CN106867407B - A kind of bamboo and wood processing oil paint and preparation method thereof - Google Patents
A kind of bamboo and wood processing oil paint and preparation method thereof Download PDFInfo
- Publication number
- CN106867407B CN106867407B CN201710272397.3A CN201710272397A CN106867407B CN 106867407 B CN106867407 B CN 106867407B CN 201710272397 A CN201710272397 A CN 201710272397A CN 106867407 B CN106867407 B CN 106867407B
- Authority
- CN
- China
- Prior art keywords
- parts
- added
- powder
- bamboo
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of environment-friendly type bamboo and wood processing oil paints and preparation method thereof, paint component includes 40-60 parts of natural resin in parts by weight, 5-10 parts of titanium dioxide, 8-12 parts of white carbon black, 10-20 parts of turpentine oil, 10-25 parts of polyethyleneimine, 10-20 parts of nano-zinc oxide powder, 5-15 parts of cellulose acetate, 8-12 parts of adhesive, 10-20 parts of modified Nano diatomite in powder, 10-25 parts of sodium carboxymethylcellulose, 1-4 parts of levelling agent, 5-15 parts and 8-17 parts of modified polyorganosiloxane of bean plant short oil class alkyd resin, preparation process of the present invention is simple, preparation process is environment friendly and pollution-free, paint obtained is environment-protecting and non-poisonous, with moisture resistance waterproof, anti-aging, wear-resisting feature, coated on bamboo and wood products surface, it is able to extend the use of bamboo and wood products Service life.
Description
Technical field
The present invention relates to bamboo and wood processing oil paint preparation technical field, specially a kind of bamboo and wood processing oil paint and its preparation
Method.
Background technique
Bamboo and wood products refer to that with bamboo be the process raw material product of manufacture, mostly daily necessities, such as chopsticks, chopsticks cage, chopping block, cool
Seat, tea cup mat, curtain etc., bamboo flooring popular in recent years and bamboo furniture etc., also some values are higher, such as bamboo carving
Craftwork.The bamboo and wood products processed need to coat one layer of paint on its surface, and bamboo and wood products in the prior art paint
Poor, wear-resisting, the anti-scratch effect of environmental-protecting performance is poor, causes bamboo and wood products' service life short.
Summary of the invention
The purpose of the present invention is to provide a kind of bamboo and wood processing oil paints and preparation method thereof, to solve above-mentioned background technique
The problem of middle proposition.
To achieve the above object, the invention provides the following technical scheme: a kind of bamboo and wood processing oil paint, paint component is by weight
Measuring number includes 40-60 parts of natural resin, 5-10 parts of titanium dioxide, 8-12 parts of white carbon black, 10-20 parts of turpentine oil, polyethyleneimine
10-25 parts, 10-20 parts of nano-zinc oxide powder, 5-15 parts of cellulose acetate, 8-12 parts of adhesive, modified Nano diatomite in powder
10-20 parts, 10-25 parts of sodium carboxymethylcellulose, 1-4 parts of levelling agent, 5-15 parts of bean plant short oil class alkyd resin and change
8-17 parts of polysiloxanes of property；
Preparation method includes the following steps:
A, natural resin, titanium dioxide, white carbon black, nano-zinc oxide powder, modified Nano diatomite in powder, bean plant is short
It is added in stirred tank and is stirred after the mixing of oils alkyd resin, stirring rate is 1000-2000 revs/min, and mixing time is
10min-30min obtains mixture A；
B, turpentine oil, polyethyleneimine, cellulose acetate, adhesive are added in mixture A, grinder is added after mixing
Middle grinding 20-40min, obtains mixture B；
C, mixture B is added in kneading machine later and is kneaded, melting temperature is 55 DEG C -75 DEG C, mixing time 10min-
30min；30min is stood after being slowly cooled to room temperature later；
D, sodium carboxymethylcellulose, levelling agent, modified poly- silicon oxygen are finally sequentially added in the mixture that step C is obtained
Alkane is added heating vessel in heating, is stirred continuously in heating process after mixing；Constant temperature 20min, is again heated to after being heated to 50 DEG C
Constant temperature 10min after 80 DEG C after being slowly cooled to room temperature later, stands 1h to get environment protection oil paint is arrived.
