CN107139299A - A kind of process for the glossiness for improving the wicker woven for wicker plaiting article - Google Patents
A kind of process for the glossiness for improving the wicker woven for wicker plaiting article Download PDFInfo
- Publication number
- CN107139299A CN107139299A CN201710533507.7A CN201710533507A CN107139299A CN 107139299 A CN107139299 A CN 107139299A CN 201710533507 A CN201710533507 A CN 201710533507A CN 107139299 A CN107139299 A CN 107139299A
- Authority
- CN
- China
- Prior art keywords
- wicker
- sent
- drying
- glossiness
- polished
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of process for the glossiness for improving the wicker woven for wicker plaiting article, is related to wicker processing technology field, passes through polishing, polishing, immersion, drying, polishing, upper powder, japanning, sterilization, refrigeration, warehouse entry and other process steps.The present invention can carry out the lifting of glossiness to wicker, carry out technology processing to wicker during early stage is processed to wicker, effectively protect the integrality and aesthetic property on wicker surface to have the lifting effect of good glossiness to the product that the later stage is woven into.
Description
Technical field：
The present invention relates to wicker processing technology field, and in particular to a kind of raising is used for the glossiness for the wicker that wicker plaiting article weaves
Process.
Background technology：
Wicker plaiting article is one of folks of china traditional handicraft product, and people are intended only as common daily utility in ancient times, directly
Decades just gradually rise after to 20th century, also the project exported goods and earned foreign currency as selected areas of China gradually.Wicker is soft easily
Curved, thickness is well-balanced, color and luster is graceful, by novel design, can be woven into that various honesties are natural, handsome in appearance, Portable durable
Practical art product.Wicker products is the artifacts of China's widespread among the people, " compile basket, compile basket, every household has ".This be because
Raw material sources for this technique are quite varied.The primary raw material that the north is used to compile basket volume basket has withy, Chinese tamarisk branch, mulberry shoot, chaste tree
Bar, false indigo stem etc. are a variety of, are produced in salt-soda soil and marshland.
The quality of wicker plaiting article product and the using effect of product are caused by many aspects, wherein crucial point
It is exactly the quality of wicker, wicker can all carry out some processing using early stage and process, including polishing, colouring etc., this
A kind of a kind of technique and method improved to wicker glossiness of patent publicity.
The content of the invention：
The technical problems to be solved by the invention are to provide a kind of lifting that can be to wicker progress glossiness, in early stage
Technology processing is carried out to wicker during being processed to wicker, the integrality and aesthetic property on wicker surface is effectively protected to rear
The product that phase is woven into has the lifting effect of good glossiness.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of process for the glossiness for improving the wicker woven for wicker plaiting article, comprises the following steps：
(1) the straight and upright wicker without bending and without stammerer is selected, it is polished, polished, is used during polishing
The sand paper of 60 mesh is polished for the first time, is eliminated flash, is then fed into polishing machine and is polished；
(2) wicker after polishing is put into soaking box and soaked, immersion is using the leaching allocated exclusively for wicker
Liquid is steeped, after wicker is submerged in soak completely, the soak in soaking box is heated up, until temperature rises to 40-
Stop heating at 60 DEG C, and keep constant temperature 30-40 minutes；
(3) wicker is sent in dryer after soaking and dried for the first time, dryer fire box temperature is set as 60-75
DEG C, drying time is 20 minutes, and wicker is sent in gag press after first drying and carries out straightening, secondary baking is then carried out again
