CN106349908A - High-performance wickerwork coating - Google Patents
High-performance wickerwork coating Download PDFInfo
- Publication number
- CN106349908A CN106349908A CN201610781337.XA CN201610781337A CN106349908A CN 106349908 A CN106349908 A CN 106349908A CN 201610781337 A CN201610781337 A CN 201610781337A CN 106349908 A CN106349908 A CN 106349908A
- Authority
- CN
- China
- Prior art keywords
- wicker
- coating
- water
- performance
- plaiting article
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-performance wickerwork coating which is prepared from the following components: waterborne polyurethane, silicon-acrylate emulsion, dioctyl phthalate, shellac resin, mung bean starch, polyvinyl alcohol, a filler, an antibacterial additive and water. Compared with the existing wickerwork coating, the wickerwork coating disclosed by the invention is high in storage stability and long in coating film service life; compared with the coating film service life of the common wickerwork coating, the coating film service life of the high-performance wickerwork coating is prolonged by twice or triple; a paint layer formed by the coating is touch, high in brightness, high in adhesive force, anti-acid, anti-sulfur, high in salt resistance, stable in performance, and not liable to corrode and discolor; the coating disclosed by the invention is extremely high in high-temperature resistance, high in adhesive force, and not liable to fall off; furthermore, during use, the coating can be quickly dried and is high in leveling property; moreover, the coating is harmless to the environment and a human body, and is environment-friendly.
Description
Technical field
The present invention relates to wicker plaiting article paint field, more particularly to a kind of high-performance wicker wicker plaiting article coating.
Background technology
Wicker wicker plaiting article is the artware accepting extensively for a lot of people currently on the market, and its shape is varied, function
Very abundant, existing large bamboo or wicker basket for filling thing, fruit basket etc., there are the various products for decoration, a variety of wicker productses again
It is all the article of people's close contact it is therefore desirable to be processed using nontoxic coating or inorganic agent, prevent toxic residue,
Because wicker products is to be formed with the braiding of willow rattan, easily corrodes in use and shorten its service life, however existing
Not only not environmentally, and anticorrosion anti-insect effect is general for wicker plaiting article coating, and wicker plaiting article service life cannot ensure.
Content of the invention
Above-mentioned in order to overcome the shortcomings of, the invention provides a kind of high-performance wicker wicker plaiting article coating.
The present invention is achieved through the following technical solutions:
A kind of high-performance wicker wicker plaiting article coating, is made up of following component by weight: aqueous polyurethane 80-100, silicon third breast
Liquid 26-28, dioctyl phthalate 2-4, lac resin 0.2-0.4, green starch 3-4, polyvinyl alcohol 7-8, filler 25-
26th, antibacterial additives 4-6, water 74-76.
Further, described antibacterial additives, are made up of following component by weight: phytate 9, nano zine oxide 2,
Diisocyanate 1, ripple microballon 0.2, tourmaline stone powder 0.5, silicon carbide whisker 1, hydroxypropyl PASELLI EASYGEL 2, Plant Powder
7th, hydroxyethyl cellulose 2, xylitol 3；
Described Plant Powder is made up of following component by weight: stalky tea 4, Lignum cinnamomi camphorae 2, Semen Vitis viniferae 3, Folium cinnamomi camphorae 4, mottled bamboo leaf 5, its
Preparation method is: after stalky tea, Lignum cinnamomi camphorae, Semen Vitis viniferae, Folium cinnamomi camphorae, mottled bamboo leaf are uniformly mixed, obtains mixed material, by mixed material
Put into after soaking 35-40min in the clarification lime water under room temperature, take out, clean water 1 time is adopted using surface, is then placed in
Dry 35-40min in dehydrator and be less than 10% to water content, then pulverized, grinding particle size is 300-350 mesh, obtains mixed powder
End, mixed-powder is added in the maleic acid solution that mass concentration is 1.3% and is heated to 60 DEG C, then add mixed-powder quality
5% silane coupler, stirs 30min with 100r/min rotating speed, then filters, and surface adopts clean water 1 time, places into baking
Dry in dry machine and be less than 8% to water content, obtain final product required Plant Powder.
Further, described filler is nano diatomite, and granularity is 25-28nm.