Preferably, preferred composition proportion are as follows: 50 parts of natural resin, 8 parts of titanium dioxide, 10 parts of white carbon black, 15 parts of turpentine oil,
17 parts of polyethyleneimine, 15 parts of nano-zinc oxide powder, 10 parts of cellulose acetate, 10 parts of adhesive, modified Nano diatomite in powder
15 parts, 17 parts of sodium carboxymethylcellulose, 3 parts of levelling agent, 10 parts of bean plant short oil class alkyd resin and modified polyorganosiloxane
13 parts.
Compared with prior art, the beneficial effects of the present invention are: preparation process of the present invention is simple, the environmentally friendly no dirt of preparation process
Dye, paint obtained is environment-protecting and non-poisonous, has the characteristics that moisture resistance waterproof, anti-aging, wear-resisting, can coated on bamboo and wood products surface
Extend the service life of bamboo and wood products, the titanium dioxide of addition can further enhance the antiseptic property of paint；The nano oxygen of addition
Changing zinc, modified Nano diatomite in powder has the effect of antibacterial bacteriostatic, taste of dispelling anti-enzyme, be able to extend the storage time 2 years of paint with
On；The sodium carboxymethylcellulose of addition, it can be ensured that the stability and uniformity of viscosity are painted, to improve paint application efficiency
30% or more；In addition, being added with bean plant short oil class alkyd resin in the present invention, it can prevent bamboo and wood products surface paint from opening
It splits；The modified polyorganosiloxane of addition can further increase paint wear-resisting property and anti-scratch performance.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
Art personnel every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
The invention provides the following technical scheme: a kind of bamboo and wood processing oil paint, paint component includes natural in parts by weight
40-60 parts of resin, 5-10 parts of titanium dioxide, 8-12 parts of white carbon black, 10-20 parts of turpentine oil, 10-25 parts of polyethyleneimine, nano oxygen
Change zinc powder 10-20 parts, 5-15 parts of cellulose acetate, 8-12 parts of adhesive, 10-20 parts of modified Nano diatomite in powder, carboxymethyl
10-25 parts of sodium cellulosate, 1-4 parts of levelling agent, 5-15 parts of bean plant short oil class alkyd resin and modified polyorganosiloxane 8-17
Part.
Embodiment one:
Paint component includes 40 parts of natural resin, 5 parts of titanium dioxide, 8 parts of white carbon black, 10 parts of turpentine oil, gathers in parts by weight
10 parts of aziridine, 10 parts of nano-zinc oxide powder, 5 parts of cellulose acetate, 8 parts of adhesive, 10 parts of modified Nano diatomite in powder,
10 parts of sodium carboxymethylcellulose, 1 part of levelling agent, 5 parts and 8 parts of modified polyorganosiloxane of bean plant short oil class alkyd resin.
The preparation method of the present embodiment the following steps are included:
A, natural resin, titanium dioxide, white carbon black, nano-zinc oxide powder, modified Nano diatomite in powder, bean plant is short
It is added in stirred tank and is stirred after the mixing of oils alkyd resin, stirring rate is 1000 revs/min, and mixing time is
10minmin obtains mixture A；
B, turpentine oil, polyethyleneimine, cellulose acetate, adhesive are added in mixture A, grinder is added after mixing
Middle grinding 20min, obtains mixture B；
C, mixture B is added in kneading machine later and is kneaded, melting temperature is 55 DEG C, mixing time 10min；Delay later
30min is stood after slow cool down to room temperature；
D, sodium carboxymethylcellulose, levelling agent, modified poly- silicon oxygen are finally sequentially added in the mixture that step C is obtained
Alkane is added heating vessel in heating, is stirred continuously in heating process after mixing；Constant temperature 20min, is again heated to after being heated to 50 DEG C
Constant temperature 10min after 80 DEG C after being slowly cooled to room temperature later, stands 1h to get environment protection oil paint is arrived.