Dry, the temperature of secondary drying is identical with first drying temperature, and drying time is 30-35 minutes；
(4) wicker is sent in sander after drying and polished, is served as during polishing using the emery dust of the mesh of 500 mesh -600
Medium, polishing enables to wicker surface to produce tiny cut and groove, is that next process is prepared；
(5) wicker polished is put into progress rolling mixing in roller together with crystal powder, then used wicker
Pressing plate is rolled, and wicker is uniformly rolled under pressing plate, crystal powder is uniformly penetrated into the cut and ditch on wicker surface
In groove；
(6) wicker after rolling is sent to paint locker and carries out japanning, wicker is protected using the paint of white clear
By wicker dry for standby after the completion of the coating of cuticula, japanning；
(7) wicker is sent in ultraviolet sterilization room after wicker drying and sterilized, will be single with preservative film after sterilization
Wicker tightly wraps up and does encapsulation process；
(8) wicker after sealing is sent to after being refrigerated 10-12 hours in refrigerating chamber and taken out；
(9) wicker after taking out can be transported into warehouse storage or directly carry out braiding and use；
The soak used in above-mentioned steps (2) be formulated soak, the soak have following components prepare and
Into：
Hydrogen peroxide, nonionic surfactant, anion surfactant, softening agent, boric acid, aliphatic acid, ethanol, dioxy
SiClx；
Said components are calculated according to the mass fraction, and the mass fraction of each component is：Hydrogen peroxide 60-65%, non-ionic surface are lived
Property agent 3-5%, anion surfactant 3-5%, softening agent 5-8%, boric acid 6-10%, aliphatic acid 10-20%, ethanol 10-
15%th, silica 4-8%；
After above-mentioned soak in the preparation uniformly mixes each component, 5-8 minutes are at the uniform velocity stirred using centrifugal blender, so
After be sent in heating furnace and heat, stop heating when being warming up to 90 DEG C, and allow its natural cooling, be poured into after cooling in soaking box
Used；
The crystal powder used in above-mentioned processing step (5) passes through sterilization processing, the stand for uniformly dividing crystal powder during sterilization
It is cool to open, it is sent in ultraviolet room and is sterilized；
After being handled by the above method wicker, our storage time, pliability, glossiness and tables to wicker
Face smoothness carries out measurement of comparison and draws following data：
| Classification | Storage time | Pliability | Glossiness | Surface flatness |
| Numerical value | 3-5 | It is very soft | 80-90% | Light |
Carrying out immersion to wicker using soak in above-mentioned technical process effectively can help wicker to soften, and then promote willow
The sizing of bar, is that the straightening in later stage plays good facilitation, by the effects such as the softening of soak and effect can be willow
Good booster action is played in bar following process and operation, and medium is served as using emery dust while polishing in addition wicker, can be with
Wicker surface is formed cut and gully when polishing, so contribute to crystal powder to exist when the later stage is using crystal powder
Attachment on wicker, makes it produce protecting film after uniform attachment by painting to fix it, is then protected by sterilizing and sealing
Deposit, can effectively extend the storage time of wicker prevents from damaging by worms, the light of wicker is caused in the presence of crystal powder and celluloid paint
Damp degree is more beautiful, and will not be over time extension and become intensely dark, effectively improve the retention time of glossiness；
The beneficial effects of the invention are as follows：The lifting of glossiness, the process processed in early stage to wicker can be carried out to wicker
In technology processing is carried out to wicker, effectively protect the product tool that the integrality and aesthetic property on wicker surface be woven into the later stage
There is the lifting effect of good glossiness.
Embodiment：
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific example is closed, the present invention is expanded on further.