A kind of using method of high-performance wicker wicker plaiting article coating is:
1. by wicker wicker plaiting article be placed on 28 DEG C, relative air humidity be 65% in the environment of, till reaching balance；
2. the wicker wicker plaiting article after being up to balance is put in inorganic agent and is soaked 1-1.5 days, and soaking temperature is maintained at 16-18 DEG C,
After immersion terminates, take out, after naturally draining, then after standing 10 minutes, then with 16-18 DEG C of clear water flushing 1-2 time, then drip again
It is dry, you can；
3., again by high-performance wicker wicker plaiting article coating described in the wicker wicker plaiting article brushing of 2. middle process, at a temperature of 28-30 DEG C, dry
It is dry, you can；
Described inorganic agent parts by weights meter, is made up of following component: water 80, sulfurized castor oil 5, ethylene glycol 3, polyvinyl alcohol 1, secondary
Sodium alkyl sulfonate 0.5, sodium citrate 1, Borax 4；
Described sulfurized castor oil is made up of following component by weight: Oleum Ricini 4, silver birch juice 1, quick lime 1, Cosan
1.5th, sodium carbonate 0.3, water 24, its preparation method is: quick lime is placed in pot, the water adding 4 weight portions makes lime digestion, adjusts
Become pasty state lime cream, then Cosan is equally tuned into pasty state using the water of 4 weight portions with sodium carbonate, be then added in lime cream mixed
Even, now add Oleum Ricini, then add the water that 10 weight are divided, the waterline in labelling pot, be then heated to seethe with excitement, keep boiling
After rising 30-35 minute, add silver birch juice, then add the water that 6 weight are divided, continue to be heated to seething with excitement, keep boiling 10 minutes
Afterwards, stirred to being cooled to room temperature with 220r/min rotating speed, take out stock solution and filter off dregs, filtrate is sulfurized castor oil.
The wicker plaiting article coating that the present invention prepares is effectively prevented growing and breeding of various antibacterials, and kills on coating
The ability of various antibacterials.The ion exchange that the present invention is produced by tourmaline stone powder, can adsorb harmful composition and
Various bacteria group, then coordinate the synergism of the Plant Powder of configuration, various bacteria and funguses are effectively suppressed and are killed,
The antibiotic property of the dope layer after coating coating can be made more lasting, As time goes on the antibiotic property of paint coatings changes not
Greatly, there is excellent antibacterial stability, using phytate, nano zine oxide, diisocyanate, ripple microballon, silicon carbide whisker
Coordinated effect, can improve hardness and the wearability of paint coatings further, and the adsorptivity of dust can be reduced, protect
Hold more preferable cleanliness, environmental protection, generation that is antibacterial, can effectively suppressing various pathogenic bacterium, fungistatic effect is lasting, and green ring
Protect, will not be to environment, it can be avoided that tradition is used alone the pollution that organic antibacterial agent brings and is used alone inorganic
The high cost problem of antibacterial；Add the present invention configuration antibacterial additives so that preparation wicker plaiting article coating, to colibacillary
Bacteriostasis rate is up to 98.2%, is up to 97.0% to the suppression ratio of gold-coloured staphylococci, and the suppression ratio of mycete is up to
99.1%.
Before using coating of the present invention, first inorganic agent is adopted to process wicker wicker plaiting article, the inorganic agent of present invention configuration
There is very strong permeability, can infiltrate through in fiber reach enhancing, toughness reinforcing, soften the effects such as, more can strong strengthen
The lasting effect of the antiseptic insect-repelling of the wicker after process, wicker softness number is high, can keep the pliability of wicker for a long time, pass through
In the present invention, the synergism of sulfurized castor oil and Borax is so that the more affine present invention of wicker wicker plaiting article surface energy after processing
The coating prepared, greatly improves the adhesive force of the coating of present invention preparation, thus improve the use longevity of coating of the present invention
Life, comprcssive strength relatively compared with untreated wicker for the treated wicker averagely improves 25.1%, and bending strength averagely improves
28.7%.
The invention has the beneficial effects as follows: with existing wicker wicker plaiting article coating ratio, wicker wicker plaiting article coating storage of the present invention is surely
Qualitative height, coating film life-span length, apply membrane lifetime compared to common wicker wicker plaiting article coating and improve 2-3 times, coating of the present invention
The enamelled coating being formed after coating is tough and tensile, and brightness is high, and adhesive force is strong, and acidproof, sulfur resistive, salt resistant character are strong, and stable performance is difficult rotten
Erosion, invariant color, the coating of the present invention has extraordinary resistance to elevated temperatures, and adhesion is strong, and coating is difficult for drop-off, and dry when using
Dry fast, good leveling property, coating is to environment non-hazardous simultaneously, to human body fanout free region, environmental protection.