Embodiment two:
Paint component include in parts by weight 60 parts of natural resin, 10 parts of titanium dioxide, 12 parts of white carbon black, 20 parts of turpentine oil,
25 parts of polyethyleneimine, 20 parts of nano-zinc oxide powder, 15 parts of cellulose acetate, 12 parts of adhesive, modified Nano diatomite in powder
20 parts, 25 parts of sodium carboxymethylcellulose, 4 parts of levelling agent, 15 parts of bean plant short oil class alkyd resin and modified polyorganosiloxane
17 parts.
The preparation method of the present embodiment the following steps are included:
A, natural resin, titanium dioxide, white carbon black, nano-zinc oxide powder, modified Nano diatomite in powder, bean plant is short
It is added in stirred tank and is stirred after the mixing of oils alkyd resin, stirring rate is 2000 revs/min, and mixing time 30min is obtained
To mixture A；
B, turpentine oil, polyethyleneimine, cellulose acetate, adhesive are added in mixture A, grinder is added after mixing
Middle grinding 40min, obtains mixture B；
C, mixture B is added in kneading machine later and is kneaded, melting temperature is 75 DEG C, mixing time 30min；Delay later
30min is stood after slow cool down to room temperature；
D, sodium carboxymethylcellulose, levelling agent, modified poly- silicon oxygen are finally sequentially added in the mixture that step C is obtained
Alkane is added heating vessel in heating, is stirred continuously in heating process after mixing；Constant temperature 20min, is again heated to after being heated to 50 DEG C
Constant temperature 10min after 80 DEG C after being slowly cooled to room temperature later, stands 1h to get environment protection oil paint is arrived.
Embodiment three:
Paint component includes 45 parts of natural resin, 6 parts of titanium dioxide, 9 parts of white carbon black, 12 parts of turpentine oil, gathers in parts by weight
12 parts of aziridine, 12 parts of nano-zinc oxide powder, 6 parts of cellulose acetate, 9 parts of adhesive, 12 parts of modified Nano diatomite in powder,
12 parts of sodium carboxymethylcellulose, 2 parts of levelling agent, 7 parts and 9 parts of modified polyorganosiloxane of bean plant short oil class alkyd resin.
The preparation method of the present embodiment the following steps are included:
A, natural resin, titanium dioxide, white carbon black, nano-zinc oxide powder, modified Nano diatomite in powder, bean plant is short
It is added in stirred tank and is stirred after the mixing of oils alkyd resin, stirring rate is 1200 revs/min, and mixing time 12min is obtained
To mixture A；
B, turpentine oil, polyethyleneimine, cellulose acetate, adhesive are added in mixture A, grinder is added after mixing
Middle grinding 25min, obtains mixture B；
C, mixture B is added in kneading machine later and is kneaded, melting temperature is 60 DEG C, mixing time 15min；Delay later
30min is stood after slow cool down to room temperature；
D, sodium carboxymethylcellulose, levelling agent, modified poly- silicon oxygen are finally sequentially added in the mixture that step C is obtained
Alkane is added heating vessel in heating, is stirred continuously in heating process after mixing；Constant temperature 20min, is again heated to after being heated to 50 DEG C
Constant temperature 10min after 80 DEG C after being slowly cooled to room temperature later, stands 1h to get environment protection oil paint is arrived.
Example IV:
Paint component includes 55 parts of natural resin, 9 parts of titanium dioxide, 11 parts of white carbon black, 18 parts of turpentine oil, gathers in parts by weight
22 parts of aziridine, 18 parts of nano-zinc oxide powder, 14 parts of cellulose acetate, 11 parts of adhesive, modified Nano diatomite in powder 18
Part, 22 parts of sodium carboxymethylcellulose, 3 parts of levelling agent, 14 parts of bean plant short oil class alkyd resin and modified polyorganosiloxane 15
Part.
