CN106272822A - A kind of inorganic agent improving rattan toughness - Google Patents

A kind of inorganic agent improving rattan toughness Download PDF

Info

Publication number
CN106272822A
CN106272822A CN201610845431.7A CN201610845431A CN106272822A CN 106272822 A CN106272822 A CN 106272822A CN 201610845431 A CN201610845431 A CN 201610845431A CN 106272822 A CN106272822 A CN 106272822A
Authority
CN
China
Prior art keywords
rattan
parts
inorganic agent
toughness
soak
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610845431.7A
Other languages
Chinese (zh)
Inventor
宋迎楼
宋运宁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI HONGRUN ARTS AND CRAFTS Co Ltd
Original Assignee
ANHUI HONGRUN ARTS AND CRAFTS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI HONGRUN ARTS AND CRAFTS Co Ltd filed Critical ANHUI HONGRUN ARTS AND CRAFTS Co Ltd
Priority to CN201610845431.7A priority Critical patent/CN106272822A/en
Publication of CN106272822A publication Critical patent/CN106272822A/en
Pending legal-status Critical Current

Abstract

The invention belongs to the processing technique field of braiding rattan, be specifically related to a kind of inorganic agent improving rattan toughness, by water, tert-butylbenzene formic acid, acetanilide, Herba Abutili kind oil, dimethylphosphite, sodium sulfonate, hexakis(hydroxymethyl)melamine pregnancy ether, auxiliary agent.The present invention has the advantage that in the present invention, auxiliary agent has the effect of mildew-resistant, sterilization compared to existing technology; different pressure is utilized to change in immersion process; accelerate medicament to penetrate into; make the lignin Fast Stripping within rattan simultaneously; enable inorganic agent by the capillary tube entrance internal action of rattan surface fiber in rattan center, protect carbohydrate, improve the toughness of rattan; improve the stitchability of rattan, it is adaptable to the product higher to rattan toughness reguirements.