Specific embodiment
Embodiment 1: a kind of high-performance wicker wicker plaiting article coating, it is made up of following component by weight: aqueous polyurethane
80th, silicone acrylic emulsion 26, dioctyl phthalate 2, lac resin 0.2, green starch 3, polyvinyl alcohol 7, filler 25, antibacterial add
Plus agent 4, water 74, described antibacterial additives, it is made up of following component by weight: phytate 9, nano zine oxide 2, two isocyanides
Acid esters 1, ripple microballon 0.2, tourmaline stone powder 0.5, silicon carbide whisker 1, hydroxypropyl PASELLI EASYGEL 2, Plant Powder 7, hydroxyl second
Base cellulose 2, xylitol 3；
Described Plant Powder is made up of following component by weight: stalky tea 4, Lignum cinnamomi camphorae 2, Semen Vitis viniferae 3, Folium cinnamomi camphorae 4, mottled bamboo leaf 5.
Embodiment 2: a kind of high-performance wicker wicker plaiting article coating, it is made up of following component by weight: aqueous polyurethane
100th, silicone acrylic emulsion 28, dioctyl phthalate 4, lac resin 0.4, green starch 4, polyvinyl alcohol 8, filler 26, antibacterial
Additive 6, water 76, described antibacterial additives, it is made up of following component by weight: phytate 9, nano zine oxide 2, two are different
Cyanate 1, ripple microballon 0.2, tourmaline stone powder 0.5, silicon carbide whisker 1, hydroxypropyl PASELLI EASYGEL 2, Plant Powder 7, hydroxyl
Ethyl cellulose 2, xylitol 3；
Described Plant Powder is made up of following component by weight: stalky tea 4, Lignum cinnamomi camphorae 2, Semen Vitis viniferae 3, Folium cinnamomi camphorae 4, mottled bamboo leaf 5.
Embodiment 3: a kind of high-performance wicker wicker plaiting article coating, it is made up of following component by weight: aqueous polyurethane
90th, silicone acrylic emulsion 27, dioctyl phthalate 3, lac resin 0.3, green starch 3.5, polyvinyl alcohol 7.5, filler 25.5,
Antibacterial additives 5, water 75, described antibacterial additives, be made up of following component by weight: phytate 9, nano zine oxide 2,
Diisocyanate 1, ripple microballon 0.2, tourmaline stone powder 0.5, silicon carbide whisker 1, hydroxypropyl PASELLI EASYGEL 2, Plant Powder
7th, hydroxyethyl cellulose 2, xylitol 3；
Described Plant Powder is made up of following component by weight: stalky tea 4, Lignum cinnamomi camphorae 2, Semen Vitis viniferae 3, Folium cinnamomi camphorae 4, mottled bamboo leaf 5.
A kind of using method of high-performance wicker wicker plaiting article coating is:
1. by wicker wicker plaiting article be placed on 28 DEG C, relative air humidity be 65% in the environment of, till reaching balance；
2. the wicker wicker plaiting article after being up to balance is put in inorganic agent and is soaked 1-1.5 days, and soaking temperature is maintained at 16-18 DEG C,
After immersion terminates, take out, after naturally draining, then after standing 10 minutes, then with 16-18 DEG C of clear water flushing 1-2 time, then drip again
It is dry, you can；
3., again by high-performance wicker wicker plaiting article coating described in the wicker wicker plaiting article brushing of 2. middle process, at a temperature of 28-30 DEG C, dry
It is dry, you can；
Described inorganic agent parts by weights meter, is made up of following component: water 80, sulfurized castor oil 5, ethylene glycol 3, polyvinyl alcohol 1, secondary
Sodium alkyl sulfonate 0.5, sodium citrate 1, Borax 4；
Described sulfurized castor oil is made up of following component by weight: Oleum Ricini 4, silver birch juice 1, quick lime 1, Cosan
1.5th, sodium carbonate 0.3, water 24.
Coating property test of the present invention:
Table 1
As can be seen from Table 1, coating various aspects of performance all comparative superiorities of the present invention.
