CN106116150A - 一种陶瓷釉料及其制备方法 - Google Patents
一种陶瓷釉料及其制备方法 Download PDFInfo
- Publication number
- CN106116150A CN106116150A CN201610499440.5A CN201610499440A CN106116150A CN 106116150 A CN106116150 A CN 106116150A CN 201610499440 A CN201610499440 A CN 201610499440A CN 106116150 A CN106116150 A CN 106116150A
- Authority
- CN
- China
- Prior art keywords
- parts
- calcium
- ceramic glaze
- graphite
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种陶瓷釉料，由以下按照重量份数的原料组成：氧化锌2‑10份，萤石粉3‑9份，粉煤灰2‑8份，二氧化钛3‑13份，苏州土1‑7份，白云石2‑8份，冰晶石3‑9份，碳酸氢钙2‑10份，玻璃粉3‑13份，石墨5‑15份，氧化钙3‑13份。本发明具有硬度高和光泽度高等优点。
Description
技术领域
本发明涉及一种釉料的加工方法，尤其涉及一种陶瓷釉料及其制备方法。
背景技术
目前，随着科学技术的发展，工业以及陶瓷等领域也在快速发展，而且陶瓷的制品中，陶瓷釉料对陶瓷的制品有着重要的影响，直接觉得了陶瓷的美观程度，但是现有的陶瓷釉料因其加工过程不合理或材质选择等问题，导致陶瓷制品表面的釉料存在气泡或光泽度差等缺点，从而导致陶瓷制品不能够达到人们的需求。
发明内容
为了克服上述现有技术的缺陷，本发明的目的是提供一种陶瓷釉料及其制备方法。
本发明是采取以下技术方案来实现的：一种陶瓷釉料，由以下按照重量份数的原料组成：氧化锌2-10份，萤石粉3-9份，粉煤灰2-8份，二氧化钛3-13份，苏州土1-7份，白云石2-8份，冰晶石3-9份，碳酸氢钙2-10份，玻璃粉3-13份，石墨5-15份，氧化钙3-13份。
上述的一种陶瓷釉料，由以下按照重量份的原料组成：氧化锌2-8份，萤石粉3-7份，粉煤灰2-6份，二氧化钛3-11份，苏州土1-5份，白云石2-6份，冰晶石3-7份，碳酸氢钙2-8份，玻璃粉3-11份，石墨5-13份，氧化钙3-11份。
上述的一种陶瓷釉料，由以下按照重量份的原料组成：氧化锌6份，萤石粉6份，粉煤灰5份，二氧化钛8份，苏州土4份，白云石5份，冰晶石6份，碳酸氢钙6份，玻璃粉8份，石墨10份，氧化钙8份。
上述的一种陶瓷釉料的制备方法，由以下步骤组成：
（1）选取权利要求3中的物料的份数，将氧化锌、萤石粉、粉煤灰、二氧化钛、苏州土、白云石、冰晶石和石墨进行粉碎处理，粉碎时间为20min，然后使其通过200目的网筛进行筛分处理，得到混料A；
（2）将碳酸氢钙、玻璃粉和氧化钙进行搅拌处理，使其充分的搅拌混合，并通过300目的网筛进行筛分，得到混料B；
（3）将混料A和混料B共同搅拌后，然后通过高温加热，且加热时间为30min，然后放入冷水中进行淬制，得到熔块；
（4）将步骤3中的熔块放置在球磨机中研磨成釉浆，即可得到所需材料。
综上所述本发明具有以下有益效果：本发明具有硬度高和光泽度高等优点，且可以有效的防止产生气泡等不良情况，使陶瓷的加工更加美观。
具体实施方式
一种陶瓷釉料，由以下按照重量份数的原料组成：氧化锌2-10份，萤石粉3-9份，粉煤灰2-8份，二氧化钛3-13份，苏州土1-7份，白云石2-8份，冰晶石3-9份，碳酸氢钙2-10份，玻璃粉3-13份，石墨5-15份，氧化钙3-13份。
上述的一种陶瓷釉料，由以下按照重量份的原料组成：氧化锌2-8份，萤石粉3-7份，粉煤灰2-6份，二氧化钛3-11份，苏州土1-5份，白云石2-6份，冰晶石3-7份，碳酸氢钙2-8份，玻璃粉3-11份，石墨5-13份，氧化钙3-11份。
上述的一种陶瓷釉料，由以下按照重量份的原料组成：氧化锌6份，萤石粉6份，粉煤灰5份，二氧化钛8份，苏州土4份，白云石5份，冰晶石6份，碳酸氢钙6份，玻璃粉8份，石墨10份，氧化钙8份。
上述的一种陶瓷釉料的制备方法，由以下步骤组成：
（1）选取权利要求3中的物料的份数，将氧化锌、萤石粉、粉煤灰、二氧化钛、苏州土、白云石、冰晶石和石墨进行粉碎处理，粉碎时间为20min，然后使其通过200目的网筛进行筛分处理，得到混料A；
（2）将碳酸氢钙、玻璃粉和氧化钙进行搅拌处理，使其充分的搅拌混合，并通过300目的网筛进行筛分，得到混料B；
（3）将混料A和混料B共同搅拌后，然后通过高温加热，且加热时间为30min，然后放入冷水中进行淬制，得到熔块；
（4）将步骤3中的熔块放置在球磨机中研磨成釉浆，即可得到所需材料。
本发明具有硬度高和光泽度高等优点，且可以有效的防止产生气泡等不良情况，使陶瓷的加工更加美观。
以上所述是本发明的实施例，故凡依本发明申请范围所述的构造、特征及原理所做的等效变化或修饰，均包括于本发明专利申请范围内。
Claims (4)
1.一种陶瓷釉料，其特征在于，由以下按照重量份数的原料组成：氧化锌2-10份，萤石粉3-9份，粉煤灰2-8份，二氧化钛3-13份，苏州土1-7份，白云石2-8份，冰晶石3-9份，碳酸氢钙2-10份，玻璃粉3-13份，石墨5-15份，氧化钙3-13份。
2.根据权利要求1所述的一种陶瓷釉料，其特征在于，由以下按照重量份的原料组成：氧化锌2-8份，萤石粉3-7份，粉煤灰2-6份，二氧化钛3-11份，苏州土1-5份，白云石2-6份，冰晶石3-7份，碳酸氢钙2-8份，玻璃粉3-11份，石墨5-13份，氧化钙3-11份。
3.根据权利要求1所述的一种陶瓷釉料，其特征在于，由以下按照重量份的原料组成：氧化锌6份，萤石粉6份，粉煤灰5份，二氧化钛8份，苏州土4份，白云石5份，冰晶石6份，碳酸氢钙6份，玻璃粉8份，石墨10份，氧化钙8份。
4.根据权利要求1所述的一种陶瓷釉料的制备方法，其特征在于，由以下步骤组成：
（1）选取权利要求3中的物料的份数，将氧化锌、萤石粉、粉煤灰、二氧化钛、苏州土、白云石、冰晶石和石墨进行粉碎处理，粉碎时间为20min，然后使其通过200目的网筛进行筛分处理，得到混料A；
（2）将碳酸氢钙、玻璃粉和氧化钙进行搅拌处理，使其充分的搅拌混合，并通过300目的网筛进行筛分，得到混料B；
（3）将混料A和混料B共同搅拌后，然后通过高温加热，且加热时间为30min，然后放入冷水中进行淬制，得到熔块；
（4）将步骤3中的熔块放置在球磨机中研磨成釉浆，即可得到所需材料。