inner wall putty of the present invention has added the pearlstone with thermal insulation function, compares with traditional wall putty powder, and the putty powder that uses this prescription to produce has the functional performances such as insulation, heat insulation, sound-absorbing.
Inner wall putty of the present invention itself is without hazardous and noxious substances, and because the effect that the component that adds also has the objectionable impurities in the appropriate absorbing air.
Inner wall putty of the present invention: grinability: 54% (standard 20-80%), cohesive strength: 0.74MPa (standard: 0.5mpa), folding strength: 4.2MPa (standard: without), ultimate compression strength: 10.6MPa (standard: without).
The above; only be the better embodiment of the present invention; but protection scope of the present invention is not limited to this; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses; be equal to replacement or change according to technical scheme of the present invention and inventive concept thereof, all should be encompassed within protection scope of the present invention.
Claims (3)
1. environmental protection inner wall putty powder, it is characterized in that, this putty powder is comprised of following component in weight part: white cement 15-18 part, ash calcium powder 3-5 part, cassava pasted starch 6-8 part,-320 order heavy calcium carbonate 22-26 parts,-200 order pearlstone 3-5 parts, 3-5mm polypropylene fibre 1.5-2.5 part, polyvinyl alcohol 2-4 part, carboxymethyl cellulose 2-3 part, three grades of flyash 2.5-3.5 parts, sodium bentonite 5-7 part, Sodium Silicofluoride 1-2 part, dispersion agent 2-4 part, defoamer 0.4-0.6 part, mould inhibitor 0.2-0.4 part.
2. environmental protection inner wall putty powder as claimed in claim 1, it is characterized in that, this putty powder is comprised of following component in weight part: white cement 16-17 part, ash calcium powder 3.5-4.5 part, cassava pasted starch 6.5-7.5 part,-320 order heavy calcium carbonate 23-25 parts,-200 order pearlstone 3.5-4.5 parts, 3-5mm polypropylene fibre 1.8-2.2 part, polyvinyl alcohol 2.5-3.5 part, carboxymethyl cellulose 2.3-2.7 part, three grades of flyash 2.8-3.2 parts, sodium bentonite 5.5-6.5 part, Sodium Silicofluoride 1.3-1.7 part, dispersion agent 2.5-3.5 part, defoamer 0.45-0.55 part, mould inhibitor 0.25-0.35 part.
3. environmental protection inner wall putty powder as claimed in claim 2 is characterized in that, this putty powder is comprised of following component in weight part: 16.5 parts of white cements, 4 parts of ash calcium powders, 7 parts of cassava pasted starches, 24 parts of-320 order heavy calcium carbonates, 4 parts of-200 order pearlstones, 2.0 parts of 3-5mm polypropylene fibres, 3 parts of polyvinyl alcohol, 2.5 parts of carboxymethyl celluloses, 3.0 parts in three grades of flyash, 6 parts of sodium bentonites, 1.5 parts of Sodium Silicofluorides, 3 parts of dispersion agents, 0.5 part of defoamer, 0.3 part of mould inhibitor.