CN106947355A - Environmentally friendly baking vanish door-plate and its manufacturing process with sterilizing function - Google Patents
Environmentally friendly baking vanish door-plate and its manufacturing process with sterilizing function Download PDFInfo
- Publication number
- CN106947355A CN106947355A CN201710101910.2A CN201710101910A CN106947355A CN 106947355 A CN106947355 A CN 106947355A CN 201710101910 A CN201710101910 A CN 201710101910A CN 106947355 A CN106947355 A CN 106947355A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- priming paint
- environmentally friendly
- plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environmentally friendly baking vanish door-plate with sterilizing function, including substrate, it is characterised in that:The substrate outer application has priming paint, and being baked in the outer side spray of priming paint has finish paint, and the priming paint includes following components by weight:50 60 parts of modified epoxy, 10 20 parts of nano zine oxide, 10 20 parts of organosilicon, 25 parts of rare earth nitrades, 12 parts of dispersant, 12 parts of defoamer, 25 parts of thickener, 25 parts of levelling agent;The finish paint includes following components by weight:50 70 parts of phenol-formaldehyde resin modified, 10 20 parts of Nano Silver, 10 20 parts of nano titanium oxide, 12 parts of dispersant, 12 parts of defoamer, 25 parts of thickener, 25 parts of levelling agent.The reasonable raw material proportioning of priming paint and finish paint wherein in the present invention, can kill the germs such as staphylococcus aureus and Escherichia coli, antibiotic rate is up to more than 98%, and significantly, environmental pollution is few for antibacterial effect.
Description
Technical field
The present invention relates to a kind of door-plate, environmentally friendly baking vanish door-plate and its manufacturing process particularly with sterilizing function.
Background technology
Baking vanish door-plate, which refers to paint substrate, paint door-plate obtained by laggard drying room heat drying.Due to baking vanish door-plate color and luster
Bright-coloured to be easy to moulding, with very strong visual impact, even water resistance is splendid when very attractive in appearance, and stain resistance is strong, Yi Qing
Wash, so can all be applied to baking vanish door-plate in many places.
But always inevitably grown on door-plate and breed the fatal bacterium such as golden color staphylococcus, Escherichia coli
And black-koji mould, green pus mould, saccharomycete etc., in particular for dining table, computer desk, chess and card table, desk, bathroom door
The door-plate surface of plate, kitchen kitchen tools, fatal bacterium and mould it is more, directly affect the healthy of people, trigger
The generation and infection of disease.
The content of the invention
The invention aims to solve above-mentioned the deficiencies in the prior art and provide a kind of sterilization ability it is good, production facility
Environmentally friendly baking vanish door-plate with sterilizing function and its manufacturing process.
To achieve these goals, the environmentally friendly baking vanish door-plate with sterilizing function designed by the present invention, including substrate, institute
Stating substrate outer application has priming paint, and being baked in the outer side spray of priming paint has finish paint, and the priming paint includes following components by weight:Change
50-60 parts of epoxy resin of property, 10-20 parts of nano zine oxide, 10-20 parts of organosilicon, 2-5 parts of rare earth nitrades, dispersant 1-2
Part, 1-2 parts of defoamer, 2-5 parts of thickener, 2-5 parts of levelling agent;Wherein nano zine oxide and organosilicon have synergy, two
Person can effectively improve the anti-microbial property of priming paint under the catalytic action of rare earth nitrades.
The finish paint includes following components by weight:50-70 parts of phenol-formaldehyde resin modified, 10-20 parts of Nano Silver, nanometer
10-20 parts of titanium dioxide, 1-2 parts of dispersant, 1-2 parts of defoamer, 2-5 parts of thickener, 2-5 parts of levelling agent;Wherein nano
Silver and nano titanium oxide can improve the hydrophobicity of finish paint, and the breeding environment of bacterium can be impacted.
