CN107199611B - A kind of process increasing wicker color retention time - Google Patents
A kind of process increasing wicker color retention time Download PDFInfo
- Publication number
- CN107199611B CN107199611B CN201710533986.2A CN201710533986A CN107199611B CN 107199611 B CN107199611 B CN 107199611B CN 201710533986 A CN201710533986 A CN 201710533986A CN 107199611 B CN107199611 B CN 107199611B
- Authority
- CN
- China
- Prior art keywords
- wicker
- sent
- drying
- polishing
- toner
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of process increasing wicker color retention time, is related to wicker processing technology field, passes through polishing, polishing, immersion, drying, polishing, upper powder, japanning, sterilization, refrigeration, warehouse entry and other process steps.The present invention can effective protection wicker lacquer painting, extend color retention time, good protective action can be played to the surface of wicker, to reduce the abrasion to paint lacquer painting, reduce the wicker surface degree that suffers erosion and wear.
Description
Technical field:
The present invention relates to wicker processing technology fields, and in particular to a kind of technique side for increasing wicker color retention time
Method.
Background technique:
Wicker plaiting article is one of folks of china traditional handicraft product, and people are intended only as common daily utility in ancient times, directly
Decades just gradually rise after to 20th century, also the project for becoming selected areas of China foreign exchange earning gradually.Wicker is soft easily
It is curved, thickness is well-balanced, color is graceful, by novel design, can be woven into that various honesties are natural, handsome in appearance, Portable durable
Practical art product.Wicker products are the artifacts of the civil widespread in China.This is because the raw material sources of this technique
It is very extensive.The north has withy, Chinese tamarisk branch, mulberry shoot, the twigs of the chaste tree, false indigo stem etc. a variety of for compiling the primary raw material that basket compiles basket,
Salt-soda soil and marshland are produced.
The color that wicker plaiting article product enriches wicker plaiting article product after woven generally can all paint for wicker plaiting article product
Colouring, but common spray painting will cause color dim due to abrasion etc. after some time has elapsed, color falls off
The problems such as, and along with the extension for using the time, each position is frequent by constantly abrasion and the naked lacquer painting being exposed on the external
It will receive various erosions, these are all easy to accelerate falling for color.
Summary of the invention:
Technical problem to be solved by the present invention lies in provide one kind can effective protection wicker lacquer painting, extend color retain
The process of time, this method can play good protective action to the surface of wicker, so that the abrasion to paint is reduced,
Reduce the degree that wicker surface suffers erosion and wears.
The following technical solution is employed for the technical problems to be solved by the invention to realize:
A kind of process increasing wicker color retention time, comprising the following steps:
(1) the straight and upright wicker without bending and without stammerer is selected, it is polished, is polished, is used during polishing
The sand paper of 100 mesh is polished for the first time, is eliminated flash, is then fed into polishing machine and is polished；
(2) wicker after polishing is put into soaking box and is impregnated, impregnated using the leaching deployed exclusively for wicker
Bubble liquid heats up to the soak in soaking box after wicker is submerged in soak completely, until temperature rises to 70-
Stop heating at 90 DEG C, and keeps constant temperature 20-30 minutes；
(3) wicker is sent in dryer after impregnating and is dried for the first time, dryer fire box temperature is set as 110-115
DEG C, drying time is 3-10 minutes, and wicker is sent in gag press after first drying and carries out straightening, then carries out secondary baking again
Dry, the temperature of secondary drying is identical as first drying temperature, and drying time is 30-35 minutes；