Description

A kind of inorganic agent improving rattan toughness
Technical field
The invention belongs to the processing technique field of braiding rattan, be specifically related to a kind of inorganic agent improving rattan toughness.
Background technology
Rattan is the liana that a kind of strong but pliable in texture, figure is extremely grown, and rattan crust is bright in luster, and feel smooths, elastic Splendid, like the thin bamboo strip rather than the thin bamboo strip, it is natural braided material, can be used for working out the daily apparatus such as rattan chair, rattan case, due to rattan-weaved products Diversified development, rattan woven furniture has been used not only for the simple furniture such as rattan table, rattan chair, has gradually been used in exquisiter, artistic The higher rattan of property is expensive, in rattan bed lamp or the relative complex furniture of other outward appearances, existing rattan teaching aid can be original processed Through a series for the treatment of process such as steaming and decocting, dry, drift color, mildew-resistant, sterilizations in journey, to strengthen the serviceability of rattan, but These processing methods cannot ensure the goods that rattan weaving is more complicated, accordingly, it would be desirable to carry out the toughness strengthening rattan further Research.
Summary of the invention
It is an object of the invention to for existing problem, it is provided that a kind of.
The present invention is achieved by the following technical solutions: a kind of inorganic agent improving rattan toughness, by following weight portion Preparation of raw material form: 100 parts of water, tert-butylbenzene formic acid 2-4 part, acetanilide 0.5-0.7 part, Herba Abutili kind oil 1-3 part, phosphorous Dimethyl phthalate 1-2 part, sodium sulfonate 0.1-0.3 part, hexakis(hydroxymethyl)melamine pregnancy ether 0.1-0.2 part, auxiliary agent 2-3 part；
Wherein, auxiliary agent is made up of the raw material of following weight portion: Herba Ranunculi Japonici 10 parts, Radix Aconiti Brachypodi (Radix Aconiti Szechenyiani) 8 parts, Radix Clematidis 4 parts, Cortex Magnoliae Officinalis 5 parts, Caulis Piperis Kadsurae 2 parts, Fructus Toosendan 8 parts, Lagotis clarkei Hook. F (Lagotis brevituba Maxim.) 2 parts；
Its compound method is: after heating the water to 55-65 DEG C, adds sodium sulfonate, hexakis(hydroxymethyl)melamine pregnancy ether and helps Agent, after dispersion is stirred 15-20 minute, is cooled to 30-35 DEG C, adds surplus stock, dispersion stirring 1.5-2 hour, to obtain final product.
As further improvement of these options, the preparation method of described auxiliary agent is: use phase after being mixed by described raw material When in the soak by water of its weight 3-4 times, decocting time is 2-3 hour, in decoction process, stirring in every 10 minutes once, is stirred every time 20 seconds；Decoct five times, collect filtrate and merge, be concentrated into 1st/20th of original volume and get final product.
As further improvement of these options, the using method of described inorganic agent is: immersed in inorganic agent by rattan After, under conditions of negative pressure 0.16-0.18MPa, soak 1-2 hour；Then, under conditions of being forced into 1.4-1.5MPa, soak 25-30 minute；Recover Dipping 30-40 minute, repressurization to 1.2-1.3MPa, soak 1-1.5 hour.
As further improvement of these options, described rattan is being 35-40% with inorganic agent water content before treatment.
As further improvement of these options, the rattan after described process needs to use in 5 hours after treatment.
The present invention has the advantage that in the present invention, auxiliary agent has the effect of mildew-resistant, sterilization compared to existing technology, is soaking During utilize different pressure to change, accelerate medicament penetrate into, make the lignin Fast Stripping within rattan simultaneously, make inorganic agent energy Enough by the capillary tube entrance internal action of rattan surface fiber in rattan center, protect carbohydrate, improve the tough of rattan Property, improve the stitchability of rattan, it is adaptable to the product higher to rattan toughness reguirements.
Detailed description of the invention
Embodiment 1
A kind of inorganic agent improving rattan toughness, is formed by the preparation of raw material of following weight portion: 100 parts of water, tert-butylbenzene formic acid 2 Part, acetanilide 0.6 part, Herba Abutili kind oil 3 parts, dimethylphosphite 2 parts, sodium sulfonate 0.2 part, hexakis(hydroxymethyl)melamine six Methyl ether 0.2 part, auxiliary agent 3 parts；
Wherein, auxiliary agent is made up of the raw material of following weight portion: Herba Ranunculi Japonici 10 parts, Radix Aconiti Brachypodi (Radix Aconiti Szechenyiani) 8 parts, Radix Clematidis 4 parts, Cortex Magnoliae Officinalis 5 parts, Caulis Piperis Kadsurae 2 parts, Fructus Toosendan 8 parts, Lagotis clarkei Hook. F (Lagotis brevituba Maxim.) 2 parts；
Its compound method is: after heating the water to 55 DEG C, adds sodium sulfonate, hexakis(hydroxymethyl)melamine pregnancy ether and auxiliary agent, After dispersion stirring 20 minutes, it is cooled to 32 DEG C, adds surplus stock, dispersion stirring 1.5 hours, to obtain final product.
Wherein, the preparation method of described auxiliary agent is: use the soak by water being equivalent to its weight 3 times after being mixed by described raw material, Decocting time is 2 hours, and in decoction process, stirring in every 10 minutes is once, stirring 20 seconds every time；Decoct five times, collect filtrate and close And, it is concentrated into 1st/20th of original volume and get final product.
Wherein, the using method of described inorganic agent is: be after 40% rattan immerses in inorganic agent by water content, in negative pressure Under conditions of 0.18MPa, soak 2 hours；Then, under conditions of being forced into 1.5MPa, soak 28 minutes；Recover Dipping 40 Minute, repressurization to 1.3MPa, soak 1.5 hours.
Wherein, the rattan after described process needs to use in 5 hours after treatment.
Embodiment 2
A kind of inorganic agent improving rattan toughness, is formed by the preparation of raw material of following weight portion: 100 parts of water, tert-butylbenzene formic acid 3 Part, acetanilide 0.5 part, Herba Abutili kind oil 2 parts, dimethylphosphite 2 parts, sodium sulfonate 0.3 part, hexakis(hydroxymethyl)melamine six Methyl ether 0.2 part, auxiliary agent 2 parts；
Wherein, auxiliary agent is made up of the raw material of following weight portion: Herba Ranunculi Japonici 10 parts, Radix Aconiti Brachypodi (Radix Aconiti Szechenyiani) 8 parts, Radix Clematidis 4 parts, Cortex Magnoliae Officinalis 5 parts, Caulis Piperis Kadsurae 2 parts, Fructus Toosendan 8 parts, Lagotis clarkei Hook. F (Lagotis brevituba Maxim.) 2 parts；
Its compound method is: after heating the water to 60 DEG C, adds sodium sulfonate, hexakis(hydroxymethyl)melamine pregnancy ether and auxiliary agent, After dispersion stirring 18 minutes, it is cooled to 35 DEG C, adds surplus stock, dispersion stirring 2 hours, to obtain final product.
The using method of the preparation method of its auxiliary agent, the using method of inorganic agent and rattan is same as in Example 1.
Embodiment 3
A kind of inorganic agent improving rattan toughness, is formed by the preparation of raw material of following weight portion: 100 parts of water, tert-butylbenzene formic acid 4 Part, acetanilide 0.7 part, Herba Abutili kind oil 3 parts, dimethylphosphite 1 part, sodium sulfonate 0.2 part, hexakis(hydroxymethyl)melamine six Methyl ether 0.1 part, auxiliary agent 3 parts；
Wherein, auxiliary agent is made up of the raw material of following weight portion: Herba Ranunculi Japonici 10 parts, Radix Aconiti Brachypodi (Radix Aconiti Szechenyiani) 8 parts, Radix Clematidis 4 parts, Cortex Magnoliae Officinalis 5 parts, Caulis Piperis Kadsurae 2 parts, Fructus Toosendan 8 parts, Lagotis clarkei Hook. F (Lagotis brevituba Maxim.) 2 parts；
Its compound method is: after heating the water to 65 DEG C, adds sodium sulfonate, hexakis(hydroxymethyl)melamine pregnancy ether and auxiliary agent, After dispersion stirring 20 minutes, it is cooled to 30 DEG C, adds surplus stock, dispersion stirring 1.5 hours, to obtain final product.
The using method of the preparation method of its auxiliary agent, the using method of inorganic agent and rattan is same as in Example 1.
Matched group 1 is set, uses clear water commonsense method to soak；Matched group 2 is set, uses method in the clear water present invention Soak；Matched group 3 is set, uses softening agent commonsense method in the present invention to soak；Wherein commonsense method is that directly immersion 12 is little Time.
The Vitex chinensis Mill. after processing each group rate that fractures during braiding all compares with matched group 1, matched group 2 comparison Reducing 5.8% according to group 1, mildew-resistant simultaneously, vermins-proof effect have certain reduction than matched group 1；Matched group 3 reduces than matched group 1 4.2%, its mildew-resistant, vermins-proof effect improve than matched group 1；Embodiment 1 reduces 14.2% than matched group 1, its mildew-resistant, anti- Worm effect is significantly improved than matched group 3；Embodiment 2 reduces 14.6% than matched group 1, and its mildew-resistant, vermins-proof effect compare matched group 3 are significantly improved；3 classes of matched groups 1 of embodiment reduce 14.3%, and its mildew-resistant, vermins-proof effect are significantly improved than matched group 3；Say The rate that fractures when softening agent can be substantially reduced braiding with the use of method in the bright present invention, improves the profit of Vitex chinensis Mill. under the same terms By rate, the processing method of this inorganic agent can strengthen the mildew-resistant of rattan, vermins-proof effect simultaneously, has stronger dissemination.