Above-mentioned dispersant is polyphosphate or polyacrylic acid sodium salt, defoamer are that methyl polysiloxane, thickener are carboxylic
Methylcellulose, levelling agent are fluorin modified crylic acid ester.
The priming paint is the priming paint with antibacterial, sterilizing function, and the finish paint is with hydrophobic, antibacterial functions finish paints.
The hydrophobic effect of such finish paint can for door-plate environment not moisture-sensitive, thus the possibility of surface breed bacteria is also significantly
Reduce, and finish paint and priming paint are respectively provided with antibacterial functions, bacterium once touches door-plate, also can because the antibacterial in priming paint and finish paint,
Sterile material and it is dead.
The modified epoxy includes following components by weight:80 parts of epoxy resin, 5 parts of lanthana, silver oxide 5
5 parts of part, 5 parts of phosphoric acid and polyethylene glycol.Silver oxide in the modified epoxy equally plays a part of antibacterial, and lanthana
Then play a part of catalysis so that the antibacterial effect of silver oxide mentions raising, and phosphoric acid then improves levelability.
The phenol-formaldehyde resin modified includes following components by weight:90 parts of phenolic resin, 3 parts of cerium oxide, silane are even
Join 5 parts of 2 parts of agent and ethyl silicon oil.Cerium oxide in the phenol-formaldehyde resin modified enable to phenolic resin corrosion resistance and
Hydrophobicity is improved, so as to strengthen the hydrophobicity of finish paint.
A kind of manufacturing process of above-mentioned environmentally friendly baking vanish door-plate with sterilizing function, comprises the following steps:
Weigh by weight first, by 80 parts of epoxy resin, 5 parts of lanthana, 5 parts of silver oxide, 5 parts of phosphoric acid and polyethylene glycol
5 parts of mixings obtain modified epoxy, stand-by;It is same by 90 parts of phenolic resin, 3 parts of cerium oxide, 2 parts of silane coupler
It is stand-by and 5 parts of mixings of ethyl silicon oil obtain phenol-formaldehyde resin modified;
Then by 50-60 parts of modified epoxy, 10-20 parts of nano zine oxide, 10-20 parts of organosilicon, 2-5 parts of rare earth nitrades
It is put into retort and carries out heating stirring, whipping temp is 160-180 DEG C, mixing time 30-60min, when above-mentioned mixing
After liquid natural cooling, 1-2 parts of dispersant, 1-2 parts of defoamer, 2-5 parts of thickener, 2-5 parts of levelling agent are added, at 60-80 DEG C
Priming paint is obtained after grinding 10-15min, sieving in input grinder after stirring 5-10min;
Then 50-70 parts of phenol-formaldehyde resin modified, 10-20 parts of Nano Silver, 10-20 parts of nano titanium oxide are equally put into reaction
Heating stirring is carried out in tank, whipping temp is 200-250 DEG C, mixing time 30-60min, when above-mentioned mixed liquor natural cooling
Afterwards, 1-2 parts of dispersant, 1-2 parts of defoamer, 2-5 parts of thickener, 2-5 parts of levelling agent are added, 5- is stirred at 60-80 DEG C
Put into after 10min after grinding 10-15min, sieving in grinder and obtain finish paint;
Finally the first spray-applied primer on the outside of substrate, is dried when after preliminarily dried, putting barn into, and baking temperature is 30 DEG C, baking
Time is 6-8h, then is so repeated twice the roasting priming paint of progress spray, then bakes an aspect paint, preliminarily dried in the outer side spray of priming paint
Afterwards, put barn into dry, baking temperature is 80 DEG C, and baking time is 6-8h, be so repeated a further three times the roasting finish paint of progress spray, finally
The environmentally friendly baking vanish door-plate with sterilizing function is obtained after sanding, polishing grinding.
The environmentally friendly baking vanish door-plate with sterilizing function that the present invention is obtained, it is had the technical effect that by priming paint and finish paint
Anti-biotic material is added, so as to improve the anti-microbial property of baking vanish door-plate.The raw material proportioning of priming paint and finish paint wherein in the present invention
Rationally, the germs such as staphylococcus aureus and Escherichia coli can be killed, antibiotic rate is up to more than 98%, and antibacterial effect is notable, to ring
Border pollution is few.
