CN106380924A - Crack-resistant building wall putty and preparation method thereof - Google Patents
Crack-resistant building wall putty and preparation method thereof Download PDFInfo
- Publication number
- CN106380924A CN106380924A CN201610739167.9A CN201610739167A CN106380924A CN 106380924 A CN106380924 A CN 106380924A CN 201610739167 A CN201610739167 A CN 201610739167A CN 106380924 A CN106380924 A CN 106380924A
- Authority
- CN
- China
- Prior art keywords
- parts
- architecture
- agent
- putty
- crack resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the technical field of paint production, and particularly relates to a crack-resistant building wall putty and a preparation method thereof. The crack-resistant building wall putty comprises the following raw materials in parts by weight: 15-30 parts of cement, 3-6 parts of guar gum, 4-10 parts of vinyl acetate-acetate copolymer, 30-45 parts of attapulgite clay, 10-15 parts of zeolite, 10-15 parts of diatomaceous earth, 15-25 parts of talcum powder, 2-5 parts of thickening agent, 1-4 parts of water-retaining agent, 0.5-3 parts of penetrant, 2-6 parts of polypropylene fibers, and 1-5 parts of polystyrene fibers. According to the invention, the crack-resistant building wall putty is strong in adhesive force, good in adhesive property and strong in crack-resistant performance.
Description
Technical field
The present invention relates to coating material production technical field is and in particular to a kind of crack resistance putty for scraping walls of architecture and its preparation side
Method.
Background technology
Putty powder for exterior wall is mainly used in cement wall surface, concrete wall surface and other need smooth metope, building with
The impact of the factor such as time and natural climate, the slaked lime in metope generates Calcium Carbonate with the carbon dioxide reaction of in the air, makes
Become volumetric expansion, make exterior wall surface that Paint Falling to occur, metope ftractures, body of wall produces the phenomenons such as seepage, and this is primarily due to greasy
The cracking resistance of sub- powder, water resistance are inadequate, low intensity, and adhesive force is not strong.
Content of the invention
For the deficiencies in the prior art, the invention provides a kind of adhesive force is strong, adhesive property is good, strong the resisting of cracking resistance
Fragility putty for scraping walls of architecture and preparation method thereof.
For realizing object above, the present invention is achieved by the following technical programs：
A kind of crack resistance putty for scraping walls of architecture, is made up of the raw material of following parts by weight：Cement 15-30 part, guar gum 3-6
Part, vinylacetate-acetate multipolymer 4-10 part, attapulgite clay 30-45 part, zeolite 10-15 part, kieselguhr 10-15 part,
Pulvis Talci 15-25 part, thickening agent 2-5 part, water-retaining agent 1-4 part, penetrating agent 0.5-3 part, polypropylene fibre 2-6 part, polystyrene
Fiber 1-5 part.
Further, described crack resistance putty for scraping walls of architecture, is made up of the raw material of following parts by weight：Cement 15-20
Part, guar gum 3-5 part, vinylacetate-acetate multipolymer 4-7 part, attapulgite clay 30-38 part, zeolite 10-12 part, silicon
Diatomaceous earth 10-13 part, Pulvis Talci 15-20 part, thickening agent 2-3 part, water-retaining agent 1-2 part, penetrating agent 0.5-1 part, polypropylene fibre 2-4
Part, polystyrene fiber 1-3 part.
Further, described crack resistance putty for scraping walls of architecture, is made up of the raw material of following parts by weight：Cement 20-30
Part, guar gum 5-6 part, vinylacetate-acetate multipolymer 7-10 part, attapulgite clay 38-45 part, zeolite 12-15 part, silicon
Diatomaceous earth 13-15 part, Pulvis Talci 20-25 part, thickening agent 3-5 part, water-retaining agent 2-4 part, penetrating agent 1-3 part, polypropylene fibre 4-6
Part, polystyrene fiber 3-5 part.
Further, the granularity of described zeolite is 300 mesh.
Further, described polypropylene fibre length is 12-15mm.
A kind of preparation method of crack resistance putty for scraping walls of architecture, comprises the steps：
(1) measure each raw material by weight respectively；
(2) cement, vinylacetate-acetate multipolymer, polypropylene fibre, polystyrene fiber are added conical double ribbon rotation
Stir in blender, obtain the first mixture；
(3) attapulgite clay, zeolite, kieselguhr, Pulvis Talci, guar gum, thickening agent, water-retaining agent, penetrating agent are added
Stir in conical double ribbon rotation blender, obtain the second mixture；
(4) the second mixture stirring mixing that the first mixture obtaining step (2) and step (3) obtain, obtains outer
Wall water-proof putty powder.