Claims (5)

1. the inorganic agent improving rattan toughness, it is characterised in that formed by the preparation of raw material of following weight portion: 100 parts of water, Tert-butylbenzene formic acid 2-4 part, acetanilide 0.5-0.7 part, Herba Abutili kind oil 1-3 part, dimethylphosphite 1-2 part, sodium sulfonate 0.1-0.3 part, hexakis(hydroxymethyl)melamine pregnancy ether 0.1-0.2 part, auxiliary agent 2-3 part；
Wherein, auxiliary agent is made up of the raw material of following weight portion: Herba Ranunculi Japonici 10 parts, Radix Aconiti Brachypodi (Radix Aconiti Szechenyiani) 8 parts, Radix Clematidis 4 parts, Cortex Magnoliae Officinalis 5 parts, Caulis Piperis Kadsurae 2 parts, Fructus Toosendan 8 parts, Lagotis clarkei Hook. F (Lagotis brevituba Maxim.) 2 parts；
Its compound method is: after heating the water to 55-65 DEG C, adds sodium sulfonate, hexakis(hydroxymethyl)melamine pregnancy ether and helps Agent, after dispersion is stirred 15-20 minute, is cooled to 30-35 DEG C, adds surplus stock, dispersion stirring 1.5-2 hour, to obtain final product.
A kind of inorganic agent improving rattan toughness the most as claimed in claim 1, it is characterised in that the preparation method of described auxiliary agent It is: using the soak by water being equivalent to its weight 3-4 times after being mixed by described raw material, decocting time is 2-3 hour, every in decoction process Stirring in 10 minutes once, is stirred 20 seconds every time；Decocting five times, collect filtrate and merge, being concentrated into 1st/20th of original volume is ?.
A kind of inorganic agent improving rattan toughness the most as claimed in claim 2, it is characterised in that the using method of described inorganic agent For: after rattan is immersed in inorganic agent, under conditions of negative pressure 0.16-0.18MPa, soak 1-2 hour；Then 1.4-it is forced into Under conditions of 1.5MPa, soak 25-30 minute；Recover Dipping 30-40 minute, repressurization to 1.2-1.3MPa, soak 1-1.5 hour.
A kind of inorganic agent improving rattan toughness the most as claimed in claim 3, it is characterised in that described rattan is being used at inorganic agent Water content before reason is 35-40%.
A kind of inorganic agent improving rattan toughness the most as claimed in claim 3, it is characterised in that the rattan after described process needs Use in 5 hours after treatment.
CN201610845431.7A 2016-09-24 2016-09-24 A kind of inorganic agent improving rattan toughness Pending CN106272822A (en)