CN106077428A - A kind of resin sand of instrument casting - Google Patents
A kind of resin sand of instrument casting Download PDFInfo
- Publication number
- CN106077428A CN106077428A CN201610609843.0A CN201610609843A CN106077428A CN 106077428 A CN106077428 A CN 106077428A CN 201610609843 A CN201610609843 A CN 201610609843A CN 106077428 A CN106077428 A CN 106077428A
- Authority
- CN
- China
- Prior art keywords
- parts
- sand
- casting
- resin
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The resin sand of a kind of instrument casting, it includes the raw material of following parts by weight: 100 parts of matrix sand material, epoxy resin 1 ~ 3 part, 0.2 ~ 1 part of firming agent, chlorinated paraffin 0.5 ~ 2 part, alkali-free glass fibre 1 ~ 4 part, modifying agent 10 ~ 20 parts;Described matrix sand material is quartz sand and CBN abrasive material, and its mass parts ratio is 1 ~ 3:1;Described modifying agent is one or more in Gypsum Fibrosum powder, calcium bicarbonate, kaolin powder, Pulvis Talci, hydroxylapatite powder.The resin sand sand mold intensity of a kind of instrument casting that the present invention prepares is high, dimensional discrepancy is little, collapsibility good, energy resource consumption is few, and the feature of environmental protection is excellent simultaneously, can be used for the production casting of various resin sand instrument foundry goods, and the surface quality of foundry goods and dimensional accuracy are high.
Description
Technical field
The present invention relates to a kind of resin casting technical field, be specifically related to the resin sand material of a kind of instrument casting
Material.
Background technology
Resin sand effect in Foundry Production is particularly important, and the casting wasted product caused because of the poor quality of resin sand is about
Account for the 30~50% of the total rejection number of foundry goods.Foundry Production generally requirement to resin sand is: have higher intensity and thermally-stabilised
Property, to bear the effect of various external force and high temperature;Good mobility, i.e. resin sand be sand grains under external force or action of gravity own
Between the ability that is mutually shifted;Certain plasticity, i.e. resin sand deform under external force, can keep being given after external force is removed
The ability of the shape given;Preferably breathability, i.e. resin sand hole are through the ability of gas;High knockability, also known as collapsibility,
I.e. after casting solidification, whether resin sand is easily destroyed, if the performance easily removed from foundry goods.
Casting resin sand used is required higher by instrument and equipment, and existing resin sand casting apparatus is at foundry production
In often there is various different casting flaw, such as crackle, pore, sand holes, shrinkage cavity etc., have impact on resin sand casting apparatus
Serviceability, and the generation of these defects and the caking property between foundry goods and casting resin sand, detachment are relevant, existing casting
Resin sand serviceability is poor, easily produces bonding with foundry goods, causes foundry goods to be not easily stripped, and cast breathability, plasticity
And mobility is bad, thus cause cast(ing) surface coarse so that Mechanical processing of casting percent defective is higher.
Summary of the invention
Not enough for prior art, the invention provides the instrument resin casting material of a kind of high-performance, high intensity.
The present invention solve above-mentioned technical problem use technical scheme be: a kind of instrument casting resin sand, including with
The raw material of lower parts by weight: 100 parts of matrix sand material, epoxy resin 1 ~ 3 part, 0.2 ~ 1 part of firming agent, chlorinated paraffin 0.5 ~ 2 part, nothing
Alkali containing glass fibre 1 ~ 4 part, modifying agent 10 ~ 20 parts;
Described matrix sand material is quartz sand and CBN abrasive material, and its mass parts ratio is 1 ~ 3:1;
Described modifying agent is one or more in Gypsum Fibrosum powder, calcium bicarbonate, kaolin powder, Pulvis Talci, hydroxylapatite powder.
Further, the resin sand of described a kind of instrument casting, including the raw material of following parts by weight: matrix sand material
100 parts, epoxy resin 2 parts, 0.5 part of firming agent, chlorinated paraffin 1 part, alkali-free glass fibre 2 parts, modifying agent 15 parts;Described base
Body sand material is quartz sand and CBN abrasive material, and its mass parts is than for 2:1;Described modifying agent be Gypsum Fibrosum powder, calcium bicarbonate Pulvis Talci and
Hydroxylapatite powder.
Further, the resin sand of described a kind of instrument casting, including the raw material of following parts by weight: matrix sand material
100 parts, epoxy resin 1 part, 0.2 part of firming agent, chlorinated paraffin 0.5 part, alkali-free glass fibre 1 part, modifying agent 10 parts;Described
Matrix sand material is quartz sand and CBN abrasive material, and its mass parts is than for 1:1;Described modifying agent is Gypsum Fibrosum powder and Pulvis Talci.
Further, the resin sand of described a kind of instrument casting, including the raw material of following parts by weight: matrix sand material
100 parts, epoxy resin 3 parts, 1 part of firming agent, chlorinated paraffin 2 parts, alkali-free glass fibre 4 parts, modifying agent 20 parts;Described matrix
Sand material is quartz sand and CBN abrasive material, and its mass parts is than for 3:1;Described modifying agent be Gypsum Fibrosum powder, calcium bicarbonate, kaolin powder,
Pulvis Talci and hydroxylapatite powder.
