CN105437337A - Smoothness and toughness pre-treating agent for braiding wicker and preparation method thereof - Google Patents
Smoothness and toughness pre-treating agent for braiding wicker and preparation method thereof Download PDFInfo
- Publication number
- CN105437337A CN105437337A CN201510738921.2A CN201510738921A CN105437337A CN 105437337 A CN105437337 A CN 105437337A CN 201510738921 A CN201510738921 A CN 201510738921A CN 105437337 A CN105437337 A CN 105437337A
- Authority
- CN
- China
- Prior art keywords
- wicker
- toughness
- smoothness
- treating agent
- braiding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of modification of braiding wicker, in particular to a smoothness and toughness pre-treating agent for braiding wicker and a preparation method thereof. The raw materials of the smoothness and toughness pre-treating agent for the braiding wicker comprise, by weight, 0.01-0.02 part of borax, 10-12 parts of silica sol with the solid content of 20-25%, 1-2 parts of starch ether, 6-8 parts of clarification limewater, 0.2-0.3 part of secondary alkyl sodium sulfonate, 0.01-0.02 part of sodium hyaluronate and 40-50 parts of water. The smoothness and toughness pre-treating agent has good permeability and is seeped into wicker fibers through high pressure when used, the clarification limewater can assist the silica sol, the starch ether and other components in adhering to plant fibers, and therefore the strength and toughness of the wicker are increased more efficiently, and the braiding performance is improved. In combination with other components, the wicker treated through the smoothness and toughness pre-treating agent is antimicrobial, resistant to corrosion and smooth and holds water, and wickerwork is longer is service life, higher in skin-friendly sense, higher in weight bearing capacity and wider in use range.
Description
Technical field
The present invention relates to wicker plaiting article wicker modification treatment technology field, be specifically related to a kind of smooth tough pretreating agent for wicker plaiting article wicker and preparation method thereof.
Background technology
Wicker plaiting article is one of folks of china traditional handicraft product, people are just as common daily utility in ancient times, until after 20th century decades just rise gradually, the also project becoming selected areas of China foreign exchange earning gradually, Anhui Province has become one of three large wicker plaiting article production bases, the whole nation.
Wicker is as the material of wicker plaiting article, and it is by novel design, can be woven into that various honesty is natural, handsome in appearance, the practical art product of Portable durable.Along with industry development, product is constantly brought forth new ideas, and the willow having more Nover practical attractive in appearance is presented in face of client.But, because wicker is pure natural plant fiber, not humidity and drying, causes mechanical property to reduce, fracture of easily going mouldy, and bearing capacity is poor, govern further developing of product, if carry out pretreatment to wicker before establishment, improve the adaptability of its environment to external world, improve mechanical property, obtaining wicker plaiting article product quality like this will significantly be improved.
Summary of the invention
The object of the invention is to provide a kind of smooth tough pretreating agent for wicker plaiting article wicker and preparation method thereof, and in order to improve the serviceability of wicker, reach the object improving knitting quality, to achieve these goals, the technical solution used in the present invention is as follows:
A kind of smooth tough pretreating agent for wicker plaiting article wicker, it is characterized in that, this inorganic agent is made up of the raw material of following weight portion: borax 0.01-0.02, solid content are Ludox 10-12, the starch ether 1-2 of 20-25%, clarification limewash 6-8, SAS 0.2-0.3, Sodium Hyaluronate 0.01-0.02, water 40-50.
For a preparation method for the smooth tough pretreating agent of wicker plaiting article wicker, it is characterized in that, the preparation method of this inorganic agent is:
(1) first borax, SAS are dropped in water, stir after material is dissolved completely, mixed solution is heated to 40-50 DEG C, then adds starch ether, be uniformly mixed 30-40min, gained solution for standby;
(2) clarification limewash is dropwise added in Ludox slowly, and constantly stir, after dropwising, the solution of mixed solution and step (1) gained and other residual components are mixed completely, obtain wicker pretreating agent.
Pretreating agent advantage prepared by the present invention is: preparation method is simple for this pretreating agent, composition environment-protecting asepsis, it has good permeability, high pressure is utilized to be penetrated in wicker fiber during use, clarification limewash energy auxiliary silicon colloidal sol, the compositions such as starch ether adhere to bonding in string, thus increase intensity and the toughness of wicker more efficiently, improve knitting property, again in conjunction with other composition, make the antibacterial corrosion resistant of wicker after inorganic agent process of the present invention, water conservation is smooth, the assembling-disassembling life-span is longer, pro-skin sense is strong, bearing capacity increases, widen the scope of application further.
Detailed description of the invention
Embodiment
The pretreating agent of the present embodiment is obtained by the raw material of following weight portion (kilogram): borax 0.01, solid content be 25% Ludox 10, starch ether 1.5, clarification limewash 7, SAS 0.3, Sodium Hyaluronate 0.02, water 45.
The preparation method of the present embodiment inorganic agent is:
(1) first borax, SAS are dropped in water, stir after material is dissolved completely, mixed solution is heated to 40-50 DEG C, then adds starch ether, be uniformly mixed 35min, gained solution for standby;
(2) clarification limewash is dropwise added in Ludox slowly, and constantly stir, after dropwising, the solution of mixed solution and step (1) gained and other residual components are mixed completely, obtain wicker pretreating agent.
The compression strength of passing through the untreated wicker of comparatively same batch of the wicker that this pre-treatment treatment is crossed on average improves 32%, and bending strength on average improves 35%, and surface is more smooth, and the product bearing capacity be woven on average improves 42%.
Claims (2)
1. the smooth tough pretreating agent for wicker plaiting article wicker, it is characterized in that, this inorganic agent is made up of the raw material of following weight portion: borax 0.01-0.02, solid content are Ludox 10-12, the starch ether 1-2 of 20-25%, clarification limewash 6-8, SAS 0.2-0.3, Sodium Hyaluronate 0.01-0.02, water 40-50.
2. the preparation method of a kind of smooth tough pretreating agent for wicker plaiting article wicker as claimed in claim 1, it is characterized in that, described preparation method is:
(1) first borax, SAS are dropped in water, stir after material is dissolved completely, mixed solution is heated to 40-50 DEG C, then adds starch ether, be uniformly mixed 30-40min, gained solution for standby;
(2) clarification limewash is dropwise added in Ludox slowly, and constantly stir, after dropwising, the solution of mixed solution and step (1) gained and other residual components are mixed completely, obtain wicker pretreating agent.