Embodiment 1：
A kind of process for the glossiness for improving the wicker woven for wicker plaiting article, comprises the following steps：
(1) the straight and upright wicker without bending and without stammerer is selected, it is polished, polished, is used during polishing
The sand paper of 60 mesh is polished for the first time, is eliminated flash, is then fed into polishing machine and is polished；
(2) wicker after polishing is put into soaking box and soaked, immersion is using the leaching allocated exclusively for wicker
Liquid is steeped, after wicker is submerged in soak completely, the soak in soaking box is heated up, until temperature rises to 40 DEG C
When stop heating, and keep constant temperature 40 minutes；
(3) wicker is sent in dryer after soaking and dried for the first time, dryer fire box temperature is set as 60 DEG C, baking
The dry time is 20 minutes, and wicker is sent in gag press after first drying and carries out straightening, secondary drying is then carried out again, secondary
The temperature of drying is identical with first drying temperature, and drying time is 35 minutes；
(4) wicker is sent in sander after drying and polished, medium is served as using the emery dust of 500 mesh during polishing,
Polishing enables to wicker surface to produce tiny cut and groove, is that next process is prepared；
(5) wicker polished is put into progress rolling mixing in roller together with crystal powder, then used wicker
Pressing plate is rolled, and wicker is uniformly rolled under pressing plate, crystal powder is uniformly penetrated into the cut and ditch on wicker surface
In groove, crystal powder passes through sterilization processing, opens the spreading for cooling that crystal powder is uniformly divided during sterilization, is sent in ultraviolet room and is killed
Bacterium；
(6) wicker after rolling is sent to paint locker and carries out japanning, wicker is protected using the paint of white clear
By wicker dry for standby after the completion of the coating of cuticula, japanning；
(7) wicker is sent in ultraviolet sterilization room after wicker drying and sterilized, will be single with preservative film after sterilization
Wicker tightly wraps up and does encapsulation process；
(8) wicker after sealing is sent to after being refrigerated 10 hours in refrigerating chamber and taken out；
(9) wicker after taking out can be transported into warehouse storage or directly carry out braiding and use；
The soak wherein used in step (2) is calculated according to the mass fraction, has following components to be prepared from：Hydrogen peroxide
60%th, nonionic surfactant 3%, anion surfactant 3%, softening agent 5%, boric acid 6%, aliphatic acid 10%, second
Alcohol 15%, silica 4%；
After above-mentioned soak in the preparation uniformly mixes each component, 8 minutes are at the uniform velocity stirred using centrifugal blender, then
It is sent in heating furnace and heats, stop heating when being warming up to 90 DEG C, and allow its natural cooling, is poured into soaking box after cooling
Exercise and use；
Embodiment 2：
A kind of process for the glossiness for improving the wicker woven for wicker plaiting article, comprises the following steps：
(1) the straight and upright wicker without bending and without stammerer is selected, it is polished, polished, is used during polishing
The sand paper of 60 mesh is polished for the first time, is eliminated flash, is then fed into polishing machine and is polished；
(2) wicker after polishing is put into soaking box and soaked, immersion is using the leaching allocated exclusively for wicker
Liquid is steeped, after wicker is submerged in soak completely, the soak in soaking box is heated up, until temperature rises to 60 DEG C
When stop heating, and keep constant temperature 30 minutes；
(3) wicker is sent in dryer after soaking and dried for the first time, dryer fire box temperature is set as 75 DEG C, baking
The dry time is 20 minutes, and wicker is sent in gag press after first drying and carries out straightening, secondary drying is then carried out again, secondary
The temperature of drying is identical with first drying temperature, and drying time is 30 minutes；
(4) wicker is sent in sander after drying and polished, medium is served as using the emery dust of 600 mesh during polishing,
Polishing enables to wicker surface to produce tiny cut and groove, is that next process is prepared；
(5) wicker polished is put into progress rolling mixing in roller together with crystal powder, then used wicker
Pressing plate is rolled, and wicker is uniformly rolled under pressing plate, crystal powder is uniformly penetrated into the cut and ditch on wicker surface
In groove, crystal powder passes through sterilization processing, opens the spreading for cooling that crystal powder is uniformly divided during sterilization, is sent in ultraviolet room and is killed