(4) it wicker is sent in sander polishes after drying, the abrasive powder of -600 mesh of 500 mesh is used when polishing
Medium is served as, polishing enables to wicker surface to generate tiny scratch and groove, prepares for next process；
(5) wicker polished is put into togerther in roller with synthesis toner and carries out rolling and mixes, then adopt wicker
It is rolled with pressing plate, rolls wicker uniformly under pressing plate, toner is made uniformly to penetrate into the scratch and ditch on wicker surface
In slot；
(6) wicker after rolling is sent to paint locker and carries out japanning, wicker is protected using the paint of white clear
Wicker is dried for standby by the coating of cuticula, japanning after the completion；
(7) wicker is sent in ultraviolet sterilization room after wicker drying and is sterilized, it will be single with preservative film after sterilization
Wicker tightly wraps up and does encapsulation process；
(8) wicker after sealing is sent to after being refrigerated 10-12 hours in refrigerating chamber and is taken out；
(9) wicker after taking out can be transported into warehouse storage or directly carry out braiding use；
Soak used in above-mentioned steps (2) be formulated soak, the soak have following components prepare and
At:
Hydrogen peroxide, nonionic surfactant, anionic surfactant, softening agent, boric acid, fatty acid, ethyl alcohol, thickening
Agent；
Said components are calculated according to the mass fraction, the mass fraction of each component are as follows: hydrogen peroxide 60-65%, non-ionic surface are living
Property agent 3-5%, anionic surfactant 3-5%, softening agent 5-8%, boric acid 6-10%, fatty acid 10-20%, ethyl alcohol 10-
15%, tackifier 10-12%；
Above-mentioned soak after evenly mixing, at the uniform velocity stirs 5-8 minutes using centrifugal blender, so in the preparation by each component
After be sent in heating furnace and heat, stop heating when being warming up to 90 DEG C, and allow its natural cooling, be poured into soaking box after cooling
Carry out using；
The synthesis toner used in above-mentioned processing step (5) is by toner, anti-blushing agent powder, crystal powder and drier according to 5:1:
The ratio of 1:1 is mixed, and again through sterilization processing after mixing, when sterilization will synthesize the spreading for cooling that toner is uniformly divided and open, and is sent to
Ultraviolet light is sterilized in room；
After being handled by the above method wicker, we retain the color of the product using the braiding of above-mentioned wicker
Time, surface flatness, glossiness and wear-resistant slippery compare measurement and obtain following data:
| Color retention time | Surface flatness | Glossiness | Wear-resistant degree |
| 4-6 | Light | 80-90% | By force |
Wicker is impregnated and effectively wicker can be helped to soften using soak in above-mentioned technical process, then promotes willow
The sizing of item plays good facilitation for the straightening in later period, and adding tackifier in soak can make wicker exist
Some tackifier can be absorbed when immersion to make wicker with certain adsorption capacity, pass through the function such as the softening of soak
Effect and effect can play good booster action for wicker following process and operation, using gold while in addition polishing wicker
Emery powder serves as medium, wicker surface can be made to form scratch and gully when polishing, use secondary colour in the later period in this way
Facilitate attachment of the toner on wicker when powder, being fixed by paint to it after uniform attachment makes it generate protecting film,
It can thus to synthesize toner retention time extension on wicker, to increase the persistence of color, then pass through sterilization
Be sealed, the storage time that can also effectively extend wicker prevents from damaging by worms；
The beneficial effects of the present invention are: can effective protection wicker lacquer painting, extend color retention time, can be to wicker
Good protective action is played on surface, to reduce the abrasion to paint lacquer painting, reduces wicker surface and suffers erosion and wear
Degree.
Specific embodiment:
In order to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, tie below
Specific example is closed, the present invention is further explained.