Bacteriostasis property contrasts:
Table 2
Wherein, comparative example 1 is: by the embodiment of the present invention 1 without tourmaline stone powder, other components unchanged, the wicker plaiting article made
Coating；
Comparative example 2 is: by the embodiment of the present invention 1 without Plant Powder, other components unchanged, the wicker plaiting article coating made；
Comparative example 3 is:, makes in plant meal component in the embodiment of the present invention 1 without mottled bamboo leaf and stalky tea, other components unchanged
The wicker plaiting article coating becoming；
As can be seen from Table 2, antibacterial additives of the present invention can greatly improve the anti-microbial property of wicker plaiting article coating, lacks tourmaline stone
Powder, Plant Powder, mottled bamboo leaf and stalky tea can be different degrees of reduction coating antibiosis performance.
Claims (4)
1. a kind of high-performance wicker wicker plaiting article coating is it is characterised in that be made up of following component by weight: aqueous polyurethane
80-100, silicone acrylic emulsion 26-28, dioctyl phthalate 2-4, lac resin 0.2-0.4, green starch 3-4, polyvinyl alcohol
7-8, filler 25-26, antibacterial additives 4-6, water 74-76.
2. a kind of high-performance wicker wicker plaiting article coating according to claim 1 is it is characterised in that described antibacterial additives,
It is made up of following component by weight: phytate 9, nano zine oxide 2, diisocyanate 1, ripple microballon 0.2, tourmaline stone
Powder 0.5, silicon carbide whisker 1, hydroxypropyl PASELLI EASYGEL 2, Plant Powder 7, hydroxyethyl cellulose 2, xylitol 3；
Described Plant Powder is made up of following component by weight: stalky tea 4, Lignum cinnamomi camphorae 2, Semen Vitis viniferae 3, Folium cinnamomi camphorae 4, mottled bamboo leaf 5, its
Preparation method is: after stalky tea, Lignum cinnamomi camphorae, Semen Vitis viniferae, Folium cinnamomi camphorae, mottled bamboo leaf are uniformly mixed, obtains mixed material, by mixed material
Put into after soaking 35-40min in the clarification lime water under room temperature, take out, clean water 1 time is adopted using surface, is then placed in
Dry 35-40min in dehydrator and be less than 10% to water content, then pulverized, grinding particle size is 300-350 mesh, obtains mixed powder
End, mixed-powder is added in the maleic acid solution that mass concentration is 1.3% and is heated to 60 DEG C, then add mixed-powder quality
5% silane coupler, stirs 30min with 100r/min rotating speed, then filters, and surface adopts clean water 1 time, places into baking
Dry in dry machine and be less than 8% to water content, obtain final product required Plant Powder.
3. a kind of high-performance wicker wicker plaiting article coating according to claim 1 is it is characterised in that described filler is nano-silicon
Diatomaceous earth, granularity is 25-28nm.
4. a kind of high-performance wicker wicker plaiting article coating according to claim 1 is it is characterised in that described high-performance wicker system
The using method of wicker plaiting article coating is:
1. by wicker wicker plaiting article be placed on 28 DEG C, relative air humidity be 65% in the environment of, till reaching balance；
2. the wicker wicker plaiting article after being up to balance is put in inorganic agent and is soaked 1-1.5 days, and soaking temperature is maintained at 16-18 DEG C,
After immersion terminates, take out, after naturally draining, then after standing 10 minutes, then with 16-18 DEG C of clear water flushing 1-2 time, then drip again
It is dry, you can；
3., again by high-performance wicker wicker plaiting article coating described in the wicker wicker plaiting article brushing of 2. middle process, at a temperature of 28-30 DEG C, dry
It is dry, you can；
Described inorganic agent parts by weights meter, is made up of following component: water 80, sulfurized castor oil 5, ethylene glycol 3, polyvinyl alcohol 1, secondary
Sodium alkyl sulfonate 0.5, sodium citrate 1, Borax 4；
Described sulfurized castor oil is made up of following component by weight: Oleum Ricini 4, silver birch juice 1, quick lime 1, Cosan
1.5th, sodium carbonate 0.3, water 24, its preparation method is: quick lime is placed in pot, the water adding 4 weight portions makes lime digestion, adjusts
Become pasty state lime cream, then Cosan is equally tuned into pasty state using the water of 4 weight portions with sodium carbonate, be then added in lime cream mixed
Even, now add Oleum Ricini, then add the water that 10 weight are divided, the waterline in labelling pot, be then heated to seethe with excitement, keep boiling
After rising 30-35 minute, add silver birch juice, then add the water that 6 weight are divided, continue to be heated to seething with excitement, keep boiling 10 minutes
Afterwards, stirred to being cooled to room temperature with 220r/min rotating speed, take out stock solution and filter off dregs, filtrate is sulfurized castor oil.