Further, the stir speed (S.S.) in described step (2) is 1500-2000r/min, and mixing time is 45min；Described
Stir speed (S.S.) in step (3) is 2000-3000r/min, and mixing time is 30min；Stir speed (S.S.) in described step (4) is
500-1000r/min, mixing time is 45min.
Beneficial effects of the present invention are：
Adhesive force is good, and gluing power is strong,
(1) polypropylene fibre and polystyrene fiber are favorably improved the cracking resistance of girl's powder body, and it is through vinyl acetate
After use checked by ester-acetate multipolymer, guar gum, thickening agent, water-retaining agent, penetrating agent, can integrally improve the caking property of powder of lacquer putty for use on
Can, and then improve the resistivity to rainwater for the powder of lacquer putty for use on, it is allowed to be difficult to produce crack performance, powder of lacquer putty for use on cracking resistance because of moisture absorption
Good.
(2) attapulgite clay, zeolite, kieselguhr contribute to conserving the moisture of powder body, improve powder body moisture pick-up propertiess, and then
Improve the water-fast pliability of powder of lacquer putty for use on, reduce its drying shrinkage, Pulvis Talci and cement are as matrix skeleton material so that powder body
Intensity is higher.
(3) rationally, each component compatibility is good, and preparation method is simple for the formula that the present invention provides, it is easy to accomplish, product adheres to
Power is strong, and adhesive property is good, and cracking resistance is strong.
Specific embodiment
Purpose, technical scheme and advantage for making the embodiment of the present invention are clearer, below in conjunction with the enforcement of the present invention
Example, is clearly and completely described to the technical scheme in the embodiment of the present invention.Based on the embodiment in the present invention, this area
The every other embodiment that those of ordinary skill is obtained under the premise of not making creative work, broadly falls into present invention protection
Scope.
Embodiment 1：
A kind of crack resistance putty for scraping walls of architecture, is made up of the raw material of following parts by weight：15 parts of cement, 6 parts of guar gum, vinegar
4 parts of vinyl acetate-acetate multipolymer, 45 parts of attapulgite clay, granularity is 10 parts of the zeolite of 300 mesh, 15 parts of kieselguhr, Talcum
15 parts of powder, 5 parts of thickening agent, 1 part of water-retaining agent, 3 parts of penetrating agent, length is 2 parts of the polypropylene fibre of 12-15mm, and polystyrene is fine
5 parts of dimension.
Its preparation method, comprises the steps：
(1) measure each raw material by weight respectively；
(2) cement, vinylacetate-acetate multipolymer, polypropylene fibre, polystyrene fiber are added conical double ribbon rotation
Stir in blender, stir speed (S.S.) is 1800r/min, mixing time is 45min, obtains the first mixture；
(3) attapulgite clay, zeolite, kieselguhr, Pulvis Talci, guar gum, thickening agent, water-retaining agent, penetrating agent are added
Stir in conical double ribbon rotation blender, stir speed (S.S.) is 2400r/min, mixing time is 30min, obtains the second mixture；
(4) the second mixture stirring mixing that the first mixture obtaining step (2) and step (3) obtain, stirring speed
Rate is 900r/min, and mixing time is 45min, obtains waterproof powder of lacquer putty for use on external wall.
Embodiment 2：
A kind of crack resistance putty for scraping walls of architecture, is made up of the raw material of following parts by weight：30 parts of cement, 3 parts of guar gum, vinegar
7 parts of vinyl acetate-acetate multipolymer, 38 parts of attapulgite clay, granularity is 15 parts of the zeolite of 300 mesh, 13 parts of kieselguhr, Talcum
25 parts of powder, 3 parts of thickening agent, 4 parts of water-retaining agent, 1 part of penetrating agent, length is 6 parts of the polypropylene fibre of 12-15mm, and polystyrene is fine
3 parts of dimension.
Its preparation method, comprises the steps：
(1) measure each raw material by weight respectively；
(2) cement, vinylacetate-acetate multipolymer, polypropylene fibre, polystyrene fiber are added conical double ribbon rotation
Stir in blender, stir speed (S.S.) is 1500r/min, mixing time is 45min, obtains the first mixture；
(3) attapulgite clay, zeolite, kieselguhr, Pulvis Talci, guar gum, thickening agent, water-retaining agent, penetrating agent are added
Stir in conical double ribbon rotation blender, stir speed (S.S.) is 3000r/min, mixing time is 30min, obtains the second mixture；
(4) the second mixture stirring mixing that the first mixture obtaining step (2) and step (3) obtain, stirring speed
Rate is 500r/min, and mixing time is 45min, obtains waterproof powder of lacquer putty for use on external wall.