The preparation method of the present embodiment the following steps are included:
A, natural resin, titanium dioxide, white carbon black, nano-zinc oxide powder, modified Nano diatomite in powder, bean plant is short
It is added in stirred tank and is stirred after the mixing of oils alkyd resin, stirring rate is 1800 revs/min, and mixing time 25min is obtained
To mixture A；
B, turpentine oil, polyethyleneimine, cellulose acetate, adhesive are added in mixture A, grinder is added after mixing
Middle grinding 35min, obtains mixture B；
C, mixture B is added in kneading machine later and is kneaded, melting temperature is 70 DEG C, mixing time 25min；Delay later
30min is stood after slow cool down to room temperature；
D, sodium carboxymethylcellulose, levelling agent, modified poly- silicon oxygen are finally sequentially added in the mixture that step C is obtained
Alkane is added heating vessel in heating, is stirred continuously in heating process after mixing；Constant temperature 20min, is again heated to after being heated to 50 DEG C
Constant temperature 10min after 80 DEG C after being slowly cooled to room temperature later, stands 1h to get environment protection oil paint is arrived.
Embodiment five:
Paint component includes 52 parts of natural resin, 7 parts of titanium dioxide, 11 parts of white carbon black, 16 parts of turpentine oil, gathers in parts by weight
20 parts of aziridine, 16 parts of nano-zinc oxide powder, 8 parts of cellulose acetate, 9 parts of adhesive, 16 parts of modified Nano diatomite in powder,
15 parts of sodium carboxymethylcellulose, 3 parts of levelling agent, 8 parts and 15 parts of modified polyorganosiloxane of bean plant short oil class alkyd resin.
The preparation method of the present embodiment the following steps are included:
A, natural resin, titanium dioxide, white carbon black, nano-zinc oxide powder, modified Nano diatomite in powder, bean plant is short
It is added in stirred tank and is stirred after the mixing of oils alkyd resin, stirring rate is 1000-2000 revs/min, and mixing time is
10min-30min obtains mixture A；
B, turpentine oil, polyethyleneimine, cellulose acetate, adhesive are added in mixture A, grinder is added after mixing
Middle grinding 20-40min, obtains mixture B；
C, mixture B is added in kneading machine later and is kneaded, melting temperature is 55 DEG C -75 DEG C, mixing time 10min-
30min；30min is stood after being slowly cooled to room temperature later；
D, sodium carboxymethylcellulose, levelling agent, modified poly- silicon oxygen are finally sequentially added in the mixture that step C is obtained
Alkane is added heating vessel in heating, is stirred continuously in heating process after mixing；Constant temperature 20min, is again heated to after being heated to 50 DEG C
Constant temperature 10min after 80 DEG C after being slowly cooled to room temperature later, stands 1h to get environment protection oil paint is arrived.
Embodiment six:
Paint component includes 50 parts of natural resin, 8 parts of titanium dioxide, 10 parts of white carbon black, 15 parts of turpentine oil, gathers in parts by weight
17 parts of aziridine, 15 parts of nano-zinc oxide powder, 10 parts of cellulose acetate, 10 parts of adhesive, modified Nano diatomite in powder 15
Part, 17 parts of sodium carboxymethylcellulose, 3 parts of levelling agent, 10 parts of bean plant short oil class alkyd resin and modified polyorganosiloxane 13
Part.
