CN107663386A - A kind of fire retarding wood composite coating - Google Patents
A kind of fire retarding wood composite coating Download PDFInfo
- Publication number
- CN107663386A CN107663386A CN201711207458.4A CN201711207458A CN107663386A CN 107663386 A CN107663386 A CN 107663386A CN 201711207458 A CN201711207458 A CN 201711207458A CN 107663386 A CN107663386 A CN 107663386A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- fire retarding
- composite coating
- wood composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of fire retarding wood composite coating, it is composed of the following components in parts by weight：23 parts of 10 15 parts of aluminum ore, 37 parts of high alumina micro mist, 25 parts of titanium dioxide, 58 parts of silicon ash, 12 parts of exciting agent, 13 parts of rhodan ammonium, 25 parts of polyacrylamide, 34 parts of sodium metasilicate, 45 parts of potassium hydroxide, 58 parts of activated carbon, 15 parts of polyurethane aqueous dispersions, 10 20 parts of water, 25 parts of dispersant, 12 parts of 13 part, part film forming agent of color inhibition agent, 5 10 parts of active powdered carbon, 68 parts of quartz sand, 58 parts of zeolite powder and kaolin.The present invention is advantageous to popularization and application.
Description
Technical field
The present invention relates to building coating technical field, in particular to a kind of fire retarding wood composite coating.
Background technology
When the main filmogen of coating is for aqueous polyurethane, water soluble acrylic acid and aqueous epoxide resin paint etc., wherein
Aqueous polyurethane coating is because its premium properties has been widely used, in particular by acrylic ester modified water-soluble polyurethane emulsion system
Standby inexpensive, safe and nontoxic, environmentally friendly new coating, thus the preparation and research of water flame-proof paint focus primarily on it is organic into
The adhesive property of membrane material and wood surface, and growth mechanism and fire-retardant effect of the inorganic nano-particle in organic film-forming material
Should.But the research to inorganic silicon Sol SYSTEMS coating is less, lack the fire retarding wood coating using inorganic siliceous filmogen as base-material
Preparation and performance study.
The content of the invention
It is an object of the invention to provide a kind of fire retarding wood composite coating, to solve the deficiencies in the prior art.
To realize the object of the invention, the technical scheme that uses for：
A kind of fire retarding wood composite coating, it is characterised in that be composed of the following components in parts by weight：Aluminum ore 10-15 parts, high alumina
Micro mist 3-7 parts, titanium dioxide 2-5 parts, silicon ash 5-8 parts, exciting agent 1-2 parts, rhodan ammonium 1-3 parts, polyacrylamide 2-5 parts,
Sodium metasilicate 3-4 parts, potassium hydroxide 4-5 parts, activated carbon 5-8 parts, polyurethane aqueous dispersions 1-5 parts, water 10-20 parts, dispersant
2-5 parts, color inhibition agent 1-3 parts, part film forming agent 1-2 parts, active powdered carbon 5-10 parts, quartz sand 6-8 parts, zeolite powder 5-8 parts and height
Ridge soil 2-3 parts.
Further, the fire retarding wood composite coating is composed of the following components in parts by weight：11 parts of aluminum ore, high alumina are micro-
5 parts of powder, 3 parts of titanium dioxide, 6 parts of silicon ash, 1 part of exciting agent, 1 part of rhodan ammonium, 2 parts of polyacrylamide, 3 parts of sodium metasilicate, hydrogen-oxygen
Change 4 parts of potassium, 6 parts of activated carbon, 1 part of polyurethane aqueous dispersions, 10 parts of water, 3 parts of dispersant, part, part film forming agent 1 of color inhibition agent 2
Part, 6 parts of active powdered carbon, 7 parts of quartz sand, 6 parts of zeolite powder and 2 parts of kaolin.
The beneficial effects of the invention are as follows：
The preparation process cost of raw material of the present invention is cheap, environmentally friendly, can scale using Industrial Solid Waste silicon ash prepare fire retarding wood apply
Material, and coating is nontoxic in whole life cycle.
Embodiment
The present invention is described in further detail below by specific examples of the implementation.
Embodiment 1：
A kind of fire retarding wood composite coating, it is characterised in that be composed of the following components in parts by weight：Aluminum ore 10-15 parts, high alumina
Micro mist 3-7 parts, titanium dioxide 2-5 parts, silicon ash 5-8 parts, exciting agent 1-2 parts, rhodan ammonium 1-3 parts, polyacrylamide 2-5 parts,
Sodium metasilicate 3-4 parts, potassium hydroxide 4-5 parts, activated carbon 5-8 parts, polyurethane aqueous dispersions 1-5 parts, water 10-20 parts, dispersant
2-5 parts, color inhibition agent 1-3 parts, part film forming agent 1-2 parts, active powdered carbon 5-10 parts, quartz sand 6-8 parts, zeolite powder 5-8 parts and height
Ridge soil 2-3 parts.
Further, the fire retarding wood composite coating is composed of the following components in parts by weight：11 parts of aluminum ore, high alumina are micro-
5 parts of powder, 3 parts of titanium dioxide, 6 parts of silicon ash, 1 part of exciting agent, 1 part of rhodan ammonium, 2 parts of polyacrylamide, 3 parts of sodium metasilicate, hydrogen-oxygen
Change 4 parts of potassium, 6 parts of activated carbon, 1 part of polyurethane aqueous dispersions, 10 parts of water, 3 parts of dispersant, part, part film forming agent 1 of color inhibition agent 2
Part, 6 parts of active powdered carbon, 7 parts of quartz sand, 6 parts of zeolite powder and 2 parts of kaolin.
The preparation process cost of raw material of the present invention is cheap, environmentally friendly, can scale prepare fire-retardant wood using Industrial Solid Waste silicon ash
Material coating.The present invention contains titanium dioxide, causes that the surface gloss of coating is high while greatly enhancing bacteria-eliminating efficacy, weatherability
By force, living environment is improved.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, for the skill of this area
For art personnel, the present invention can have various modifications and variations.Within the spirit and principles of the invention, that is made any repaiies
Change, equivalent substitution, improvement etc., should be included in the scope of the protection.
Claims (2)
1. a kind of fire retarding wood composite coating, it is characterised in that be composed of the following components in parts by weight：Aluminum ore 10-15 parts, height
Aluminium micro mist 3-7 parts, titanium dioxide 2-5 parts, silicon ash 5-8 parts, exciting agent 1-2 parts, rhodan ammonium 1-3 parts, polyacrylamide 2-5
It is part, sodium metasilicate 3-4 parts, potassium hydroxide 4-5 parts, activated carbon 5-8 parts, polyurethane aqueous dispersions 1-5 parts, water 10-20 parts, scattered
Agent 2-5 parts, color inhibition agent 1-3 parts, part film forming agent 1-2 parts, active powdered carbon 5-10 parts, quartz sand 6-8 parts, zeolite powder 5-8 parts and
Kaolin 2-3 parts.
2. a kind of fire retarding wood composite coating according to claim 1, it is characterised in that 11 parts of aluminum ore, high alumina micro mist 5
Part, 3 parts of titanium dioxide, 6 parts of silicon ash, 1 part of exciting agent, 1 part of rhodan ammonium, 2 parts of polyacrylamide, 3 parts of sodium metasilicate, potassium hydroxide
4 parts, it is 6 parts of activated carbon, 1 part of polyurethane aqueous dispersions, 10 parts of water, 3 parts of dispersant, 1 part of 2 part, part film forming agent of color inhibition agent, living
Property 2 parts of 6 parts of powdered carbon, 7 parts of quartz sand, 6 parts of zeolite powder and kaolin.