CN105503080A - Dry powder paint for buildings - Google Patents
Dry powder paint for buildings Download PDFInfo
- Publication number
- CN105503080A CN105503080A CN201510984663.6A CN201510984663A CN105503080A CN 105503080 A CN105503080 A CN 105503080A CN 201510984663 A CN201510984663 A CN 201510984663A CN 105503080 A CN105503080 A CN 105503080A
- Authority
- CN
- China
- Prior art keywords
- parts
- dry powder
- powder paint
- starch
- powder coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses dry powder paint for buildings. The dry powder paint comprises components in parts by weight as follows: 1-2 parts of hexyldecanol, 2.8 parts of polyoxypropyl glyceryl ether, 1.9 parts of nonyl phenol ethylene oxide carboxylate, 3.4 parts of aluminic acid ester, 6.7 parts of starch, 8.4 parts of organic bentonite, 5.8 parts of activated aluminum oxide, 12.4 parts of bauxite and 62.3 parts of white cement. The dry powder paint has the properties of water leakage prevention, fireproofing, temperature and humidity adjustment, anti-bacteria, negative ion release, adsorption and decomposition of formaldehyde and absorption of carbon dioxide.
Description
Technical field
The present invention relates to building dry-powder coating.
Background technology
Current dry powder paint, its anti-seep water, fire prevention, conditioning, antibacterial, anion releasing, adsorption-decomposition function formaldehyde and absorbing carbon dioxide performance all have much room for improvement.
Summary of the invention
The object of the present invention is to provide a kind of building dry-powder coating, there is the performance of anti-seep water, fire prevention, conditioning, antibacterial, anion releasing, adsorption-decomposition function formaldehyde and absorbing carbon dioxide.
For achieving the above object, technical scheme of the present invention is a kind of building dry-powder coating of design, composed of the following components by weight:
1 ~ 2 part of hexyl decyl alcohol, 2.8 parts of polyoxyethyl propyl glyceryl ethers, 1.9 parts of nonylphenol ethoxylate carboxylate salts, 3.4 parts of Aluminates, 6.7 parts of starch, 8.4 parts of organobentonites, 5.8 parts of activated aluminas, 12.4 parts of bauxitic clays, 62.3 parts of white cements.
Preferably, building dry-powder coating, composed of the following components by weight:
1 part of hexyl decyl alcohol, 2.8 parts of polyoxyethyl propyl glyceryl ethers, 1.9 parts of nonylphenol ethoxylate carboxylate salts, 3.4 parts of Aluminates, 6.7 parts of starch, 8.4 parts of organobentonites, 5.8 parts of activated aluminas, 12.4 parts of bauxitic clays, 62.3 parts of white cements.
Preferably, building dry-powder coating, composed of the following components by weight:
2 parts of hexyl decyl alcohol, 2.8 parts of polyoxyethyl propyl glyceryl ethers, 1.9 parts of nonylphenol ethoxylate carboxylate salts, 3.4 parts of Aluminates, 6.7 parts of starch, 8.4 parts of organobentonites, 5.8 parts of activated aluminas, 12.4 parts of bauxitic clays, 62.3 parts of white cements.
Advantage of the present invention and beneficial effect are: provide a kind of building dry-powder coating, have the performance of anti-seep water, fire prevention, conditioning, antibacterial, anion releasing, adsorption-decomposition function formaldehyde and absorbing carbon dioxide.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of building dry-powder coating, composed of the following components by weight:
1 ~ 2 part of hexyl decyl alcohol, 2.8 parts of polyoxyethyl propyl glyceryl ethers, 1.9 parts of nonylphenol ethoxylate carboxylate salts, 3.4 parts of Aluminates, 6.7 parts of starch, 8.4 parts of organobentonites, 5.8 parts of activated aluminas, 12.4 parts of bauxitic clays, 62.3 parts of white cements.
Embodiment 2
Building dry-powder coating, composed of the following components by weight:
1 part of hexyl decyl alcohol, 2.8 parts of polyoxyethyl propyl glyceryl ethers, 1.9 parts of nonylphenol ethoxylate carboxylate salts, 3.4 parts of Aluminates, 6.7 parts of starch, 8.4 parts of organobentonites, 5.8 parts of activated aluminas, 12.4 parts of bauxitic clays, 62.3 parts of white cements.
Embodiment 3
Building dry-powder coating, composed of the following components by weight:
2 parts of hexyl decyl alcohol, 2.8 parts of polyoxyethyl propyl glyceryl ethers, 1.9 parts of nonylphenol ethoxylate carboxylate salts, 3.4 parts of Aluminates, 6.7 parts of starch, 8.4 parts of organobentonites, 5.8 parts of activated aluminas, 12.4 parts of bauxitic clays, 62.3 parts of white cements.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. building dry-powder coating, is characterized in that, composed of the following components by weight:
1 ~ 2 part of hexyl decyl alcohol, 2.8 parts of polyoxyethyl propyl glyceryl ethers, 1.9 parts of nonylphenol ethoxylate carboxylate salts, 3.4 parts of Aluminates, 6.7 parts of starch, 8.4 parts of organobentonites, 5.8 parts of activated aluminas, 12.4 parts of bauxitic clays, 62.3 parts of white cements.
2. building dry-powder coating according to claim 1, is characterized in that, composed of the following components by weight:
1 part of hexyl decyl alcohol, 2.8 parts of polyoxyethyl propyl glyceryl ethers, 1.9 parts of nonylphenol ethoxylate carboxylate salts, 3.4 parts of Aluminates, 6.7 parts of starch, 8.4 parts of organobentonites, 5.8 parts of activated aluminas, 12.4 parts of bauxitic clays, 62.3 parts of white cements.
3. building dry-powder coating according to claim 1, is characterized in that, composed of the following components by weight:
2 parts of hexyl decyl alcohol, 2.8 parts of polyoxyethyl propyl glyceryl ethers, 1.9 parts of nonylphenol ethoxylate carboxylate salts, 3.4 parts of Aluminates, 6.7 parts of starch, 8.4 parts of organobentonites, 5.8 parts of activated aluminas, 12.4 parts of bauxitic clays, 62.3 parts of white cements.