Embodiment
With reference to embodiment, the present invention is further described.
Embodiment 1:
The environmentally friendly baking vanish door-plate with sterilizing function that the present embodiment is provided, including substrate, the substrate outer application have priming paint,
Being baked in the outer side spray of priming paint has finish paint, and the priming paint includes following components by weight:50 parts of modified epoxy, nano oxygen
Change 10 parts of zinc, 10 parts of organosilicon, 5 parts of gadolinium nitrate, 2 parts of polyphosphate, 2 parts of methyl polysiloxane, 5 parts of carboxymethyl cellulose, fluorine
5 parts of modification acrylate;The finish paint includes following components by weight:50 parts of phenol-formaldehyde resin modified, 10 parts of Nano Silver, receive
10 parts of titanium dioxide of rice, 1 part of polyacrylic acid sodium salt, 1 part of methyl polysiloxane, 5 parts of carboxymethyl cellulose, fluorin modified crylic acid ester
5 parts;
The modified epoxy includes following components by weight:80 parts of epoxy resin, 5 parts of lanthana, 5 parts of silver oxide,
5 parts of 5 parts of phosphoric acid and polyethylene glycol.
The phenol-formaldehyde resin modified includes following components by weight:90 parts of phenolic resin, 3 parts of cerium oxide, silane are even
Join 5 parts of 2 parts of agent and ethyl silicon oil.
A kind of manufacturing process of above-mentioned environmentally friendly baking vanish door-plate with sterilizing function, comprises the following steps:
Weigh by weight first, by 80 parts of epoxy resin, 5 parts of lanthana, 5 parts of silver oxide, 5 parts of phosphoric acid and polyethylene glycol
5 parts of mixings obtain modified epoxy, stand-by;It is same by 90 parts of phenolic resin, 3 parts of cerium oxide, 2 parts of silane coupler
It is stand-by and 5 parts of mixings of ethyl silicon oil obtain phenol-formaldehyde resin modified;
Then 50 parts of modified epoxy, 10 parts of nano zine oxide, 10 parts of organosilicon, 5 parts of rare earth nitrades are put into reaction
Heating stirring is carried out in tank, whipping temp is 160-180 DEG C, mixing time 30-60min, when above-mentioned mixed liquor natural cooling
Afterwards, 2 parts of polyphosphate, 2 parts of methyl polysiloxane, 5 parts of carboxymethyl cellulose, 5 parts of fluorin modified crylic acid ester are added, in 60-80
Stirred at DEG C and obtain priming paint after grinding 10-15min, sieving in input grinder after 5-10min;
Then same 50 parts of phenol-formaldehyde resin modified, 10 parts of Nano Silver, 10 parts of nano titanium oxide are put into retort is carried out
Heating stirring, whipping temp is 200-250 DEG C, mixing time 30-60min, poly- when after above-mentioned mixed liquor natural cooling, adding
1 part of acrylic acid sodium salt, 1 part of methyl polysiloxane, 5 parts of carboxymethyl cellulose, 5 parts of fluorin modified crylic acid ester, at 60-80 DEG C
Finish paint is obtained after grinding 10-15min, sieving in input grinder after stirring 5-10min;
Finally the first spray-applied primer on the outside of substrate, is dried when after preliminarily dried, putting barn into, and baking temperature is 30 DEG C, baking
Time is 8h, then is so repeated twice the roasting priming paint of progress spray, then after the outer side spray of priming paint bakes an aspect paint, preliminarily dried,
Put barn into dry, baking temperature is 80 DEG C, and baking time is 8h, be so repeated a further three times the roasting finish paint of progress spray, eventually pass
The environmentally friendly baking vanish door-plate with sterilizing function is obtained after sanding, polishing grinding.