Embodiment 1:
A kind of process increasing wicker color retention time, comprising the following steps:
(1) the straight and upright wicker without bending and without stammerer is selected, it is polished, is polished, is used during polishing
The sand paper of 100 mesh is polished for the first time, is eliminated flash, is then fed into polishing machine and is polished；
(2) soak is prepared, is calculated according to the mass fraction, by following component hydrogen peroxide 60%, nonionic surfactant
3%, anionic surfactant 3%, softening agent 5%, boric acid 6%, fatty acid 10%, ethyl alcohol 15%, tackifier 10% are uniform
It after mixing, is at the uniform velocity stirred 8 minutes using centrifugal blender, is then fed into heating furnace and heats, stop rising when being warming up to 90 DEG C
Temperature, and allow its natural cooling is poured into soaking box after cooling and carries out using the wicker after polishing is then put into immersion
It is impregnated, is impregnated using the soak deployed exclusively for wicker, after wicker is submerged in soak completely, to leaching in case
Soak in bubble case heats up, until temperature stops heating when rising to 70 DEG C, and keeps constant temperature 30 minutes；
(3) wicker is sent in dryer after impregnating and is dried for the first time, dryer fire box temperature is set as 110 DEG C,
Drying time is 10 minutes, and wicker is sent in gag press after first drying and carries out straightening, then carries out secondary drying again, two
The temperature of secondary drying is identical as first drying temperature, and drying time is 35 minutes；
(4) it wicker is sent in sander polishes after drying, serve as Jie using the abrasive powder of 500 mesh when polishing
Matter, polishing enable to wicker surface to generate tiny scratch and groove, prepare for next process；
(5) preparation synthesis toner: toner, anti-blushing agent powder, crystal powder and drier are mixed according to the ratio of 5:1:1:1
Close, again through sterilization processing after mixing, the spreading for cooling that when sterilization uniformly divides toner is opened, be sent in ultraviolet light room carry out sterilization will
The wicker polished is put into togerther in roller with toner to carry out rolling and mixes, and then rolls wicker using pressing plate, makes
Wicker is uniformly rolled under pressing plate, penetrates into toner uniformly in the scratch and groove on wicker surface, and toner is by sterilization
Processing, the spreading for cooling that when sterilization uniformly divides toner open, are sent in ultraviolet light room and are sterilized；
(6) wicker after rolling is sent to paint locker and carries out japanning, wicker is protected using the paint of white clear
Wicker is dried for standby by the coating of cuticula, japanning after the completion；
(7) wicker is sent in ultraviolet sterilization room after wicker drying and is sterilized, it will be single with preservative film after sterilization
Wicker tightly wraps up and does encapsulation process；
(8) wicker after sealing is sent to after being refrigerated 10 hours in refrigerating chamber and is taken out；
(9) wicker after taking out can be transported into warehouse storage or directly carry out braiding use.
Embodiment 2:
A kind of process increasing wicker color retention time, comprising the following steps:
(1) the straight and upright wicker without bending and without stammerer is selected, it is polished, is polished, is used during polishing
The sand paper of 100 mesh is polished for the first time, is eliminated flash, is then fed into polishing machine and is polished；
(2) soak is prepared, is calculated according to the mass fraction, by following component hydrogen peroxide 663%, nonionic surfactant
4%, anionic surfactant 4%, softening agent 6%, boric acid 8%, fatty acid 15%, ethyl alcohol 13%, tackifier 11% are uniform
It after mixing, is at the uniform velocity stirred 8 minutes using centrifugal blender, is then fed into heating furnace and heats, stop rising when being warming up to 90 DEG C
Temperature, and allow its natural cooling is poured into soaking box after cooling and carries out using the wicker after polishing is then put into immersion
It is impregnated, is impregnated using the soak deployed exclusively for wicker, after wicker is submerged in soak completely, to leaching in case
Soak in bubble case heats up, until temperature stops heating when rising to 90 DEG C, and keeps constant temperature 20 minutes；
(3) wicker is sent in dryer after impregnating and is dried for the first time, dryer fire box temperature is set as 115 DEG C,
Drying time is 8 minutes, and wicker is sent in gag press after first drying and carries out straightening, then carries out secondary drying again, two
The temperature of secondary drying is identical as first drying temperature, and drying time is 30 minutes；