The preparation method of the present embodiment the following steps are included:
A, natural resin, titanium dioxide, white carbon black, nano-zinc oxide powder, modified Nano diatomite in powder, bean plant is short
It is added in stirred tank and is stirred after the mixing of oils alkyd resin, stirring rate is 1500 revs/min, and mixing time 20min is obtained
To mixture A；
B, turpentine oil, polyethyleneimine, cellulose acetate, adhesive are added in mixture A, grinder is added after mixing
Middle grinding 30min, obtains mixture B；
C, mixture B is added in kneading machine later and is kneaded, melting temperature is 65 DEG C, mixing time 20min；Delay later
30min is stood after slow cool down to room temperature；
D, sodium carboxymethylcellulose, levelling agent, modified poly- silicon oxygen are finally sequentially added in the mixture that step C is obtained
Alkane is added heating vessel in heating, is stirred continuously in heating process after mixing；Constant temperature 20min, is again heated to after being heated to 50 DEG C
Constant temperature 10min after 80 DEG C after being slowly cooled to room temperature later, stands 1h to get environment protection oil paint is arrived.
Preparation process of the present invention is simple, preparation process is environment friendly and pollution-free, and paint obtained is environment-protecting and non-poisonous, has moisture resistance anti-
Water, anti-aging, wear-resisting feature are coated on bamboo and wood products surface, are able to extend the service life of bamboo and wood products, the titanium white of addition
Powder can further enhance the antiseptic property of paint；The nano zine oxide of addition, modified Nano diatomite in powder have antibacterial bacteriostatic,
The effect of taste of dispelling anti-enzyme, it is able to extend the storage time of paint；The sodium carboxymethylcellulose of addition, it can be ensured that paint viscosity
Stability and uniformity, to improve paint application efficiency；In addition, being added with bean plant short oil class alkyd tree in the present invention
Rouge can prevent bamboo and wood products' surface oil paint cracking；The modified polyorganosiloxane of addition can further increase the wearability of paint
It can be with anti-scratch performance.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (2)
1. a kind of bamboo and wood processing oil paint, it is characterised in that: paint component includes 40-60 parts of natural resin, titanium in parts by weight
5-10 parts of white powder, 8-12 parts of white carbon black, 10-20 parts of turpentine oil, 10-25 parts of polyethyleneimine, nano-zinc oxide powder 10-20
Part, 5-15 parts of cellulose acetate, 8-12 parts of adhesive, 10-20 parts of modified Nano diatomite in powder, sodium carboxymethylcellulose 10-25
Part, 1-4 parts of levelling agent, 5-15 parts and 8-17 parts of modified polyorganosiloxane of bean plant short oil class alkyd resin；
Preparation method includes the following steps:
A, by natural resin, titanium dioxide, white carbon black, nano-zinc oxide powder, modified Nano diatomite in powder, bean plant short oil class
It is added in stirred tank and is stirred after alkyd resin mixing, stirring rate is 1000-2000 revs/min, mixing time 10min-
30min obtains mixture A；
B, turpentine oil, polyethyleneimine, cellulose acetate, adhesive are added in mixture A, is added in grinder and grinds after mixing
20-40min is ground, mixture B is obtained；
C, mixture B is added in kneading machine later and is kneaded, melting temperature is 55 DEG C -75 DEG C, mixing time 10min-
30min；30min is stood after being slowly cooled to room temperature later；
D, sodium carboxymethylcellulose, levelling agent, modified polyorganosiloxane are finally sequentially added in the mixture that step C is obtained, and are mixed
Heating vessel in heating is added after conjunction, is stirred continuously in heating process；Constant temperature 20min after being heated to 50 DEG C, is again heated to 80 DEG C
Constant temperature 10min afterwards after being slowly cooled to room temperature later, stands 1h to get environment protection oil paint is arrived.
2. a kind of bamboo and wood processing oil paint according to claim 1, it is characterised in that: preferred composition proportion are as follows: natural
50 parts of resin, 8 parts of titanium dioxide, 10 parts of white carbon black, 15 parts of turpentine oil, 17 parts of polyethyleneimine, 15 parts of nano-zinc oxide powder, vinegar
It is 10 parts of acid cellulose, 10 parts of adhesive, 15 parts of modified Nano diatomite in powder, 17 parts of sodium carboxymethylcellulose, 3 parts of levelling agent, big
10 parts and 13 parts of modified polyorganosiloxane of beans plant short oil class alkyd resin.