CN109233386A - A kind of spraying method of environmental protection door-plate - Google Patents
A kind of spraying method of environmental protection door-plate Download PDFInfo
- Publication number
- CN109233386A CN109233386A CN201810802198.3A CN201810802198A CN109233386A CN 109233386 A CN109233386 A CN 109233386A CN 201810802198 A CN201810802198 A CN 201810802198A CN 109233386 A CN109233386 A CN 109233386A
- Authority
- CN
- China
- Prior art keywords
- parts
- finishing coat
- plate
- spraying method
- environmental protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of spraying methods of environmentally friendly door-plate first to spray priming after plate surface carries out frosted processing on the door, sprays finishing coat again after waiting drying, last low-temperature bake is dry;Wherein the priming paint is powder of lacquer putty for use on, which includes 30-50 parts of diatomite, 10-15 parts of concave convex rod, without 15-20 parts of styrene, 1-5 parts of ethyl acetate, 1-5 parts of cobalt iso-octoate, 1-5 parts of hydroquinone, 1-5 parts of dimethylbenzene, 15-25 parts of cobalt hydroxide, 10-15 parts of portland cement, 5-6 parts of silica, 2-3 parts of polyvinyl alcohol, 5-8 parts of nano zine oxide and 2-5 parts of rare earth nitrades by weight.Above-mentioned priming paint be a kind of powder of lacquer putty for use on, can quick-drying and Self-leveling, to save the time of polishing.
Description
Technical field
The present invention relates to a kind of technique of door-plate, especially a kind of spraying method of environmentally friendly door-plate.
Background technique
Door-plate, which refers to paint substrate, paints door-plate obtained by laggard drying chamber heat drying.Its general procedure is first to polish,
Then it primes, waits and coat finishing coat again after polishing flat after drying, finally dry.Due to needing to polish after priming paint drying, the time
On more waste, and the drying of finishing coat generally takes 1-2 days, and come into force inefficiency.
Summary of the invention
A kind of spray for the environmentally friendly door-plate for providing quick-drying the purpose of the present invention is to solve above-mentioned the deficiencies in the prior art
Coating method.
To achieve the goals above, the spraying method of a kind of environmentally friendly door-plate designed by the present invention, plate surface carries out on the door
After frosted processing, priming is first sprayed, sprays finishing coat again after waiting drying, last low-temperature bake is dry;The wherein bottom
Paint is powder of lacquer putty for use on, which includes 30-50 parts of diatomite, 10-15 parts of concave convex rod, without 15-20 parts of styrene, second by weight
1-5 parts of acetoacetic ester, 1-5 parts of cobalt iso-octoate, 1-5 parts of hydroquinone, 1-5 parts of dimethylbenzene, 15-25 parts of cobalt hydroxide, silicate cement
10-15 parts of mud, 5-6 parts of silica, 2-3 parts of polyvinyl alcohol, 5-8 parts of nano zine oxide and 2-5 parts of rare earth nitrades;
The finishing coat includes 30-50 parts of phenolic resin, 20-30 parts of epoxy resin, 10-20 parts of nano silver, nanometer two by weight
10-20 parts of titanium oxide, 1-2 parts of dispersing agent, 1-2 parts of methyl polysiloxane, 2-5 parts of carboxymethyl cellulose, silane coupling agent 2-3
Part, 2-5 parts of fluorin modified crylic acid ester, 1-5 parts of lanthana, 1-5 parts of silver oxide and 60-70 parts of Porous deproteinized bone, vegetable oil 20-30
Part.
Dispersing agent in the finishing coat is polyphosphate or polyacrylic acid sodium salt.
The low-temperature bake temperature of the finishing coat is 80 DEG C, time 30min.
The preparation method of the priming paint is by 30-50 parts of diatomite, 10-15 parts of concave convex rod, without 15-20 parts of styrene, second
1-5 parts of acetoacetic ester, 1-5 parts of cobalt iso-octoate, 1-5 parts of hydroquinone, 1-5 parts of dimethylbenzene, 15-25 parts of cobalt hydroxide, silicate cement
2-5 parts of 10-15 parts of mud, 5-6 parts of silica, 2-3 parts of polyvinyl alcohol, 5-8 parts of nano zine oxide and rare earth nitrades are simultaneously
It is put into mixer, utilizes centrifugal three axis blender mix 5-15 minutes.