(4) it wicker is sent in sander polishes after drying, serve as Jie using the abrasive powder of 550 mesh when polishing
Matter, polishing enable to wicker surface to generate tiny scratch and groove, prepare for next process；
(5) preparation synthesis toner: toner, anti-blushing agent powder, crystal powder and drier are mixed according to the ratio of 5:1:1:1
Close, again through sterilization processing after mixing, the spreading for cooling that when sterilization uniformly divides toner is opened, be sent in ultraviolet light room carry out sterilization will
The wicker polished is put into togerther in roller with toner to carry out rolling and mixes, and then rolls wicker using pressing plate, makes
Wicker is uniformly rolled under pressing plate, penetrates into toner uniformly in the scratch and groove on wicker surface, and toner is by sterilization
Processing, the spreading for cooling that when sterilization uniformly divides toner open, are sent in ultraviolet light room and are sterilized；
(6) wicker after rolling is sent to paint locker and carries out japanning, wicker is protected using the paint of white clear
Wicker is dried for standby by the coating of cuticula, japanning after the completion；
(7) wicker is sent in ultraviolet sterilization room after wicker drying and is sterilized, it will be single with preservative film after sterilization
Wicker tightly wraps up and does encapsulation process；
(8) wicker after sealing is sent to after being refrigerated 11 hours in refrigerating chamber and is taken out；
(9) wicker after taking out can be transported into warehouse storage or directly carry out braiding use.
Embodiment 3:
A kind of process increasing wicker color retention time, comprising the following steps:
(1) the straight and upright wicker without bending and without stammerer is selected, it is polished, is polished, is used during polishing
The sand paper of 100 mesh is polished for the first time, is eliminated flash, is then fed into polishing machine and is polished；
(2) soak is prepared, is calculated according to the mass fraction, by following component hydrogen peroxide 65%, nonionic surfactant
5%, anionic surfactant 5%, softening agent 8%, boric acid 10%, fatty acid 20%, ethyl alcohol 15%, tackifier 12% are uniform
It after mixing, is at the uniform velocity stirred 8 minutes using centrifugal blender, is then fed into heating furnace and heats, stop rising when being warming up to 90 DEG C
Temperature, and allow its natural cooling is poured into soaking box after cooling and carries out using the wicker after polishing is then put into immersion
It is impregnated, is impregnated using the soak deployed exclusively for wicker, after wicker is submerged in soak completely, to leaching in case
Soak in bubble case heats up, until temperature stops heating when rising to 90 DEG C, and keeps constant temperature 20 minutes；
(3) wicker is sent in dryer after impregnating and is dried for the first time, dryer fire box temperature is set as 115 DEG C,
Drying time is 10 minutes, and wicker is sent in gag press after first drying and carries out straightening, then carries out secondary drying again, two
The temperature of secondary drying is identical as first drying temperature, and drying time is 35 minutes；
(4) it wicker is sent in sander polishes after drying, serve as Jie using the abrasive powder of 600 mesh when polishing
Matter, polishing enable to wicker surface to generate tiny scratch and groove, prepare for next process；
(5) preparation synthesis toner: toner, anti-blushing agent powder, crystal powder and drier are mixed according to the ratio of 5:1:1:1
Close, again through sterilization processing after mixing, the spreading for cooling that when sterilization uniformly divides toner is opened, be sent in ultraviolet light room carry out sterilization will
The wicker polished is put into togerther in roller with toner to carry out rolling and mixes, and then rolls wicker using pressing plate, makes
Wicker is uniformly rolled under pressing plate, penetrates into toner uniformly in the scratch and groove on wicker surface, and toner is by sterilization
Processing, the spreading for cooling that when sterilization uniformly divides toner open, are sent in ultraviolet light room and are sterilized；
(6) wicker after rolling is sent to paint locker and carries out japanning, wicker is protected using the paint of white clear
Wicker is dried for standby by the coating of cuticula, japanning after the completion；
(7) wicker is sent in ultraviolet sterilization room after wicker drying and is sterilized, it will be single with preservative film after sterilization
Wicker tightly wraps up and does encapsulation process；
(8) wicker after sealing is sent to after being refrigerated 12 hours in refrigerating chamber and is taken out；
(9) wicker after taking out can be transported into warehouse storage or directly carry out braiding use.