Embodiment 3：
A kind of crack resistance putty for scraping walls of architecture, is made up of the raw material of following parts by weight：15 parts of cement, 5 parts of guar gum, vinegar
10 parts of vinyl acetate-acetate multipolymer, 30 parts of attapulgite clay, granularity is 12 parts of the zeolite of 300 mesh, 10 parts of kieselguhr, sliding
20 parts of stone powder, 2 parts of thickening agent, 2 parts of water-retaining agent, 0.5 part of penetrating agent, length is 4 parts of the polypropylene fibre of 12-15mm, poly- third second
1 part of alkene fiber.
Its preparation method, comprises the steps：
(1) measure each raw material by weight respectively；
(2) cement, vinylacetate-acetate multipolymer, polypropylene fibre, polystyrene fiber are added conical double ribbon rotation
Stir in blender, stir speed (S.S.) is 2000r/min, mixing time is 45min, obtains the first mixture；
(3) attapulgite clay, zeolite, kieselguhr, Pulvis Talci, guar gum, thickening agent, water-retaining agent, penetrating agent are added
Stir in conical double ribbon rotation blender, stir speed (S.S.) is 2000r/min, mixing time is 30min, obtains the second mixture；
(4) the second mixture stirring mixing that the first mixture obtaining step (2) and step (3) obtain, stirring speed
Rate is 1000r/min, and mixing time is 45min, obtains waterproof powder of lacquer putty for use on external wall.
Above example only in order to technical scheme to be described, is not intended to limit；Although with reference to the foregoing embodiments
The present invention has been described in detail, it will be understood by those within the art that：It still can be to aforementioned each enforcement
Technical scheme described in example is modified, or carries out equivalent to wherein some technical characteristics；And these modification or
Replace, do not make the essence of appropriate technical solution depart from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (7)
1. a kind of crack resistance putty for scraping walls of architecture is it is characterised in that be made up of the raw material of following parts by weight：Cement 15-30 part,
Guar gum 3-6 part, vinylacetate-acetate multipolymer 4-10 part, attapulgite clay 30-45 part, zeolite 10-15 part, diatom
Native 10-15 part, Pulvis Talci 15-25 part, thickening agent 2-5 part, water-retaining agent 1-4 part, penetrating agent 0.5-3 part, polypropylene fibre 2-6
Part, polystyrene fiber 1-5 part.
2. crack resistance putty for scraping walls of architecture as claimed in claim 1 is it is characterised in that raw material group by following parts by weight
Become：Cement 15-20 part, guar gum 3-5 part, vinylacetate-acetate multipolymer 4-7 part, attapulgite clay 30-38 part, boiling
Stone 10-12 part, kieselguhr 10-13 part, Pulvis Talci 15-20 part, thickening agent 2-3 part, water-retaining agent 1-2 part, penetrating agent 0.5-1 part,
Polypropylene fibre 2-4 part, polystyrene fiber 1-3 part.
3. crack resistance putty for scraping walls of architecture as claimed in claim 2 is it is characterised in that raw material group by following parts by weight
Become：Cement 20-30 part, guar gum 5-6 part, vinylacetate-acetate multipolymer 7-10 part, attapulgite clay 38-45 part, boiling
Stone 12-15 part, kieselguhr 13-15 part, Pulvis Talci 20-25 part, thickening agent 3-5 part, water-retaining agent 2-4 part, penetrating agent 1-3 part, gather
Tacryl 4-6 part, polystyrene fiber 3-5 part.
4. crack resistance putty for scraping walls of architecture as claimed in claim 1 is it is characterised in that the granularity of described zeolite is 300 mesh.
5. crack resistance putty for scraping walls of architecture as claimed in claim 1 is it is characterised in that described polypropylene fibre length is 12-
15mm.
6. a kind of preparation method of the crack resistance putty for scraping walls of architecture as any one of claim 1-5 it is characterised in that
Comprise the steps：
(1) measure each raw material by weight respectively；
(2) cement, vinylacetate-acetate multipolymer, polypropylene fibre, polystyrene fiber are added conical double ribbon rotation stirring
Stir in machine, obtain the first mixture；
(3) attapulgite clay, zeolite, kieselguhr, Pulvis Talci, guar gum, thickening agent, water-retaining agent, penetrating agent are added taper
Stir in twin-shaft mixer, obtain the second mixture；
(4) the second mixture stirring mixing that the first mixture obtaining step (2) and step (3) obtain, obtains exterior wall resistance to
Water powder of lacquer putty for use on.
7. the preparation method of crack resistance putty for scraping walls of architecture as claimed in claim 6 is it is characterised in that in described step (2)
Stir speed (S.S.) be 1500-2000r/min, mixing time be 45min；Stir speed (S.S.) in described step (3) is 2000-
3000r/min, mixing time is 30min；Stir speed (S.S.) in described step (4) is 500-1000r/min, and mixing time is
45min.