Bacterium；
(6) wicker after rolling is sent to paint locker and carries out japanning, wicker is protected using the paint of white clear
By wicker dry for standby after the completion of the coating of cuticula, japanning；
(7) wicker is sent in ultraviolet sterilization room after wicker drying and sterilized, will be single with preservative film after sterilization
Wicker tightly wraps up and does encapsulation process；
(8) wicker after sealing is sent to after being refrigerated 10 hours in refrigerating chamber and taken out；
(9) wicker after taking out can be transported into warehouse storage or directly carry out braiding and use；
The soak wherein used in step (2) is calculated according to the mass fraction, has following components to be prepared from：Hydrogen peroxide
65%th, nonionic surfactant 5%, anion surfactant 5%, softening agent 8%, boric acid 10%, aliphatic acid 20%, second
Alcohol 15%, silica 8%；
After above-mentioned soak in the preparation uniformly mixes each component, 8 minutes are at the uniform velocity stirred using centrifugal blender, then
It is sent in heating furnace and heats, stop heating when being warming up to 90 DEG C, and allow its natural cooling, is poured into soaking box after cooling
Exercise and use；
Embodiment 3：
A kind of process for the glossiness for improving the wicker woven for wicker plaiting article, comprises the following steps：
(1) the straight and upright wicker without bending and without stammerer is selected, it is polished, polished, is used during polishing
The sand paper of 60 mesh is polished for the first time, is eliminated flash, is then fed into polishing machine and is polished；
(2) wicker after polishing is put into soaking box and soaked, immersion is using the leaching allocated exclusively for wicker
Liquid is steeped, after wicker is submerged in soak completely, the soak in soaking box is heated up, until temperature rises to 50 DEG C
When stop heating, and keep constant temperature 35 minutes；
(3) wicker is sent in dryer after soaking and dried for the first time, dryer fire box temperature is set as 70 DEG C, baking
The dry time is 20 minutes, and wicker is sent in gag press after first drying and carries out straightening, secondary drying is then carried out again, secondary
The temperature of drying is identical with first drying temperature, and drying time is 33 minutes；
(4) wicker is sent in sander after drying and polished, medium is served as using the emery dust of 550 mesh during polishing,
Polishing enables to wicker surface to produce tiny cut and groove, is that next process is prepared；
(5) wicker polished is put into progress rolling mixing in roller together with crystal powder, then used wicker
Pressing plate is rolled, and wicker is uniformly rolled under pressing plate, crystal powder is uniformly penetrated into the cut and ditch on wicker surface
In groove, crystal powder passes through sterilization processing, opens the spreading for cooling that crystal powder is uniformly divided during sterilization, is sent in ultraviolet room and is killed
Bacterium；
(6) wicker after rolling is sent to paint locker and carries out japanning, wicker is protected using the paint of white clear
By wicker dry for standby after the completion of the coating of cuticula, japanning；
(7) wicker is sent in ultraviolet sterilization room after wicker drying and sterilized, will be single with preservative film after sterilization
Wicker tightly wraps up and does encapsulation process；
(8) wicker after sealing is sent to after being refrigerated 11 hours in refrigerating chamber and taken out；
(9) wicker after taking out can be transported into warehouse storage or directly carry out braiding and use；
The soak wherein used in step (2) is calculated according to the mass fraction, has following components to be prepared from：Hydrogen peroxide
63%th, nonionic surfactant 5%, anion surfactant 3%, softening agent 8%, boric acid 6%, aliphatic acid 15%, second
Alcohol 13%, silica 8%；
After above-mentioned soak in the preparation uniformly mixes each component, 6 minutes are at the uniform velocity stirred using centrifugal blender, then
It is sent in heating furnace and heats, stop heating when being warming up to 90 DEG C, and allow its natural cooling, is poured into soaking box after cooling
Exercise and use；
Comparative example 1：
(1) the straight and upright wicker without bending and without stammerer is selected, it is polished, polished, flash is eliminated, is then fed into
It is polished in polishing machine；
(2) wicker after polishing is sent to paint locker and carries out japanning, wicker is protected using the paint of white clear
By wicker dry for standby after the completion of the coating of cuticula, japanning；