1,2,3 comparative experiments respectively obtains following data through the foregoing embodiment:
| Surface flatness | Glossiness | Wear-resistant degree | |
| Embodiment 1 | 1 grade of light | 80-90% | By force |
| Embodiment 2 | 2 grades of light | 85-90% | By force |
| Embodiment 3 | 1 grade of light | 80-85& | It is relatively strong |
By the comparison summaries of above-mentioned three kinds of embodiments, it can be seen that the present invention can effective protection wicker lacquer painting, extend
Color retention time can play good protective action to the surface of wicker, to reduce the abrasion to paint lacquer painting, reduce
The degree that wicker surface suffers erosion and wears.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (3)
1. a kind of process for increasing wicker color retention time, it is characterised in that: the following steps are included:
(1) the straight and upright wicker without bending and without stammerer is selected, it is polished, is polished, 100 mesh are used during polishing
Sand paper polished for the first time, eliminate flash, be then fed into polishing machine and polished；
(2) wicker after polishing is put into soaking box and is impregnated, impregnated using the soak deployed exclusively for wicker,
It after wicker is submerged in soak completely, heats up to the soak in soaking box, until when temperature rises to 70-90 DEG C
Stop heating, and keeps constant temperature 20-30 minutes；
(3) wicker is sent in dryer after impregnating and is dried for the first time, dryer fire box temperature is set as 110-115 DEG C,
Drying time is 3-10 minutes, and wicker is sent in gag press after first drying and carries out straightening, then carries out secondary drying again,
The temperature of secondary drying is identical as first drying temperature, and drying time is 30-35 minutes；
(4) it wicker is sent in sander polishes after drying, when polishing is served as using the abrasive powder of -600 mesh of 500 mesh
Medium, polishing enable to wicker surface to generate tiny scratch and groove, prepare for next process；
(5) wicker polished is put into togerther in roller with synthesis toner and carries out rolling and mixes, then by wicker using pressing
Plate is rolled, and rolls wicker uniformly under pressing plate, penetrates into toner uniformly in the scratch and groove on wicker surface；
(6) wicker after rolling is sent to paint locker and carries out japanning, protective film is carried out to wicker using the paint of white clear
Coating, wicker is dried for standby after the completion of japanning；
(7) it wicker is sent in ultraviolet sterilization room sterilizes after wicker drying, with preservative film by single wicker after sterilization
It tightly wraps up and does encapsulation process；
(8) wicker after sealing is sent to after being refrigerated 10-12 hours in refrigerating chamber and is taken out；
(9) wicker after taking out can be transported into warehouse storage or directly carry out braiding use；
Soak used in above-mentioned steps (2) is prepared from the following components:
Hydrogen peroxide, nonionic surfactant, anionic surfactant, softening agent, boric acid, fatty acid, ethyl alcohol, tackifier.
2. a kind of process for increasing wicker color retention time according to claim 1, it is characterised in that: soak
In the preparation after evenly mixing by each component, it is at the uniform velocity stirred 5-8 minutes using centrifugal blender, is then fed into heating furnace and adds
Heat stops heating when being warming up to 90 DEG C, and allows its natural cooling, be poured into soaking box after cooling carry out using.
3. a kind of process for increasing wicker color retention time according to claim 1, it is characterised in that: step
(5) the synthesis toner used in is mixed by toner, anti-blushing agent powder, crystal powder and drier according to the ratio of 5:1:1:1:1,
Again through sterilization processing after mixing, the spreading for cooling that when sterilization uniformly divides toner is opened, and is sent in ultraviolet light room and is sterilized.