The preparation method of the finishing coat is 30-50 parts of phenolic resin, 20-30 parts of epoxy resin, 10-20 parts of nano silver, receives
10-20 parts of titanium dioxide of rice, 1-5 parts of lanthana, 1-5 parts of silver oxide and 60-70 parts of Porous deproteinized bone, 20-30 parts of vegetable oil are simultaneously
Low-temperature heat stirring is carried out into reactor tank, whipping temp is 100-150 DEG C, mixing time 30-60min, waits until above-mentioned mixing
After liquid natural cooling, 1-2 parts of dispersing agent, 1-2 parts of methyl polysiloxane, 2-5 parts of carboxymethyl cellulose, silane coupling agent are added
2-3 parts, 2-5 parts of fluorin modified crylic acid ester put into grinder after stirring 5-10min at 60-80 DEG C and grind 10-15min,
Finishing coat is obtained after sieving.
The spraying method for the environmentally friendly door-plate that the present invention obtains first sprays priming after plate surface carries out frosted processing on the door,
Deng spraying upper finishing coat again after dry, last low-temperature bake is dry.The priming paint is a kind of powder of lacquer putty for use on, being capable of quick-drying and gravity flow
It is flat, to save the time of polishing.The finishing coat has the characteristics of quick-drying, and drying time can be become to half from original 1-2 days
Hour.
Specific embodiment
Below with reference to embodiment, the present invention is further described.
Embodiment 1:
A kind of spraying method of environmentally friendly door-plate provided in this embodiment, after plate surface carries out frosted processing on the door, first sprays upper bottom
Paint sprays finishing coat after waiting drying again, and last low-temperature bake is dry;Wherein the priming paint is powder of lacquer putty for use on, which presses
Parts by weight include 30 parts of diatomite, 10 parts of concave convex rod, without 15 parts of styrene, 1 part of ethyl acetate, 1 part of cobalt iso-octoate, hydroquinone
1 part, 1 part of dimethylbenzene, 15 parts of cobalt hydroxide, 10 parts of portland cement, 5 parts of silica, 2 parts of polyvinyl alcohol, nano zine oxide 5
Part and 2 parts of rare earth nitrades;
The finishing coat includes 30 parts of phenolic resin, 20 parts of epoxy resin, 10 parts of nano silver, nano-titanium dioxide 10 by weight
Part, 1 part of dispersing agent, 1 part of methyl polysiloxane, 2 parts of carboxymethyl cellulose, 2 parts of silane coupling agent, 2 parts of fluorin modified crylic acid ester,
60 parts of 1 part of lanthana, 1 part of silver oxide and Porous deproteinized bone, 20 parts of vegetable oil.
Dispersing agent in the finishing coat is polyphosphate or polyacrylic acid sodium salt.
The low-temperature bake temperature of the finishing coat is 80 DEG C, time 30min.
The preparation method of the priming paint be by 30 parts of diatomite, 10 parts of concave convex rod, without 15 parts of styrene, 1 part of ethyl acetate,
1 part of cobalt iso-octoate, 1 part of dimethylbenzene, 15 parts of cobalt hydroxide, 10 parts of portland cement, 5 parts of silica, gathers 1 part of hydroquinone
2 parts of vinyl alcohol, 5 parts of nano zine oxide and 2 parts of rare earth nitrades are put into mixer simultaneously, utilize centrifugal three axis blender
Mix 5-15 minutes.
The preparation method of the finishing coat is 30 parts of phenolic resin, 20 parts of epoxy resin, 10 parts of nano silver, nano-titanium dioxide
60 parts of 10 parts, 1 part of lanthana, 1 part of silver oxide and Porous deproteinized bone, 20 parts of vegetable oil carry out low-temperature heat into reactor tank simultaneously and stir
It mixes, whipping temp is 100-150 DEG C, mixing time 30-60min, after above-mentioned mixed liquor natural cooling, adds dispersing agent
1 part, 1 part of methyl polysiloxane, 2 parts of carboxymethyl cellulose, 2 parts of silane coupling agent, 2 parts of fluorin modified crylic acid ester, in 60-80
It is put into grinder after stirring 5-10min at DEG C and grinds 10-15min, obtain finishing coat after sieving.
Embodiment 2:
A kind of spraying method of environmentally friendly door-plate provided in this embodiment, substantially ingredient is same as Example 1, and difference is institute
Stating priming paint is powder of lacquer putty for use on, which includes 50 parts of diatomite, 15 parts of concave convex rod, without 20 parts of styrene, acetic acid second by weight
5 parts of ester, 5 parts of cobalt iso-octoate, 5 parts of hydroquinone, 5 parts of dimethylbenzene, 25 parts of cobalt hydroxide, 15 parts of portland cement, silica 6
Part, 3 parts of polyvinyl alcohol, 8 parts of nano zine oxide and 5 parts of rare earth nitrades.