Compared with prior art, what the present invention possessed has the beneficial effect that
The resin sand sand mold intensity of a kind of instrument casting that the present invention prepares is high, dimensional discrepancy is little, collapsibility good, energy resource consumption
Few, use the matrix sand material feature of environmental protection excellent, concurrently facilitate the cost reducing resin sand;The resin sand of the present invention can be used for various
The production casting of resin sand instrument foundry goods, the surface quality of foundry goods and dimensional accuracy are high.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described further.
Embodiment 1: the resin sand of a kind of instrument casting, including the raw material of following parts by weight: 100 parts of matrix sand material,
Epoxy resin 2 parts, 0.5 part of firming agent, chlorinated paraffin 1 part, alkali-free glass fibre 2 parts, modifying agent 15 parts;Described matrix sand material
For quartz sand and CBN abrasive material, its mass parts is than for 2:1;Described modifying agent is Gypsum Fibrosum powder, calcium bicarbonate Pulvis Talci and hydroxyl phosphorus
Limestone flour.
Embodiment 2: the resin sand of a kind of instrument casting, including the raw material of following parts by weight: 100 parts of matrix sand material,
Epoxy resin 1 part, 0.2 part of firming agent, chlorinated paraffin 0.5 part, alkali-free glass fibre 1 part, modifying agent 10 parts;Described matrix sand
Material is for quartz sand and CBN abrasive material, and its mass parts ratio is for 1:1;Described modifying agent is Gypsum Fibrosum powder and Pulvis Talci.
Embodiment 3: the resin sand of a kind of instrument casting, including the raw material of following parts by weight: 100 parts of matrix sand material,
Epoxy resin 3 parts, 1 part of firming agent, chlorinated paraffin 2 parts, alkali-free glass fibre 4 parts, modifying agent 20 parts;Described matrix sand material is
Quartz sand and CBN abrasive material, its mass parts is than for 3:1;Described modifying agent is Gypsum Fibrosum powder, calcium bicarbonate, kaolin powder, Pulvis Talci
And hydroxylapatite powder.
Concrete, in use, it is on the waiting list raw material by described parts by weight, by described matrix sand material, modifying agent, solidification
Agent, chlorinated paraffin, alkali-free glass fibre, epoxy resin are blended in being sequentially added into continuous muller, obtain the resin of the present invention
Sand.
The above is only the preferred embodiment of the present invention, it is noted that for the common skill of the art
For art personnel, under the premise without departing from the principles of the invention, it is also possible to make some improvement and modification, these improve and modify
Also should be regarded as protection scope of the present invention.
Claims (4)
1. the resin sand of instrument casting, it is characterised in that include the raw material of following parts by weight: 100 parts of matrix sand material,
Epoxy resin 1 ~ 3 part, 0.2 ~ 1 part of firming agent, chlorinated paraffin 0.5 ~ 2 part, alkali-free glass fibre 1 ~ 4 part, modifying agent 10 ~ 20 parts;
Described matrix sand material is quartz sand and CBN abrasive material, and its mass parts ratio is 1 ~ 3:1;
Described modifying agent is one or more in Gypsum Fibrosum powder, calcium bicarbonate, kaolin powder, Pulvis Talci, hydroxylapatite powder.
The resin sand of a kind of instrument the most according to claim 1 casting, it is characterised in that include following parts by weight
Raw material: 100 parts of matrix sand material, epoxy resin 2 parts, 0.5 part of firming agent, chlorinated paraffin 1 part, alkali-free glass fibre 2 parts, modifying agent
15 parts;Described matrix sand material is quartz sand and CBN abrasive material, and its mass parts is than for 2:1;Described modifying agent is Gypsum Fibrosum powder, carbon
Acid hydrogen calcium Pulvis Talci and hydroxylapatite powder.
The resin sand of a kind of instrument the most according to claim 1 casting, it is characterised in that include following parts by weight
Raw material: 100 parts of matrix sand material, epoxy resin 1 part, 0.2 part of firming agent, chlorinated paraffin 0.5 part, alkali-free glass fibre 1 part, modification
Agent 10 parts;Described matrix sand material is quartz sand and CBN abrasive material, and its mass parts is than for 1:1;Described modifying agent be Gypsum Fibrosum powder and
Pulvis Talci.
The resin sand of a kind of instrument the most according to claim 1 casting, it is characterised in that include following parts by weight
Raw material: 100 parts of matrix sand material, epoxy resin 3 parts, 1 part of firming agent, chlorinated paraffin 2 parts, alkali-free glass fibre 4 parts, modifying agent 20
Part;Described matrix sand material is quartz sand and CBN abrasive material, and its mass parts is than for 3:1;Described modifying agent is Gypsum Fibrosum powder, carbonic acid
Hydrogen calcium, kaolin powder, Pulvis Talci and hydroxylapatite powder.