Detection method:According to《GB 21866-2008-T antibiotic paints (paint film) antibiotic property determination method and antibacterial effect》,
By liftout inoculated bacteria on model to be tested, bacterium is set uniformly to contact model with the method for pad pasting, by certain time
After culture, the viable count in detection model, and calculate the antibacterium rate of model.The door by antimicrobial component is not added with is needed simultaneously
Plate is as blank group, and bacterium is using staphylococcus aureus and Escherichia coli as test bacterium.
Testing result:
Antibacterium rate(Staphylococcus aureus)=(Blank group-experimental group)/ blank group * 100%=98.6%.
Antibacterium rate(Escherichia coli)=(Blank group-experimental group)/ blank group * 100%=99.96%.
Embodiment 2:
The environmentally friendly baking vanish door-plate with sterilizing function and its manufacturing process that the present embodiment is provided are substantially same as Example 1, its
Main distinction point is:The priming paint includes following components by weight:60 parts of modified epoxy, nano zine oxide 20
Part, 20 parts of organosilicon, 3 parts of neodymium nitrate, 2 parts of polyphosphate, 2 parts of methyl polysiloxane, 3 parts of carboxymethyl cellulose, fluorine richness third
4 parts of olefin(e) acid ester;The finish paint includes following components by weight:70 parts of phenol-formaldehyde resin modified, 20 parts of Nano Silver, nano-silica
Change 20 parts of titanium, 1 part of polyphosphate, 1 part of methyl polysiloxane, 3 parts of carboxymethyl cellulose, 3 parts of fluorin modified crylic acid ester.
Testing result:
Antibacterium rate(Staphylococcus aureus)=(Blank group-experimental group)/ blank group * 100%=99.2%.
Antibacterium rate(Escherichia coli)=(Blank group-experimental group)/ blank group * 100%=99.98%.
Embodiment 3:
The environmentally friendly baking vanish door-plate with sterilizing function and its manufacturing process that the present embodiment is provided are substantially same as Example 1, its
Main distinction point is:60 parts of modified epoxy, 15 parts of nano zine oxide, 20 parts of organosilicon, 5 parts of samaric nitrate, polyphosphate 2
Part, 2 parts of methyl polysiloxane, 4 parts of carboxymethyl cellulose, 4 parts of fluorin modified crylic acid ester;The finish paint by weight include with
Lower component:60 parts of phenol-formaldehyde resin modified, 20 parts of Nano Silver, 15 parts of nano titanium oxide, 1 part of polyphosphate, methyl polysiloxane 2
Part, 4 parts of carboxymethyl cellulose, 4 parts of fluorin modified crylic acid ester.
Testing result:
Antibacterium rate(Staphylococcus aureus)=(Blank group-experimental group)/ blank group * 100%=98.5%.
Antibacterium rate(Escherichia coli)=(Blank group-experimental group)/ blank group * 100%=99.93%.
Embodiment 4:
The environmentally friendly baking vanish door-plate with sterilizing function and its manufacturing process that the present embodiment is provided are substantially same as Example 1, its
Main distinction point is:60 parts of modified epoxy, 15 parts of nano zine oxide, 15 parts of organosilicon, 4 parts of neodymium nitrate, polyacrylic acid
2 parts of sodium salt, 22 parts of methyl polysiloxane, 3 parts of carboxymethyl cellulose, 3 parts of fluorin modified crylic acid ester;The finish paint is by weight
Including following components:60 parts of phenol-formaldehyde resin modified, 10 parts of Nano Silver, 18 parts of nano titanium oxide, 2 parts of polyphosphate, methyl gather
2 parts of siloxanes, 5 parts of carboxymethyl cellulose, 4 parts of fluorin modified crylic acid ester.
Testing result:
Antibacterium rate(Staphylococcus aureus)=(Blank group-experimental group)/ blank group * 100%=99.5%.
Antibacterium rate(Escherichia coli)=(Blank group-experimental group)/ blank group * 100%=99.96%.