Embodiment 3:
A kind of spraying method of environmentally friendly door-plate provided in this embodiment, substantially ingredient is same as Example 1, and difference is institute
Stating finishing coat by weight includes 50 parts of phenolic resin, 30 parts of epoxy resin, 20 parts of nano silver, 20 parts of nano-titanium dioxide, dispersion
2 parts of agent, 2 parts of methyl polysiloxane, 5 parts of carboxymethyl cellulose, 3 parts of silane coupling agent, 5 parts of fluorin modified crylic acid ester, lanthana 5
Part, 5 parts of silver oxide and 70 parts of Porous deproteinized bone, 30 parts of vegetable oil.
Claims (5)
1. a kind of spraying method of environmental protection door-plate, it is characterised in that: after plate surface carries out frosted processing on the door, first spray upper bottom
Paint sprays finishing coat after waiting drying again, and last low-temperature bake is dry;Wherein the priming paint is powder of lacquer putty for use on, which presses
Parts by weight include 30-50 parts of diatomite, 10-15 parts of concave convex rod, without 15-20 parts of styrene, 1-5 parts of ethyl acetate, cobalt iso-octoate
1-5 parts, 1-5 parts of hydroquinone, 1-5 parts of dimethylbenzene, 15-25 parts of cobalt hydroxide, 10-15 parts of portland cement, silica 5-6
Part, 2-3 parts of polyvinyl alcohol, 5-8 parts of nano zine oxide and 2-5 parts of rare earth nitrades;
The finishing coat includes 30-50 parts of phenolic resin, 20-30 parts of epoxy resin, 10-20 parts of nano silver, nanometer two by weight
10-20 parts of titanium oxide, 1-2 parts of dispersing agent, 1-2 parts of methyl polysiloxane, 2-5 parts of carboxymethyl cellulose, silane coupling agent 2-3
Part, 2-5 parts of fluorin modified crylic acid ester, 1-5 parts of lanthana, 1-5 parts of silver oxide and 60-70 parts of Porous deproteinized bone, vegetable oil 20-30
Part.
2. the spraying method of environmental protection door-plate according to claim 1, it is characterised in that: the dispersing agent in the finishing coat is poly-
Phosphate or polyacrylic acid sodium salt.
3. the spraying method of environmental protection door-plate according to claim 1 or 2, it is characterised in that: the low-temperature bake of the finishing coat
Temperature is 80 DEG C, time 30min.
4. it is according to claim 1 environmental protection door-plate spraying method, it is characterised in that: the preparation method of the priming paint be by
30-50 parts of diatomite, 10-15 parts of concave convex rod, without 15-20 parts of styrene, 1-5 parts of ethyl acetate, 1-5 parts of cobalt iso-octoate, to benzene
1-5 parts of diphenol, 1-5 parts of dimethylbenzene, 15-25 parts of cobalt hydroxide, 10-15 parts of portland cement, 5-6 parts of silica, polyethylene
2-3 parts of alcohol, 5-8 parts of nano zine oxide and 2-5 parts of rare earth nitrades are put into mixer simultaneously, are stirred using centrifugal three axis
Machine mix 5-15 minutes.
5. the spraying method of environmental protection door-plate according to claim 1, it is characterised in that: the preparation method of the finishing coat is phenol
30-50 parts of urea formaldehyde, 20-30 parts of epoxy resin, 10-20 parts of nano silver, 10-20 parts of nano-titanium dioxide, 1-5 parts of lanthana,
1-5 parts of silver oxide and 60-70 parts of Porous deproteinized bone, 20-30 parts of vegetable oil carry out low-temperature heat stirring, stirring into reactor tank simultaneously
Temperature is 100-150 DEG C, mixing time 30-60min, after the above-mentioned mixed liquor natural cooling, add 1-2 parts of dispersing agent,
1-2 parts of methyl polysiloxane, 2-5 parts of carboxymethyl cellulose, 2-3 parts of silane coupling agent, 2-5 parts of fluorin modified crylic acid ester,
It is put into grinder after stirring 5-10min at 60-80 DEG C and grinds 10-15min, obtain finishing coat after sieving.