(3) take the wicker after japanning to be transported into warehouse storage or directly carry out braiding to use；
Following record is drawn by the comparative experimental data respectively of above-mentioned comparative example and embodiment 1,2,3：
| Storage time | Pliability | Glossiness | |
| Embodiment 1 | 5 years | It is very soft | 85% |
| Embodiment 2 | 4 years | It is very soft | 88% |
| Embodiment 3 | 5 years | It is very soft | 90% |
| Comparative example 1 | 3 years | It is soft | 10 |
It is not difficult to find out embodiment 1,2,3 compared to comparative example in storage time and pliability and glossiness from upper table
There is obvious advantage, this has also more confirmed the present invention can carry out the lifting of glossiness to wicker, and wicker is added in early stage
Technology processing is carried out to wicker during work, effectively protects the integrality and aesthetic property on wicker surface to be woven into the later stage
Product there is the lifting effect of good glossiness.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (4)
1. a kind of process for the glossiness for improving the wicker woven for wicker plaiting article, it is characterised in that：Comprise the following steps：
(1) the straight and upright wicker without bending and without stammerer is selected, it is polished, polished, 60 mesh are used during polishing
Sand paper polished for the first time, eliminate flash, be then fed into polishing machine and be polished；
(2) wicker after polishing is put into soaking box and soaked, immersion uses the soak allocated exclusively for wicker,
After wicker is submerged in soak completely, the soak in soaking box is heated up, until when temperature rises to 40-60 DEG C
Stop heating, and keep constant temperature 30-40 minutes；
(3) wicker is sent in dryer after soaking and dried for the first time, dryer fire box temperature is set as 60-75 DEG C, baking
The dry time is 20 minutes, and wicker is sent in gag press after first drying and carries out straightening, secondary drying is then carried out again, secondary
The temperature of drying is identical with first drying temperature, and drying time is 30-35 minutes；
(4) wicker is sent in sander after drying and polished, Jie is served as using the emery dust of the mesh of 500 mesh -600 during polishing
Matter, polishing enables to wicker surface to produce tiny cut and groove, is that next process is prepared；
(5) wicker polished is put into progress rolling mixing in roller together with crystal powder, wicker is then used into pressing plate
Rolled, wicker is uniformly rolled under pressing plate, crystal powder is uniformly penetrated into the cut and groove on wicker surface；
(6) wicker after rolling is sent to paint locker and carries out japanning, diaphragm is carried out to wicker using the paint of white clear
Coating, by wicker dry for standby after the completion of japanning；
(7) wicker is sent in ultraviolet sterilization room sterilized after wicker drying, with preservative film by single wicker after sterilization
Tightly wrap up and do encapsulation process；
(8) wicker after sealing is sent to after being refrigerated 10-12 hours in refrigerating chamber and taken out；
(9) wicker after taking out can be transported into warehouse storage or directly carry out braiding and use；
The soak used in above-mentioned steps (2) is prepared from the following components：
Hydrogen peroxide, nonionic surfactant, anion surfactant, softening agent, boric acid, aliphatic acid, ethanol, titanium dioxide
Silicon.
2. a kind of process of glossiness for improving the wicker woven for wicker plaiting article according to claim 1, its feature
It is：The soak is calculated according to the mass fraction, and the mass fraction of each component is：Hydrogen peroxide 60-65%, non-ionic surface active
Agent 3-5%, anion surfactant 3-5%, softening agent 5-8%, boric acid 6-10%, aliphatic acid 10-20%, ethanol 10-
15%th, silica 4-8%.
3. a kind of process of glossiness for improving the wicker woven for wicker plaiting article according to claim 2, its feature
It is：After soak in the preparation uniformly mixes each component, at the uniform velocity stirred 5-8 minutes, be then fed into using centrifugal blender
Heated into heating furnace, stop heating when being warming up to 90 DEG C, and allow its natural cooling, be poured into soaking box to enter to exercise after cooling
With.
4. a kind of process of glossiness for improving the wicker woven for wicker plaiting article according to claim 1, its feature
It is：The crystal powder used in step (5) passes through sterilization processing, opens the spreading for cooling that crystal powder is uniformly divided during sterilization, is sent to
Ultraviolet is sterilized in room.