Claims (3)
1. a kind of environmentally friendly baking vanish door-plate with sterilizing function, including substrate, it is characterised in that:The substrate outer application has bottom
Paint, being baked in the outer side spray of priming paint has finish paint, and the priming paint includes following components by weight:50-60 parts of modified epoxy,
10-20 parts of nano zine oxide, 10-20 parts of organosilicon, 2-5 parts of rare earth nitrades, 1-2 parts of dispersant, 1-2 parts of defoamer, thickening
2-5 parts of agent, 2-5 parts of levelling agent;The finish paint includes following components by weight:50-70 parts of phenol-formaldehyde resin modified, Nano Silver
10-20 parts, 10-20 parts of nano titanium oxide, 1-2 parts of dispersant, 1-2 parts of defoamer, 2-5 parts of thickener, 2-5 parts of levelling agent;
Wherein above-mentioned dispersant is polyphosphate or polyacrylic acid sodium salt, defoamer are that methyl polysiloxane, thickener are carboxymethyl
Cellulose, levelling agent are fluorin modified crylic acid ester.
2. the environmentally friendly baking vanish door-plate according to claim 1 with sterilizing function, it is characterised in that:The modified epoxy tree
Fat includes following components by weight:80 parts of epoxy resin, 5 parts of lanthana, 5 parts of silver oxide, 5 parts of phosphoric acid and polyethylene glycol
5 parts;
The phenol-formaldehyde resin modified includes following components by weight:90 parts of phenolic resin, 3 parts of cerium oxide, silane coupler 2
5 parts of part and ethyl silicon oil.
3. a kind of manufacturing process of the environmentally friendly baking vanish door-plate as claimed in claim 2 with sterilizing function, it is characterised in that bag
Include following steps:
Weigh by weight first, by 80 parts of epoxy resin, 5 parts of lanthana, 5 parts of silver oxide, 5 parts of phosphoric acid and polyethylene glycol
5 parts of mixings obtain modified epoxy, stand-by;It is same by 90 parts of phenolic resin, 3 parts of cerium oxide, 2 parts of silane coupler
It is stand-by and 5 parts of mixings of ethyl silicon oil obtain phenol-formaldehyde resin modified;
Then by 50-60 parts of modified epoxy, 10-20 parts of nano zine oxide, 10-20 parts of organosilicon, 2-5 parts of rare earth nitrades
It is put into retort and carries out heating stirring, whipping temp is 160-180 DEG C, mixing time 30-60min, when above-mentioned mixing
After liquid natural cooling, 1-2 parts of dispersant, 1-2 parts of defoamer, 2-5 parts of thickener, 2-5 parts of levelling agent are added, at 60-80 DEG C
Priming paint is obtained after grinding 10-15min, sieving in input grinder after stirring 5-10min;
Then 50-70 parts of phenol-formaldehyde resin modified, 10-20 parts of Nano Silver, 10-20 parts of nano titanium oxide are equally put into reaction
Heating stirring is carried out in tank, whipping temp is 200-250 DEG C, mixing time 30-60min, when above-mentioned mixed liquor natural cooling
Afterwards, 1-2 parts of dispersant, 1-2 parts of defoamer, 2-5 parts of thickener, 2-5 parts of levelling agent are added, 5- is stirred at 60-80 DEG C
Put into after 10min after grinding 10-15min, sieving in grinder and obtain finish paint;
Finally the first spray-applied primer on the outside of substrate, is dried when after preliminarily dried, putting barn into, and baking temperature is 30 DEG C, baking
Time is 6-8h, then is so repeated twice the roasting priming paint of progress spray, then bakes an aspect paint, preliminarily dried in the outer side spray of priming paint
Afterwards, put barn into dry, baking temperature is 80 DEG C, and baking time is 6-8h, be so repeated a further three times the roasting finish paint of progress spray, finally
The environmentally friendly baking vanish door-plate with sterilizing function is obtained after sanding, polishing grinding.